采用自制耐热改性剂N-苯基马来酰亚胺-马来酸酐二元共聚物(NMA)与纳米有机蒙脱土(nanoOMMT)复配对聚酰胺(PA)6进行共混改性,研究了不同m(NMA)∶m(nano-OMMT)对PA 6熔融结晶行为、热性能及力学性能的影响。结果表明:nano-OMMT剥离分散在PA 6基体中;随着nano-OMMT含量增加,PA 6/NMA/nano-OMMT复合材料的熔融温度、结晶温度、结晶度及熔融焓均先升后降;m(NMA)∶m(nano-OMMT)为8∶2时,复合材料弯曲强度、弯曲模量、拉伸强度和负荷变形温度均达最大,分别为117.1,3 301,80.5 MPa及82.7℃,较不加nano-OMMT分别提高21.2%,25.0%,12.9%,27.8%。     

PA6/NMA共混物的制备及其性能研究

以聚酰胺6(PA6)为基体、自制N-苯基马来酰亚胺-马来酸酐二元共聚物(NMA)为耐热改性剂,通过熔融共混法制备了PA6//NMA共混材料。并采用差示扫描量热法(DSC)、热重分析(TGA)、热变形温度及力学性能测试等手段研究了NMA用量对PA6/NMA共混物熔融结晶行为、热性能及力学性能的影响。结果表明:随着NMA用量的增加,PA6/NMA共混物的熔融温度、结晶温度、结晶度以及熔融焓均逐渐降低,而且共混物的最大分解温度较纯PA6显著提高;随着NMA用量的增加,PA6/NMA共混物的力学性能及热性能均明显改善,其中当NMA用量为10份时,共混物的弯曲强度、弯曲模量、拉伸强度及热变形温度分别增至113.8 MPa、3 146 MPa、80.4 MPa以及71.5℃,较纯PA6提高了25.1%、31.9%、15.7%和27.5%;另外,随着NMA用量的增加,共混物的熔体流动速率(MFR)大幅下降,其中当NMA用量增至10份时,共混物的MFR降至5.3 g/10min。     

PA6/SMA/N-PMI复合材料的热性能和力学性能研究

采用熔融共混法制备了聚酰胺6/苯乙烯-马来酸酐共聚物/N-苯基马来酰亚胺复合材料(PA6/SMA/N-PMI),利用差示扫描量热法(DSC)、热重分析(TGA)及力学性能测试等手段研究了N-PMI用量对PA6/SMA/N-PMI复合材料熔融结晶行为、热性能以及力学性能的影响。结果表明:复合材料的最大分解温度较纯PA6有所提高;随着N-PMI用量的增加,复合材料的结晶温度、结晶度以及熔融焓均逐渐降低;当N-PMI用量为15份时,复合材料的弯曲强度、弯曲模量、拉伸强度以及热变形温度均达到最大值,分别为101.0、2 892、71.6 MPa以及56.6℃,较纯PA6分别提高了11.0%、21.3%、3.1%和10.0%。     

PA6/NMA/EP共混物的热性能及其力学性能研究

采用熔融共混法制备PA6/NMA/EP共混物;利用差示扫描量热法(DSC)、热重分析(TGA)、热变形温度测试仪、微机控制电子万能试验机等对其性能进行测试,并研究了EP与PA6的质量比对PA6/NMA/EP共混物的结晶行为、热性能及力学性能的影响。结果表明:随着EP与PA6的质量比的增加,PA6/NMA/EP共混物的结晶度先减小后增加,但热稳定性呈现先增加后减小的趋势;当EP与PA的质量比为2%时,PA6/NMA/EP共混物的热变形温度和拉伸强度均达到最大值72.8℃和77.7 MPa,分别较纯PA6的提高了37.6%和11.8%;而弯曲强度随EP与PA6的质量比的增加呈现逐渐增大的趋势。     

PA6/SMA/LGF复合材料的制备及其性能研究

采用熔融共混法制备了聚酰胺6/苯乙烯-马来酸酐共聚物/长玻璃纤维(PA6/SMA/LGF)复合材料,利用差示扫描量热法(DSC)、热重分析(TGA)、热变形温度及力学性能测试等手段研究了LGF含量对PA6/SMA/LGF复合材料熔融结晶行为、热性能及力学性能的影响。结果表明:随着LGF含量的增加,PA6/SMA/LGF复合材料的结晶温度、结晶度以及熔融焓均先升高再降低,而且复合材料的最大分解温度较纯PA6显著提高;另外,随着LGF含量的增加,PA6/SMA/LGF复合材料的热性能及力学性能均明显改善,其中当LGF含量为27%时,复合材料的热变形温度、弯曲强度、弯曲模量、拉伸强度和冲击强度分别增至206.0℃、227.8 MPa、7 335 MPa、180.6 MPa和18.7 kJ/m2。     

聚酰胺6/环氧树脂改性蒙脱土纳米复合材料的制备与性能

采用环氧树脂改性蒙脱土（MMT）得到有机化蒙脱土（OMMT）,再用熔融插层法制备了聚酰胺6 （PA6）/ OMMT纳米复合材料。采用X射线衍射仪、透射电子显微镜、万能材料试验机、热重分析仪等研究了PA6/OMMT复合材料的形态结构、力学性能和热稳定性。结果表明,经环氧树脂改性得到的OMMT的层间距明显增加,从未改性的1.22 nm增加到5.13 nm,并以纳米尺度分散于PA6基体中;随着OMMT含量的增加,PA6/ OMMT复合材料的强度和模量增加,热变形温度提高,其拉伸强度可达76 MPa,弯曲模量达到3.462 GPa,热变形温度为134 ℃;PA6/ OMMT复合材料失重10 %时的温度为422 ℃,比纯PA6的406 ℃提高了16 ℃,改善了PA6的热稳定性。     

PA6/SMA/N-PMI共混物的制备及其性能研究

采用熔融共混法制备了尼龙6/苯乙烯-马来酸酐共聚物/N-苯基马来酰亚胺共混物(PA6/SMA/N-PMI),并利用DSC、TGA及力学性能测试等手段研究了SMA用量对PA6/SMA/N-PMI共混物熔融结晶行为、热学性能以及力学性能的影响。结果表明,共混物的最大分解温度较纯PA6有较大提高;SMA用量的增加,共混物的结晶温度、结晶度以及熔融焓均先降低再升高;当SMA用量为5份时,共混物的弯曲强度、弯曲模量以及热变形温度均达到最大值,分别为113.8、3 053 MPa及61.3℃,较纯PA6分别提高了25.1%、28.0%及19.0%;拉伸强度在SMA用量为7.5份时达到最大值81.4 MPa,较纯PA6提高了17.1%。     

插层剂对PA66/蒙脱土纳米复合材料性能影响

将不同插层剂改性的蒙脱土与尼龙66(PA66)通过熔融共混制得了纳米复合材料,对复合材料的热变形温度和力学性能进行了研究。结果表明,与纯PA66相比,3种插层剂改性的蒙脱土／PA66纳米复合材料的热变形温度、弯曲模量、弯曲强度均有明显提高,拉伸模量和屈服强度也有所提高,但断裂伸长率和缺口冲击强度则明显下降;含极性羟基的插层剂对复合材料的综合改性效果较好,含2个长链非极性烃基的插层剂改性效果较差;加入环氧树脂后,复合材料的热变形温度、拉伸模量和弯曲模量有所降低,屈服强度、弯曲强度、断裂伸长率和缺口冲击强度则有所增加。     

马来酸酐接枝共聚物增容聚乳酸/改性淀粉复合材料的制备与性能研究

采用熔融共混方法制备聚乳酸/改性淀粉复合材料。研究了不同含量的马来酸酐接枝共聚物对聚乳酸/改性淀粉复合材料力学性能的影响,并且采用差示扫描量热(DSC)仪和扫描电子显微镜(SEM)对复合材料的微观结构进行分析。结果表明,马来酸酐接枝共聚物的加入改善了聚乳酸与淀粉的相容性,提高了复合材料的力学性能,添加量为0.5份时复合材料的拉伸强度提高了61.6%,断裂伸长率提高了53.1%,弯曲强度提高了104.7%,同时还能提高复合材料的热变形温度和耐水性;改性淀粉与聚乳酸两相紧密连接。     

组分对PA6/PP/滑石粉三元复合材料的影响

通过双螺杆挤出制备了尼龙6(PA6)/聚丙烯(PP)/滑石粉三元复合材料,考察不同PA6、PP及滑石粉和增容剂种类及含量对PA6/PP/滑石粉三元复合材料力学性能的影响。结果表明,中黏度(2.4~2.7 Pa·s)PA6、聚乙烯(PE)含量达到7%~9%的嵌段共聚PP及粒径为2~5μm的滑石粉制备的PA/PP/滑石粉三元复合材料具有优异的力学性能;随着PA6含量增加,PA6/PP/滑石粉三元复合材料的拉伸、弯曲强度增加,吸水率上升,PP含量增加,PA6/PP/滑石粉三元复合材料吸水率下降,拉伸强度和弯曲强度也下降;滑石粉的粒径越大,PA6/PP/滑石粉三元复合材料的刚性越好,冲击强度越差,滑石粉的粒径越小,则容易团聚,三元复合材料形成应力集中点;增容剂马来酸酐接枝乙烯-醋酸乙烯酯共聚物(EVAC-g-MAH)和马来酸酐接枝三元乙丙橡胶(EPDM-g-MAH)复配对PA6/PP/滑石粉三元复合材料增容效果优于马来酸酐接枝聚丙烯(PP-g-MAH)或EPDM-g-MAH;当EVAC-gMAH和EPDM-g-MAH添加量各为5%,PA6/PP/滑石粉质量比为50/20/20时,制备出的PA6/PP/滑石粉三元复合材料具有较佳的力学性能,并有优异的加工性能,其缺口冲击强度可达6.6 k J/m^2。     

Effects of support and additive on oxidation state and activity of Pt catalyst in propane combustion

The effects of support and additive on the oxidation state and catalytic activity of Pt catalyst in the low temperature propane combustion were systematically investigated on Pt/MgO, Pt/Al₂O₃ and Pt/SiO₂–Al₂O₃. The catalytic activity varied much with both support materials and additives. The catalyst on the more acidic support showed higher activity, and the catalytic activity on every support materials increased as the electronegativity of additives increased, while some additives decreased the activity. The oxidation state of platinum, estimated by white line intensity of Pt L_III-edge XANES spectrum, also varied with the support and additives, and additives with higher electronegativity greatly prevented the platinum from its oxidation under oxidising atmosphere. Among almost all the catalysts with various supports and various additives, a clear relationship was observed between the oxidation state of platinum and the catalytic activity; the more metallic platinum showed higher activity. Thus, it was concluded that the total electrophilic/electrophobic property derived from those of the support and additive controls the oxidation state of platinum, which intensively affects the catalytic activity; i.e. higher electrophilic property provides less oxidised platinum, resulting in high catalytic activity. The mechanism of this effect was also discussed on the basis of thermochemical data, and it was proposed that the electrophobic materials promote the noble metal oxidation since the noble metal oxo-anion such as PtO^δ− is more stabilised with electrophobic cation.     

核壳型纳米粒子合成方法及其性能的研究进展

核壳纳米粒子作为复合纳米粒子一个重要的分支,由于其光、磁和催化等方面的优异性能,近年来引起了人们广泛的关注.本文主要介绍了核壳纳米粒子的制备方法及诸多性能,并对核壳纳米粒子的发展进行了展望.     

聚丙烯基抗菌塑料的制备与性能研究

利用熔融挤出共混技术制备了聚丙烯(PP)基抗菌塑料。研究了抗菌母料Antim-PP对PP的抗菌性能和力学性能的影响。结果表明,当抗菌母料与PP的质量比为4:100时,抗菌PP塑料对大肠杆菌的抗菌率大于99%,抗菌母料的加入使共混物的冲击性能有明显改善,其他力学性能基本不受影响。     

丁腈橡胶的伏安特性与功率特性的研究

本文对乙炔碳黑填充丁腈橡胶（NBR）的伏安特性及其功率特性进行了研究,分析了丁腈橡胶在交、直流电场下的导电机理,并对环境温度变化时的丁腈橡胶的功率及功率与电压的变化规律提出了相应的关系式,同时对导电丁腈橡胶的物理机械性能进行了研究与测定。     

聚氨酯种类对机械性能以及阻尼性能影响研究

分别以聚四氢呋喃醚二醇(PTMEG)、聚氧化丙烯二醇(PPG-1000)为软段,以二苯基甲烷二异氰酸酯(MDI-50、MDI-100LL),以及扩链剂1,4-丁二醇(BDO)、三羟甲基丙烷(TMP)为硬段,采用预聚体法制备了聚氨酯弹性体。并系统研究了聚氨酯体系中各组分的种类对材料机械性能和阻尼性能的影响。     

金麦丝的抗静电与染色性能

测试了金麦丝的回潮率、质量比电阻、蛋白质含量和上染率;并与棉纤维、黏胶纤维、蛋白质黏胶纤维与羊毛纤维进行比较。结果表明:金麦丝的抗静电性能良好,与黏胶纤维相似,便于加工下游产品;K型活性橙染料对金麦丝的染色上染率高,染色牢度好。     

氟硅橡胶的制备与性能研究

以γ-三氟丙基甲基环三硅氧烷、八甲基环四硅氧烷为原料,乙烯基封端聚二甲基硅氧烷作为封端剂,合成了不同氟硅含量的乙烯基封端γ-三氟丙基甲基硅氧烷-二甲基硅氧烷共聚物,相同硅氧链节的共聚物随三氟丙基甲基硅氧烷CF3CH2CH2(CH3)SiO链节含量的增加,共聚物的黏度也增大.以此共聚物为生胶制备热硫化氟硅橡胶,硫化胶的耐油性能随共聚物中CF3CH2CH2(CH3)SiO链节含量的增加而逐步提高,但对不同油呈现差异.在乙烯基封端聚有机硅氧烷分子链中引入CF3CH2CH2(CH3)SiO链段,通过CF3CH2CH2(CH3)SiO链节含量的调节,可以制备满足不同耐油性能的硅橡胶,既能降低氟硅橡胶的成本,又能达到不同环境下耐油的使用的要求.     

MAX phase Zr2SeC and its thermal conduction behavior

The elemental diversity is crucial to screen out ternary MAX phases with outstanding properties via tuning of bonding types and strength between constitutive atoms. As a matter of fact, the interactions between M and A atoms largely determine the physical and chemical properties of MAX phases. Herein, Se element was experimentally realized to occupy the A site of a MAX phase, Zr₂SeC, becoming a new member within this nanolaminated ternary carbide family. Comprehensive characterizations including Rietveld refinement of X-ray Diffraction and atom-resolved transmission electron microscopy techniques were employed to validate this novel MAX phase. The distinct thermal conduction behaviors emerged are attributed to the characteristic interactions between Zr and Se atoms.     

铝矾土的组成和工艺性能研究

对比研究了几种铝矾土的化学组成、相组成和分散性能。认为所选贵州铝矾土样品氧化铝含量高,适合生产高铝陶瓷球、氢氧化铝、氧化铝和金属铝等;河南和湖南样品铝矾土铝硅配比适中,是生产高强度耐火材料和陶瓷球的较好原料;湖南铝矾土样品分散性能好,特别适于原料需要预处理成均匀料浆的工艺过程。     

聚噻吩纳米复合材料的制备及性能

以各组分尺寸大小为基础对聚噻吩/无机物纳米复合材料进行了分类,详细阐述了各类材料的制备方法。同时强调了聚噻吩/无机物纳米复合材料除了具有聚噻吩、无机物的原有性能外,还会由于聚噻吩与无机物粒子之间的协同作用而具有优异的电性能、光性能,并从分子角度对这些性能提高的机理进行了阐述。