钢板力学性能对FLD0影响的试验研究

对上海宝钢公司生产的15种冷轧冲压用钢进行了力学和FLD试验，探讨了σs／σb、δ、n值、r值对成形极限平面应变特征点(FLD0)的影响。研究表明：FLD0随σs／σb上升而下降，随着δ、n值、r值的上升而提高。在板材力学性能指标中，n值对FLD0的影响最为显著。     

海外文献速报

20050701НикитинСЛ.主要合金元素对Al Mg Si系合金组织、工艺性能的影响.Металл,2004(3):70～77研究了Al Mg Si系合金最佳Mg、Si含量范围,作出了铸态、T4热处理态镁含量和强度极限σb、屈服极限σ0.2、伸长率δ及断面收缩率α的关系图表,随镁含量上升,铸态时σb、σ0.2在Mg的质量分数为7.5%后不再升高,而δ则由于存在粗大的Mg2Si相而下降,至Mg的质量分数大于8.0%后接近于零,T4态时,σb、σ0.2、δ及α均单调升高,但w(Mg)>8.0%后升高相对缓慢,据此,最佳Mg含量范围为6.5%～8.0%,w(Mg)<6.5%时σb、σ0.2均明显降低;Si能…     

Zr-Sn-Nb 合金织构与性能研究

对Zr-Sn-Nb合金带材在25℃、200℃、400℃下进行拉伸试验,采用背散射电子衍射技术(EBSD)研究了织构对锆合金力学性能的影响。结果表明,带材具有较强的{0001}基面双峰织构,[0002]基轴在TD-ND平面内,并向TD方向倾斜约30°,大晶粒多为{0001}< >和{0001}< >取向,小晶粒为{0001}< >取向。织构造成带材力学性能呈现各向异性,σs在TD方向最高,在RD方向最低;σb在RD方向最高,在45°方向最低。随着温度的升高,σs与σb都有所降低,Δσs与Δσb也随之减小,且Δσs较Δσb受温度的影响更为明显。带材的延伸率随温度升高而增加,但400℃时的延伸率较200℃时的低,晶界强度的下降以及动态应变时效是造成这种现象的主要原因。     

Fe72.7Cu1Nb2V1.8Si13.5B9合金的热磁分析

研究了Fe(72.7)Cu1Nb2V(1.8)Si(13.5)B9非晶合金在不同温度（763—883K）退火1h后的热磁曲线（σs－T曲线）借助于碰分析的方法，由σs1/B－T曲线并通过X射线衍射分析确定了合金中α－Fe（Si）相和剩余非晶相的体积分数、饱和磁化强度及Curie温度随退火温度Ta的变化及其相互关系.结果表明，当Ta＜823K时α－Fe（Si）相的饱和磁化强度σsα和Curie温度随Ta的增加略有下降，当Ta≥823K时σsα和TCα保持不变；剩余非晶相的饱和磁化强σsA度和Curie温度在整个退火温度范围内均随Ta的增加而单调下降并且两者之间呈近似直线关系。     

高强钢氢脆敏感性和氢致附加应力的相关性

采用慢应变速率试验(SSRT)研究了高强钢40CrMoTi的氢脆敏感性与氢致附加应力的关系。试验表明,氢致附加应力aσd随试样的屈服强度sσ以及固溶氢浓度C0的对数的增加而线性升高,其关系为,aσd=-260+0.226sσ+63.9 lnC0,高强钢恒载荷下氢致滞后断裂门槛应力随氢浓度对数的升高而线性下降,即,σHIC=863-145lnC0(sσ=900 MPa),σHIC=891-183 lnC0(sσ=1 050 MPa)。预充氢试样慢应变速率拉伸时的相对断裂应力σF(H)/σF随氢浓度对数的升高而线性下降,即,σF(H)/σF=0.97-0.18 lnC0(sσ=900 MPa),σF(H)/σF=0.95-0.24 lnC0(sσ=1 050 MPa)。     

冷轧压下率对高强度IF钢再结晶温度和力学性能的影响

将含P高强度Nb-Ti IF钢不同厚度的热轧板料统一轧成0.8mm厚的冷轧板料,来获得不同冷轧压下率的试样,采用盐浴炉退火试验和表面洛氏硬度测定方法,测定了不同冷轧压下率下的50%软化和100%软化的再结晶温度(T50和T100);冷轧试样经800℃退火后,进行单向拉伸试验,测定屈服强度σs、抗拉强度σb、延伸率δ和轧向塑性应变比r0.试验结果表明,冷轧压下率增大,能降低T100,提高δ和r0,但对T50和σs、σb无明显影响.     

不锈钢薄板拉伸、冲压成形性能的试验研究

采用德国产SCHENCK TREBEL RM250电子万能试验机对别SUS304不锈钢0．5mm薄板进行了拉伸试验，研究了SUS304不锈钢薄板的硬化指数(n值)、屈服强度(σs)、极限强度(σb)、均匀延伸率(δ)等机械性能，并分析了SUS304薄板的冲压成形性能。     

应用超快冷工艺开发540MPa级C-Mn双相钢试验

介绍了在包钢CSP线上应用超快速冷却工艺开发540MPa级热轧双相钢的工业试验概况;以0．07% C—1．20%Mn—0．15%Si钢为原料,采用薄板坯连铸连轧、层流冷却和超快速冷却工艺,得到厚6mm的热轧双相钢带;其微观组织为铁素体和马氏体,马氏体体积分数为12%,σb为555～565MPa,σs为335～355MPa,δ为31%～34%,σs/σb为0．59～0．64,n值为0．18,整卷带钢性能均匀,应用于重型卡车横梁,性能良好。     

热处理对超高碳钢组织和性能的影响

采用几种不同的热处理工艺对超高碳钢进行球化处理,并对不同热处理状态下的试样进行了组织观察和力学性能测试分析,探讨了热处理对超高碳钢组织和性能的影响。结果表明,随着碳化物球化率的提高,钢的塑性得到明显改善。经840℃×20min淬火+650℃×3h高温回火处理样品因能获得圆整度高的球状碳化物,而拥有σs=576MPa、σb=835MPa的高强度和δ5=18·4%的良好塑性。经1200℃×4h高温正火+800℃×2h球化退火处理的超高碳钢由于获得的球状碳化物颗粒细小且分布均匀,基体在变形时受到的阻碍作用较弱,故强度较高(σs=622MPa,σb=927MPa),但塑性稍有下降(δ5=16·0%)。经720℃×3·5h退火处理和840℃×20min空冷+720℃×2·5h退火处理的超高碳钢尽管含有一定量的片状碳化物,也能获得高的强度(σs>590MPa,σb>870MPa)和较好的塑性(δ>11%)。     

半固态挤压原位自生Al-4Cu-0.8Mg/TiCP复合材料的组织与性能

对原位自生Al 4Cu 0 8Mg/TiCP 复合材料采用T4和T6两种热处理制度 ,测试了该材料的σb、σs、E和δ。通过SEM观察和分析了半固态挤压原位自生Al 4Cu 0 8Mg/TiCP 复合材料的显微组织和断口形貌。结果表明 ,在T6工艺处理下TiCP 含量为 15wt%的复合材料的σb、σs、E分别达到 5 40MPa、430MPa、92GPa ,δ为 3 2 % ,断裂形式为韧性断裂 ,由此可以认为 ,原位自生Al 4Cu 0 8Mg/TiCP复合材料具有优良的综合力学性能     

Q550高强钢焊接接头强韧性匹配

在不预热条件下采用不同合金成分焊丝焊接Q550高强钢,试验研究焊丝中合金对焊缝组织、接头抗拉强度及冲击韧性的影响.结果表明,使用MK.G60-1焊丝可获得以针状铁素体为主的焊缝组织.焊缝中沿晶界分布的先共析铁素体在承受拉应力时易萌生裂纹,提高焊缝中针状铁素体含量可以提高接头抗拉强度和韧性.采用MK.G60-1焊丝接头抗拉强度接近母材的抗拉强度,断裂发生在熔合区.接头热影响区的冲击吸收功最高,而熔合区的抗拉强度和韧性最低.焊缝冲击断口纤维区均以穿晶断裂为主,断口韧窝产生的机理是微孔聚集型,针状铁素体区对应的韧窝较大,先共析铁素体对应的韧窝较小.     

��ѧ������״����߼��ˮƽ�ij���̽��

 力学测试是钢铁质量检验的最后一道把关，如何提高力学测试及研究水平关系到减少质量异议和提升企业信誉度，因此，有必要从专业的角度借鉴其它先进经验和学习先进检测手段。本章综合力学测试的相关进展，结合笔者工作的相关数据，针对如何提高力学测试及研究水平进行了探讨。     

Characterizations of friction welding joint interface for AISI 316

Because of heat amount is different from peripheral to central of friction welding interface, which is leaded to vary the characterizations along that interface. Current study, respectively, focused on the effect of different friction pressure on micro-structural and mechanical properties of that friction welding joint interface. Presently, these friction pressures are 110, 130, 150 and 170 MPa while kept all other conditions constant. The effects of different friction pressure on welding interface characterization were investigated by EDX, SEM, tensile, compression, impact and hardness tests. The tensile tests carried out on the standardized test piece with diameter 6 mm and 8 mm, thus, compression tests were extracted from the positions of 0°, 45° 90° with test specimen of 4 mm diameter and 6.5 mm length at weld center. Whereas, the impact test pieces were picked up in two positions, the first one is symmetrical, which it obtained to the respect of the rotation axis and the interface, on the other hand, the second one is non-symmetrical with the axis of rotation and symmetrical to the interface, for making the notch head coincide with the center of the welded joint, The obtained results showed that with reducing of friction pressure will present lack of bonding increasing from peripheral toward the welding center, which will responsible on reducing of the mechanical properties such as tensile, compression and impact strength.     

��ǿ����˨����ǿ�Ȳ�����ȷ���ȵ�����

 参照JIS Z2241 1998金属材料拉伸试验方法对KS B1010 M22×70 mm F10T高强度螺栓抗拉强度进行测量,对测量不确定度来源进行分析并对螺栓抗拉强度的测量不确定度进行了评定,并且给出了扩展不确定度。     

Electrically assisted blanking using the electroplasticity of ultra-high strength metal alloys

The electroplastic tensile behavior of ultra-high strength steels (UHSS) subject to a single pulse of electric current is briefly introduced, and electrically-assisted (EA) blanking, which utilizes this electroplastic characteristic, is suggested. The experimental result shows that the blanking load of EA blanking is clearly lower than that of blanking with local resistance heating, which is lower than that of cold blanking. No significant change in material properties was observed in the EA blanked parts at the electric energy densities selected in the present study. EA blanking or trimming is expected to minimize or even eliminate the need for expensive and time-consuming laser trimming in the manufacture of automotive parts using UHSS.     

热流道喷嘴壳体的强度校核

分析了热流道喷嘴在注射压力下的疲劳强度问题。提出了壳体壁厚的设计计算方法。喷嘴与流道板间螺纹联接时,还必须校核喷嘴壳体承受弯曲变形下的强度。     

金属铍的微屈服行为及机理

为研究金属铍的微屈服行为,通过透射电镜观察了1×10-5、50×10-6和200×10-6 3种不同微屈服阶段材料位错的变化,初探了铍的微屈服机理.通过130多个铍试样的微屈服强度与屈服强度的比较试验证明,用常规简单的屈服强度试验代替冗长的微屈服强度试验是可能的.     

有机酯硬化剂对水玻璃砂的影响

通过正交试验分析了水玻璃的加入量增加和有机酯的加入对水玻璃砂的残留强度和24h熟强度的影响程度大小，结果表明：有机酯的加入使水玻璃砂的24h终强度达到了普通水玻璃砂的要求；水玻璃加入量的减少，使有机酯硬化水玻璃砂的溃散性有较大提高。     

Si_3N_4/Ti/Ni/Ti/Si_3N_4部分瞬间液相连接接头的强度与断裂

在温度为１２７３ ～１４２３ Ｋ、时间为０ ．９ ～７ ．２ ｋｓ 和０ ．１ ＭＰａ 压应力的条件下进行了Ｓｉ３Ｎ４／Ｔｉ／Ｎｉ／Ｔｉ／Ｓｉ３Ｎ４ 的部分瞬间液相连接, 结合ＳＥＭ, ＥＤＳ 和ＸＲＤ 测试结果, 分析了连接温度和时间对接头常温四点弯曲强度和断裂方式的影响。通过用反应层厚度来表征界面强度, 用σＲｅｓθｍａｘ 来评价近界面陶瓷断裂, 用σＲｅｓθ＝ ０ 来评价界面断裂, 建立了界面强度、陶瓷强度和残余应力与接头强度和三种断裂类型的关系模型。     

热处理对硬钎焊焊缝性能的影响

通过对YG8合金与35CrMnSi钢硬钎焊焊缝热处理后的组织和性能的研究，分析了淬火工艺对焊缝剪切强度和抗弯强度产生的影响。结果表明，淬火温度越高焊缝性能越差，低温回火可使焊缝具有良好的性能。