Fabrication,permeation, and corrosion stability measurements of silica membranes for HI decomposition in the thermochemical iodine–sulfur process

In this study, a corrosion-stable silica membrane was developed to be used in H₂ purification during the hydrogen iodide decomposition (2HI → H₂ + I₂), which is a new application of the silica membranes. From a practical perspective, the membrane separation length was enlarged up to 400 mm and one end of the membrane tubes was closed to avoid any thermal variation along the membrane length and sealing issues. The silica membranes consisted of a three-layer structure comprising a porous α-Al₂O₃ ceramic support, an intermediate layer, and a top silica layer. The intermediate layer was composed of γ-Al₂O₃ or silica, and the top silica layer that is H₂ selective was prepared via counter-diffusion chemical vapor deposition of a hexyltrimethoxysilane.To the best of our knowledge, this is the first report of 400-mm-long closed-end silica membranes supported on Si-formed α-Al₂O₃ tubes produced via chemical vapor deposition method. A 400-mm-long closed-end membrane using a Si-formed α-Al₂O₃ tube exhibited a higher H₂/SF₆ selectivity of 1240 but lower H₂ permeance of 1.4 × 10^?7 mol Pa^?1 m^?2 s^?1 with compared with the membrane using a γ-Al₂O₃-formed α-Al₂O₃ tube (907 and 5.6 × 10^?7 mol Pa^?1 m^?2 s^?1, respectively). The membrane using the Si-formed α-Al₂O₃ tube was more stable in corrosive HI gas than a membrane with a γ-Al₂O₃-formed α-Al₂O₃ tube after 300 h of stability tests. In conclusion, the developed silica membranes using the Si-formed α-Al₂O₃ tubes seem suitable for membrane reactors that produce H₂ on large scale using HI decomposition in the thermochemical iodine–sulfur process.