A new solid‐state mode of hot corrosion at temperatures below 700°C

Preliminary results on a single‐crystal nickel‐based superalloy indicated that hot corrosion can occur at temperatures as low as 550°C, where liquid formation, generally believed to be responsible for Type II hot corrosion, is not predicted. Additional tests were conducted on pure‐nickel samples at 650°C and below to more clearly elucidate the mechanism of this very low‐temperature hot corrosion. Environments in dry air and O₂‐(2.5, 10, 100, and 1000) ppm SO₂ were studied. Based on the results obtained, a solid‐state corrosion mechanism was inferred. The mechanism relies on the formation of a previously unreported compound phase, which was identified using transmission electron microscope analysis that indicated the stoichiometry of Na₂Ni₂SO₅. Furthermore, it was nanocrystalline in structure and metastable. It was deduced that the Na₂Ni₂SO₅ formation was responsible for the rapid nickel transport required for the observed accelerated corrosion process. Moreover, its eventual decomposition resulted in a mixed product of porous NiO with embedded particles of Na₂SO₄. Application of the proposed mechanism to nickel‐based alloys is discussed.