Pervaporation separation of water/isopropanol mixtures through crosslinked carboxymethyl chitosan/polysulfone hollow‐fiber composite membranes

Carboxymethyl chitosan (CMCS)/polysulfone (PS) hollow‐fiber composite membranes were prepared through glutaraldehyde (GA) as the crosslinking agent and PS hollow‐fiber ultrafiltration membrane as the support. The permeation and separation characteristics for dehydration of isopropanol were investigated by the pervaporation method. Pure chitosan, carboxymethyl chitosan, and crosslinked carboxymethyl chitosan membranes were characterized by Fourier transform infrared (FT‐IR) spectroscopy and X‐ray diffraction (XRD) to study the crosslinking reaction mechanism and degree of crystallinity, respectively. The effects of feed composition, crosslinking agent, membrane thickness, and feed temperature on membrane performance were investigated. The results show that the crosslinked CMCS/PS hollow‐fiber composite membranes possess high selectivity and promising permeability. The permeation flux and separation factor for isopropanol/water is 38.6 g/m²h and 3238.5, using 87.5 wt % isopropanol concentration at 45°C, respectively. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 1959–1965, 2007     

Preparation and characterization of poly(vinyl chloride)/polystyrene/poly(ethylene glycol) hollow‐fiber ultrafiltration membranes

Hollow‐fiber ultrafiltration (UF) membranes were prepared from blends of poly(vinyl chloride) (PVC) and polystyrene (PS) with a dry/wet phase inversion method. Poly(ethylene glycol) (PEG) and N,N‐dimethylacetamide were used as the additive and solvent, respectively. The effects of the PEG concentration in the dope solution as an additive on the cross sections and inner and outer surface morphologies, permeability, and separation performance of the hollow fibers were examined. The mean pore size, pore size distribution, and mean roughness of both the inner and outer surfaces of the produced hollow fibers were determined by atomic force microscopy. Also, the mechanical properties of the hollow‐fiber membranes were investigated. UF experiments were conducted with aqueous solutions of poly(vinyl pyrrolidone) (PVP; K‐90, M_w = 360 kDa). From the results, we found that the PVC/PS hollow‐fiber membranes had two layers with a fingerlike structure. These two layers were changed from a wide and long to a thin and short morphology with increasing PEG concentration. A novel and until now undescribed shape of the nodules in the outer surfaces, which was denoted as a sea‐waves shape, was observed. The outer and inner pore sizes both increased with increasing PEG concentration. The water permeation flux of the hollow fibers increased from 104 to 367 L m^?2 h^?1 bar^?1) at higher PEG concentrations. The PVP rejection reached the highest value at a PEG concentration of 4 wt %, whereas at higher values (from 4 to 9 wt %), the rejection decreased. The same trend was found also for the tensile stress at break, Young's modulus, and elongation at break of the hollow fibers. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 989‐1004, 2013     

Polyvinyl alcohol/polysulfone (PVA/PSF) hollow fiber composite membranes for pervaporation separation of ethanol/water solution

Polysulfone (PSF) hollow fiber membranes were spun by phase‐inversion method from 29 wt % solids of 29 : 65 : 6 PSF/NMP/glycerol and 29 : 64 : 7 PSF/DMAc/glycol using 93.5 : 6.5 NMP/water and 94.5 : 5.5 DMAc/water as bore fluids, respectively, while the external coagulant was water. Polyvinyl alcohol/polysulfone (PVA/PSF) hollow fiber composite membranes were prepared after PSF hollow fiber membranes were coated using different PVA aqueous solutions, which were composed of PVA, fatty alcohol polyoxyethylene ether (AEO₉), maleic acid (MAC), and water. Two coating methods (dip coating and vacuum coating) and different heat treatments were discussed. The effects of hollow fiber membrane treatment methods, membrane structures, ethanol solution temperatures, and MAC/PVA ratios on the pervaporation performance of 95 wt % ethanol/water solution were studied. Using the vacuum‐coating method, the suitable MAC/PVA ratio was 0.3 for the preparation of PVA/PSF hollow fiber composite membrane with the sponge‐like membrane structure. Its pervaporation performance was as follows: separation factor (α) was 185 while permeation flux (J) was 30g/m²·h at 50°C. Based on the experimental results, it was found that separation factor (α) of PVA/PSF composite membrane with single finger‐void membrane structure was higher than that with the sponge‐like membrane structure. Therefore, single finger‐void membrane structure as the supported membrane was more suitable than sponge‐like membrane structure for the preparation of PVA/PSF hollow fiber composite membrane. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 247–254, 2005     

Effect of operation conditions in the pervaporation of ethanol–water mixtures with poly(1‐trimethylsilyl‐1‐propyne) membranes

Poly(1‐trimethylsilyl‐1‐propyne) (PTMSP) is known to show preferential permeation of ethanol in the pervaporation of ethanol–water mixture. Although this polymer presents good characteristics for the separation of organic–water solutions, operation conditions and membrane characteristics, such as thickness, affect its pervaporation performance. The effect of temperature and feed concentration on pervaporation was studied. During pervaporation of 10 wt % ethanol–water solution, the separation factor (α_H2O^EtOH) remains almost constant, whereas the permeation flux (F) increases exponentially with operation temperature. On the other hand, the separation factor decreases, whereas the permeation flux increases with ethanol content in the feed mixture. The membrane thickness also affects the performance of PTMSP polymer films: selectivity increases sharply with membrane thickness up to 50 μm, whereas it remains constant for thicker membranes. The permeation flux decreases with membrane thickness in the whole range studied. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94:1395–1403, 2004     

管式支撑体内表面NaA分子筛膜的合成与表征

采用转动合成方式通过二次生长法在管式α-Al₂O₃支撑体内表面合成了NaA分子筛膜,采用X射线衍射仪（XRD）、场发射扫描式电子显微镜（FE-SEM）和渗透汽化分离技术对所合成的膜进行了系统表征。考察了合成釜转速对分子筛膜合成的影响,结果表明合成釜转速的提高有利于分子筛膜合成。在转速为4 r·min^-1时所合成NaA分子筛膜分离因子高达2370,渗透通量1.86 kg·h^-1·m^-2左右（乙醇/相似文献   

Teflon AF2400/Ultem composite hollow fiber membranes for alcohol dehydration by high‐temperature vapor permeation

High‐temperature vapor permeation has a stringent requirement of membrane stability under harsh feed environments. This work reports the design of Teflon AF2400/Ultem composite hollow fiber (HF) membranes for alcohol dehydration via vapor permeation. Fabrication parameters such as Teflon concentration and coating time were systematically investigated. Interestingly, the fabricated composite HF membranes possess an unusual surface with honeycomb‐like microstructure patterns. Owing to the Teflon protective layer, the newly developed composite HF shows a promising and stable separation performance with a flux of 4265 gm^?2 h^?1 and a separation factor of 383 for 95% isopropanol dehydration at 125°C. The composite HF also performs well under extreme vapor feed compositions from 87 to 99 wt % isopropanol. In addition, it exhibits impressive separation performance for the dehydration of ethanol and n‐butanol. This work may provide useful insights of designing thermal‐stable and high‐performance composite polymeric membranes for vapor permeation. © 2016 American Institute of Chemical Engineers AIChE J, 62: 1747–1757, 2016     

A study on the characteristics and pervaporation performance of polyamide thin‐film composite membranes with modified polyacrylonitrile as substrate for bioethanol dehydration

To improve the pervaporation performance in separating an aqueous ethanol solution, polyamide thin‐film composite (TFC) membranes (m‐tolidine‐H‐TMC/mPAN) were prepared through the interfacial polymerization reaction between trimesoyl chloride (TMC) and 2,2'‐dimethylbenzidine hydrochloride (m‐tolidine‐H) on the surface of a modified polyacrylonitrile (mPAN) membrane. The effects of the feed ethanol concentration on the pervaporation performance and the durability of m‐tolidine‐H‐TMC/mPAN TFC membranes were investigated. To choose the optimal mPAN membrane as the TFC substrate, the effect of hydrolysis time on the chemical properties and separation performance of an mPAN substrate was also studied. An appropriate hydrolysis time of 15 min was chosen to obtain the mPAN substrate due to the corresponding high permeation flux. The m‐tolidine‐H‐TMC/mPAN TFC membrane exhibited a high pervaporation performance for ethanol dehydration. A positron annihilation lifetime spectroscopy experiment was used to estimate the mean free‐volume radius of the m‐tolidine‐H‐TMC polyamide selective layer, which lay between the radii of the water and ethanol molecules. © 2013 Society of Chemical Industry     

Pervaporation of water/alcohol mixtures through chitosan/cellulose acetate composite hollow‐fiber membranes

For the purpose of separating aqueous alcohol by the use of pervaporation technique, a composite membrane of chitosan (CT) dip‐coated cellulose acetate (CA) hollow‐fiber membranes, CT‐d‐CA, was investigated. The effects of air‐gap distance in the spinning of CA hollow‐fiber membranes, chitosan concentration, and sorts of aqueous alcohol solutions on the pervaporation performances were studied. Compared with unmodified CA hollow‐fiber membrane, the CT‐d‐CA composite hollow‐fiber membrane effectively increases the permselectivity of water. The thickness of coating layer increases with an increase in chitosan concentration. As the concentration of chitosan solution increased, the permeation rate decreased and the concentration of water in the permeate increased. In addition, the effects of feed composition and feed solution temperature on the pervaporation performances were also investigated. The permeation rate and water content in permeate at 25°C for a 90 wt % aqueous isopropanol solution through the CT‐d‐CA composite hollow‐fiber membrane with a 5‐cm air‐gap distance spun, 2 wt % chitosan dip‐coated system were 169.5 g/m² h and 98.9 wt %, respectively. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 1562–1568, 2004     

Second interfacial polymerization of thin-film composite hollow fibers with amine-cyclodextrins for pervaporation dehydration

High performance thin-film composite (TFC) hollow fiber membranes have been developed for pervaporation dehydration by second interfacial polymerization (SIP) modification with three kinds of amine-functionalized β-cyclodextrin (amine-CDs), which were synthesized by modifying β-CD with ammonia, ethylenediamine (EDA), and tris(2-aminoethyl)amine, respectively. The chemical properties of amine-CDs and SIP-modified TFC membranes were characterized by various techniques. The effects of amine-CD type and SIP parameters (pH or concentration of CD-EDA solution) were studied systematically to acquire the optimized selective layer of TFC membranes for ethanol dehydration. Among all SIP-modified TFC membranes, the one with SIP by 2 wt% CD-EDA aqueous solution (pH = 2) exhibited the most outstanding separation performance with a ultrahigh permeation flux (3,018.0 ± 12.0 g/m² hr) and permeate concentration (98.7 ± 0.2 wt% water) at 50°C (equivalent to separation factor of 415), contributed by the effectively incorporated CD with rich hydrophilic functional groups and intrinsic nanocavities facilitating the passage of water molecules.     

A polyvinyl alcohol-based mixed matrix membrane with uniformly distributed Schiff base network-1 for ethanol dehydration

In this study, Schiff base network (SNW)-1 nanoparticles with high hydrophilicity and large specific surface area were used to prepare polyvinyl alcohol (PVA)-based mixed matrix membranes (MMMs), which were evaluated for ethanol dehydration. Because of the low difference of density between SNW-1 and PVA, the as-prepared nanoparticles can be uniformly distributed into the PVA active layer. The effects of SNW-1 loading, feed temperature, and water concentration on pervaporation (PV) performance were further studied. The results showed the MMM with 10 wt% of SNW-1 loading exhibited a separation factor of 1,501 and a permeation flux of 187 g m⁻² h⁻¹ for feeding 95 wt% ethanol/water binary solution at 75°C. Overall, the SNW-1/PVA MMMs showed great prospect in ethanol dehydration via PV.     

Modified polydimethylsiloxane/polystyrene blended IPN pervaporation membrane for ethanol/water separation

In this article a modified polydimethylsiloxane (PDMS) blended polystyrene (PS) interpenetrating polymer network (IPN) membranes supported by Teflon (polytetrafluoroethylene) ultrafiltration membrane were prepared for the separation of ethanol in water by pervaporation application. The relationship between the surface characteristics of the surface‐modified PDMS membranes and their permselectivity for aqueous ethanol solutions by pervaporation are discussed. The IPN supported membranes were prepared by sequential IPN technique. The IPN supported membrane were tested for the separation performance on 10 wt % ethanol in water and were characterized by evaluating their mechanical properties, swelling behavior, density, and degree of crosslinking. The results indicated that separation performance, mechanical properties, density, and the percentage of swelling of IPN membranes were influenced by degree of crosslink density. Depending on the feed temperature, the supported membranes had separation factors between 2.03 and 6.00 and permeation rates between 81.66 and 144.03 g m^?2 h^?1. For the azeotropic water–ethanol mixture (10 wt % ethanol), the supported membrane had at 30°C a separation factor of 6.00 and a permeation rate of 85 g m^?2 h^?1. Compared to the PDMS supported membranes, the PDMS/PS IPN supported blend membrane ones had a higher selectivity but a somewhat lower permeability. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Pervaporation dehydration of water/ethanol/ethyl acetate mixtures using poly(vinyl alcohol)–silica hybrid membranes

The novel organic–inorganic hybrid membranes were prepared from poly(vinyl alcohol) (PVA) and vinyltriethoxysilane (VTES). They were characterized using Fourier transform infrared (FTIR), X‐ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), thermogravimetric analysis (TGA), and contact angle metering. The as‐prepared membranes are formed at a molecular scale at a low VTES content. Aggregations in the surface of the as‐prepared membranes were clearly evident above 18.43 wt % VTES loading. The introduction of VTES into the PVA matrix resulted in a decrease in the crystalline and an increase in compactness and thermal stability of the as‐prepared membranes. Silica hybridization reduced the swelling of the as‐prepared membranes in water/ethanol/ethyl acetate mixtures, decreased the permeation flux, and remarkably enhanced water permselectivity in pervaporation dehydration of ethanol/ethyl acetate aqueous solution. The hybrid membrane with 24.04 wt % VTES has the highest separation factor of 1079 and permeation flux of 540 g m^?2 h^?1. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Application of jojoba wax bound to polyethylene membranes and hollow fibers in ion‐exchange and pervaporation processes

Chlorosulfonated polyethylene membranes and hollow fibers were reacted with allylic amino jojoba to bind the wax chemically to the polymer. The modified membranes and hollow fibers were then tested in the ion‐exchange and pervaporation processes, respectively. The jojoba‐bound polyethylene membranes were selective in preventing transfer of divalent ions such as Ca²⁺ and Mg²⁺, while monovalent ion such as K⁺ and Na⁺ could penetrate the membranes. The flux of the monovalent ions depended on the amount of jojoba bound to the polymer, which acted as a barrier to the ions (the monovalent ions could be eluted by acid washing). The concentration of ions (in the range of 0.05–1.0 N) in the feed solution had little effect on the flux. Preliminary results of pervaporation of a dioxane/water mixture through hollow fibers made of jojoba‐bound chlorosulfonated polyethylene show separation of the dioxane from the water with a separation factor of 6. This technique can be applied to remove residual organic solvents in the purification of industrial waste water. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 80: 763–768, 2001     

Pervaporation characteristics and structure of poly(vinyl alcohol)/poly(ethylene glycol)/tetraethoxysilane hybrid membranes

Poly(vinyl alcohol) (PVA) blended with poly(ethylene glycol) (PEG) was crosslinked with tetraethoxysilane (TEOS) to prepare organic–inorganic PVA/PEG/TEOS hybrid membranes. The membranes were then used for the dehydration of ethanol by pervaporation (PV). The physicochemical structure of the hybrid membranes was studied with Fourier transform infrared spectra (FT‐IR), wide‐angle X‐ray diffraction WXRD, and scanning electron microscopy (SEM). PVA and PEG were crosslinked with TEOS, and the crosslinking density increased with increases in the TEOS content, annealing temperature, and time. The water permselectivity of the hybrid membranes increased with increasing annealing temperature or time; however, the permeation fluxes decreased at the same time. SEM pictures showed that phase separation took place in the hybrid membranes when the TEOS content was greater than 15 wt %. The water permselectivity increased with the addition of TEOS and reached the maximum at 10 wt % TEOS. The water permselectivity decreased, whereas the permeation flux increased, with an increase in the feed water content or feed temperature. The hybrid membrane that was annealed at 130°C for 12 h exhibited high permselectivity with a separation factor of 300 and a permeation flux of 0.046 kg m^?2 h^?1 in PV of 15 wt % water in ethanol. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Nanometric thin skinned dual‐layer hollow fiber membranes for dehydration of isopropanol

A novel sulfonated polyphenylsulfone (sPPSU)/polyphenylsulfone (PPSU)‐based dual‐layer hollow fiber membrane with a nanometric thin skin layer has been designed for biofuel dehydration via pervaporation. The thickness of skin selective layer is in the range of 15–90 nm under different spinning conditions measured by positron annihilation spectroscopy (PAS) coupled with a mono‐energetic positron beam. The effects of outer‐layer dope properties, coagulation temperature, and dope flow rate during spinning were systematically investigated. By tuning these spinning parameters, a high performance sPPSU/PPSU‐based dual‐layer hollow fiber membrane with desirable morphology was successfully obtained. Particularly owing to its nanometric thin skin layer, a high flux of 3.47 kg/m²h with a separation factor of 156 was achieved for dehydration of an 85 wt % isopropanol aqueous solution at 50°C. After post thermal treatment at 150°C for 2 h, the separation factor was dramatically improved to 687 while flux dropped to 2.30 kg/m²h, which make it comparable to the inorganic membranes. In addition, excellent correlations were found among the results from field emission scanning electron microscopy, PAS spectra, and separation performance. © 2013 American Institute of Chemical Engineers AIChE J, 59: 2943–2956, 2013     

Effect of the Addition of Fructose on the Pervaporation of Ethanol/Water Mixtures by Silicone-Rubber-Coated Polyethersulfone Membranes

Abstract

Composite hollow fiber membranes were prepared by coating polyethersulfone hollow fibers with silicone rubber. The hollow fiber membranes so produced were found to be water selective when they were used for the separation of feed ethanol/water mixtures by pervaporation. When fructose was added to feed ethanol/water mixtures, a decrease in permeation rate and an increase in water selectivity were observed. The decrease in the permeation rate was possible to assume, but the noticed increase in water selectivity was against our expectation, since the vapor pressure of water decreases while that of ethanol increases when sugars are added to mixtures of ethanol and water. Water selectivity of the membrane was enhanced with an increase in the amount of fructose in the feed.     

Pervaporation separation of water–isopropyl alcohol mixture by PVA/LiBr membrane

Hydrophilic polyvinyl alcohol membranes, modified by lithium bromide, were prepared with glutaraldehyde as a crosslinking reagent. The membranes were investigated for the pervaporation dehydration of a water–isopropyl systems. The effect of the feed temperature on permeation flux and membrane selectivity was studied. The characterization of modified membranes was performed using Fourier transform infrared spectroscopy (FT‐IR), differential scanning calorimeter (DSC) and X‐ray diffraction. It was observed that the crystallinity of membranes increased as lithium bromide was added to the polymer. High performance liquid chromatography (HPLC) was used to analyze water content and isopropyl alcohol in the feed and permeate samples The pervaporation tests also confirmed an enhancement in water permeability through adding LiBr to the polymer, because of the high hydrophilic properties of this salt. According to pervaporation experiments conducted at 50°C, the water flux increased from 0.1049 kg/ m² hr to 0.1114 kg/ m² hr as 0.5 wt% of LiBr was added to the polymer matrix. Furthermore, an addition of 1 wt% of LiBr compared to homogeneous PVA membrane increased selectivity from 76 to 779. POLYM. ENG. SCI., 59:E101–E111, 2019. © 2018 Society of Plastics Engineers     

Dehydration of ethanol/water mixtures by pervaporation using soluble polyimide membranes

A series of soluble polyimides derived from 3,3′,4,4′‐benzhydrol tetracarboxylic dianhydride (BHTDA) with various diamines such as 1,4‐bis(4‐aminophenoxy)‐2‐tert‐butylbenzene (BATB), 1,4‐bis(4‐aminophenoxy)‐2,5‐di‐tert‐butylbenzene (BADTB), and 2,2′‐dimethyl‐4,4′‐ bis(4‐aminophenoxy)biphenyl (DBAPB) were investigated for pervaporation separation of ethanol/water mixtures. Diamine structure effect on the pervaporation of 90 wt% aqueous ethanol solution through the BHTDA‐based polyimide membranes was studied. The separation factor ranked in the following order: BHTDA–DBAPB > BHTDA–BATB > BHTDA–BADTB. The increase in molecular volume for the substituted group in the polymer backbone increased the permeation rate. As the feed ethanol concentration increased, the permeation rate increased, while the water concentration in the permeate decreased for all polyimide membranes. The optimum pervaporation performance was obtained by the BHTDA–DBAPB membrane with a 90 wt% aqueous ethanol solution, giving a separation factor of 141, permeation rate of 255 g m^?2 h^?1 and 36 000 pervaporation separation index (PSI) value. Copyright © 2006 Society of Chemical Industry     

Fabrication of efficient pervaporation desalination membrane by reinforcement of poly(vinyl alcohol)–silica film on porous polysulfone hollow fiber

Pervaporation membrane technology is commercially successful in the dehydration of organic solvents, and the technology has potential for seawater desalination with high recovery because of its capability to treat highly saline water. But to make the technology advantageous over the other available membrane desalination technologies in terms of productivity flux without additional energy cost, the selective barrier layer is required to be extremely thin, defect‐free, hydrophilic, and selective to water. In this work, we prepared an efficient membrane by reinforcing a highly water‐permeable but continuous barrier layer of poly(vinyl alcohol)–silica (PVA‐SiO₂) hybrid material on porous polysulfone hollow fibers. The PVA‐SiO₂ in acidified and hydrated ethanol was aged at room temperature for a period to allow solvent evaporation to obtain the solution concentration desired for the reinforcement. The reinforced hollow fiber membrane with optimal PVA‐SiO₂ barrier layer thickness exhibited a performance with a flux of 20.6 L m^?2 h^?1 and 99.9% salt rejection from a saline feed of 2000 ppm NaCl at 333 K. The effects of PVA‐SiO₂, temperature, and feed salinity on the pervaporation performance of the membrane were also studied. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 45718.     

Synthesis of highly selective copolymer membranes and their application for the dehydration of tetrahydrofuran by pervaporation

Acrylonitrile was copolymerized with 2‐hydroxyethyl methacrylate (HEMA) at three different copolymer compositions by emulsion polymerization to produce polyacrylonitrile–2‐hydroxyethyl methacrylate (PANHEMA) copolymer membranes containing increasing amounts of HEMA from PANHEMA‐1 to PANHEMA‐3. The dehydration of tetrahydrofuran (THF) over a concentration range of 0–14 wt % water in the feed was studied by pervaporation with these three copolymer membranes. The permeate water flux and separation factor for water was measured over the same concentration range at 30, 40, and 50°C. Among the copolymer membranes, PANHEMA‐1 exhibited a reasonable water flux (34.9 g m^?2 h^?1) with a very high water selectivity (264), whereas PANHEMA‐3 showed a higher water flux (52 g m^?2 h^?1) but a lower water selectivity (176.5) for highly concentrated THF (0.56 wt % water in the feed) at 30°C. The permeation factors of water for all of the membranes were much greater than unity, which signified a strong positive coupling effect of THF on water permeation. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 728–737, 2007