Structural evolution of mechanically alloyed Al-12Si/TiB2/h-BN composite powder coating by atmospheric plasma spraying |
|
| Authors: | Cagri Tekmen Ismail Ozdemir Yoshiki Tsunekawa |
| Affiliation: | a Toyota Technological Institute, Materials Processing Lab., 2-12-1, Hisakata Tempaku, Nagoya, 468-8511, Japan b Dokuz Eylul University, Metallurgical and Materials Engineering, Buca, Izmir, 35100, Turkey c Technische Universität Chemnitz, Fakultät für Maschinenbau, Lehrstuhl für Verbundwerkstoffe, Erfenschlager Str. 73, D-09125 Chemnitz, Germany |
| Abstract: | In the present study, mechanically alloyed Al-12Si/TiB2/h-BN composite powder was deposited onto an aluminum substrate by atmospheric plasma spraying. The effect of mechanical alloying (MA) and plasma spray parameters on composite powder and coating structure were investigated. It has been observed that the MA process has a significant effect on the composite powder morphology and reactivity between the selective powders. Results also demonstrate that, at relatively high milling time h-BN decomposes into B and N and forms a solid solution. Also, it has been found that, the relative amount of the in-situ formed AlN through the reaction between h-BN and Al and/or the decomposition of Al-B-N solid solution is independent from the plasma parameters (arc current and secondary gas flow rate). However, spray parameters remarkably affects the coating hardness due to coarsening of Si during the solidification of the coating. |
| Keywords: | Al-Si TiB2 h-BN Plasma spray Mechanical alloying |
| 本文献已被 ScienceDirect 等数据库收录！ | |