A comparison of composition and sequence distribution of p(AM-MADQUAT) prepared by solution and inverse microemulsion polymerization

Acrylamide (AM)/2-(methacryloyloxy)ethyltrimethylammonium chloride (MADQUAT) copolymers were prepared by solution and inverse microemulsion polymerization using ammonium persulfate ((NH₄)₂S₂O₈)/sodium hydrosulfite (NaHSO₃) as redox initiator at 30 °C. The comonomer reactivity ratios, determined using the Kelen–Tudos (KT) method, were r _A = 0.30, r _M = 1.31 in solution and r _A = 0.63, r _M = 1.13 in the inverse microemulsion, respectively. The copolymer microstructure was deduced from the run number and the heterogeneity, based on reactivity ratios. It was found that copolymerization in the inverse microemulsion resulted in close to ideal copolymerization, giving almost random copolymers; copolymerization in solution resulted in some alternating copolymers. The copolymer compositions indicated that high-conversion samples obtained from the inverse microemulsion are much more homogeneous in composition compared with those obtained in solution. It was found that the composition distribution of the copolymer prepared by inverse microemulsion polymerization remained at approximately the feed ratio. The sequence distribution of the copolymer was predicted by first-order Markov statistical and Bernoulli statistical models, respectively. The results showed that the sequence distribution of the copolymer prepared by inverse microemulsion polymerization was almost random, which led to a wider cationic charge distribution and a microstructure that was coincident with the feed ratio.     

Copolymerization of 2-methyl-N-1,3-thiazole-2-ylacrylamide with glycidyl methacrylate: synthesis, characterization, reactivity ratios and biological activity

The free-radical copolymerization of 2-methyl-N-1,3-thiazole-2-ylacrylamide monomer (TMA) with glycidyl methacrylate (GMA) was carried out in 1,4-dioxane at 65 ± 1 °C using azobisisobutironitril (AIBN) as an initiator. The copolymers were characterized by FTIR, ¹³C-NMR and ¹H-NMR spectroscopic methods. The copolymer compositions were determined by elemental analysis. The weight-average and number-average molecular weights of the copolymers were obtained by gel permeation chromatography (GPC). The polydispersity indices of the polymers, determined with gel permeation chromatography, suggested a strong tendency for chain termination by disproportionation. Thermal properties of the polymers were also studied by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The monomer reactivity ratios were calculated according to the general copolymerization equation using Kelen–Tudos and Fineman–Ross linearization methods. The reactivity ratios indicated a tendency toward for alternation. The thermal decomposition activation energies of the polymers were evaluated by Ozawa method. The antibacterial and antifungal effects of the copolymers were also investigated on various bacteria and fungi. All the products showed moderate activity against different strains of bacteria and fungi.     

Copolymerization of 4-cyanophenyl methacrylate with methyl methacrylate: Synthesis,characterization and determination of monomer reactivity ratios

Summary A novel methacrylic monomer, 4-cyanophenyl methacrylate (CPM) was synthesized by reacting 4-cyanophenol dissolved in methyl ethyl ketone (MEK) with methacryloyl chloride in the presence of triethylamine as a catalyst. Copolymers of CPM with methyl methacrylate(MMA) at different composition was prepared by free radical solution polymerization at 70±1 °C using benzoyl peroxide as initiator. The copolymers were characterized by FT-IR, ¹H-NMR and ¹³C-NMR spectroscopic techniques. The solubility of the polymers was tested in various polar and non polar solvents. The molecular weight and polydispersity indices of the copolymers were determined using gel permeation chromatography. The glass transition temperature of the copolymers increases with increase in mole fraction of MMA content. The thermal stability of the copolymer increases with increases in mole fraction of CPM content in the copolymer. The copolymer composition was determined by using ¹H-NMR spectroscopy. The monomer reactivity ratios estimated by the application of linearization methods such as Fineman-Ross (r₁=2.524±0.038, r₂=0.502±0.015), Kelen-Tudos (r₁=2.562±0.173, r₂=0.487±0.005) and extended Kelen-Tudos methods (r₁=2.735±0.128, r₂=0.4915±0.007).     

Synthesis,characterizations and thermal behavior of methyl methacrylate and N‐(p‐carboxyphenyl) methacrylamide/acrylamide copolymers

The synthesis, characterization, and thermal properties of copolymers of methyl methacrylate (MMA) and N‐(p‐carboxyphenyl) methacrylamide/acrylamide (CPMA/CPA) are described. The copolymerization was carried out in solution by taking different mole fractions (0.1–0.5) of CPMA/CPA in the initial feed using azobisisobutyronitrile as an initiator and dimethylformamide as a solvent at 60°C. The copolymer composition was determined from ¹H‐NMR spectra by taking the ratio of the proton resonance signal due to the  OCH₃ of MMA (δ = 3.59 ppm) and the aromatic protons (δ = 7.6–7.8 ppm) of CPMA/CPA. The monomer reactivity ratios of MMA:CPMA and MMA:CPA were determined using the Fineman Ross and Kelen Tudos methods and were found to be 1.32 ± 0.01 [MMA], 1.11 ± 0.02 [CPMA], 2.60 ± 0.01 [MMA], and 0.20 ± 0.01 [CPA]. Incorporation of these comonomers in the MMA backbone resulted in an improvement in the glass‐transition temperature and thermal stability. The percent char also increased with the increase of CPMA/CPA content in the copolymers. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 78: 259–267, 2000     

Synthesis of imide‐based methacrylic monomers and their copolymerization with methyl methacrylate: monomer reactivity ratios and heat resistance properties

The newly designed methacrylic monomer series 4‐phthalimidocyclohexyl methacrylate (PCMA ), 4‐hexahydrophthalimidocyclohexyl methacrylate (HPCMA) and 4‐hexahydro‐3,6‐methanophthalimidocyclohexyl methacrylate (HMPCMA) were synthesized. Their homopolymers and methyl methacrylate (MMA) based copolymer series were polymerized by free‐radical polymerization. The copolymer compositions were characterized using ¹H NMR spectra. The monomer reactivity ratios were calculated employing the Fineman?Ross (F‐T) and Kelen?Tüdös (K‐T) methods at low conversion. The values of r₁ and r₂ obtained by the F‐T and K‐T methods appear to be in close agreement (their average values are r₁ = 1.3061 and r₂ = 0.7336 for poly(PCMA‐co‐MMA), r₁ = 1.5169 and r₂ = 0.6840 for poly(HPCMA‐co‐MMA), r₁ = 1.7748 and r₂ = 0.5664 for poly(HMPCMA‐co‐MMA)) . The thermal stabilities and thermomechanical characteristics of the homopolymer and copolymer series were investigated by differential scanning calorimetry, thermogravimetric analysis and dynamic mechanical thermal analysis. © 2018 Society of Chemical Industry     

Copolymerization of 2-(4-tert-butylphenoxy)-2-oxo-ethyl Methacrylate with Methyl Methacrylate and Styrene: Synthesis, Characterization, and Monomer Reactivity Ratios

A tertierbutylphenoxy group containing methacrylate based monomer 2-(4-tert-butylphenoxy)-2-oxo-ethyl methacrylate (TBPOEMA) was synthesized by reacting 4-tertierbutylphenyl chloroacetate (TBPClAcO) with sodium methacrylate in acetonitrile. TBPClAcO was prepared by reacting tertierbutylphenol dissolved in benzene with chloroacetylchloride. The free-radical-initiated copolymerization of TBPOEMA, with methyl methacrylate (MMA) and styrene (ST) was carried out in dimethylsulphoxide (DMSO) solution at 65°C using 2,2-azobisisobutyronitrile (AIBN) as an initiator with different monomer-to-monomer ratios in the feed. The monomer TBPOEMA and copolymers were characterized by FTIR, ¹H- and ¹³C-NMR spectral studies. The copolymer composition obtained from the ¹H-NMR spectra led to the determination of reactivity ratios. The reactivity ratios of the monomers were determined by the application of Finemann–Ross and Kelen–Tüdös linear methods and the Behnken nonlinear least-squares method. The analysis of reactivity ratios revealed that MMA and ST are more reactive than TBPOEMA, and copolymers formed are statistical in nature. The molecular weights _w and _n) and polydispersity index of the polymers were determined using gel permation chromagtography. Thermogravimetric analysis of the polymers reveal that the thermal stability of the copolymers increases with an increase in the mole fraction of TBPOEMA in the copolymers. Glass transition temperatures of the copolymers were found to decrease with an increase in the mole fraction of TBPOEMA in the copolymers. The apparent thermal decomposition activation energies (E _d) were calculated by Ozawa method using the SETARAM Labsys TGA thermobalance.     

Photocrosslinkable copolymers based on 4‐acryloyloxyphenyl‐3′‐chlorostyryl ketone and methyl methacrylate: synthesis,comonomer reactivity ratios and UV photosensitivity

A new photosensitive acrylate monomer having a pendant chlorocinnamoyl moiety (APCSK) was copolymerized with methyl methacrylate (MMA) in different feed compositions in ethyl acetate solution at 70°C using benzoyl peroxide as a free‐radical initiator. The newly synthesized copolymers were characterized by FTIR, ¹H and ¹³C nuclear magnetic resonance (NMR) spectral techniques, as well as by size‐exclusion chromatography. Their thermal behaviour was assessed by thermogravimetric analysis in air and differential scanning calorimetry under nitrogen atmosphere. The copolymers exhibit no phase separation since there is only one glass transition temperature (T_g) value in the region of copolymer composition studied. The reactivity ratios of the comonomers were calculated by adopting linearization methods such as the Fineman–Ross (F‐R), Kelen–Tudos (K‐T) and extended Kelen–Tudos (ExtK‐T) methods, and by a non‐linear error‐in‐variables model method (EVM) using a computer program (RREVM). The results suggest that MMA is more reactive than APCSK and that their copolymerization leads to the formation of random copolymers. The photosensitivity of the copolymer samples was studied in solution as well as in thin films through UV irradiation. The influence of different factors, including solvent nature, concentration, temperature, photosensitizer and copolymer composition, on the rate of photocrosslinking of the photoreactive copolymers was investigated for effective industrial application of these polymers as negative photoresists. Copyright © 2004 Society of Chemical Industry     

Copolymerization of methyl methacrylate with 4‐vinylpyridine initiated by a novel Ni(II)α‐Benzoinoxime complex

Copolymerizations of methyl methacrylate (MMA) with 4‐vinylpyridine (4VP) were performed from different monomer feed ratios in 1,4‐dioxan at 30°C under free radical initiation experimental conditions, using Ni(II)α‐Benzoinoxime complex as initiator. The obtained copolymers (PMMA4VP) were examined by FTIR and ¹H NMR spectroscopies. The composition of these copolymers was calculated, using ¹H NMR spectra and elemental analysis. Monomer reactivity ratios were estimated from Fineman–Ross (FR, r_m = 0.550, r_v = 1.165) and Kelen–Tudos (KT, r_m = 0.559, r_v = 1.286) linearization methods, as well as nonlinear error in variables model (EVM) method using the RREVM computer program (RREVM, r_m = 0.559, r_v = 1.264). These values suggest that MMA‐4VP pair copolymerizes randomly. ¹H NMR spectra provide information about the stereochemistry of the copolymers in terms of sequence distributions and configurations. These results showed that the age of the Ni complex has an impact not only on its activity towards polymerization reactions but also on the features of the corresponding copolymers, whereas the chemical composition was insensitive to this prominent factor. The mechanism of MMA‐4VP copolymerization is consistent with a radical process as supported by microstructure and molecular weight distribution studies. Thermal behaviours of these copolymers were investigated by differential scanning calorimetry and thermogravimetric analysis. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008     

Silicone/polypropylene oxide-polyethylene oxide copolymer/clay composites (i) - curing behavior,intermolecular interaction and thermomechanical properties

The copolymerization of 2-(3-mesityl-3-methylcyclobutyl)-2-ketoethyl methacrylate monomer with acrylonitrile and styrene were carried out in 1,4-dioxane solution at 60^○C using AIBN as an initiator. The copolymers were characterized by Fourier transform infrared, ¹H-NMR, and ¹³C-NMR spectroscopic techniques. Thermal properties of the polymers were also studied by thermogravimetric analysis and differential scanning calorimetry. The copolymer compositions were determined by elemental analysis and ¹H-NMR technique. The monomer reactivity ratios were calculated by the application of conventional linearization methods as a result of Fineman–Ross and Kelen–Tüdös to less than 1 for both monomers.     

Copolymerization of 4-biphenyl methacrylate with glycidyl methacrylate: Synthesis, Characterization, thermal properties and determination of monomer reactivity ratios

Summary The methacrylic monomer, 4-biphenylmethacrylate (BPM) was synthesized by reacting 4-biphenyl phenol dissolved in ethyl methyl ketone (EMK) with methacryloyl chloride in presence of triethylamine as a catalyst. The copolymers of BPM with glycidyl methacrylate (GMA) were synthesized by free radical polymerization in EMK solution at 70±1 °C using benzoyl peroxide as a free radical initiator. The copolymerization behaviour was studied in a wide composition interval with the mole fractions of BPM ranging from 0.15 to 0.9 in the feed. The copolymers were characterized by FT-IR, ¹H-NMR and ¹³C-NMR spectroscopic techniques. The solubility was tested in various polar and non polar solvents. The molecular weight and polydispersity indices of the polymers were determined using gel permeation chromatography. The glass transition temperature of the copolymers increases with increase in BPM content. The thermogravimetric analysis of the polymers showed that the thermal stability of the copolymer increases with BPM content. The copolymer composition was determined using ¹H-NMR spectra. The monomer reactivity ratios were determined by the application of conventional linearization methods such as Fineman-Ross (r₁=0.392 ± 0.006, r₂ = 0.358 ± 0.007, Kelen-Tudos (r₁= 0.398 ± 0.004, r₂= 0.365 ± 0.013) and extended Kelen-Tudos methods (r₁= 0.394 ± 0.004, r₂= 0.352 ± 0.006).     

Synthesis, Characterization and Reactivity Ratios of Phenylethyl Acrylate/Methacrylate Copolymers

2-Phenylethyl acrylate (PEA) and 2-Phenylethyl methacrylate (PEMA) were synthesized by reacting 2-Phenyl ethanol with acryloyl and methacryloyl chloride respectively. Homopolymers and copolymers were prepared by free radical polymerization technique using benzoylperoxide as initiator. Copolymers of PEA and PEMA with methyl acrylate (MA) and N-vinyl pyrollidone (NVP) of different compositions were prepared. The monomers and polymers were characterized by IR and NMR techniques. Thermal stability of the polymers were determined by TG analysis. The composition of the copolymer was determined using ¹H-NMR analysis. The reactivity ratios of the monomers were determined by the application of Finemann–Ross and Kelen–Tudos methods. The prepared copolymers were tested on leather for their pressure sensitive adhesive property.     

Synthesis,characterization and thermal properties of homo and copolymers of 3,5-dimethoxyphenyl methacrylate with glycidyl methacrylate: Determination of monomer reactivity ratios

The new methacrylic monomer, 3,5-dimethoxyphenyl methacrylate (DMOPM) was synthesized by reacting 3,5-dimethoxyphenol dissolved in ethyl methyl ketone (EMK) with methacryloyl chloride in presence of triethylamine as a catalyst. The homopolymer and copolymers of DMOPM with glycidyl methacrylate (GMA) were synthesized by free radical polymerization in EMK solution at 70 ± 1 °C using benzoyl peroxide as a free radical initiator. The copolymerization behaviour was studied in a wide composition interval with the mole fractions of DMOPM ranging from 0.15 to 0.9 in the feed. The homopolymer and the copolymers were characterized by FT-IR, ¹H NMR and ¹³C NMR spectroscopic techniques. The solubility was tested in various polar and non-polar solvents. The molecular weight and polydispersity indices of the polymers were determined using gel permeation chromatography. The glass transition temperature of the copolymers increases with increase in DMOPM content. The thermogravimetric analysis of the polymers showed that the thermal stability of the copolymer increases with DMOPM content. The copolymer composition was determined using ¹H NMR spectra. The monomer reactivity ratios were determined by the application of conventional linearization methods such as Fineman–Ross (r₁ = 0.520, r₂ = 2.521), Kelen–Tudos (r₁ = 0.629, r₂ = 2.554) and extended Kelen–Tudos methods (r₁ = 0.600, r₂ = 2.502).     

Copolymerization of 4-chlorophenyl acrylate with methyl acrylate: synthesis,characterization, reactivity ratios,and their applications in the leather industry

4-Chlorophenyl acrylate (CPA) was prepared by reacting 4-chlorophenol and acryloyl chloride in the presence of triethylamine in ethyl acetate solution. Poly(4-chlorophenyl acrylate) and copoly(4-chlorophenyl acrylate–methyl acrylate) were synthesized by the free radical polymerization in ethyl acetate at 70°C. All the polymers were characterized by infrared (IR) and nuclear magnetic resonance (NMR) spectroscopic techniques. The composition of the copolymers was determined by the ¹H-NMR spectroscopic technique, that is, by integrating the aromatic peaks corresponding to the 4-chlorophenyl acrylate unit against the carbomethoxy group in the methyl acrylate unit. The reactivity ratios were calculated by Fineman–Ross, Kelen–Tudos (K–T), and the extended Kelen–Tudos methods. The values of r₁ and r₂ obtained by these methods were in close agreement with each other; that is, r₁(CPA) = 0.64 and r₂(MA) = 0.13 by the K–T method. The number-average molecular weight (M̄_n = 1.55 × 10³), the weight-average molecular weight (M̄_w = 8.39 × 10³), and the polydispersity index (M̄_w/M̄_n = 5.42) of poly(CPA) were determined by gel permeation chromatography (GPC). Thermal properties of the polymers were studied in a nitrogen atmosphere using thermogravimetric analysis (TGA). As the CPA increases in the copolymer, thermal stability of the copolymer increases (e.g., 90% weight loss occurs at 480°C for 20 mol % CPA, whereas the same weight loss occurs at 571°C for 80 mol % CPA). Acrylic binders, based on the CPA–MA–BA terpolymer, of different glass transition temperatures were prepared for applications in leather industry as top coat and base coat materials. These acrylic emulsions were cast into thin films, and their characteristics were tested for physical properties. These acrylic emulsions were applied as a base coat on leather, and the compositions having T_g values of 1.08 and 9.25°C were found to have excellent properties as base coats for leather when compared with commercial samples. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 73: 1153–1160, 1999     

Sequencing of methyl methacrylate/vinylidene chloride copolymers by NMR spectroscopy

Methyl methacrylate/vinylidene chloride (M/V) copolymers of different monomer concentrations were prepared by photopolymerization using the uranyl ion as photosensitizer. The copolymer composition was determined by chlorine estimation of the copolymers. The complete assignment of the ¹³C{¹H} NMR spectra of these copolymers is made by comparison with the spectra of poly(methyl methacrylate) and observing the changes in the intensities of the resonances with copolymer composition. The quaternary carbon of V- and M- center resonances were used for determining the sequence in terms of the distribution of V- and M- centered triads. The triad fractions thus obtained were compared with theoretically determined triad concentrations. The Monte Carlo simulation method was also used for estimating the copolymerization behavior. The variation of V- and M- centered triad concentrations was reported as a function of fractional conversions. The comonomer reactivity ratios, determined by both Kelen Tudos and nonlinear error in variables methods are r_V = 0.26 ± 0.04 and r_M = 2.88 ± 0.23. © 1998 John Wiley & Sons, Inc. J. Appl. Polym. Sci. 70: 373–381, 1998     

Homopolymer of 4-chloro-3-methyl Phenyl Methacrylate and its Copolymers with Butyl Methacrylate: Synthesis, Characterization, Reactivity Ratios and Antimicrobial Activity

The methacrylate monomer 4-chloro-3‐methyl phenyl methacrylate (CMPM) was synthesized by reacting 4-chloro-3‐methyl phenol with methacryloyl chloride. The homopolymer and various copolymers of CMPM with n-butyl methacrylate were synthesized by free-radical polymerization in toluene at 70°C using 2,2′-azobis(isobutyronitrile) as the initiator. The CMPM monomer was characterized by Fourier transform IR and ¹H-NMR studies. The copolymers were characterized by IR spectroscopy. The molecular weights (M _n and M _w) and the polydispersity index were obtained from gel permeation chromatography. The solubility and intrinsic viscosity of the homopolymer and the copolymers are also discussed here. The copolymer composition obtained from UV spectra led to the determination of reactivity ratios employing Fineman-Ross and Kelen-Tudos linearization methods. Thermogravimetric analyses of the homopolymer and the copolymers were carried out under a nitrogen atmosphere. The homopolymer and the copolymers prepared were tested for their antimicrobial activity against bacteria, fungi and yeasts.     

Study of the Copolymerization Parameters of 2-Thiozyl Methacrylamide with Different Alkyl Acrylates

2-thiozyl methacrylamide (TMA) was synthesized by the reaction of 2-aminothiazole with either methacryloyl chloride or methacrylic acid in the presence of triethylamine and N, N′-dicyclohexylcarbodiimide, respectively. Binary copolymerization reactions of the prepared monomer with methyl acrylate (MA), ethyl acrylate (EA), n-butyl acrylate (BA) and tert-butylacrylate (t.BA) were performed in dimethylformamide at 65^○C using 1 mol% azobisisobutyronitrile (AIBN) as initiator. The structure of the 2-thiozyl methacrylamide monomer and the prepared copolymers was investigated by IR and ¹H NMR spectroscopy. The copolymer compositions were determined from sulphur analysis. Copolymerization parameters for each system were calculated by the Finemen–Ross and Kelen–Tüdös methods. The monomer reactivity ratios for the systems TMA-MA, TMA-EA, TMA-BA, and TMA-tBA were found to be r₁=0.128, r₂=0.740; r₁=0.235, r₂=0.420; r₁=0.420, r₂=0.330 and r₁=1.690, r₂=0.027, respectively. The reactivities of acrylic esters decrease as the alkyl group become bulkier. The average Q and e values for TMA were calculated from the monomer reactivity ratios determined in the present and previous studies.     

Radical copolymerization of photocrosslinkable cinnamoylphenylmethacrylate and acrylamide

Copolymers of 4-Cinnamoylphenylmethacrylate (4-CPMA) and acrylamide (AA) were prepared in a ethylmethylketone (MEK) solution with benzoylperoxide (BPO) as a radical initiator at 70 °C. They were characterized by IR, ¹H NMR, and ¹³C NMR techniques. Copolymer compositions were determined from ¹H NMR spectra. The monomer reactivity ratios and the copolymer composition were determined by using Finemann–Ross (F–R) and Kelen-Tudos (K–T) methods. Thermogravimetric analysis of copolymers reveals that the thermal stability of the copolymer increases with an increase in the mole fraction of CPMA in the copolymer. The photocrosslinking of the copolymer were studied in solution.     

Reactivity ratios and copolymer properties of 2‐(diisopropylamino)ethyl methacrylate with methyl methacrylate and styrene

Free radical copolymerization kinetics of 2‐(diisopropylamino)ethyl methacrylate (DPA) with styrene (ST) or methyl methacrylate (MMA) was investigated and the corresponding copolymers obtained were characterized. Polymerization was performed using tert‐butylperoxy‐2‐ethylhexanoate (0.01 mol dm^?3) as initiator, isothermally (70 °C) to low conversions (<10 wt%) in a wide range of copolymer compositions (10 mol% steps). The reactivity ratios of the monomers were calculated using linear Kelen–Tüd?s (KT) and nonlinear Tidwell–Mortimer (TM) methods. The reactivity ratios for MMA/DPA were found to be r₁ = 0.99 and r₂ = 1.00 (KT), r₁ = 0.99 and r₂ = 1.03 (TM); for the ST/DPA system r₁ = 2.74, r₂ = 0.54 (KT) and r₁ = 2.48, r₂ = 0.49 (TM). It can be concluded that copolymerization of MMA with DPA is ideal while copolymerization of ST with DPA has a small but noticeable tendency for block copolymer building. The probabilities for formations of dyad and triad monomer sequences dependent on monomer compositions were calculated from the obtained reactivity ratios. The molar mass distribution, thermal stability and glass transition temperatures of synthesized copolymers were determined. Hydrophobicity of copolymers depending on the composition was determined using contact angle measurements, decreasing from hydrophobic polystyrene and poly(methyl methacrylate) to hydrophilic DPA. Copolymerization reactivity ratios are crucial for the control of copolymer structural properties and conversion heterogeneity that greatly influence the applications of copolymers as rheology modifiers of lubricating oils or in drug delivery systems. © 2015 Society of Chemical Industry     

Characterization of styrene/methacrylic acid copolymers by 2D-NMR spectroscopy

Styrene/methacrylic acid copolymers were prepared by free-radical photopolymerization using the uranyl nitrate ion as the initiator. The copolymer composition was determined from ¹H-NMR spectroscopy. The comonomer reactivity ratios determined using Kelen Tudos and nonlinear error in variable methods (EVM) are r_m = 0.61 ± 0.05 and r_s = 0.14± 0.07. The broad and overlapping ¹H-NMR spectrum was assigned using the help of 2D TOCSY and NOESY experiments. These methods were used to ascertain the various geminal, vicinal, and spatial couplings between the protons. The methyl and methine protons also show configurational and compositional sensitivity. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 82: 2444–2453, 2001     

Studies on the copolymerization of methyl methacrylate and N-aryl maleimides

This article describes the synthesis and characterization of copolymers of methyl methacrylate (MMA) and N-4-chlorophenyl maleimide (PC)/N-3-chlorophenyl maleimide (MC). The copolymers were synthesized by varying the mole fraction of N-aryl maleimides from 0.1 to 0.5 in the initial feed using azobisisobutyronitrile (AIBN) as an initiator and tetrahydrofuran (THF) as the solvent. The copolymer composition was determined from the ¹H-NMR spectra by taking the ratio of proton resonance signals due to methoxy protons (δ = 3.59 ppm) of MMA and aromatic protons (δ = 7.2–7.4 ppm) of N-aryl maleimides. The reactivity ratios for MMA–PC and MMA–MC copolymers were found to be 0.952 (r₁), 0.029 (r₂) and 0.833 (r₁) and 0.033 (r₂), respectively. Thermal characterization of the copolymers was done using differential scanning calorimetry (DSC) and dynamic thermo-gravimetry. Initial decomposition temperature and glass transition temperature increased with increasing mole fraction of N-aryl maleimide content in the copolymers. © 1996 John Wiley & Sons, Inc.