HRTEM studies of NiNbZr + Ag amorphous-nanocrystalline composites

Amorphous powder of composition corresponding to Ni60Ti20Zr20 (in at%) was obtained by ball milling in a high-energy mills starting from pure elements. Formation of the amorphous structure was observed already after 20 h of milling, although complete amorphization occurred after 40 h. The microhardness of powders increased from about 30 HV for pure elements to above 400 HV (1290 MPa) after 40 h of milling. Transmission electron microscopy (TEM) allowed to identify nanocrystalline inclusions of intermetallic phases of size 2–10 nm. Uniaxial hot pressing was performed in vacuum at temperature below the crystallization T_x it is 510°C and pressure of 600 MPa, Mixed amorphous powders and nanocrystalline silver powders were used to form a composite, in which microhardness was near 970 MPa HV and 400 HV for the amorphous phase and nanocrystalline silver, respectively. The compression strength of the composite containing 20 wt% of nanocrystalline Ag powder was equal to 600 MPa and plastic strain was 2%. Microstructure studies showed low porosity of composites of less than 1%, uniform distribution of the silver phase and a transition zone between both components, about 150 nm thick, where diffusion of nickel, niobium and zirconium into silver was observed. High-resolution TEM allowed identifying the structure of nanocrystalline inclusions in the amorphous matrix after hot pressing as either Ni₃Zr or Ni₁₇Nb₃. The identification was performed basing on measurements of angles and interatomic distances using inverse Fourier transformed images with enhanced contrast using Digital Micrograph computer program.