Influences of processing parameters on microstructure during investment casting of nickel-base single crystal superalloy DD3
Authors:Gao Sifeng  Liu Lin  Xu Yiku  Yang Chubin  Zhang Jun  Fu Hengzhi
Affiliation:State Key Laboratory of Solidification Processing, Northwestern Polytechnic University, Xi'an 710072, China
Abstract:The effects of solidification variables on the as-cast microstructures of nickel-base single crystal superalloy DD3 have been investigated by using the modified Bridgman apparatus.The experiments were performed under a thermal gradient of approximately 45 K·cm-1 and at withdrawal rates ranging from 30 to 200 m·s-1.The experimental results show that the primary and secondary dendritic arm spacings(PDAS and SDAS) decrease when the withdrawal rate is increased.Compared with the theoretical models of PDAS,the results are in good agreement with Trivedi’s model.The relationships of PDAS and SDAS with withdrawal rates can be described as ? 1 =649.7V -0.24±0.02 and? 2 =281V -0.32±0.03 ,respectively.In addition,the size of theγ′phase significantly decreases with increasing withdrawal rate.
Keywords:Ni-base superalloys  directional solidification  γ′phase  dendritic spacing
本文献已被 CNKI 万方数据 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号