Microstructure change of V-Ti magnetite concentrate pellets during reduction |
| |
| ZHANG Jian-liang, YANG Guang-qing, GUO Hong-wei, SHAO Jiu-gang, LI Jian, WEN Yong-cai. Microstructure change of V-Ti magnetite concentrate pellets during reduction[J]. Chinese Journal of Engineering, 2013, 35(1): 41-48. DOI: 10.13374/j.issn1001-053x.2013.01.017 |
| |
| Authors: | ZHANG Jian-liang YANG Guang-qing GUO Hong-wei SHAO Jiu-gang LI Jian WEN Yong-cai |
| |
| Affiliation: | 1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. Pangang Iron Plant, Panzhihua 617022, China;3. Panzhihua Iron and Steel Research Institute, Panzhihua 617000, China |
| |
| Abstract: | The reduction process of V-Ti magnetite concentrate pellets was studied under the simulated condition of blast furnaces. Phase compositions in the pellets at different reduction temperatures were determined by X-ray diffraction analysis. The microstructure change of the pellets during reduction was observed by optical microscopy and scanning electron microscopy. The distribution of different elements in oxides was identified by energy dispersive spectrometry. It is found that iron-titanium segregation in the pellets during reduction affects the reducibility of the pellets, and the formed ilmenite spar of high titanium content increases the difficulty in reduction of iron oxides. The dense iron shell formed at high temperature hinders the reduction of inner oxides, leads to stagnation of reduction, and makes the reducibility of the pellets poor at high temperature. When the inner liquid melt dripping down, the oxygen potential increases in the lower part of the blast furnace, which decreases the generation of Ti(C, N). |
| |
| Keywords: | magnetite ore pellets ore reduction microstructure phase composition blast furnaces |
|