Mg-substituted ZnNb2O6-TiO2 composite ceramics for RF/microwaves ceramic capacitors

Microstructure and microwave dielectric properties of Mg-substituted ZnNb₂O₆-TiO₂ microwave ceramics were investigated. Mg acted as a grain refining reagent and columbite phase stabilization reagent. With an increasing Mg content, the amount of ixiolite (Zn, Mg) TiNb₂O₈ decreased, and the amount of (Zn_0.9Mg_0.1)_0.17Nb_0.33Ti_0.5O₂ and columbite increased. ZnO-Nb₂O₅-1.75TiO₂-5 mol.%MgO exhibited excellent dielectric properties (at 950 °C): ?_r = 35.6, Q × f = 16,000 GHz (at 5.6 GHz) and τ_f = −10 ppm/°C. The material was applied successfully to make RF/microwaves ceramic capacitor, whose self-resonance frequency was 19 GHz at low capacitance of 0.13 pF.