米糠油改性环氧酯铁红防锈底漆的研究

米糠油主要由油酸、亚油酸和棕榈酸组成,属半干性油,具有了作为涂料基料的良好理化特性.研究表明,选用米糠油、桐油、环氧树脂和氧化铁红合成的铁红环氧酯防锈底漆,具有无毒、低温固化、防锈能力强等特点.本文介绍了底漆的配方、生产工艺,并讨论了影响底漆性能的因素.     

新型铁红环氧防锈底漆的研制与应用

介绍了新型铁红环氧防锈底漆的配方、性能和应用。试验结果表明：新型单组分铁红环氧防锈底漆具有干燥快、转化锈蚀、附着力高、防锈能力强等特点，用于钢铁构件的涂装保护，效果良好。     

水性醇酸防锈底漆的防锈性和贮存失干现象探讨

采用水性醇酸树脂配制了水性醇酸防锈底漆。通过与溶剂型醇酸防锈底漆的性能比较,探讨了水性醇酸防锈底漆的防锈性和贮存失干现象。     

一种利用回收泡沫作为原料的低成本防锈底漆

利用回收泡沫作为主要原材料,对其脆性进行改性优化,拼合防锈颜填料,制成了超低成本的防锈底漆。该底漆具有非常优异的物理性能、防锈性能及耐化学性能。     

改性水性环氧树脂防锈底漆的研制

采用自主合成的二氧化钛、氧化锌、硫酸钡和碳酸钙等纳(微)米颜填料对水性环氧树脂涂料进行改性,成功地制备出性能优异的改性水性环氧树脂防锈底漆。研究颜基比(w)对水性环氧树脂防锈底漆的耐盐雾腐蚀性能的影响,确定了颜基比(w);并使用扫描电镜(SEM)对改性防锈底漆的形貌和尺度进行表征。结果表明:使用纳(微)米颜填料成功地实现对环氧树脂防锈底漆的改性,当颜基比(w)为22%时,此时水性环氧防锈底漆具有最佳的综合性能。     

水性石墨烯防锈底漆的研制

研制了一种环境友好型水性石墨烯防锈底漆。讨论了防锈乳液成膜物、防锈颜料、颜料体积浓度(PVC)和助剂对底漆性能的影响。确定了水性石墨烯底漆的配方和生产工艺。     

国内信息

1 TXL-9501水性防锈涂料 目前,钢铁件涂覆采用的底漆有磷化底漆、树脂类底漆以及带锈底漆等。其中,磷化底漆干燥快、配套性好,但防锈性差;树脂类底漆虽然防锈性较好,但因使用了有机溶剂,成膜过程中溶剂的挥发对操作者和环境危害较大,且易引起火灾。带锈底漆可以直接涂覆于带锈的钢铁表     

自干型环氧酯水分散体防锈底漆的研制

采用自制的具有核-壳结构的自干型环氧酯水分散体乳液为基料,配以无毒高效的防锈颜料,制备出防锈性能优良的水性防锈底漆,对影响底漆性能的多种因素进行了探讨.     

醇溶型无机锌车间底漆的电化学行为研究

使用电化学方法对2种不同的醇溶型无机锌车间底漆进行了研究,结合浸泡以及盐雾的实验结果,发现2种车间底漆中锌含量对阴极保护时效有影响,但不是决定车间底漆防锈能力的唯一因素,锌含量与防锈颜料对于车间底漆的防锈性能有协同效果。其中,锌粉在早期提供阴极保护的作用,而防锈颜料在后期对基底提供防锈保护。对于锌粉含量相对较高的车间底漆,锌粉并不是从一开始就全部参加阴极保护作用,而是一部分具有激活潜力的锌粉在另一部分锌粉率先反应之后才由“未激活状态”转变为“激活状态”进而提供阴极保护的作用。     

可带锈涂装的水性防锈底漆的研制

探讨了成膜物质、锈转化剂对可带锈涂装的水性防锈底漆涂膜性能的影响,发现采用聚偏氯乙烯-丙烯酸乳液作成膜物质,植酸作锈转化剂,不添加磷酸,制得的可带锈涂装的水性防锈底漆附着力、耐中性盐雾性能最佳,而适量尼龙粉的引入可明显提高涂膜的耐腐蚀性能。本文制得的可带锈涂装的水性防锈底漆储存稳定,不含重金属和防锈颜料,附着力好,耐腐蚀性能佳,在钢结构翻新领域具有广泛的应用前景。     

白土精制装置过滤机滤板的腐蚀与防护

对比分析了几种常规涂料体系(如环氧富锌底漆+聚酰胺环氧中涂+聚酰胺环氧面漆及环氧铁红底漆+环氧云铁中涂+聚酰胺环氧面漆)和高性能涂料体系的优劣,最后选用了钛纳米聚合物涂料对白土精制装置中的滤板进行防护,2年多的实际应用表明了其良好的防护效果.     

水性环氧防锈底漆的开发及性能研究

以水性环氧树脂乳液及水性环氧固化剂为主要成膜物质,氧化铁红与磷酸锌为防锈颜料,滑石粉和硫酸钡为填料,研制开发了一种性能优良的水性环氧防锈底漆。     

基于丙烯酸接枝环氧树脂的防腐蚀铁红底漆制备及性能研究

根据自由基聚合机理先合成不同比例的丙烯酸接枝环氧树脂,然后加入铁红、云母粉、磷酸锌、三聚磷酸铝制备成漆料,最后加入聚酰胺树脂650固化得到丙烯酸接枝环氧树脂的铁红底漆。利用红外光谱(FT-IR)、热重(TGA)等对制备的丙烯酸-环氧树脂及加聚酰胺树脂固化的丙烯酸-环氧树脂进行分析测试,并通过仪器对涂膜的各项力学性能进行了测试。结果表明:改性后漆膜表现出优异的硬度、附着力、柔韧性、耐冲击性及优良防腐性能。     

X-Ray Photoelectron Spectroscopy of the Fracture Surfaces of Iron/ Epoxy and Titanium/Epoxy Adhesive Joints

The failure path of iron/epoxy and titanium/epoxy lap joints prepared from adherends pretreated with dilute aqueous solutions of ω-aminopropyltriethoxysilane (ω-APS) and then exposed to water at 60°C for varying times was determined using X-ray photoelectron spectroscopy (XPS). Iron/epoxy lap joints prepared using T-APS primers applied at pH 8.0 and tested without exposure to water failed near the oxide/primer interface with only a small amount of adhesive left on the substrate failure surface. Iron/epoxy joints that were primed with T-APS at pH 10.4 and tested without immersion in water failed partly within the adhesive and partly near the interface. All of the iron/epoxy joints failed in the primer near the primer/oxide interface when tested after exposure to water for seven days but very little corrosion of the substrates was observed. When titanium/epoxy lap joints were tested without exposure to water, failure was partly within the adhesive and partly near the primer/oxide interface regardless of the pH at which the primer was applied. However, the failure path shifted to near the primer/oxide interface after the joints were immersed in water for seven days. It was concluded that failure of the joints after exposure to water was associated with hydrolysis within the primer rather than with extensive corrosion of the substrate.     

环氧改性有机硅耐高温防腐涂料的研制

以环氧改性有机硅树脂作为漆基,制备了磷酸锌底漆、云母氧化铁中间漆以及不同颜色的面漆,研究了不同漆膜的耐热性以及以磷酸锌底漆加云母氧化铁中间漆复配不同颜色面漆所得复合涂层的耐热性和耐蚀性。结果表明,以磷酸锌底漆、云母氧化铁中间漆和氧化铬绿面漆复配所得的涂层具有较好的耐高温防腐蚀性能,该复合涂层在350°C烘烤3h后,耐冲击强度≥40kg·cm,附着力≤2级,柔韧性≤2mm。     

易分散纳米聚苯胺改性环氧铁红底漆的防腐性研究

通过引入表面活性剂,合成了易分散纳米聚苯胺(PANI-1)。运用傅里叶变换红外光谱仪(FTIR)和场发射扫描电镜(FE-SEM)表征了聚苯胺的结构,利用电化学方法研究了聚苯胺的防腐性,并采用聚苯胺对环氧铁红底漆进行改性。研究发现,经过表面活性剂改性的聚苯胺为松散纳米结构,容易分散于有机溶剂中;腐蚀测试结果表明,聚苯胺对碳钢有较好的防腐蚀能力,当PANI-1含量为3.5%时,纳米聚苯胺改性环氧铁红底漆涂层具有较好的防腐蚀能力,可应用于桥梁、道路护栏等钢结构的防腐工程。     

Use of auger and x-ray photoelectron spectroscopy to study the locus of failure of structural adhesive joints

The techniques of Auger electron spectroscopy (AES) and x-ray photoelectron spectroscopy (XPS) have been used to study the locus of failure of epoxy resin joints. The effects of a long water immersion and the application of a silane-based primer have also been studied. Results indicated that for dry joints fracture occurred near an epoxy resin/metal interface while with water-soaked unprimed joints, fracture occurred interfacially between the adhesive and iron oxide. The application of the primer to the metal surface prior to bonding prevented the formation of a water-formed oxide although fracture was then found to occur through the primer.     

连续法制备环氧米糠油

将双氧水、甲酸和专用催化剂滴加入米糠油中,在三个串联连接的反应釜中用连续法对米糠油进行氧化,产品精制后得到环氧米糠油。产品质量优于用传统方法生产的产品。     

新型环氧防腐涂料的研究

采用在环氧树脂中加入纳米复合铁钛粉防锈颜料WD—D-325、固化剂、制备了新型环氧树脂防腐涂料。由于纳米技术的特性，该防腐涂料具有较高的防腐性、优异的附着力和柔韧性。实验确定了复合铁钛粉防锈颜料在环氧防腐涂料中的添加量。作为新型的环保颜料，复合铁钛粉防锈颜料可以替代红丹、锌铬黄等颜料。     

无溶剂环氧输油气管内低表面处理防腐减阻涂料的研制

以液态环氧树脂、稀释剂为基体树脂,以腰果壳液改性酚醛胺为固化剂,以复合铁钛粉、磷酸锌、氧化铁红、聚四氟乙烯、沉淀硫酸钡、陶瓷微珠等为填料,在多种功能助剂的配合下制备成无溶剂环氧输油气管内低表面处理防腐减阻涂料.集带锈带油、带湿涂装为一体,具有防腐、减阻、耐磨等特性.