| 低碳高硫易切削钢冷拔纵裂纹分析和改进工艺措施 |
| |
| 引用本文： | 万长杰,白瑞娟,申丽娟,赵新伟. 低碳高硫易切削钢冷拔纵裂纹分析和改进工艺措施[J]. 特殊钢, 2016, 37(2): 47-48 |
| |
| 作者姓名： | 万长杰 白瑞娟 申丽娟 赵新伟 |
| |
| 作者单位： | 河南济源钢铁集团有限公司科技质量处,济源 459000 |
| |
| 摘 要： | 对100t BOF-LF—165 mm×165 mm方坯连铸-热轧至Φ14 mm-冷拔至Φ12 mm的低碳高硫易切削钢(/%:0.07C,1.24Mn,0.06P,0.39S)冷拔材开裂现象进行系统分析,得出该钢在冶炼连铸过程中由于卷渣、氧化等原因造成钢坯内部缺陷是材料冷拔纵裂纹形成的主要原因。通过控制连铸过程结晶器冷却水量,二冷区采用弱冷工艺,比水量0.83 L/kg,拉速1.5 m/min,无氧化保护浇铸及采用1300℃粘度为0.6 Pa·s专用保护渣等工艺措施,有效避免冷拔纵裂纹的发生。
|
| 关 键 词： | 低碳高硫易切削钢 冷拔材 纵裂纹 |
| 收稿时间： | 2015-11-03 |
Analysis on Formation Cause of Cold-Drawn Rod longitudinal Crack of Low-Carbon High-Sulphur Free-Cutting Steel and Process Improved Measures |
| |
| Wan Changjie,Bai Ruijuan,Shen Lijuan,Zhao Xinwei. Analysis on Formation Cause of Cold-Drawn Rod longitudinal Crack of Low-Carbon High-Sulphur Free-Cutting Steel and Process Improved Measures[J]. Special Steel, 2016, 37(2): 47-48 |
| |
| Authors: | Wan Changjie Bai Ruijuan Shen Lijuan Zhao Xinwei |
| |
| Affiliation: | Technology and Quality Department, Henan Jiyuan Iron and Steel Group Co Ltd, Jiyuan 459000 |
| |
| Abstract: | The crack phenomenon of cold-drawn Φ12 mm bar of low-carbon high-sulphur free cutting steel (/% : 0.07 C, 1.24Mn, 0.06P, 0.39S) produced by 100t BOF-LF-165 mm x 165 mm casting billet -Φ14 mm hot-rolled bar-cold drawn to Φ12 mm rod process has been systematically analyzed to get the main cause of cold-drawn rod longitudinal crack is the billet inner defect formed in steelmaking and casting process by slag enclosure and oxidation etc factors. With the process measures including controlling mold cooling water rate in casting process, using weak secondary water cooling process with ratio water amount 0.83 L/kg, casting speed 1.5 m/min, non-oxidizing shielding casting and using viscosity 0.6 Pa·s at 1300℃ specialty mold powder, the occurrence of cold-drawn rod longitudinal crack is effectively avoided. |
| |
| Keywords: | Low-Carbon High-Sulphur Free Cutting Steel Cold-Drawn Rod Longitudinal Crack |