Enhancing the dehydrogenation properties of LiAlH4 using K2NiF6 as additive

Lithium alanate (LiAlH₄) is a material that can be potentially used for solid-state hydrogen storage due to its high hydrogen content (10.5 wt%). Nevertheless, a high desorption temperature, slow desorption kinetic, and irreversibility have restricted the application of LiAlH₄ as a solid-state hydrogen storage material. Hence, to lower the decomposition temperature and to boost the dehydrogenation kinetic, in this study, we applied K₂NiF₆ as an additive to LiAlH₄. The addition of K₂NiF₆ showed an excellent improvement of the LiAlH₄ dehydrogenation properties. After adding 10 wt% K₂NiF₆, the initial decomposition temperature of LiAlH₄ within the first two dehydrogenation steps was lowered to 90 °C and 156 °C, respectively, that is 50 °C and 27 °C lower than that of the аs-milled LiAlH₄. In terms of dehydrogenation kinetics, the dehydrogenation rate of K₂NiF₆-doped LiAlH₄ sample was significantly higher as compared to аs-milled LiAlH₄. The K₂NiF₆-doped LiAlH₄ sample can release 3.07 wt% hydrogen within 90 min, while the milled LiAlH₄ merely release 0.19 wt% hydrogen during the same period. According to the Arrhenius plot, the apparent activation energies for the desorption process of K₂NiF₆-doped LiAlH₄ are 75.0 kJ/mol for the first stage and 88.0 kJ/mol for the second stage. These activation energies are lower compared to the undoped LiAlH₄. The morphology study showed that the LiAlH₄ particles become smaller and less agglomerated when K₂NiF₆ is added. The in situ formation of new phases of AlNi and LiF during the dehydrogenation process, as well as a reduction in particle size, is believed to be essential contributors in improving the LiAlH₄ dehydrogenation characteristics.