C-276哈氏合金焊接换热管在服役中发生了腐蚀失效,焊缝区域明显减薄,焊缝局部有小孔。通过金相、扫描电镜、能谱分析等分析手段对失效的C-276焊接管进行了分析。分析结果表明,仅对焊缝做了冷拉处理、不当的焊接工艺以及随后的不完善固溶处理是导致焊缝区域耐腐蚀性能降低的主要原因。最后提出了相应的预防措施。

Failure Analysis and Protection of Hastelioy Alloy C- 276 Heat Exchange Tube

C -276 Hastelloy alloy heat exchange welding tube happened corrosion failure in service,there is a obvious thinning phenomenon in bead area and a hole in local area of the bead. The reason for failed C -276 welded tube was researched through metallography, scanning electric mirror, energy spectrum etc. The results indicate that only cold working plete solution treatment are the root causes ventive measures have been put forward. on bead, improper welding of low corrosive resistance proeedure and subsequent incom- in bead. Finally, the relevant pre-ventive measures have been put forward.