| Q345E钢0800 mm铸坯表面网状裂纹的分析及控制措施 |
| |
| 引用本文： | 陈远清,仇圣桃,李刚,陈树军,汪德伟. Q345E钢0800 mm铸坯表面网状裂纹的分析及控制措施[J]. 特殊钢, 2018, 39(3): 43-46 |
| |
| 作者姓名： | 陈远清 仇圣桃 李刚 陈树军 汪德伟 |
| |
| 作者单位： | 1钢铁研究总院连铸技术国家工程研究中心，北京100081 ；2张家港联峰钢铁研究所有限公司,张家港215628 |
| |
| 摘 要： | 采用金相显微镜和扫描电镜分析了Q345E钢Φ800 mm铸坯（/%:0.15C,0.27Si,1.37Mn,0.009P,0.001S,0.03Nb,0.04V,0.030A1,0.008 ON）表面网状裂纹,得出结晶器壁和凝固坯壳之间保护渣膜厚度不均匀,使坯壳局部受挤压,产生凹坑,冷却速度降低,产生热应力裂纹。通过将保护渣碱度（CaO）/（SiO2）从1.03提高到1.15,熔点从1 235℃降至1 210℃,1 300℃粘度从0.87 Pa·s提高到1.10 Pa·s,使Φ800 mm连铸坯表面凹坑和网状裂纹的发生率从原60.5%降至0.5%以下。
|
| 收稿时间： | 2018-01-03 |
Analysis on Surface Net Cracks of C>800 mm Casting Bloom of Steel Q345E and Control Measures |
| |
| Chen Yuanqing,Qiu Shengtao,Li Gang,Chen Shujun,Wang Dewei. Analysis on Surface Net Cracks of C>800 mm Casting Bloom of Steel Q345E and Control Measures[J]. Special Steel, 2018, 39(3): 43-46 |
| |
| Authors: | Chen Yuanqing Qiu Shengtao Li Gang Chen Shujun Wang Dewei |
| |
| Affiliation: | 1 National Engineering Research Center for Continuous Casting Technology, Central Iron and Steel Research Institute,Beijing 100081;2 Zhangjiagang Lianfeng Iron and Steel Research Institute Co Ltd, Zhangjiagang 215628 |
| |
| Abstract: | The surface net cracks of Φ 800 mm casting bloom of steel Q345E (/% : 0.15C, 0.27Si, 1. 37Mn, 0. 009P, 0. 001S, 0. 03Nb, 0. 04V, 0. 030Al, 0.008 ON) have been analyzed by metallurgy and scanning electron microscope. It is obtained that the uneven thickness of flux film in between mold wall and solid shell leads to extruding local shell, forming depression, decreasing cooling rate and forming thermal stress cracks. With increasing basicity of mold powder (CaO)/(SiO2) from 1. 03 to 1.15, decreasing melting point form 1 235 °C to 1 210 °C , and increasing viscosity at 1 300 °C from 0. 87 Pa · s to 1. 10 Pa· s, the occurring rate of surface depression and net cracks of 0800 mm casting bloom decreases from original 60. 5% to less than 0. 5%. |
| |
| Keywords: | Steel Q345E Φ 800 mm Casting Bloom Net Cracks Depression Mold Powder |
|