Biobased composites prepared by compression molding with a novel thermoset resin from soybean oil and a natural‐fiber reinforcement

Biobased composites were manufactured with a compression‐molding technique. Novel thermoset resins from soybean oil were used as a matrix, and flax fibers were used as reinforcements. The air‐laid fibers were stacked randomly, the woven fabrics were stacked crosswise (0/90°), and impregnation was performed manually. The fiber/resin ratio was 60 : 40. The prepared biobased composites were characterized by impact and flexural testing. Scanning electron microscopy of knife‐cut cross sections of the specimens was also done to investigate the fiber–matrix interface. Thermogravimetric analysis of the composites was carried out to provide indications of thermal stability. Three resins from soybean oil [methacrylated soybean oil, methacrylic anhydride modified soybean oil (MMSO), and acetic anhydride modified soybean oil] were used as matrices. The impact strength of the composites with MMSO resin reinforced with air‐laid flax fibers was 24 kJ/m², whereas that of the MMSO resin reinforced with woven flax fabric was between 24 and 29 kJ/m². The flexural strength of the MMSO resin reinforced with air‐laid flax fibers was between 83 and 118 MPa, and the flexural modulus was between 4 and 6 GPa, whereas the flexural strength of the MMSO resin reinforced with woven fabric was between 90 and 110 MPa, and the flexural modulus was between 4.87 and 6.1 GPa. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Concentration effect of γ‐glycidoxypropyltrimethoxysilane on the mechanical properties of glass fiber–epoxy composites

In this study, glass fibers were modified using γ‐glycidoxypropyltrimethoxysilane of different concentrations to improve the interfacial adhesion at interfaces between fibers and matrix. Effects of γ‐glycidoxypropyltrimethoxysilane on mechanical properties and fracture behavior of glass fiber/epoxy composites were investigated experimentally. Mechanical properties of the composites have been investigated by tensile tests, short beam tests, and flexural tests. The short‐beam method was used to measure the interlaminar shear strength (ILSS) of laminates. The tensile and flexural properties of composites were characterized by tensile and three‐point bending tests, respectively. The fracture surfaces of the composites were observed with a scanning electron microscope. On comparing the results obtained for the different concentrations of silane solution, it was found that the 0.5% GPS silane treatment provided the best mechanical properties. The ILSS value of heat‐cleaned glass fiber reinforced composite is enhanced by ∼59% as a result of the glass fiber treatment with 0.5% γ‐GPS. Also, an improvement of about 37% in tensile strength, about 78% in flexural strength of the composite with the 0.5% γ‐GPS treatment of glass fibers was observed. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers     

Development and application of triglyceride-based polymers and composites

Triglyceride oils derived from plants have been used to synthesize several different monomers for use in structural applications. These monomers have been found to form polymers with a wide range of physical properties. They exhibit tensile moduli in the 1–2 GPa range and glass transition temperatures in the range 70–120 °C, depending on the particular monomer and the resin composition. Composite materials were manufactured utilizing these resins and produced a variety of durable and strong materials. At low glass fiber content (35 wt %), composites produced from acrylated epoxidized soybean oil by resin transfer molding displayed a tensile modulus of 5.2 GPa, a flexural modulus of 9 GPa, a tensile strength of 129 MPa, and flexural strength of 206 MPa. At higher fiber contents (50 wt %) composites produced from acrylated epoxidized soybean oil displayed tensile and compression moduli of 24.8 GPa each, and tensile and compressive strengths of 463.2 and 302.6 MPa, respectively. In addition to glass fibers, natural fibers such as flax and hemp were used. Hemp composites of 20% fiber content displayed a tensile strength of 35 MPa and a tensile modulus of 4.4 GPa. The flexural modulus was ∼2.6 GPa and the flexural strength was in the range 35.7–51.3 MPa, depending on the test conditions. The flax composite materials had tensile and flexural strengths in the ranges 20–30 and 45–65 MPa, respectively. The properties exhibited by both the natural- and synthetic fiber-reinforced composites can be combined through the production of “hybrid” composites. These materials combine the low cost of natural fibers with the high performance of synthetic fibers. Their properties lie between those displayed by the all-glass and all-natural composites. Characterization of the polymer properties also presents opportunities for improvement through genetic engineering technology. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 82: 703–723, 2001     

Mechanical and viscoelastic properties of soybean oil thermoset reinforced with jute fabrics and carded lyocell fiber

Composites and hybrid composites were manufactured from renewable materials based on jute fibers, regenerated cellulose fibers (Lyocell), and thermosetting polymer from soybean oil. Three different types of jute fabrics with biaxial weave architecture but different surface weights, and carded Lyocell fiber were used as reinforcements. Hybrid composites were also manufactured by combining the jute reinforcements with the Lyocell. The Lyocell composite was found to have better mechanical properties than other composites. It has tensile strength and modulus of about 144 MPa and 18 GPa, respectively. The jute composites also have relatively good mechanical properties, as their tensile strengths and moduli were found to be between 65 and 84 MPa, and between 14 and 19 GPa, respectively. The Lyocell‐reinforced composite showed the highest flexural strength and modulus, of about 217 MPa and 13 GPa, respectively. In all cases, the hybrid composites in this study showed improved mechanical properties but lower storage modulus. The Lyocell fiber gave the highest impact strength of about 35 kJ/m², which could be a result of its morphology. Dynamic mechanical analysis showed that the Lyocell reinforced composite has the best viscoelastic properties. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Microstructure and fracture behavior of (co)injection‐molded polyamide 6 composites with short glass/carbon fiber hybrid reinforcement

The mechanical and fracture properties of injection molded short glass fiber)/short carbon fiber reinforced polyamide 6 (PA 6) hybrid composites were studied. The short fiber composites of PA 6 glass fiber, carbon fiber, and the hybrid blend were injection molded using a conventional machine whereas the two types of sandwich skin–core hybrids were coinjection molded. The fiber volume fraction for all formulations was fixed at 0.07. The overall composite density, volume, and weight fraction for each formulation was calculated after composite pyrolysis in a furnace at 600°C under nitrogen atmosphere. The tensile, flexural, and single‐edge notch‐bending tests were performed on all formulations. Microstructural characterizations involved the determination of thermal properties, skin–core thickness, and fiber length distributions. The carbon fiber/PA 6 (CF/PA 6) formulation exhibits the highest values for most tests. The sandwich skin‐core hybrid composites exhibit values lower than the CF/PA 6 and hybrid composite blends for the mechanical and fracture tests. The behaviors of all composite formulations are explained in terms of mechanical and fracture properties and its proportion to the composite strength, fiber orientation, interfacial bonding between fibers and matrix, nucleating ability of carbon fibers, and the effects of the skin and core structures. Failure mechanisms of both the matrix and the composites, assessed by fractographic studies in a scanning electron microscope, are discussed. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 957–967, 2005     

Improvement in mechanical and thermal properties of unsaturated polyester- based hybrid composites

Polymer matrix composites are used in automobile, structure and aerospace industries due to their light weight and high strength. The present research has an aim to reinforce locally developed silica nanoparticles and glass fibers in unsaturated polyester to produce polymer-based hybrid composites. Composites were synthesized by hand lay-up method with 1, 2, 3 and 4 wt% of silica sand nanoparticles and glass fiber. Mechanical tests like tensile, impact and micro-hardness were performed on the obtained polymer hybrid composites. The results of mechanical properties of the hybrid polymer matrix composites revealed an increasing trend. The SEM analysis was performed on the developed and fractured tensile testing samples. The SEM analysis showed the presence of silica nanoparticles in the samples and pulling action of fibers were seen under fractured tensile tests. The pulling actions of fibers from polymer matrix delayed the fractured mechanism and enhanced the mechanical properties. Silica nanoparticles filled the cavities generated during tensile test and extensive enhancement was revealed in tensile as well as impact energy. Toughness of the hybrid composite was also enhanced as a result. The thermal properties of the hybrid polymer composites were analyzed using thermogravimetric analysis. Thermal stability of the composite has been marginally increased with increasing wt% of reinforcement.     

Experimental assessment of the improved properties during aging of flax/glass hybrid composite laminates for marine applications

The investigation for natural fibers composites in terms of performance, durability, and environmental impact for structural applications in marine environments is a relevant challenge in scientific and industrial field. On this context, the aim of this work is to assess the durability and mechanical stability in severe environment of epoxy/glass–flax hybrid composites. For the sake of comparison, also full flax and glass epoxy composites were investigated. All samples were exposed to salt–fog environmental conditions up to 60 aging days. Wettability behavior during time was compared with water uptake evolution to assess water sensitivity of hybrid composite configurations. Moreover, quasi-static flexural and dynamic mechanical analysis were carried to evaluate as aging conditions, laminate configuration influence the surface and mechanical performances stability of the hybrid composites. The addition of glass fibers on flax laminate allows to enhance both flexural strength by 90%, and modulus by 128%, even if these properties are lower than those of full glass laminates. The results evidenced that the hybridization of flax fibers with glass ones is a practical approach to enhance the aging durability of epoxy/flax composite laminates in marine environmental conditions, obtaining a suitable compromise among environmental impact, mechanical properties, aging resistance, and costs. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47203.     

Experimental Investigation of Mechanical and Morphological Properties of Flax-Glass Fiber Reinforced Hybrid Composite using Finite Element Analysis

The use of cellulosic fibers as reinforcing materials in polymer composites has gained popularity due to an increasing trend for developing sustainable materials. In the present experimental study, flax and glass fiber reinforced partially eco-friendly hybrid composites are fabricated with two different fiber orientations of 0° and 90°. The mechanical properties of these composites such as tensile, flexural and impact strengths have been evaluated. From the experiments, it has been observed that the composites with the 0° fiber orientation can hold the maximum tensile strength of 82.71 MPa, flexural strength of 143.99 MPa, and impact strength of 4 kJ/m². Whereas the composites with 90° fiber orientation can withstand the maximum tensile strength of 75.64 MPa, flexural strength of 134.86 MPa, and impact strength of 3.99 kJ/m². Morphological analysis is carried out to analyze fiber matrix interfaces and the structure of the fractured surfaces by using scanning electron microscopy (SEM). The finite element analysis (FEA) has been carried out to predict the resulting important mechanical properties by using ANSYS 12.0. From the results it is found that the experimental results are very close to the results predicted from FEA model values. It is suggested that these hybrid composites can be used as alternate materials for pure synthetic fiber reinforced polymer composite materials.     

Polyamide‐6 composites reinforced with cellulose fibers and fabricated by extrusion: Effect of fiber bleaching on mechanical properties and stability

We prepared polyamide‐6 (PA‐6) composites using bleached and semibleached cellulose fibers from Eucalyptus species by processing in a corotating interpenetrating twin‐screw extruder. PA‐6 is a challenging matrix because of its high processing temperature, which overlaps the thermodegradation temperature of the fibers. The selection of the processing conditions for extrusion and the use of the lubricant ethylene bis (stearamide) permitted the production of composites with 20, 30, and 40 wt% of bleached fibers, which are lighter than the corresponding glass fiber composites. Composites with 30 wt% of bleached fibers yield the best mechanical properties and good fiber/matrix interaction, as demonstrated by mechanical tests and scanning electron microscopy. X‐ray photoelectron spectroscopy studies showed that the natural moisture in the fibers promotes the fiber/matrix interaction through the formation of ester bonds. We assessed the effect caused by the presence of lignin in the fibers. Composites containing 30 wt% of semibleached fibers maintained the flexural properties and showed small improvements in thermal stability when compared with bleached fiber composites; however, there is a slight decrease in the tensile properties. Through accelerated aging tests, we observed that increased lignin concentration in the fibers reduced the formation of carbonyl compounds on sample surfaces, indicating a stabilization effect. POLYM. COMPOS., 38:299–308, 2017. © 2015 Society of Plastics Engineers     

Polypropylene Hybrid Composites: A Preliminary Study on the use of Glass and Coconut Fiber as Reinforcements in Polypropylene Composites

Polypropylene hybrid composites were made using coconut and glass fibers as reinforcing agents in the polypropylene matrix. The incorporation of both fibers into the PP matrix has resulted in the reduction of flex-ural, tensile, and impact strengths and elongation at break. The reduction has been attributed to the increased incompatibility between the fibers and the PP matrix, and the irregularity in fiber size, especially for biofibers as shown by scanning electron micrographs. Both the flexural and tensile moduli have been improved with the increasing level of fiber loading. Most of the properties tested for Composites with high glass fibers/low biofiber loading are comparable with the ones with low glass fiber/high biofiber loading. The results show that more biofibers could be incorporated in hybrid composites which would give the same range of properties as the composites with higher loading of glass fibers.     

Effect of macromolecular coupling agent on the property of PP/GF composites

Silane‐grafted polypropylene manufactured by a reactive grafting process was used as the coupling agent in polypropylene/glass‐fiber composites to improve the interaction of the interfacial regions. Polypropylene reinforced with 30% by weight of short glass fibers was injection‐molded and the mechanical behaviors were investigated. The results indicate that the mechanical properties (tensile strength, tensile modulus, flexural strength, flexural modulus, and Izod impact strength) of the composite increased remarkably as compared with the noncoupled glass fiber/polypropylene. SEM of the fracture surfaces of the coupled composites shows a good adhesion at the fiber/matrix interface: The fibers are coated with matrix polymer, and a matrix transition region exists near the fibers. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 1537–1542, 1999     

Interfacial Microstructure and Chemistry of SiC/BN Dual-Coated Nicalon-Fiber-Reinforced Glass-Ceramic Matrix Composites

Glass-ceramic composites with improved high-temperature mechanical properties have been produced by incorporating continuous SiC fibers into a barium magnesium aluminosilicate matrix. Control of the fiber/matrix interface was achieved by a dual-layer coating of SiC/BN(C) applied to the fibers by CVD. The weakly bonded interface resulted in composites with high fracture toughness and strength up to 1100°C, and the composite system was oxidatively stable during long-term exposure to air at high temperatures. Composites with different thermal and mechanical histories were studied, and interfaces were characterized using transmission electron microscopy (TEM), Auger electron spectroscopy, and fiber pushout tests. Observations of interfacial microstructure were correlated with the mechanical properties of the composite and with interface properties determined from fiber push-out tests.     

Physical and mechanical properties of kenaf/flax hybrid composites

This research investigates the physical and mechanical properties of hybrid composites made of epoxy reinforced by kenaf and flax natural fibers to investigate the hybridization influences of the composites. Pure and hybrid composites were fabricated using bi-directional kenaf and flax fabrics at different stacking sequences utilizing the vacuum-assisted resin infusion method. The pure and hybrid composites' physical properties, such as density, fiber volume fraction (FVF), water absorption capacity, and dimensional stability, were measured. The tests of tensile, flexural, interlaminar shear and fracture toughness (Mode II) were examined to determine the mechanical properties. The results revealed that density remained unchanged for the hybrid compared to pure kenaf/epoxy composites. The tensile, flexural, and interlaminar shear performance of flax/epoxy composite is improved by an increment of kenaf FVF in hybrid composites. The stacking sequence significantly affected the mechanical properties of hybrid composites. The highest tensile strength (59.8 MPa) was obtained for FK2 (alternative sequence of flax and kenaf fibers). However, FK3 (flax fiber located on the outer surfaces) had the highest interlaminar shear strength (12.5 MPa) and fracture toughness (3302.3 J/m²) among all tested hybrid composites. The highest water resistance was achieved for FK5 with the lowest thickness swelling.     

Thermoset lactic acid‐based resin as a matrix for flax fibers

Thermoset composites were produced from flax fibers and a novel lactic acid (LA)‐based thermoset resin. This resin is based on methacrylated, star‐shaped oligomers of LA. The main purpose of this work was to evaluate whether this resin can be used to produce structural composites from flax fibers. Composites were prepared by spray impregnation followed by compression molding at elevated temperature. The tests showed that composites can be produced with as much as 70 wt% fiber. The composites were evaluated by tensile testing, flexural testing, charpy impact test, dynamic mechanical thermal analysis (DMTA), and low‐vacuum scanning electron microscopy. The ageing properties in high humid conditions were evaluated, the Young's modulus ranged from 3 GPa to 9 GPa in the best case. This work shows that structural composites can be produced from renewable material. It is clear from the results that these composites have properties that make them suitable for furniture, panels, or automotive parts. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Effect of stacking sequence on mechanical properties of hybrid flax/jute fibers reinforced thermoplastic composites

In this study, the hybrid composites were prepared by stacking jute/PP nonwoven and flax/MAPP woven fabrics in defined sequences. Polypropylene (PP) and maleic anhydride grafted polypropylene (MAPP) were used as matrix materials. Jute and flax fibers were treated with alkali solution in order to improve the interface properties of the resultant composites. The mechanical properties of these hybrid composites were analyzed by means of tensile, flexural, and drop‐weight impact tests. The effect of fabric stacking sequence on the mechanical properties of the composites was investigated. The stacking of nonwovens at the top and in alternate layers has resulted in maximum flexural strength, flexural stiffness, and impact force. It was also shown that hybrid composites have improved tensile, flexural, and impact properties in comparison to neat PP matrix. POLYM. COMPOS., 36:2167–2173, 2015. © 2014 Society of Plastics Engineers     

剑麻纤维/长玻纤混杂增强PP复合材料的力学性能研究

采用剑麻纤维(SF)和长玻璃纤维(LGF)混杂增强聚丙烯(PP)复合材料,考察了SF/LGF的比例和含量对PP复合材料力学性能的影响。结果表明:SF/LGF在聚丙烯树脂基体中呈交叉网状分布,这有利于提高复合材料的冲击强度、弯曲模量、拉伸强度和软化点。在SF/LGF质量比为2 2∶,二者总质量分数为30%时,SF/LGF混杂增强PP复合材料的综合力学性能较好。     

Unidirectional hemp and flax EP‐ and PP‐composites: Influence of defined fiber treatments

In some technical areas, mainly in the automotive industry, glass fiber reinforced polymers are intended to be replaced by natural fiber reinforced polymer systems. Therefore, higher requirements will be imposed to the physical fiber properties, fiber‐matrix adhesion, and the quality assurance. To improve the properties of epoxy resins (EP) and polypropylene (PP) composites, flax and hemp fibers were modified by mercerization and MAH‐PP coupling agent was used for preparing the PP composites. The effects of different mercerization parameters such as concentration of alkali (NaOH), temperature, and duration time along with tensile stress applied to the fibers on the structure and properties of hemp fibers were studied and judged via the cellulose I–II lattice conversion. It was observed that the mechanical properties of the fibers can be controlled in a broad range by using appropriate mercerization parameters. Unidirectional EP composites were manufactured by the filament winding technique; at the PP matrix material, a combination with a film‐stacking technique was used. The influence of mercerization parameters on the properties of EP composites was studied with hemp yarn as an example. Different macromechanical effects are shown at hemp‐ and flax‐PP model composites with mercerized, MAH‐PP‐treated, or MAH‐PP‐treated mercerized yarns. The composites' properties were verified by tensile and flexural tests. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2150–2156, 2004     

High-performance composite from epoxy and glass fibers: Morphology,mechanical, dynamic mechanical,and thermal analysis

Diglycidyl ether of bisphenol-A type epoxy resin cured with diamino diphenyl sulfone was used as the matrix for fiber-reinforced composites to get improved mechanical and thermal properties for the resulting composites. E-glass fiber was used for fiber reinforcement. The morphology, tensile, flexural, impact, dynamic mechanical, and thermal properties of the composites were analyzed. The tensile, flexural, and impact properties showed dramatic improvement with the addition of glass fibers. Dynamic mechanical analysis was performed to obtain the T_g of the cured matrix as well as the composites. The improved thermal stability of the composites was clear from the thermogravimetric analysis. Scanning electron micrographs were taken to understand the interfacial adhesion between the fiber and the matrix. The values of mechanical properties were compared with modified epoxy resin composite system. Predictive models were applied using various equations to compare the mechanical data obtained theoretically and experimentally. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers     

Short glass fiber reinforced ABS and ABS/PA6 composites: Processing and characterization

In this study acrylonitrile‐butadiene‐styrene (ABS) terpolymer was reinforced with 3‐aminopropyltrimethoxysilane (APS)‐treated short glass fibers (SGFs). The effects of SGF concentration and extrusion process conditions, such as the screw speed and barrel temperature profile, on the mechanical properties of the composites were examined. Increasing the SGF concentration in the ABS matrix from 10 wt% to 30 wt% resulted in improved tensile strength, tensile modulus and flexural modulus, but drastically lowered the strain‐at‐break and the impact strength. The average fiber length decreased when the concentration of glass fibers increased. The increase in screw speed decreased the average fiber length, and therefore the tensile strength, tensile modulus, flexural modulus, and impact strength were affected negatively and the strain‐at‐break was affected positively. The increase in extrusion temperature decreased the fiber length degradation, and therefore the tensile strength, tensile modulus, flexural modulus, and impact strength increased. At higher temperatures the ABS matrix degraded and the mechanical strength of the composites decreased. To obtain a strong interaction at the interface, polyamide‐6 (PA6) at varying concentrations was introduced into the ABS/30 wt% SGF composite. The incorporation and increasing amount of PA6 in the composites broadened the fiber length distribution (FLD) owing to the low melt viscosity of PA6. Tensile strength, tensile modulus, flexural modulus, and impact strength values increased with an increase in the PA6 content of the ABS/PA6/SGF systems due to the improved adhesion at the interface, which was confirmed by the ratio of tensile strength to flexural strength as an adhesion parameter. These results were also supported by scanning electron micrographs of the ABS/PA6/SGF composites, which exhibited an improved adhesion between the SGFs and the ABS/PA6 matrix. POLYM. COMPOS. 26:745–755, 2005. © 2005 Society of Plastics Engineers     

Static and dynamic mechanical properties of a kenaf fiber–wood flour/polypropylene hybrid composite

A natural fiber hybrid composite containing equal proportions of kenaf fibers (KFs) and wood flour (WF) as the reinforcements and polypropylene (PP) as the polymer matrix was prepared, and its static and dynamic mechanical properties were compared with KF/PP and WF/PP composites. Static tensile and flexural tests and dynamic mechanical analysis (DMA) were carried out. The hybrid composite exhibited tensile and flexural moduli and strength values closer to those of the KF composite, which indicated a higher reinforcing efficiency of KFs compared with WF. DMA revealed that although the glass‐transition temperature remained unchanged by the replacement of half of the WF by KFs, the α‐transition temperature of the hybrid composite was identical to that of WF composite. The magnitudes of both the α and β (glass) transitions of the hybrid composite were comparable to that of the WF/PP composite. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 665–672, 2005