聚醚型合成压缩机油的研制 |
| |
引用本文: | 周康,张遂心,于海,范丰奇,伏喜胜.聚醚型合成压缩机油的研制[J].石油炼制与化工,2020,51(11):90-93. |
| |
作者姓名: | 周康 张遂心 于海 范丰奇 伏喜胜 |
| |
作者单位: | 1.中国石油兰州润滑油研究开发中心
2.中国石油天然气集团公司润滑油重点实验室 |
| |
摘 要: | 使用聚醚基础油,通过对抗氧剂、极压抗磨剂、助溶剂和防锈剂等添加剂的筛选及性能考察,研制了一种聚醚型合成压缩机油。该产品黏度指数达到210以上,旋转氧弹时间超过1 000 min ,铜片腐蚀(100 ℃,3h)为1b级,四球试验的钢球磨斑直径为0.5 mm左右,具有优异的黏温性能、氧化安定性、防锈抗腐性和良好的极压抗磨性,达到国外同类油品质量水平。经过一年的实际使用,油品磨损金属质量分数低于30 μg/g,表明研制产品能够满足烃类气体压缩机的润滑要求。
|
关 键 词: | 聚醚 压缩机油 烃类气体 |
收稿时间: | 2020-04-03 |
修稿时间: | 2020-07-01 |
RESEARCH ON SYNTHETIC COMPRESSOR OILS BASED ON POLYETHER |
| |
Abstract: | Using polyether base oil, a kind of polyether type synthetic compressor oil was developed by screening and investigating the properties of additives such as antioxidation agent, extreme pressure antiwear agent, co-solvent and anti-rust agent. The viscosity index of the product was more than 210, the rotary oxygen bomb time was more than 1000 minutes, the copper strip corrosion(100 ℃,3 h) was grade 1b, and the scar diameter after the four ball milling test was about 0.5mm. The developed product has an excellent performance in viscosity-temperature,oxidation stability,rust resistance and anti-corrosion and good extreme pressure anti-wear. The quality of the product reached the level of foreign similar oils. After practical use for one year,the wear metal content was less than 30 μg/g, showing that the developed product can meet the lubrication requirements of hydrocarbon gas compressors. |
| |
Keywords: | polyether compressor lubricant hydrocarbon gas |
|