| 高孔隙率 Ce-TiO2微粉的制备及其光催化性能研究 |
| |
| 引用本文： | 伍勇华,兰子君,杜伟良,马平. 高孔隙率 Ce-TiO2微粉的制备及其光催化性能研究[J]. 硅酸盐通报, 2016, 35(9): 2772-2776 |
| |
| 作者姓名： | 伍勇华 兰子君 杜伟良 马平 |
| |
| 作者单位： | 西安建筑科技大学材料与矿资学院,西安,710055 |
| |
| 基金项目： | 陕西省社会发展科技攻关项目(2016SF-443) |
| |
| 摘 要： | 以自制Ce离子掺杂的TiO2纳米粉为前体，通过微波辅助水热法进行空间结构改性，获得改性Ce-TiO2微粉。所得样品用X射线衍射（XRD）、扫描电镜（SEM）、氮吸附（BET）、紫外-可见漫反射（UV-Vis）等测试方法表征。结果表明，所制备的微粉具有较高的孔隙率，平均孔径为153．4 nm，比表面积可达到154．9 m2／g。掺杂Ce离子对微粉的结构没有影响，但是拓宽了TiO2的可见光吸收范围，使吸收边红移至可见光区域，同时有效的抑制了晶粒长大，阻碍锐钛矿相向金红石相的转变。所制备的高孔隙率Ce-TiO2微粉在低浓度甲醛溶液中表现出良好的可见光催化性能。
|
| 关 键 词： | Ce-TiO2 光催化 高孔隙率 微波法 甲醛, |
Preparation of High-Porosity Ce-TiO2 Micropowder and Its Photocatalytic Performance |
| |
| WU Yong-hua,LAN Zi-jun,DU Wei-liang,MA Ping. Preparation of High-Porosity Ce-TiO2 Micropowder and Its Photocatalytic Performance[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(9): 2772-2776 |
| |
| Authors: | WU Yong-hua LAN Zi-jun DU Wei-liang MA Ping |
| |
| Abstract: | Modified Ce-TiO2 micropowder were synthesized by microwave-assisted hydrothermal method with homemade Ce-doped titania nanopowder and were characterized by X-ray diffraction ( XRD ) , scanning electron microscopy ( SEM ) , nitrogen adsorption ( BET ) , and UV-visible ( UV-Vis ) diffuse reflectance spectroscopy .The results show that modified Ce-TiO2 micropowder has high porosity , the average pore diameter is 153.4 nm and the specific surface area is 154.9 m2/g.Ce-doping has little effect on the structure of the micropowder , but it can enlarge the ability of TiO 2 for absorbing visible light , which shiftes absorption edge of TiO 2 reaching the visible region .At the same time Ce-doping effectively inhibits grain growth, hinders the crystal type transform of TiO 2 from anatase to rutile. High-Porosity Ce-TiO2 micropowder meets good visible light catalytic activity in low concentration formaldehyde solution . |
| |
| Keywords: | Ce-TiO2 photocatalysis high porosity microwave method formaldehyde, |