| 摘 要： | 用激光表面强化技术对70Mn2Mo铸钢热轧辊进行了硬化处理得到细化的马氏体组织，硬度由原始组织的200-300HV提高到920HV，硬化层深度达0.6mm，高温回火后，硬度及淬硬层仍分别保持在430HV和0.4mm以上，表明其具有良好的抗回火性能。
|
| 关 键 词： | 70Mn2Mo铸钢 热轧辊 激光表面强化 |
| 文章编号： | 0254-6051(2002)08-0032-03 |
Surface Hardening of 70Mn2Mo Cast Steel Hot Roller by Laser |
| |
| XU Qiao-yu,YU Qing,LI Zhu gang,LIU Xiang.Surface Hardening of 70Mn2Mo Cast Steel Hot Roller by Laser[J].Heat Treatment of Metals,2002,27(8):32-34. |
| |
| Authors: | XU Qiao-yu YU Qing LI Zhu gang LIU Xiang |
| |
| Abstract: | The fine martensite could be gained in 70Mn2Mo cast steel roller by laser strengthening.The microhardness and hardened depth of the roll can reach 920HV and 0 6mm respectively.After tempering at high temperature,the hardness and the hardened depth can be maintained above 430HV and 0 4mm respectively.It is showed that the laser treated rollers possess good tempering resistance. |
| |
| Keywords: | cast steel hot roller laser strengthening |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ |