热压Al2O3—ZrO2（6mol%Y2O3）陶瓷复合材料的组织性能研究

本文考察了全稳定ＺｒＯ２对Ａｌ２Ｏ３陶瓷的组织性能的影响。结果表明，热压Ａｌ２Ｏ３－ＺｒＯ２（６ｍｏｌ％Ｙ２Ｏ３）陶瓷材料的显微形貌与其它Ａｌ２Ｏ３－ＺｒＯ２陶瓷的几乎完全一样，小量ｃ－ＺｒＯ２的存在可促进Ａｌ２Ｏ３陶瓷的烧结并细化晶粒，从而提高材料的力学性能，但其增韧增强能力有限。大量ｃ－ＺｒＯ２的存在因其本身低的力学性能、缺乏相变韧化和存在残余拉应力而使材料的力学性能下降。     

(Al_2O_3,CaO)掺杂对x(MgO)=8%-ZrO_2纳米粉相组成和晶粒大小的影响

用尿素水解法制备了x(MgO)=8%-ZrO2及(Al2O3,CaO)掺杂的x(MgO)=8%-ZrO2纳米粉。经XRD、TEM等分析表明:掺入Al2O3有降低(c+t)-ZrO2体积分数和细化晶粒的作用;CaO的掺入可显著提高(c+t)-ZrO2含量,当掺入x(CaO)=3%时,可得到全稳定立方相氧化锆。     

二氧化硅和氧化铝微粉加入量对MgO基浇注料流变性的影响

采用电熔镁砂颗粒作骨料,电熔镁砂粉、电熔白刚玉粉、Al2O3微粉和SiO2微粉作基质料,固定骨料与基质料质量比为65:35,且固定基质料中Al2O3微粉与SiO2微粉的总加入量为8%,改变两种微粉的加入比例(Al2O3微粉的加入量分别为8%、6%、4%、2%、0,SiO2微粉的相应为0、2%、4%、6%、8%),分别加6.4%的水制成MgO基浇注料,并采用浇注料流变仪研究了Al2O3微粉与SiO2微粉的加入量对浇注料流变性(扭矩、流动阻力和粘度)的影响。研究结果表明:随着SiO2微粉加入量的增加,浇注料的扭矩、流动阻力和粘度呈降低趋势,但SiO2微粉加入量超过4%后变化很小。     

草酸盐络合物溶液喷雾干燥法制备ZrO2—Al2O3复合粉料及粉料性质

用草酸盐络合物溶液喷雾干燥的方法制备得到了ZrO_2、Al_2O_3及其任意比例的复合粉料,研究了喷雾干燥所制得粉料的热分解行为、四方氧化锆结晶与生长及其稳定性。复合粉料中Al_2O_3作为连续相包裹ZrO_2颗粒,从而提高了四方氧化锆结晶温度,抑制其晶粒生长并阻止四方相向单斜相的转变。     

Al2O3-ZrO2陶瓷体系中晶粒生长模型的研究

研究了Al2O3-ZrO2陶瓷体系中两相晶粒生长，提出了双相体系的晶粒生长模型，并解释了“内晶型”结构是如何形成的。研究发现，两相结构的形成与温度、保温时间及ZrO2等二相的数量有关系，其中温度的影响最为显著。内晶型ZrO2结构的形成是基体晶粒急剧长大的结果，而不是以往研究的以纳米粒子为生长点，基体粒子的成核、长大。有利于基体晶粒急剧生长的条件也有利于内晶的形成；内晶的形成过程可概括为Ostwald生长与基体晶粒的快速长大。但值得注意的是，并不是ＺrO2的含量越多，形成的内晶型结构就越多。     

Effects of Extra Al powder Additions on Properties of ZrN-based Composites Prepared by Aluminothermic Reduction and Nitridation Process

ZrN-based composites were synthesized from zirconia via aluminothermic reduction and nitridation proces with Al powders and Mg O as the reductant and sintering aids,respectively. ZrN-based composites are promising for application in the refractory materials or other high temperature industry fields. The effects of extra Al powder on physical properties,phase transformation and microstructures were investigated. Products with differen phase composition and morphologies were obtained with different Al powders additions. The products were composed of Zr N,ZrO_2,MgAl_2O_4,and Zr Al_3O_3 N by aluminothermal reduction and nitridation of zirconia with 0% extra Al powders addition. The diffraction peaks o Zr N were the strongest while peaks of ZrO_2 vanished with 6% extra Al addition. The thermodynamic calculation indicated that introducing Mg O into the system could promote the reaction process.     

ZrO_2基陶瓷注凝成型料浆流变性的研究

陶瓷料浆流变性能是注凝成型工艺的关键,料浆流变性要求高固含量,低粘度。实验通过在ZrO2表面包覆A l2O3,形成ZrO2-A l2O3复相陶瓷料浆。根据静电位阻稳定理论,通过调节pH值和分散剂的加入量,可得到满足成型要求的高固含量,低粘度的料浆。结果表明,在pH值为10左右,分散剂加入量为粉料质量的3%时,料浆固相体积分数可以达到40%。同时表明了A l2O3对ZrO2颗粒表面有改性作用,提高了悬浮体的稳定性。     

ZrB2-Al2O3复合粉体的自蔓延高温还原合成与表征

用自蔓延高温还原合成制备了ZrB2-Al2O3复合粉体。用X射线衍射仪、扫描电镜和透射电镜等分析测试手段,对所制得的复合粉体的相组成、相貌及微观组织进行了表征。结果表明：ZrB2和Al2O3以主晶相的形式存在于复合粉体之中,二者存在良好的界面结合,这主要与ZrB2在Al2O3颗粒表面结晶生长有关。     

YSZ/MgAl_2O_4复合粉末的合成及其材料的烧成活化能

采用共沉淀法在1100℃制备了70%(体积分数,下同)氧化钇稳定氧化锆[xY2O3+(1-x)ZrO2,x=0.02,0.03,0.04,in mole,yttria stabilized zirconia,YSZ]-30%镁铝尖晶石(MgAl2O4)复合粉体,2种原始粉料的配料各为70%和30%,并在1200～1500℃常压烧成制备了陶瓷材料。结果表明:在制得的所有粉末中,未发现单斜相ZrO2;2YSZ(0.02Y2O3+0.98ZrO2,摩尔分数,下同)/MgAl2O4和3YSZ/MgAl2O4这2种粉体中的ZrO2为四方相多晶氧化锆;而4YSZ/MgAl2O4粉末中的ZrO2相为全稳定立方氧化锆。对于1500℃烧结制备的陶瓷材料,2YSZ/MgAl2O4块体中的ZrO2相为部分稳定氧化锆;而3YSZ/MgAl2O4和4YSZ/MgAl2O4块体中的ZrO2相为全稳定氧化锆。(2～4)YSZ/MgAl2O4复相陶瓷的活化能为(623±80)kJ/mol。     

水煤浆气化炉用Cr2O3-ZrO2-Al2O3砖的蚀变过程

利用扫描电镜及能谱仪对水煤浆气化炉用进口铬锆铝砖的蚀变过程进行了显微观察与分析.结果表明此砖在水煤浆气化炉环境条件下的侵蚀主要由熔渣中的SiO2、CaO和P2O5引起;Cr2O3对这种渣蚀表现出很强的化学惰性,溶蚀很小,其使用过程中的主要变化是高温蒸发和在砖内蚀变液相作用下的溶蚀、溶析;而氧化锆蚀变生成的系列产物不仅在蚀变初期有利于保持砖结构致密,并且对蚀变后期基质连续网络结构的形成和保持也起了重要的作用.     

Effects of Firing and Operating Atmospheres on Microstructure and Properties of Phosphate Bonded Cr_2O_3-Al_2O_3-ZrO_2 Bricks

The microstructure and properties of phosphate bonded Cr_2O_3-Al_2O_3-ZrO_2 specimens fired in air or coke bed were investigated firstly. Then property change of the Cr_2O_3-Al_2O_3-ZrO_2 bricks after secondary treatment in simulation environment was studied. Finally,corrosion resistances of the Cr_2O_3-Al_2O_3-ZrO_2 bricks in air and simulation environment were compared; and microstructure of on-site used Cr_2O_3-Al_2O_3-ZrO_2 bricks in slagging gasifiers was analyzed. The results show that the atmosphere has significant effect on the microstructure and properties of the phosphate bonded Cr_2O_3-Al_2O_3-ZrO_2 bricks. As the specimens are fired in air,the phosphate forms a composite solid solution with Cr_2O_3 and Al_2O_3,therefore,strength of the specimens is enhanced. For specimens fired in coke bed,a certain amount of gases are generated owing to the reduction of phosphate and part of Cr_2O_3,which results in the increasing number and size of the pores,bad interfacial bonding between Cr_2O_3 aggregates and matrix as well as low strength of the specimens. During service process in reducing atmosphere,the phosphate binder and part of Cr_2O_3 in edge of the specimens are also reduced,leading to significant increase of number and size of the pores in the edge of the specimens; as a result,inreducing atmosphere,the specimens show much worse corrosion resistance than in air.     

氧化铝掺杂聚酰亚胺纳米复合薄膜的制备与性能研究

通过溶液法，成功地制备了氧化铝掺杂聚酰亚胺纳米复合薄膜。探讨了Al2O3用量对聚酰亚胺纳米复合薄膜拉伸强度、热性能、电气强度的影响。结果发现，当Al2O3的质量分数达到5％时，整个复合体系的拉伸强度达到最大，相对于聚酰亚胺母体，复合材料的拉伸强度提高了16％；当Al2O3用量较小时，对聚酰亚胺纳米复合薄膜的Td10的影响不大，但当Al2O3的质量分数超过15％时，Td10则随Al2O3用量的增加而下降；同时实验结果表明，Al2O3的引入可以在一定程度上改善其复合体系的电气强度。     

(Ni-P)-Al2O3纳米微粒化学复合镀--表面活性剂对镀层组织的影响

将纳米Al2O3应用于化学复合镀中,研究了表面活性剂对纳米Al2O3粉的分散状态和(Ni-P)-Al2O3纳米微粒复合镀层组织形貌的影响。结果表明,通过选择合适的表面活性剂对纳米Al2O3分散后再加入到镀液中进行施镀,方可得到分散均匀的复合镀层。     

S2O2－8/Fe2O3-ZrO2-SiO2固体酸催化剂合成马来酸二己酯

在铁锆氧化物中引入硅的氧化物，并用S₂O^2－₈浸渍铁锆硅复合氧化物，制得较S₂O^2－₈/Fe₂O₃-ZrO₂（PSFZ）和SO^2－₄/Fe₂O₃-ZrO₂-SiO₂（SFZS）催化活性更强的固体酸催化剂S₂O^2－₈/Fe₂O₃-ZrO₂-SiO₂（PSFZS），研究获得最佳制备条件。用马来酸酐与正己醇的酯化反应考察了催化剂活性。XRD和TEM结果表明，制备的催化剂S₂O^2－₈对铁锆硅复合氧化物的促进作用明显好于SO^2－₄；SiO₂ 和Fe₂O₃的引入使催化剂呈现多孔结构，分散性好，其稳定性增加，催化活性提高；用该催化剂代替硫酸和对甲苯磺酸用于催化马来酸酐和正己醇的酯化反应，可得无色透明的酯化产物，3 h内酯化率达97.9%，分别比PSFZ和PSFZS催化剂提高约10%20%。     

载体和制备方法对铜系一步法合成

以甲醇与乙醇一步反应合成异丁醛反应为基础，研究了不同载体对铜基催化剂反应性能的影 响。分别以SiO₂、SiO_2-ZrO₂、SiO_2-Al₂O₃、Al₂O₃和SiO₂-TiO₂为载体，采用溶胶-凝胶和 浸渍法制备催化剂。采用TPR、XRD和BET等技术对催化剂进行表征。结果表明，复合氧 化物特别是SiO₂-ZrO₂和SiO₂-TiO₂作载体能提高催化剂的比表面积，活性组分分散 好，催化剂的催化性能较好。     

MnO2对自蔓延高温合成陶瓷复合钢管陶瓷层结构和性能的影响

采用MnO2作为添加剂自蔓延高温合成法制备了具有Al2O3和FeAl2O4陶瓷层的复合钢管,研究其对陶瓷层和过渡层的结构和性能的影响.结果表明:添加了MnO2后,陶瓷层表面晶粒排布更加致密,陶瓷层的内表面为层叠状的Al2O3细晶和少量的FeAl2O4;过渡层为Al2O3和混入的FeAl2O4外,还含有SiO2和MnO2,过渡层出现了向钢基体中渗透的网状结构.MnO2的加入并未改变复合钢管Al2O3和FeAl2O4陶瓷层的物相.加入4%(质量分数)MnO2的复合管的抗压度强度和陶瓷层的抗剪强度分别达到416 MPa和19.2 MPa,比未添加MnO2的样品分别提高了18.2%和12.3%     

非化学配比对Mg_((1-3χ))Al_((2-2χ))O_4 尖晶石透明陶瓷显微结构的影响

本研究通过真空烧结和热等静压两步烧结制备了一系列的镁铝尖晶石透明陶瓷.我们利用XRD对粉体和陶瓷的物相成分进行了实验分析,并发现配比为0≤χ≤0.20 的Mg_((1-3χ))Al_((2-2χ))O_4 粉体具有单一的尖晶石成分.SEM 观察发现陶瓷主晶相边界上有利于增韧陶瓷的氧化铝晶粒.通过氧化铝颗粒的透过率和增韧效果的综合考虑,在较小的光损失条件下,采用配比χ为1.4的Mg_((1-3χ))Al_((2-2χ))O_4 粉体制备的陶瓷的显微结构将会最有利于陶瓷的强韧化.     

ZrO2对轻质烷烃异构化催化剂性能的影响

在Ni/Al2 O3 -HM和Ni-W /Al2 O3 -HM催化剂研究的基础上 ,向上述两种轻质烷烃异构化催化剂中用混合法添加一定量ZrO2 ,通过对此催化剂的评价 ,考察ZrO2 对轻质烷烃异构化催化性能的影响。结果发现 ,在较低温度下 ,Ni-Zr/Al2 O3 -HM催化剂异构化性能优于Ni/Al2 O3 -HM催化剂 ,在较高温度下 ,活性上升 ;Zr含量较低时 ,随着ZrO2 含量的增多 ,活性下降 ;对于Ni-W -Zr/Al2 O3 -HM催化剂 ,当W含量较低时 ,0 .5 相似文献   

Corrosion Resistance of High-Alumina Graphite Based Refractories to the Smelting Reduction Melts

1 Introduction The corrosion resistance of the refractories is one of the imperative problems for the development of smel- ting reduction with iron bath[1 ~4]. The Al2O3-C based refractories have been widely and successfully used in the metallurgy industr…     

多组分紫外光纤包层玻璃化学稳定性

研究了紫外光纤用包层玻璃组分的变化以及外掺ZrO2对光纤包层玻璃化学稳定性的影响。结果表明,通过改变S iO2/B2O3、B2O3/A l2O3、B2O3/(K2O Na2O)的质量比,以及适当增加外掺ZrO2含量,可以明显地提高碱硼硅酸盐玻璃化学稳定性。红外光谱分析表明玻璃化学稳定性提高的主要原因是Zr4 的加入促进了玻璃内部的[BO3]层状结构逐渐转变为[BO4]网络状结构。