The evaluation of powder processing on microstructure and mechanical properties of hydroxyapatite (HA)/yttria stabilized zirconia (YSZ) composite coatings
a Department of Materials Science and Engineering, Northwestern University, Evanston, IL 60208, USA
b School of Mechanical and Production Engineering, Nanyang Technological University, Singapore 639798, Singapore
Abstract:
In clinical applications, the mechanical failure of HA-coated titanium alloy implants suffered at the interface of the HA coating and titanium alloy substrate will be a potential weakness in prosthesis. Yttria stabilized zirconia (YSZ) reinforced HA coatings have been proven to enhance the mechanical properties of the HA coating significantly and reduce the formation of calcium oxide (CaO). In this paper, HA/YSZ (30 wt.% YSZ) composite coatings were sprayed by the plasma technique. The effects of the powder processing–mechanical ball milling method and spheroidization method on the microstructure and mechanical properties of the HA/YSZ composite coatings were evaluated. The experimental results showed that the spheroidized powders melted better than the ball milled powders during plasma spraying and formed higher mechanical property coatings (1.6326±0.08 MPa m?0.5 of fracture toughness, 58.59±2.91 GPa of elastic modulus and 43.42±2.53 MPa of tensile bond strength). HA/YSZ solid solution formed during deposition on the substrate, which played a very important role in the mechanical properties of the HA/YSZ composite coatings. Tensile bond strength tests showed that the fracture mode was cohesive and that failure occurred at the interface of HA and unmelted YSZ particles. The molten state of YSZ had a great influence on the properties of the HA/YSZ composite coatings.