| 预应变量对超低碳烘烤硬化(ULC-BH)钢硬化性能的影响 |
| |
| 引用本文： | 杨晰,李维娟,金晓龙,孙成钱. 预应变量对超低碳烘烤硬化(ULC-BH)钢硬化性能的影响[J]. 特殊钢, 2014, 35(1): 61-64 |
| |
| 作者姓名： | 杨晰 李维娟 金晓龙 孙成钱 |
| |
| 作者单位： | 1辽宁科技大学材料与冶金学院，鞍山114051 ；2鞍钢股份公司技术中心，鞍山114009 |
| |
| 基金项目： | 国家自然科学基金资助(51274121) |
| |
| 摘 要： | 测定了ULC-BH钢1 mm退火冷轧钢板(/%:0.002C,0.008Si,0.60Mn,0.043P,0.009S,0.031Al,0.071Ti)经2%~10%预应变,170℃20 min烘烤后的烘烤硬化(BH)值,通过内耗实验获得不同应变时效下的内耗谱线,利用X射线衍射技术测定位错密度,研究了Cottrell气团对ULC-BH钢烘烤硬化性能的影响。结果表明,随预应变量增加,ULC-BH钢的BH值增大;随预应变量增加,Snoek峰逐渐降低,而SKK峰逐渐升高;经2%、6%和10%预应变,位错密度增大,分别为3.9×1010/cm~2,8.4×1010/cm2和6.8×1011/cm2,相应的Cottrell气团密度逐渐减小。
|
| 关 键 词： | 预应变 超低碳烘烤硬化钢 烘烤硬化值 Cottrell气团 位错密度 |
| 收稿时间： | 2013-08-15 |
Effect of Prestrain on Bake Hardening property of Ultra-Low Carbon Bake Hardening (ULC-BH) Steel |
| |
| Yang Xi,Li Weijuan,Jin Xiaolong,Sun Chengqian. Effect of Prestrain on Bake Hardening property of Ultra-Low Carbon Bake Hardening (ULC-BH) Steel[J]. Special Steel, 2014, 35(1): 61-64 |
| |
| Authors: | Yang Xi Li Weijuan Jin Xiaolong Sun Chengqian |
| |
| Affiliation: | 1 College of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051 ；2 Technology Center, Anshan Iron and Steel Co Ltd, Anshan 114009 |
| |
| Abstract: | The bake hardening values ( BH) of ULC-BH steel 1 mm annealed cold rolled sheet (/%： 0. 002C, 0. 008Si, 0. 60Mn, 0. 043P, 0. 009S, 0. 031 Al, 0.017Ti) with prestraining by 2% ~ 10% and baking al 170 °C for 20 min have been measured, and the effect of Cottrell atmosphere on bake hardening property of ULC-BH sleet is studied by internal friction test getting internal friction spectrum curves at different strain ageing and using X-ray diffraction technique measuring dislocation density. Results show that with increasing prestrain the BH value of ULC-BH steel increases ； and with increasing prestrain the Snoek peak gradually reduces while SKK peak gradually raise； with prestraining by 2%, 6% and 10% the dislocation density increases, and that respectively are 3. 9 x 1010/cm2, 8. 4 x 1010/cm2 and 6. 8 x 1011/cm2, while corresponding Cottrell atmosphere density gradually decreases. |
| |