Synergistic flame retardant effects of activated carbon and molybdenum oxide in poly(vinyl chloride) |
| |
| Authors: | Mengjiao Zhang Weihong Wu Shaorui He Xue Wang Yunhong Jiao Hongqiang Qu Jianzhong Xu |
| |
| Affiliation: | 1. College of Chemistry and Environmental Science, Hebei University, Baoding, China;2. College of Science, Agriculture University of Hebei, Baoding, China |
| |
| Abstract: | The synergistic effects of activated carbon (AC) and molybdenum oxide (MoO3) in improving the flame retardancy of poly(vinyl chloride) (PVC) were investigated. The effects of AC, MoO3 and their mixture with a mass ratio of 1:1 on the flame retardancy and smoke suppression properties of PVC were studied using the limiting oxygen index and cone calorimeter tests. It was found that the flame retardancy of the relatively cheaper AC was slightly weaker than that of MoO3. In addition, the incorporation of AC and MoO3 greatly reduced the total heat release and improved smoke suppressant property of PVC composites. When the total content of AC and MoO3 was 10 phr, PVC/AC/MoO3 had the lowest peak heat release rate and peak smoke production rate values of 173.80 kW m?2 and 0.1472 m2 s?1, which represented reductions of 47.3 and 59.9%, respectively, compared with those of PVC. Furthermore, thermogravimetric analysis and gel content tests were used to analyze the flame retardant mechanism of AC and MoO3, with results showing that AC could promote early crosslinking in PVC. Char residue left after heating at 500 °C was analyzed using scanning electron microscopy and Raman spectroscopy, and the results showed that MoO3 produced the most compact char, with the smallest and most organized carbonaceous microstructures. © 2017 Society of Chemical Industry |
| |
| Keywords: | activated carbon molybdenum oxide PVC flame retardant synergistic effect |
|
|