Low‐Density Open Cellular Silicon Carbide Foams from Sucrose and Silicon Powder
Authors:Sujith Vijayan  Praveen Wilson  Remani Sreeja  Kuttan Prabhakaran
Affiliation:1. Department of Chemistry, Indian Institute of Space Science and Technology, Thiruvananthapuram, India;2. Vikram Sarabhai Space Center, Thiruvananthapuram, India
Abstract:Open cellular SiC foams with low densities were prepared by thermo‐foaming and setting (130°C–150°C) of silicon powder dispersions in molten sucrose followed by pyrolysis and reaction sintering at 1500°C. The bubbles generated in the dispersion by water vapor produced by the –OH condensation was stabilized by the adsorption of silicon particles on the air‐molten sucrose interface. The composition of a sucrose‐silicon powder mixture for producing SiC foam without considerable unreacted carbon was optimized. The sucrose in the thermo‐foamed silicon powder dispersion leaves 24 wt% carbon during the pyrolysis. The sintering additives such as alumina and yttria promoted the silicon‐carbon reaction. SiC nanowires with diameters in the range of 35–55 nm and length >10 μm observed on the cell walls as well as in the fractured strut region were grown by both vapor–liquid–solid and vapor–solid mechanisms. Large SiC foam bodies without crack could be prepared as the total shrinkage during pyrolysis and reaction sintering was only ~30 vol%. The relatively low compressive strength (0.06–0.41 MPa) and Young's modulus (14.9–24.2 MPa) observed was due to the large cell size (1.1–1.6 mm) and high porosity (93%–96%).
Keywords:foams  silicon carbide  nanowires  pyrolysis  reaction sintering
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号