等离子喷涂 NiCr-Cr3C2基复合自润滑涂层的组织及摩擦学性能
引用本文:陈东,罗明波,陈晓琴,陈汉宾,张隆平.等离子喷涂 NiCr-Cr3C2基复合自润滑涂层的组织及摩擦学性能[J].表面技术,2013,42(3):52-55.
作者姓名:陈东  罗明波  陈晓琴  陈汉宾  张隆平
作者单位:总参陆航部驻成都地区军事代表室;西南技术工程研究所
摘    要:将NiCr-Cr3C2复合粉和Ni包MoS2粉按不同比例混合,制成三种喷涂粉末,采用等离子喷涂技术在304不锈钢表面制备复合自润滑涂层,并对涂层的物相组成、显微组织及摩擦磨损性能进行了研究。结果表明:三种涂层的物相组成相同,主相均为Cr7C3,Ni和MoS2;涂层与基体的结合为机械结合,孔隙率较低,表面有少量微裂纹;喷涂粉末中的Ni包MoS2粉偏少或偏多都会导致涂层的摩擦磨损性能变坏,Ni包MoS2粉质量分数为30%时,涂层的摩擦系数及磨损率最低,分别约为0.36和3.3×10-4mg/s。

关 键 词:等离子喷涂  自润滑涂层  显微形貌  摩擦磨损
收稿时间:1/7/2013 12:00:00 AM
修稿时间:2013/2/25 0:00:00

Microstructure and Frictional Behaviour of Plasma-sprayed NiCr-Cr3C2Based Self-lubricating Composite Coatings
CHEN Dong,LUO Ming-bo,CHEN Xiao-qin,CHEN Han-bin and ZHANG Long-ping.Microstructure and Frictional Behaviour of Plasma-sprayed NiCr-Cr3C2Based Self-lubricating Composite Coatings[J].Surface Technology,2013,42(3):52-55.
Authors:CHEN Dong  LUO Ming-bo  CHEN Xiao-qin  CHEN Han-bin and ZHANG Long-ping
Affiliation:1.Military Delegation Office for Chengdu Region,Army Aviation Department of General Staff,Chengdu 610036,China;2.Southwest Technology and Engineering Research Institute,Chongqing 400039,China)
Abstract:NiCr-Cr3C2based self-lubricating composite coatings of different content of cladded MoS2by Ni powder were deposited on 304 stainless steel by plasma spraying technology. The phase composition, microstructure and frictional behaviour of coatings were reasearched. The results indicate that the kinds of coatings have same phase composition, whch is Cr7C3, Ni and MoS2. Mechanical bonding forms between coating and substrate, the porosity of coatings is low, a small amount microcrack exsists on the surface of coatings. Excessive or scarce cotent of cladded MoS2by Ni powder in the coatings can induce worsening of frictional behaviour, the lowest value of friction coefficient and wear rate are separately 0 . 36 and 3 . 3 X10-4mg / s, which the content of cladded MoS2by Ni powder in the coatings is 30 % .
Keywords:plasma spraying  self-lubricating coatings  microstructure  friction and wear