| 钢渣和丙烯酸树脂制备人造石及其性能研究 |
| |
| 引用本文： | 徐莉,童敏.钢渣和丙烯酸树脂制备人造石及其性能研究[J].新型建筑材料,2019(5):25-28. |
| |
| 作者姓名： | 徐莉 童敏 |
| |
| 作者单位： | 宝武集团环境资源科技有限公司 |
| |
| 摘 要： | 以丙烯酸树脂及其固化剂为基体、钢渣粉为填料,同时添加活性稀释剂、助交联剂等,采用热压成型制备了人造石试样。性能测试结果表明,所制备人造石的压缩强度、弯曲强度和拉伸强度分别为139.9、52.0、65.9MPa,巴氏硬度为60;浸泡6d材料吸水率为0.35%;同时具有良好的耐水砂摩擦性能和耐冲击性能,技术性能符合JC/T908—2013《人造石》要求。
|
| 关 键 词： | 钢渣 丙烯酸树脂 人造石 |
Study on the properties of the artificial stone with steel slag and acrylite resin |
| |
| XU Li,TONG Min.Study on the properties of the artificial stone with steel slag and acrylite resin[J].New Building Materials,2019(5):25-28. |
| |
| Authors: | XU Li TONG Min |
| |
| Affiliation: | (Baowu Group Environmental Technology Co.Ltd.,Shanghai 201900,China) |
| |
| Abstract: | The artificial stone was prepared by hot-press molding,using acrylite resin and its curing agent as matrix,steel slag powder as filler,adding reactive diluents and co-crosslinking agent.The results showed that the compressive strength,the flexural strength and tensile strength of artificial stone were 139.9,52.0,65.9 MPa respectively.The water absorption rate of the sample was 0.35%,soaking for 6 d.The Barcol hardness was 60.Meanwhile,the artificial stone had excellent friction resistance against water and sediment and good resistance to shock,which the indicators satisfied the technical parameters according to Standard JC/T 908-2013"Artificial Stone". |
| |
| Keywords: | steel slag acrylite resin artificial stone |