复配荧光增白剂对洗衣粉白度的增效作用研究

为考察不同品种的荧光增白剂对洗衣粉白度的加和增效作用,将4种常用的荧光增白剂31#、VBL、CXT、CBS-X分别以二元或三元混合配入洗衣粉中,并与单一的荧光增白剂作对照,用烘干法制作粉样,用白度计测试粉体白度,用增白指数判断增效性。结果表明：二元增白剂复配时,31#与VBL、31#与CXT无增效性;VBL与CBS-X、CXT与CBS-X、VBL与CXT有增效性：31#与CBS-X只在质量比0．06与0．04时,才显示增效性。三元增白剂复配时,31#与VBL和CXT无增效性;31#与CXT和CBS-X、31#与VBL和CBS-X、VBL与CXT和CBS-X有增效性。     

新型荧光增白剂CBW-01在洗衣粉中的应用研究

将新型荧光增白剂CBW-01配入洗衣粉中,并与常用的荧光增白剂作对比,通过粉体白度实验、去污实验、织物白度实验和稳定性实验,考察了CBW-01的性能。结果表明,CBW-01在洗衣粉中添加的质量分数为0.02%时,使粉体白度提高了20.45%;添加的质量分数为0.2%时,使去污力比值提高至1.30;添加的质量分数为0.1%时,循环洗涤20次后,对白棉布和白混纺布的白度保持率分别为112.38%和108.25%。在光照16 h和105℃加热48 h后,CBW-01在洗衣粉中的白度衰减率分别为15.36%和1.93%。CBW-01是一种性能优良的洗衣粉用荧光增白剂。     

荧光增白剂VBL的白度测量

叙述了荧光增白剂VBL的白度测量方法,建立了白度值与染色深度之间的函数关系,实验数据表明,荧光增白剂VBL的白度测量值WCIE与目测结果有很好的相关性,故“CIE1982白度公式”可以优选为白度测量的评价公式。0     

超能增白剂合丽亚BLF在洗衣粉中的应用研究

从粉体白度、织物白度和成本3方面分别对新型超能增白剂合丽亚 BLF(Heliya BLF)与3种常用的传统荧光增白剂(31#、33#及CBS-X)在无磷及含磷普通洗衣粉中的应用进行了研究。实验结果表明:新型超能增白剂合丽亚 BLF(Heliya BLF)在洗衣粉应用中的粉体白度、织物增白两方面都优于3种常用的传统荧光增白剂,洗衣粉的成本增加与31#、33#相当,但大大低于CBS-X,具有很高的性能价格比,显著提高了洗衣粉的去污力值,是传统增白剂理想的升级换代产品。同时合丽亚 BLF能够高浓度地配入液体洗涤剂中,产品外观透明,低温无沉淀浑浊,填补了国内液洗用增白剂的空白。     

超能增白剂合丽亚（R）BLF在洗衣粉中的应用研究

从粉体白度、织物白度和成本3方面分别对新型超能增白剂合丽亚 BLF(Heliya BLF)与3种常用的传统荧光增白剂(31#、33#及CBS-X)在无磷及含磷普通洗衣粉中的应用进行了研究.实验结果表明:新型超能增白剂合丽亚 BLF(Heliya BLF)在洗衣粉应用中的粉体白度、织物增白两方面都优于3种常用的传统荧光增白剂,洗衣粉的成本增加与31#、33#相当,但大大低于CBS-X,具有很高的性能价格比,显著提高了洗衣粉的去污力值,是传统增白剂理想的升级换代产品.同时合丽亚 BLF能够高浓度地配入液体洗涤剂中,产品外观透明,低温无沉淀浑浊,填补了国内液洗用增白剂的空白.     

洗涤剂用荧光增白剂—雪山XL

1979年上海合成洗涤剂三厂与上海染料研究所合作,研制成功新型的雪山荧光增白剂XL(原名#33荧光增白剂)。已正式投产,为我国高档洗衣粉提供了良好的荧米增白剂新品种。雪山XL同雪山#31、VBL荧光增白剂一样,均属双(三嗪氨基)芪二磺酸类。用于洗衣粉中能使粉色洁白悦目,对棉织物的累积洗涤白度、耐氯性是双(三嗪氨基)芪二磺酸类增白剂中最佳的品种。     

纸中荧光增白剂VBL的光老化规律研究

为解决涉案纸张物证老化时间的鉴定问题，本文通过液相色谱-荧光检测器和白度仪对打印纸中荧光增白剂VBL含量及纸张白度值进行了研究。结果表明，不同打印纸中VBL含量及白度值随纸张老化呈下降趋势。重现性实验表明，VBL与内标物峰面积比值的相对标准偏差为1.06%，并且纸张中不同部位取样的液相色谱图中两个主要色谱峰峰面积比值的相对标准偏差为9.23%和2.7%，表明取样位置不同，对实验结果无显著性差异。     

离子液体萃取-分光光度法测定纸中荧光增白剂

合成了六氟磷酸1-丁基-3-甲基-咪唑[Bmim][PF₆]离子液体,并用其对荧光增白剂VBL进行萃取。结果表明,当溶液酸度为pH 10,在10 mL溶液中,离子液体加入量为0.6 mL,在80℃萃取15 min,离子液体对荧光增白剂VBL的萃取率最大。荧光增白剂VBL的浓度在0～25μg·mL^-1范围内与吸光度呈线性关系,相关系数R=0.9985,方法的检出限为0.048μg·mL^-1,回收率在87.1%～94.2%之间。     

荧光增白剂的分散状态及其对PP白度的影响

通过使用透射电子显微、相差显微和粒度分布分析,对荧光增白剂OB和OB1的形态及在PP中的微观状态进行了研究,并结合对PP增白样板白度的测定,找到荧光增白剂分散状态与试样白度的关系。结果表明:荧光增白剂OB和OB1在添加量为0.02%～0.03%时,其在PP中大部分是以粒径小于5μm的凝聚体形式存在的。此时荧光增白剂对PP有最佳的增白效果,可将试样白度提高5～7。添加量低于0.02%时增白效果不明显。添加量高于0.03%时,由于荧光增白剂与PP相容性的关系,凝聚体开始形成大尺寸团聚体,此时增白效果下降,甚至降低试样白度。荧光增白剂的热性能和结晶性能的测试也被用来辅助上述研究。研究表明:尽管两种荧光增白剂OB和OB1的热性能和结晶性能相差较大,但它们的分散状态及对其白度的影响是类似的。     

国内洗涤剂用荧光增白剂的现状及发展建议

荧光增白剂(FWA)是一种无色的荧光染料,其产量约占全世界染料总量的10％。在洗衣粉中配入一定量的FWA(一般配合量：FWA量／洗衣粉总固体量为0．1％～0．5％)不但能改善洗衣粉本身的外观和白度,同时也增加了被洗涤物的白度和鲜艳度,改善洗涤效果,大大提高洗涤剂的商品价格,因此FWA也是洗涤剂配方中的一个重要组分。有资料介绍,目前世界上FWA消费量的50％是用于洗涤剂行业,其次是造纸、纺织印染、塑料等行业。1999年中国共生产合成洗涤剂305万t,按最低配合量0．1％计算,全年消耗FWA总量不少于3050t。     

Effects of different bleaching application durations on enamel in terms of tooth color,microhardness, and surface roughness

The aim of this research was to assess the color differences (?E₀₀), Vickers microhardness, whiteness index, and surface roughness values of different durations of bleaching the enamel. One hundred and eight teeth were utilized for color evaluation, roughness, and microhardness (n = 36). Teeth were assigned to three groups (n = 12) based on the durations of the bleaching application. Bleaching agent was applied for 20 minutes in group 1, 40 minutes in group 2, and 60 minutes in group 3. The color was measured with a Vita Easyshade Advance 4.0 spectrophotometer before applying the bleach, and 24 hours, 7, and 14 days after bleaching application. The CIEDE2000 and whiteness index for dentistry values were calculated. The microhardness and surface roughness values were obtained before application and 7 and 14 days after application. Data were analyzed using two-way ANOVA and post-hoc LSD tests Group 3 had the largest color and whiteness changes. The whiteness index for dentistry values were statistically significantly increased, considering baseline measurements within all groups (P < .05). For the Vickers micohardness values, in group 3, a statistically significant difference was observed among baseline, and 7 days after application (P < .05). However, the surface roughness values showed no significant difference in any measurement (P > .05). According to this research in all groups, effective whitening was accomplished. Based on the results evaluated for whiteness, color alteration, microhardness, and roughness, the optimal bleaching duration of application was in 40 minutes.     

提高日用细瓷产品质量的试验

针对我厂日用细瓷产吕白度下降、吸水率偏高．热稳定性能不良等质量问题，通过引入优质高岭土．调整坯料配方的研究，提高产品质量     

提高日用瓷白度值得注意的问题

本文主要讨论了提高日用瓷白度应从提高釉面白度及提高瓷胎半透明度着手，并叙述了提高瓷胎半透明度的方法。     

广西田阳高岭土精细化研究

在研究分析田阳高岭土物化性能的基础上,通过对新发现的高岭土精细化处理,使其纯度、白度、粒度等物性指标有了明显的改善,其中TiO2,Fe2O3质量分数明显降低,白度由原来的66%和70.2%提高到78.1%和82.3%,提高了10多个百分点,粒径的分布合理.为其开发应用,提供了相应实验数据.     

贵州毕节永安碗厂粘土的理化及工艺性能研究

从矿山采集具有代表性的粘土,球磨并过80目筛备用.利用X射线荧光光谱仪(XRF)、X射线衍射仪(XRD)、综合热分析仪(DTA-TG)、场发射扫描电子显微镜(FE-SEM)和透射电子显微镜(TEM)对粘土的化学成份、矿物组成、理化性质和微观形貌进行了表征,并详细考察了其多项工艺性能指标.研究结果表明:该粘士的主要矿物组成为伊利石(9.49 wt％)、累托石(45.36 wt％)和石英(43.68 wt％),呈典型的片状结构.该矿物原料可塑性良好、阳离子交换容量低、流动性较小、触变性较大、干燥收缩较大、干燥强度较低.由于该粘土矿物中碱金属和碱土金属总含量不高(4.25 wt％),因此烧结温度较高(烧结温度范围为1250～ 1300℃).该粘土矿物中Fe2 O3(0.72 wt％)和TiO2(0.27 wt％)总体含量不高,因此具有较高的烧成白度,1250℃下烧成的白度值为50.59％.     

抗热阻聚液提高PVC树脂白度的工业化试验

分析了影响聚氯乙烯（PVC）树脂白度的主要因素,通过改变聚合助剂的方法提高PVC树脂的白度,浅析了抗热阻聚（KZ）液增加树脂白度的机理.     

浅谈我公司对PVC树脂老化白度的研究

介绍了齐化化工有限责任公司对提高PVC树脂热老化白度的研究。采取的措施 :(1)单体中含铁量控制 2× 10 -6以下 ;(2 )在生产高型号PVC树脂时 ,加入可消耗高能自由基的链转移剂 ;(3)聚合转化率控制在 80 %左右时出料 ;(4 )加入 0 .0 2 %以下的C7-9Zn。改进后使PVC树脂的白度控制在 85 %、粘数为 85mL/g。     

Dependence of the whiteness of paper on surface roughness and illumination conditions

The dependence of paper whiteness on its surface roughness is studied by numerical modeling of measuring apparatus and specimen scattering properties. The dependencies computed for various specimen illumination conditions with and without allowing for the specular component of scattered light are compared. The whiteness is calculated by ISO/DIS 11475. It is found that the whiteness of the object under study depends on both surface roughness and the illumination scheme selection, whereas the chromaticity coordinates depend on neither of them. © 2000 John Wiley & Sons, Inc. Col Res Appl, 25, 170–175, 2000     

萍乡南坑高岭土增白实验研究

本文研究了提纯剂(柠檬酸钠和NaOH按一定比例配置)、还原剂(Na2S2O4)和稳定剂(草酸)用量对高岭土增白效果的影响.实验结果表明:当提纯剂用量为0.4%、还原剂用量0.2%、稳定剂用量0.3%时试样增白效果较好,由原来的62.3°增加到了86.50°.