A Fenton-like degradation mechanism for 1,4-dioxane using zero-valent iron (Fe) and UV light

In this study, the degradation mechanism of 1,4-dioxane using zero-valent iron (Fe⁰) in the presence of UV light was investigated kinetically. The degradation of 1,4-dioxane in Fe⁰-only, photolysis, and combined Fe⁰ and UV reactions followed the kinetics of a pseudo-first-order model. The degradation rate constant (19 × 10⁻⁴ min⁻¹) in the combined reaction with UV-C (4.2 mW cm⁻²) and Fe⁰ (5 mg L⁻¹) was significantly enhanced compared to Fe⁰-only (4.8 × 10⁻⁴ min⁻¹) and photolytic reactions (2.25 × 10⁻⁴ min⁻¹), respectively. The removal efficiency of 1,4-dioxane in combined reaction with Fe⁰ and UV within 4 h was enhanced by increasing UV intensity at UV-C region (34% at 4.2 mW cm⁻² and 89% at 16.9 mW cm⁻²) comparing with the removal in the combined reaction with Fe⁰ and UV-A (29% at 2.1 mW cm⁻², and 33% at 12.6 mW cm⁻²). It indicates that 1,4-dioxane was degraded mostly by OH radicals in the combined reaction. The degradation patterns in both Fe⁰-only and combined reactions were well fitted to the Langmuir-Hinshelwood model, implying that adsorption as well as the chemical reaction occurred. The transformation of Fe⁰ to Fe²⁺ and Fe³⁺ was observed in the Fe⁰-only and combined reactions, and the transformation rate of Fe⁰ was improved by UV irradiation. Furthermore, the reduction of Fe³⁺ was identified in the combined reaction, and the reduction rate was enhanced by an increase of UV energy. Our study demonstrated that the enhancement of 1,4-dioxane removal rate occurred via an increased supply of OH radicals from the Fenton-like reaction induced by the photolysis of Fe⁰ and H₂O, and with producing less sludge.