Phase Transition and Ferroelectric Characteristics of Pb[(Mg1/3Nb2/3)1-xTix]O3 Ceramics Modified with La(Mg2/3Nb1/3)O3

The effects of 0–5 mol% addition of La(Mg_2/3Nb_1/3)O₃ (LMN) on the phase transition and ferroelectric behaviors of Pb[(Mg_1/3Nb_2/3)_1-xTi_x]O₃ (PMNT) ceramics with compositions near the morphotropic phase boundary (MPB) were studied. An evolution of structure from rhombohedral to tetragonal was found with increasing PbTiO₃ (PT) content across the MPB (at ∼32.5 mol% PT), and a coexistence of both rhombohedral and tetragonal phases was also found at the MPB. The dual-phase field extended toward the lower PT content side of the MPB, and, moreover, the rhombohedrality or tetragonality was reduced, especially for the compositions near the MPB, by the addition of La in PMNT. The ferroelectric transition was found to change from normal to diffuse as the La content increased and the compositions became more rhombohedral. In accordance with the structural evolution, the change of remanent polarization ( P _r) and coercive field ( E _c) also became gradually indistinct, and both P _r and E _c were reduced. For compositions near the MPB, both PMNT and La-modified PMNT had a similar electromechanical factor ( k _p) in a range around 0.55–0.60, but the mechanical quality factor ( Q _m) was significantly reduced for the La-modified PMNT. The piezoelectric coefficient ( d ₃₃), however, was largely improved with increasing La content in PMNT of compositions at MPB. A high value of d ₃₃∼ 815 pC/N was obtained for the 5-mol%-La-modified ceramics, but it was associated with a low value of Q _m.     

Ferroelectric 90° Domain Evaluation in Tetragonal Pb(Mg1/3Nb2/3)O3–PbTiO3 Ceramics

The domain structure of ferroelectrics changes during poling has a direct influence on the macroscopic properties of the materials. The intensity variation of the different X-ray diffraction (XRD) pattern profiles was used to identify the percentage of 90° domain reorientation in the tetragonal phase of Pb(Mg_1/3Nb_2/3)O₃–PbTiO₃ (PMN–PT) ceramics after poling. The results are consistent with the change of piezoelectric properties. In addition, by using XRD patterns, a spatial distribution of polarization in a well-poled 0.62PMN–0.38PT ceramics has been determined and was found to be best described by the Cauchy function W _00l (φ)=1/(1+0.023φ²).     

Double Precursor Solution Coating Approach for Low-Temperature Sintering of [Pb(Mg1/3Nb2/3)O3]0.63[PbTiO3]0.37 Solids

Lead-based piezoelectric ceramics typically require sintering temperatures higher than 1000°C at which significant lead loss can occur. Here, we report a double precursor solution coating (PSC) method for fabricating low-temperature sinterable polycrystalline [Pb(Mg_1/3Nb_2/3)O₃]_0.63-[PbTiO₃]_0.37 (PMN–PT) ceramics. In this method, submicrometer crystalline PMN powder was first obtained by dispersing Mg(OH)₂-coated Nb₂O₅ particles in a lead acetate/ethylene glycol solution (first PSC), followed by calcination at 800°C. The crystalline PMN powder was subsequently suspended in a PT precursor solution containing lead acetate and titanium isopropoxide in ethylene glycol to form the PMN–PT precursor powder (second PSC) that could be sintered at a temperature as low as 900°C. The resultant d ₃₃ for samples sintered at 900°, 1000°, and 1100°C for 2 h were 600, 620, and 700 pm/V, respectively, comparable with the known value. We attributed the low sintering temperature to the reactive sintering nature of the present PMN–PT precursor powder. The reaction between the nanosize PT and the submicrometer-size PMN occurred roughly in the same temperature range as the densification, 850°–900°C, thereby significantly accelerating the sintering process. The present PSC technique is very general and should be readily applicable to other multicomponent systems.     

Single-Calcination Synthesis of Pyrochlore-Free 0.9Pb(Mg1/3Nb2/3)O3–0.1PbTiO3 and Pb(Mg1/3Nb2/3)O3 Ceramics Using a Coating Method

A coating approach for synthesizing 0.9Pb(Mg_1/3Nb_2/3)O₃–0.1PbTiO₃ (0.9PMN–0.1PT) and PMN using a single calcination step was demonstrated. The pyrochlore phase was prevented by coating Mg(OH)₂ on Nb₂O₅ particles. Coating of Mg(OH)₂ on Nb₂O₅ was done by precipitating Mg(OH)₂ in an aqueous Nb₂O₅ suspension at pH 10. The coating was confirmed using optical micrographs and zeta-potential measurements. A single calcination treatment of the Mg(OH)₂-coated Nb₂O₅ particles mixed with appropriate amounts of PbO and PbTiO₃ powders at 900°C for 2 h produced pyrochlore-free perovskite 0.9PMN–0.1PT and PMN powders. The elimination of the pyrochlore phase was attributed to the separation of PbO and Nb₂O₅ by the Mg(OH)₂ coating. The Mg(OH)₂ coating on the Nb₂O₅ improved the mixing of Mg(OH)₂ and Nb₂O₅ and decreased the temperature for complete columbite conversion to ∼850°C. The pyrochlore-free perovskite 0.9PMN–0.1PT powders were sintered to 97% density at 1150°C. The sintered 0.9PMN–0.1PT ceramics exhibited a dielectric constant maximum of ∼24 660 at 45°C at a frequency of 1 kHz.     

Piezoelectric Resonances, Linear Coefficients and Losses of Morphotropic Phase Boundary Pb(Mg1/3Nb2/3)O3–PbTiO3 Ceramics

A method based on the use of four piezoelectric resonances for three sample geometries that allows obtaining the full set of linear electric, mechanical, and electromechanical coefficients, and all related losses of a piezoelectric ceramic has been applied to Mn-doped 0.655Pb(Mg_1/3Nb_2/3)O₃–0.345PbTiO₃ at the morphotropic phase boundary (MPB PMN–PT). Length-poled MPB PMN–PT ceramic plates presented piezoelectric shear double resonances associated with a thickness gradient of tetragonal and rhombohedral (or monoclinic) phases that originated during poling. The versatility of the method still allowed addressing these double resonances and obtaining all the linear coefficients and losses of the well-poled material. These are given for MPB PMN–PT and compared with those of a Navy type II Pb(Zr,Ti)O₃ (PZT) ceramic. MPB PMN–PT presents piezoelectric coefficients as high as soft PZT but significantly lower losses, and so less overheating and hysteresis under high driving fields. Its thermal stability has been studied up to 100°C, and the temperature dependence of a number of linear coefficients and of the thickness and planar coupling factors and frequency constants of disks has been obtained. The latter thickness parameters hardly changed with temperature, while planar ones showed a relative variation of 10%.     

Preparation and Characterization of Relaxor Ferroelectric 0.65Pb(Mg1/3Nb2/3)O3–0.35PbTiO3 by a Polymerizable Complex Method

A modified polymerizable complex (PC) method for the preparation of the relaxor ferroelectric 0.65Pb(Mg_1/3Nb_2/3)O₃–0.35PbTiO₃ (PMN–PT) ceramics has been developed using a novel water-soluble Nb precursor. The effects of Pb content and sintering temperature on the structure, morphology, composition, and electrical properties of PMN–PT powders and ceramics were investigated systematically. It was found that the modified PC method could effectively reduce the initial crystallization temperature of the perovskite phase to 500°C. For PMN–PT samples with 15% excess Pb content sintered at 600°C for 2 h, the 87% perovskite phase can be achieved, which is much higher than that in conventional solid-state reactions and other solution-based methods at the same temperature. On further increasing the sintering temperature to 1100°C, the perovskite phase content basically remains constant. This is attributed to the Pb-deficient pyrochlore phase formation. On increasing the sintering temperature to 1250°C, the dielectric constant and remnant polarization of PMN–PT ceramics significantly improved due to the larger grain sizes, enhanced density, and the decreasing pyrochlore phase. PMN–PT ceramics with a 98.5% content of the perovskite phase have been fabricated at 1250°C. It displays typical ferroelectric relaxor characteristics with a remnant polarization of 18 μC/cm², a coercive field of 9.6 kV/cm, a piezoelectric coefficient of d ₃₃=360 pC/N, and room-temperature and maximum dielectric constants of 3600 and 10 500 at 1 kHz, respectively.     

High Piezoelectric and Dielectric Properties of La-Doped 0.3Pb(Zn1/3Nb2/3)O3–0.7Pb(ZrxTi1−x)O3 Ceramics Near Morphotropic Phase Boundary

La-doped 0.3Pb(Zn_1/3Nb_2/3)O₃–0.7Pb(Zr _x Ti_{1− x} )O₃ ( x =0.5–0.53) piezoelectric ceramics with pure perovskite phase were synthesized by a two-step hot-pressing route. The piezoelectric properties of various compositions near the morphotropic phase boundary (MPB) were systematically investigated. Not only was the exact MPB of this system determined via X-ray diffractometry analysis, but also the peak of piezoelectric properties was found near the MPB. The optimum piezoelectric properties of this series were observed in the specimen with Zr/Ti=51/49. The piezoelectric coefficient ( d ₃₃) and electromechanical coupling factor ( k _p) were 845 pC/N and 0.70, respectively, which have not been reported in this system so far. Large permittivity (ɛ_r=4088) and permittivity maximum (ɛ_m=29 500) were also obtained for the poled specimens. The temperatures ( T _max) of the permittivity maxima ranged from 206° to 213°C with various Zr/Ti ratios.     

High Strain, 〈001〉 Textured 0.675Pb(Mg1/3Nb2/3)O3–0.325PbTiO3 Ceramics: Templated Grain Growth and Piezoelectric Properties

Lead magnesium niobate–lead titanate, 0.675Pb(Mg_1/3Nb_2/3)O₃–0.325PbTiO₃ (PMN–32.5PT) ceramics were textured (grain-oriented) in the 〈001〉-crystallographic direction by the templated grain growth process. The textured PMN–32.5PT ceramics were produced by orienting {001}-SrTiO₃ (ST) platelets (∼10 μm in diameter and ∼2-μm thickness) in a submicron PMN–32.5PT matrix. The templated growth of 〈001〉-oriented PMN–32.5PT grains on the ST platelets resulted in textured ceramics with ∼70% Lotgering factor and >98% theoretical density. Unlike most lead-based ceramics, excess PbO was not needed for sintering or grain growth. Based on unipolar stain-field measurements at 0.2 Hz, the textured samples displayed >0.3% strain at 50 kV/cm. Low-field d ₃₃-coefficients of >1600 pC/N (<5 kV/cm) were measured directly from unipolar measurements. The low drive field d ₃₃-piezoelectric coefficient of the highly textured samples is two times greater than polycrystalline PMN–32.5PT.     

B-Site Order–Disorder Transition in Pb(Mg1/3Nb2/3)O3–Pb(Mg1/2W1/2)O3 Triggered by Mechanical Activation

B-site cation order–disorder transition induced by mechanical activation was observed in Pb(Mg_1/3Nb_2/3)O₃–Pb(Mg_1/2W_1/2)O₃ (PMN–PMW) solid solution, which was examined using both XRD diffraction and Raman spectroscopic study. The order–disorder transition is composition dependent. Mechanical activation triggers the B-site disordering, which can be steadily recovered by thermal annealing at elevated temperature, i.e., at temperatures around 600°C. Raman spectroscopy demonstrated that there existed tiny ordered microdomains in 0.4PMN·0.6PMW subjected to up to 20 h of mechanical activation, although they cannot be shown by X-ray diffraction. This is a result of the equilibrium between the mechanical destruction and temperature-facilitated recovering at the collision points during mechanical activation. It is therefore unlikely that a complete disordering can be realized in PMN–PMW by mechanical activation. The disordering in PMN–PMW triggered by mechanical activation occurs simultaneously with the refinement in crystallite size at the initial stage of mechanical activation, suggesting that the fragmentation of crystallites is responsible for the order–disorder transition at least during the initial stage of mechanical activation.     

Preparation of 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 Thin Films Via a Polyvinylpyrrolidone-Assisted Aqueous Sol–Gel Process and Dielectric Properties

Pb(Mg_1/3Nb_2/3)O₃–PbTiO₃ (PMN–PT) thin films were prepared by spin coating using aqueous solutions of metal salts containing polyvinylpyrrolidone, where niobium oxide layers and lead—magnesium–titanium oxide layers were laminated on Pt(111)/TiO _x /SiO₂/Si(100) substrates and fired at 750° or 800°C. 250 ± 20 nm thick 0.7PMN–0.3PT thin films of a single-phase perovskite could be prepared, and the film fired at 750°C had dielectric constants and dielectric loss of 1900 ± 350 and 0.13 ± 0.03, respectively, exhibiting polarization-electric field hysteresis with a remanent polarization of 5.1 μC/cm² and a coercive field of 21 kV/cm.     

Microwave Dielectrics in the (La1/2Na1/2)TiO3–Ca(Fe1/2Nb1/2)O3 System

Dielectric properties of the system (1 − x)(La_1/2Na_1/2)TiO₃– _x Ca(Fe_1/2Nb_1/2)O₃, where 0.4 # x # 0.6, have been investigated at microwave frequencies. The temperature coefficient of resonant frequency (τ_f), nearly 0 ppm/°C, was realized at x = 0.58. These ceramics had perovskite structure and showed relatively low dielectric losses. A new dielectric material applicable to microwave devices having Q · f of 12000–14000 GHz and a dielectric constant (ε_r) of 59–60 has been obtained at 1300–1350°C for 5–15 h sintering.     

Dielectric Properties of Ceramics in Ba (Co1/3 Nb2/3)O3–Ba(Zn1/3Nb2/3)O3 Solid Solution

The dielectric properties of the Ba (Co_1/3 Nb_2/3)O₃–Ba(Zn_1/3Nb_2/3)O₃ system were determined. Ba (Co_1/3 Nb_2/3)O₃–Ba(Zn_1/3Nb_2/3)O₃ has a complex perovskite structure, a high dielectric constant, a low dielectric loss, and a low temperature coefficient of the resonant frequency. A solid-solution ceramic with 0.7Ba (Co_1/3 Nb_2/3)O₃·0.3 Ba(Zn_1/3Nb_2/3)O₃ has a dielectric constant of K=33.5, Q=11000 at 6.5 GHz, and a temperature coefficient of the resonant frequency of τ_f=0 ppm/°C. The temperature coefficient of resonant frequency can be varied by changing the composition. The Q values of the ceramics can be increased by annealing in a nitrogen atmosphere. These ceramics can be used for resonant elements and stabilized oscillators.     

Kinetics of {001} Pb(Mg1/3Nb2/3)O3–35 mol% PbTiO3 Single Crystals Grown by Seeded Polycrystal Conversion

The kinetics of {001}-oriented Pb(Mg_1/3Nb_2/3)O₃–35 mol% PbTiO₃ (PMN–35PT) single crystals grown by seeded polycrystal conversion were systematically quantified as a function of excess PbO liquid phase. The coarsening behavior of the corresponding matrix grains was similarly quantified. Single-crystal seed plates were embedded in a matrix of PMN-35PT with varying amounts of liquid phase (PbO) content in the range of 0 to 5 vol% and annealed at 1150°C for 0–10 h. Apparent maxima in the growth rates were observed at a PbO content of ∼3 vol% for both the single crystal and matrix grains. In both cases, the growth data were found to most closely follow cubic growth kinetics. Implications regarding the effect of PbO volume fraction on the matrix and single-crystal growth mechanisms are discussed.     

Elastic, Piezoelectric, and Dielectric Properties of 0.71Pb(Mg1/3Nb2/3)O3–0.29PbTiO3 Crystals Obtained by Solid-State Crystal Growth

Single crystals with the composition of 0.71Pb(Mg_1/3Nb_2/3)O₃–0.29PbTiO₃ (PMNT29) were grown using the solid-state crystal growth (SSCG) method. Compared with the conventional Bridgman grown crystals, the SSCG PMNT29 crystals were found to possess comparable piezoelectric, dielectric, and electromechanical properties ( d ₃₃∼1500 pC/N, ɛ^T ₃₃/ ɛ ₀∼5400 and k ₃₃∼90%), with the same Curie temperature ( T _C) and ferroelectric phase transformation temperature ( T _{R – T} ). The full set of elastic, piezoelectric, and dielectric material constants were determined by the resonance method for the SSCG grown PMNT29 crystals according to IEEE standards and compared with Bridgman grown crystals. The dielectric temperature behavior and the strain field characteristics were investigated, demonstrating excellent performance over the temperature range from room temperature to 95°C. Strain behavior at high electric fields was found to be different from Bridgman growth crystals and believed to be attributed to different domain structures.     

Single-Calcination Synthesis Mechanism of Pure-Perovskite Pb(Ni1/3Nb2/3)O3-PbTiO3 Using a Coating Method

Pure-perovskite 0.64Pb(Ni_1/3Nb_2/3)O₃–0.36PbTiO₃ (PNN–PT) powder has been successfully synthesized by only one-step calcination using a coating method. SEM photograph shows that PNN–PT powder with the size of 2–4 μm is cubic and well dispersed. Based on X-ray diffraction analysis, solid-state reactions in the process of calcination in PbO–Nb₂O₅–TiO₂–NiO system are investigated. In comparison with conventional solid state method, the single-calcination synthesis mechanism of pyrochlore-free lead-based niobate ferroelectrics using a coating method is tentatively proposed. A typical coating structure of Ni precipitate-coated Nb₂O₅ powder facilitates the formation of perovskite PNN–PT phase at a relatively low calcination temperature, resulting in the successful synthesis of pyrochlore-free PNN–PT powder in one-step calcination at 900°C.     

Low-Temperature, Single Step, Reactive Sintering of Lead Magnesium Niobate Using Mg(OH)2-Coated Nb2O5 Powders

A low-temperature, single step, reactive sintering method for Pb(Mg_1/3Nb_2/3)O₃ (PMN) and PMN–PbTiO₃ (PMN–PT) processing was developed based on the coating of Mg(OH)₂ on Nb₂O₅. This method simplified the processing of PMN and PMN–PT to a single step of heat-treatment and decreased the sintering temperature to 1000°C. It was found that the pyrochlore phase formation reaction at 500°C reduced the particle size to 130 nm. The overlap of the pyrochlor-perovskite phase transformation between 700° and 900°C and the densification process between 800° and 1000°C improved the sintering process. These two factors were the major reasons of the low temperature sintering.     

Electromechanical Properties of Pb(Yb1/2Nb1/2)O3-PbZrO3-PbTiO3 Ceramics

The electromechanical and electric-field-induced strain properties of x Pb(Yb_1/2Nb_1/2)O₃· y PbZrO₃·(1− x − y )PbTiO₃ ( x = 0.12, 0.25, 0.37; y = 0.10–0.40) ceramics have been studied systematically as a function of Pb(Yb_1/2Nb_1/2)O₃ (PYN) content and PbZrO₃/PbTiO₃ (PZ/PT) ratio. In addition, the effect of MnO₂ on the electromechanical properties of 0.12Pb(Yb_1/2Nb_1/2)O₃·0.40PbZrO₃·0.48PbTiO₃ was also investigated. The maximum transverse strain values of 1.6 × 10⁻³ for x = 0.12, 1.45 × 10⁻³ for x = 0.25, and 1.36 × 10⁻³ for x = 0.37 were obtained at the compositions which were regarded as the morphotropic phase boundary (MPB). The transverse strain was maximized at the MPB composition. The value of the maximum electromechanical coupling coefficient was 0.69 for y = 0.40 and x = 0.12 composition. In the 0.12Pb(Yb_1/2Nb_1/2)O₃·0.40PbZrO₃·0.48PbTiO₃ composition, the temperature of the maximum dielectric constant decreased and the grain size increased with an addition of MnO₂. The electromechanical coupling coefficient decreased while the mechanical quality factor rapidly increased with an addition of MnO₂. These resulted mainly from the acceptor effect of manganese ions that were produced by doping MnO₂ into the perovskite structure.     

Mechanosynthesis and Thermal Stability of Piezoelectric Perovskite 0.92Pb(Zn1/3Nb2/3)O3–0.08PbTiO3 Powders

The mechanosynthesis of piezoelectric perovskite 0.92Pb(Zn_1/3Nb_2/3)O₃–0.08PbTiO₃ (PZN–PT) by direct mechanochemical activation of the constituent oxides has been studied by X-ray diffraction (XRD) and transmission electron microscopy (TEM). This and the PbO flux method are the only two procedures that have succeeded in synthesizing this phase, which has recently been shown to present very high electromechanical response. The thermal stability of the single perovskite phase powders has been studied by differential thermal analysis/thermogravimetry and by high-temperature XRD as a function of mechanical activation time and pressure. The phase was found to transform into a pyrochlore type structure at temperatures above 400°C. The transformation presented a significant time dependence, and it was slowed down by increasing mechanical activation time and by the application of pressures by hot pressing. Sintering experiments were accomplished and 85% density, 77% perovskite-phase ceramics were obtained after heating at 1000°C for 1 h. Hot pressing at this temperature failed to increase the percentage of perovskite phase. Results are discussed, and procedures for obtaining dense single-phase PZN–PT-based ceramics with ultrahigh piezoelectricity are proposed.     

Kinetics of Templated Grain Growth of 0.65Pb(Mg1/3Nb2/3)O3·0.35PbTiO3

Single-crystal layers of 0.65Pb(Mg_1/3Nb_2/3)O₃·0.35PbTiO₃ (PMN-35PT) were grown heteroepitaxially on {001}-BaTiO₃ template crystals. A {001}-BaTiO₃ crystal was embedded in a fine-grained matrix of PMN-35PT containing excess PbO and heated between 950° and 1150°C for 0–5 h. The initial growth of the PMN-35PT on the {001} surface and the growth of the matrix grains both displayed a t ^1/3 dependence which is characteristic of diffusion-controlled growth. Growth was limited to ∼100–150 μm due to the significantly reduced driving force at longer times because of matrix coarsening and porosity evolution.