| 新型2Cr1Mo2Ni钢在含二氧化碳油田采出液中的腐蚀行为 |
| |
| 引用本文： | 张瑾, 许立宁, 路民旭. 新型2Cr1Mo2Ni钢在含二氧化碳油田采出液中的腐蚀行为[J]. 工程科学学报, 2017, 39(7): 1062-1069. DOI: 10.13374/j.issn2095-9389.2017.07.012 |
| |
| 作者姓名： | 张瑾 许立宁 路民旭 |
| |
| 作者单位： | 1.北京科技大学新材料技术研究院腐蚀与防护中心, 北京 100083 |
| |
| 基金项目： | 国家科技支撑计划资助项目(2012BAK13B04) |
| |
| 摘 要： | 为弄清Mo和Ni元素在低Cr钢耐蚀方面所起的作用,炼制了新型2Cr1Mo2Ni钢,研究其在模拟油田采出液中的腐蚀行为,实验条件为80℃,0.8 MPa CO2分压.利用扫描电镜和能谱分析研究了2Cr1Mo2Ni钢和3Cr钢的腐蚀产物膜微观形貌和成分,测试了高温高压极化曲线和电化学阻抗谱,分析了腐蚀产物膜的生长过程.实验结果表明,Mo和Ni元素在提高抗CO2腐蚀性能方面的作用不及Cr元素.2Cr1Mo2Ni钢腐蚀164 h后,中低频感抗弧消失,腐蚀产物膜开始完全覆盖基体表面;腐蚀240 h后,生成的腐蚀产物膜具有较好的保护性.
|
| 关 键 词： | 2Cr1Mo2Ni钢 二氧化碳腐蚀 低Cr钢 腐蚀产物膜 电化学阻抗谱 |
| 收稿时间： | 2016-12-08 |
Corrosion behavior of novel 2Cr1Mo2Ni steel in the oil field formation water containing CO2 |
| |
| ZHANG Jin, XU Li-ning, LU Min-xu. Corrosion behavior of novel 2Cr1Mo2Ni steel in the oil field formation water containing CO2[J]. Chinese Journal of Engineering, 2017, 39(7): 1062-1069. DOI: 10.13374/j.issn2095-9389.2017.07.012 |
| |
| Authors: | ZHANG Jin XU Li-ning LU Min-xu |
| |
| Affiliation: | 1.Corrosion and Protection Center, Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China |
| |
| Abstract: | The corrosion behavior of the new 2Cr1Mo2Ni steel in the oil field formation water containing CO2 at 80℃ and 0.8 MPa was studied herein to clarify the role of Ni and Mo in the corrosion resistance of low-Cr steel. The surface morphology and the chemical composition of the corrosion scales were analyzed by scanning electron microscopy and energy dispersive spectroscopy (EDS). The polarization curves and the electrochemical impedance spectroscopy spectra were also obtained to explore the growth process of the corrosion scale. The results indicate that Mo and Ni are not as efficient as Cr in enhancing the corrosion resistance of the low-Cr steel. The low-frequency inductance loop disappears after 164 h immersion. Moreover, the corrosion scale completely covers the substrate surface. In addition, the protective corrosion scale forms after 240 h immersion. |
| |
| Keywords: | 2Cr1Mo2Ni steel carbon dioxide corrosion low-Cr steel corrosion scale EIS spectra |