| 介孔碳化钨负载铂催化剂对甲醇氧化的电催化性能 |
| |
| 引用本文： | 胡仙超,胡建冠,孙洁,李国华. 介孔碳化钨负载铂催化剂对甲醇氧化的电催化性能[J]. 无机材料学报, 2013, 28(12): 1286-1290. DOI: 10.3724/SP.J.1077.2013.13190 |
| |
| 作者姓名： | 胡仙超 胡建冠 孙洁 李国华 |
| |
| 作者单位： | (浙江工业大学 1. 分析测试中心, 2.?化学工程与材料学院, 杭州 310032) |
| |
| 基金项目： | 国家自然科学基金(21173193);浙江省教育厅科研项目(Y201225711);浙江省科技计划项目(2013C37104)~~ |
| |
| 摘 要： | 采用硬模板法制备了介孔碳化钨(m-WC), 进一步还原铂的前驱体(H2PtCl6)得到Pt/m-WC催化剂。采用X射线粉末衍射(XRD)、透射电子显微镜(TEM)和X射线光电子能谱(XPS)等测试手段对样品的物相、结构和形貌进行了表征。结果表明, 所制得的m-WC载体为单一的碳化钨相, 孔径为10~20 nm, Pt/m-WC催化剂中Pt的粒径约为3.4 nm, 主要以金属态形式存在, 相对比较均一的Pt纳米粒子均匀地分散在载体的表面和孔道中。电化学测试结果表明, 与普通WC载Pt催化剂(Pt/c-WC)相比, Pt/m-WC催化剂具有较大的电化学活性表面积, 对甲醇呈现出更高的电催化氧化活性和更好的稳定性。
|
| 关 键 词： | 直接甲醇燃料电池 碳化钨 介孔材料 电催化 |
| 收稿时间： | 2013-04-03 |
| 修稿时间： | 2013-07-01 |
Mesoporous Tungsten Carbide Supported Pt and Their Electro Catalytic Activity for Methanol Electro-oxidation |
| |
| HU Xian-Chao;HU Jian-Guan;SUN Jie;LI Guo-Hua. Mesoporous Tungsten Carbide Supported Pt and Their Electro Catalytic Activity for Methanol Electro-oxidation[J]. Journal of Inorganic Materials, 2013, 28(12): 1286-1290. DOI: 10.3724/SP.J.1077.2013.13190 |
| |
| Authors: | HU Xian-Chao HU Jian-Guan SUN Jie LI Guo-Hua |
| |
| Affiliation: | (1. Research Center of Analysis and Measurement, Zhejiang University of Technology, Hangzhou 310032, China; 2. College of Chemical Engineering and Materials Science, Zhejiang University of Technology, Hangzhou 310032, China) |
| |
| Abstract: | Mesoporous tungsten carbide supported Pt nanoparticles (Pt/m-WC) with uniform size were prepared using hard template method and H2PtCl6 as the Pt precursor. The crystal phase, structure and morphology of products were characterized with X-ray powder diffraction (XRD), transmission electronic microscope (TEM), and X-ray photoelectron spectrocope (XPS). Results show that the tungsten carbide supporter has pure tungsten carbide phase with pore size of about 10-20 nm. Pt particles (3.4 nm mean size) which are mainly in the metallic form are dispersed on the external walls and pores of m-WC. The electro-catalytic activity of the prepared Pt/m-WC towards the oxidation of methanol was investigated using cyclic voltammetry and chronoamperometry. In comparison to the common tungsten carbide supported Pt catalyst (Pt/c-WC), the Pt/m-WC catalysts exhibits high electrocatalytic activity, strong anti-poisoning ability and good stability. |
| |
| Keywords: | direct methanol fuel cell tungsten carbide mesoporous materials electro-catalysis |