Effect of Annealing Temperature on Microstructure and Mechanical Properties of Bulk 316L Stainless Steel with Nano- and Micro-crystalline Dual Phases

Microstructures and mechanical properties of 316L stainless steels with dual phases austenite prepared by an aluminothermic reaction casting were explored. It is found that the steels consist of nano- and micro-crystalline austenite phases, a little δ ferrite and contaminations. Before and after annealing at 1073 K and 1273 K (800 °C and 1000 °C), average grain sizes of the nanocrystalline austenite phase are about 32, 31, 38 nm, respectively. Tensile strength increases first from 371 to 640 MPa and then decreases to 454 MPa. However, elongation ratio increases gradually from 16 to 23 and then 31 pct after annealing. The results illustrate that the steel after annealing at 1073 K (800 °C) has better properties, also indicating that combination of dual nano- and micro-crystalline austenite phase is conductive to improving tensile properties of materials.     

Effects of Tungsten Addition on the Microstructure and Mechanical Properties of Microalloyed Forging Steels

In the current study, the effects of tungsten (W) addition on the microstructure, hardness, and room/low [223 K and 173 K (?50 °C and ?100 °C)] temperature tensile properties of microalloyed forging steels were systematically investigated. Four kinds of steel specimens were produced by varying the W additions (0, 0.1, 0.5, and 1 wt pct). The microstructure showed that the addition of W does not have any noticeable effect on the amount of precipitates. The precipitates in W-containing steels were all rich in W, and the W concentration in the precipitates increased with the increasing W content. The mean sizes of both austenite grains and precipitates decreased with the increasing W content. When the W content was equal to or less than 0.5 pct, the addition of W favored the formation of allotriomorphic ferrite, which subsequently promoted the development of acicular ferrite in the microalloyed forging steels. The results of mechanical tests indicated that W plays an important role in increasing the hardness and tensile strength. When the testing temperature was decreased, the tensile strength showed an increasing trend. Both the yield strength and the ultimate tensile strength obeyed an Arrhenius type of relation with respect to temperature. When the temperature was decreased from 223 K to 173 K (from ?50 °C to ?100 °C), a ductile-to-brittle transition (DBT) of the specimen with 1 pct W occurred. The addition of W favored a higher DBT temperature. From the microstructural and mechanical test results, it is demonstrated that the addition of 0.5 pct W results in the best combination of excellent room/low-temperature tensile strength and ductility.     

Nanoscale Analyses of High-Nickel Concentration Martensitic High-Strength Steels

Austenite reversion in martensitic steels is known to improve fracture toughness. This research focuses on characterizing mechanical properties and the microstructure of low-carbon, high-nickel steels containing 4.5 and 10 wt pct Ni after a QLT-type austenite reversion heat treatment: first, martensite is formed by quenching (Q) from a temperature in the single-phase austenite field, then austenite is precipitated by annealing in the upper part of the intercritical region in a lamellarization step (L), followed by a tempering (T) step at lower temperatures. For the 10 wt pct Ni steel, the tensile strength after the QLT heat treatment is 910 MPa (132 ksi) at 293 K (20 °C), and the Charpy V-notch impact toughness is 144 J (106 ft-lb) at 188.8 K (?84.4 °C, ?120 °F). For the 4.5 wt pct Ni steel, the tensile strength is 731 MPa (106 ksi) at 293 K (20 °C) and the impact toughness is 209 J (154 ft-lb) at 188.8 K (?84.4 °C, ?120 °F). Light optical microscopy, scanning electron and transmission electron microscopies, synchrotron X-ray diffraction, and local-electrode atom-probe tomography (APT) are utilized to determine the morphologies, volume fractions, and local chemical compositions of the precipitated phases with sub-nanometer spatial resolution. The austenite lamellae are up to 200 nm in thickness, and up to several micrometers in length. In addition to the expected partitioning of Ni to austenite, APT reveals a substantial segregation of Ni at the austenite/martensite interface with concentration maxima of 10 and 23 wt pct Ni for the austenite lamellae in the 4.5 and 10 wt pct Ni steels, respectively. Copper-rich and M₂C-type metal carbide precipitates were detected both at the austenite/martensite interface and within the bulk of the austenite lamellae. Thermodynamic phase stability, equilibrium compositions, and volume fractions are discussed in the context of Thermo-Calc calculations.     

Effect of Niobium on the Ferrite Continuous-Cooling-Transformation (CCT) Curve of Ultrahigh-Thickness Cr-Mo Steel

Pressure vessels made for petrochemical and power plants using Cr-Mo steel must be thick (≥400 mm) and have high tensile strength (≥600 MPa). However, the tensile strength in the middle portion of the vessel is very low as a result of ferrite formation. Therefore, research was performed to study the ferrite transformation that occurs in the middle portion of high-thickness Cr-Mo steel when Nb is added to it. The ferrite-formation start time of the continuous-cooling-transformation (CCT) curve decreased with an increase in Nb content until the latter reached 0.05 pct. On cooling from the austenitizing temperature, some of the NbC present at the austenitizing temperature of 1203 K (930 °C) goes into austenite solution in the temperature range of 1173 K to 1073 K (900 °C to 800 °C). However, the ferrite curve shifted to the left for the alloy containing 0.075 pct Nb. It is postulated that the surplus NbC could act as ferrite nucleation sites despite the lower cooling rate. As a result, the hardenability improved in the order of the following Nb content: 0.05 pct, 0.025 pct, 0 pct, and 0.075 pct.     

Constitutive Modeling of the Mechanical Properties of V-added Medium Manganese TRIP Steel

In this study, medium Mn transformation-induced plasticity steel with the composition Fe-0.08 pct C-6.15 pct Mn-1.5 pct Si-2.0 pct Al-0.08 pct V was investigated. After intercritical annealing at 1013 K (740 °C), the steel contained coarse-grained ferrite and two ultrafine-grained (UFG) phases: ferrite and retained austenite. The material did not deform by localized Lüders band propagation: it did not suffer from this major problem as most UFG steels do. Localization of plastic flow was shown to be suppressed because of a combination of factors, including a bimodal grain size distribution, a multiphase microstructure, the presence of nanosized vanadium carbide precipitates, and the occurrence of the deformation-induced martensitic transformation of retained austenite. A constitutive model incorporating these effects was developed. The model was used to identify the factors which can lead to a further improvement of the mechanical properties of the UFG medium Mn TRIP steels.     

Effect of Nitrogen Content on Grain Refinement and Mechanical Properties of a Reversion-Treated Ni-Free 18Cr-12Mn Austenitic Stainless Steel

Martensite reversion treatment was utilized to obtain ultrafine grain size in Fe-18Cr-12Mn-N stainless steels containing 0 to 0.44 wt pct N. This was achieved by cold rolling to 80 pct reduction followed by reversion annealing at temperatures between 973 K and 1173 K (700 °C and 900 °C) for 1 to 10⁴ seconds. The microstructural evolution was characterized using both transmission and scanning electron microscopes, and mechanical properties were evaluated using hardness and tensile tests. The steel without nitrogen had a duplex ferritic-austenitic structure and the grain size refinement remained inefficient. The finest austenitic microstructure was achieved in the steels with 0.25 and 0.36 wt pct N following annealing at 1173 K (900 °C) for 100 seconds, resulting in average grain sizes of about 0.240 ± 0.117 and 0.217 ± 0.73 µm, respectively. Nano-size Cr₂N precipitates observed in the microstructure were responsible for retarding the grain growth. The reversion mechanism was found to be diffusion controlled in the N-free steel and shear controlled in the N-containing steels. Due to a low fraction of strain-induced martensite in cold rolled condition, the 0.44 wt pct N steel displayed relatively non-uniform, micron-scale grain structure after the same reversion treatment, but it still exhibited superior mechanical properties with a yield strength of 1324 MPa, tensile strength of 1467 MPa, and total elongation of 17 pct. While the high yield strength can be attributed to strengthening by nitrogen alloying, dislocation hardening, and slight grain refinement, the moderate strain-induced martensitic transformation taking place during tensile straining was responsible for enhancement in tensile strength and elongation.     

A Novel Ni-Containing Powder Metallurgy Steel with Ultrahigh Impact,Fatigue, and Tensile Properties

The impact toughness of powder metallurgy (PM) steel is typically inferior, and it is further impaired when the microstructure is strengthened. To formulate a versatile PM steel with superior impact, fatigue, and tensile properties, the influences of various microstructures, including ferrite, pearlite, bainite, and Ni-rich areas, were identified. The correlations between impact toughness with other mechanical properties were also studied. The results demonstrated that ferrite provides more resistance to impact loading than Ni-rich martensite, followed by bainite and pearlite. However, Ni-rich martensite presents the highest transverse rupture strength (TRS), fatigue strength, tensile strength, and hardness, followed by bainite, pearlite, and ferrite. With 74 pct Ni-rich martensite and 14 pct bainite, Fe-3Cr-0.5Mo-4Ni-0.5C steel achieves the optimal combination of impact energy (39 J), TRS (2170 MPa), bending fatigue strength at 2 × 10⁶ cycles (770 MPa), tensile strength (1323 MPa), and apparent hardness (38 HRC). The impact energy of Fe-3Cr-0.5Mo-4Ni-0.5C steel is twice as high as those of the ordinary high-strength PM steels. These findings demonstrate that a high-strength PM steel with high-toughness can be produced by optimized alloy design and microstructure.     

Recovery of Ductility in Ultrafine-Grained Low-Carbon Steel Processed Through Equal-Channel Angular Pressing Followed by Cold Rolling and Flash Annealing

The low-carbon steel workpieces are deformed by equal-channel angular pressing at 293 K (20 °C) up to an equivalent strain of ~12 using route B _c, which results in the bulk ultrafine-grained (UFG) structure with high dislocation density and partial dissolution of cementite. The yield strength (YS) is enhanced from 208 (as-received) to 872 MPa and the tensile strength is increased from 362 to 996 MPa, but the material loses total elongation (TE) from 36.2 to 2.9 pct. Cold rolling of equal-channel angular pressed steel produces the refined structure of grain size 0.11 μm. The YS increases further to 924 MPa with a marginal gain in ductility due to the reappearance of the γ fiber component. Flash annealing the samples, which were equal-channel angular pressed followed by cold rolling, at 873 K (600 °C) results in 27 pct of micron-sized (9 µm) ferrite grains in submicron-sized (<1 µm) matrix with a reduced defect density and small amount of precipitation of cementite. TE increases from 2.9 to 23.3 pct. The material retains a YS of 484 MPa and tensile strength of 517 MPa, which are higher than those of the as-received material. The UFG grains are failed by cleavage, but the micron-sized grains display ductile fracture. The ductility of the flash-annealed material is recovered significantly due to bimodal grain size distribution in ferrite and the development of a good amount of γ fiber texture components. The major contribution toward recovery of ductility comes from the bimodal grain size distribution in ferrite rather the precipitation of cementite.

     

High-Temperature Tensile Properties of Nano-Oxide Dispersion Strengthened Ferritic Steels Produced by Mechanical Alloying and Spark Plasma Sintering

Oxide-dispersion strengthened (ODS) ferritic steels were produced by mechanical alloying and subsequent spark plasma sintering. Very fast heating rates were used to minimize porosity when controlling grain size and precipitation of dispersoids within a compacted material. Sintering cycles performed at 1373 K (1100 °C) induced heterogeneous, but fine grain size distribution and high density of nano-oxides. Yield strengths at room temperature and at 923 K (650 °C) are 975 MPa and 298 MPa, respectively. Furthermore, high-temperature ductility is much increased: total strain of 28 pct at 923 K (650 °C).     

Effect of Continuous Galvanizing Heat Treatments on the Microstructure and Mechanical Properties of High Al-Low Si Transformation Induced Plasticity Steels

Heat treatments were performed using an isothermal bainitic transformation (IBT) temperature compatible with continuous hot-dip galvanizing on two high Al–low Si transformation induced plasticity (TRIP)-assisted steels. Both steels had 0.2 wt pct C and 1.5 wt pct Mn; one had 1.5 wt pct Al and the other had 1 wt pct Al and 0.5 wt pct Si. Two different intercritical annealing (IA) temperatures were used, resulting in intercritical microstructures of 50 pct ferrite (α)-50 pct austenite (γ) and 65 pct α-35 pct γ. Using the IBT temperature of 465 °C, five IBT times were tested: 4, 30, 60, 90, and 120 seconds. Increasing the IBT time resulted in a decrease in the ultimate tensile strength (UTS) and an increase in the uniform elongation, yield strength, and yield point elongation. The uniform elongation was higher when using the 50 pct α-50 pct γ IA temperature when compared to the 65 pct α-35 pct γ IA temperature. The best combinations of strength and ductility and their corresponding heat treatments were as follows: a tensile strength of 895 MPa and uniform elongation of 0.26 for the 1.5 pct Al TRIP steel at the 50 pct γ IA temperature and 90-second IBT time; a tensile strength of 880 MPa and uniform elongation of 0.27 for the 1.5 pct Al TRIP steel at the 50 pct γ IA temperature and 120-second IBT time; and a tensile strength of 1009 MPa and uniform elongation of 0.22 for the 1 pct Al-0.5 pct Si TRIP steel at the 50 pct γ IA temperature and 120-second IBT time.     

Thixoforging of Wrought Aluminum Thin Plates with Microchannels

A direct die-filling thixoforging method is designed to fabricate aluminum thin plates with a pattern of microchannels in a single forming operation. Extruded AA2024 and AA7075 wrought aluminum billets are used. A recrystallization and partial remelting process is used to prepare the semisolid slurries required for the forming process. Under a thixoforging pressure of 70 MPa, AA7075 thin plates are successfully thixoforged in a temperature range of 883 K to 893 K (610 °C to 620 °C), corresponding to liquid fractions of ~30 to 50 pct in the semisolid slurry. AA2024 thin plate requires a thixoforging temperature range of 888 K to 898 K (615 °C to 625 °C), corresponding to the liquid fractions of ~45 to 60 pct. Final microstructures of the thin plates comprise primary α-Al equiaxed globular grains in a matrix of a solidified liquid phase. With increasing thixoforging temperature, the yield strength values continuously decrease. The ultimate tensile strength (UTS) values of the thin plates initially decrease with increasing thixoforging temperature from 883 K to 888 K (610 °C to 615 °C) and from 888 K to 893 K (615 °C to 620 °C) for the AA7075 and AA2024 thin plates, respectively. The UTS values stabilize and slightly enhance when the thixoforging temperatures are further increased to 893 K and 898 K (620 °C and 625 °C) for the AA7075 and AA2024 thin plates, respectively. Very brittle behavior (elongation value of ~1 pct) is observed for the AA7075 thin plates thixoforged at 883 K and 888 K (610 °C and 615 °C). The elongation value increases to 3 pct with increasing the thixoforging temperature to 893 K (620 °C). In contrast, larger elongation values (between 4 and 6 pct) are achieved for the AA2024 thin plates. Increasing the thixoforging pressures from 70 to 100 MPa and then to 150 MPa improves the tensile properties of the thin plates. The tensile properties of the thixoforged thin plates are linked to their microstructural characteristics and processing conditions and are discussed here in detail.     

Effect of Boron on the Strength and Toughness of Direct-Quenched Low-Carbon Niobium Bearing Ultra-High-Strength Martensitic Steel

The effect of boron on the microstructures and mechanical properties of laboratory-control-rolled and direct-quenched 6-mm-thick steels containing 0.08 wt pct C and 0.02 wt pct Nb were studied. The boron contents were 24 ppm and a residual amount of 4 ppm. Two different finish rolling temperatures (FRTs) of 1093 K and 1193 K (820 °C and 920 °C) were used in the hot rolling trials to obtain different levels of pancaked austenite prior to DQ. Continuous cooling transformation (CCT) diagrams were constructed to reveal the effect of boron on the transformation behavior of these steels. Microstructural characterization was carried out using various microscopy techniques, such as light optical microscopy (LOM) and scanning electron microscopy-electron backscatter diffraction (SEM-EBSD). The resultant microstructures after hot rolling were mixtures of autotempered martensite and lower bainite (LB), having yield strengths in the range 918 to 1067 MPa with total elongations to fracture higher than 10 pct. The lower FRT of 1093 K (820 °C) produced better combinations of strength and toughness as a consequence of a higher degree of pancaking in the austenite. Removal of boron lowered the 34 J/cm² Charpy-V impact toughness transition temperature from 206 K to 158 K (?67 °C to ?115 °C) when the finishing rolling temperature of 1093 K (820 °C) was used without any loss in the strength values compared to the boron-bearing steel. This was due to the finer and more uniform grain structure in the boron-free steel. Contrary to expectations, the difference was not caused by the formation of borocarbide precipitates, as verified by transmission electron microscopy (TEM) investigations, but through the grain coarsening effect of boron.     

High Strength High Carbon Low Alloy Pearlite-Ferrite-Tempered Martensite Steels

High strength multiphase steels have been developed consisting of combination of pearlite, tempered martensite and small amount of ferrite, by suitable heat treatment of a high carbon low alloy rail steel (0.7 % C). The desired microstructure has been obtained by holding fully homogenized steel in pearlitic range for small durations followed by water quenching and subsequent tempering at 773 K for 18 h. Variation in mechanical properties has been studied with the change in volume fraction of different phases. Yield strength, ultimate tensile strength and elongation are observed to be in the range of 500–1,000 MPa, 900–1,185 MPa and up to 16.8 %, respectively. Continuous and discontinuous yielding along with substantial work hardening has been explained as a function of tempered martensite content.     

Evaluation of Microstructure and Mechanical Properties of Nano-Y2O3-Dispersed Ferritic Alloy Synthesized by Mechanical Alloying and Consolidated by High-Pressure Sintering

In this study, an attempt has been made to synthesize 1.0 wt pct nano-Y₂O₃-dispersed ferritic alloys with nominal compositions: 83.0 Fe-13.5 Cr-2.0 Al-0.5 Ti (alloy A), 79.0 Fe-17.5 Cr-2.0 Al-0.5 Ti (alloy B), 75.0 Fe-21.5 Cr-2.0 Al-0.5 Ti (alloy C), and 71.0 Fe-25.5 Cr-2.0 Al-0.5 Ti (alloy D) steels (all in wt pct) by solid-state mechanical alloying route and consolidation the milled powder by high-pressure sintering at 873 K, 1073 K, and 1273 K (600°C, 800°C, and 1000°C) using 8 GPa uniaxial pressure for 3 minutes. Subsequently, an extensive effort has been undertaken to characterize the microstructural and phase evolution by X-ray diffraction, scanning and transmission electron microscopy, and energy dispersive spectroscopy. Mechanical properties including hardness, compressive strength, Young’s modulus, and fracture toughness were determined using micro/nano-indentation unit and universal testing machine. The present ferritic alloys record extraordinary levels of compressive strength (from 1150 to 2550 MPa), Young’s modulus (from 200 to 240 GPa), indentation fracture toughness (from 3.6 to 15.4 MPa√m), and hardness (from13.5 to 18.5 GPa) and measure up to 1.5 through 2 times greater strength but with a lower density (~7.4 Mg/m³) than other oxide dispersion-strengthened ferritic steels (<1200 MPa) or tungsten-based alloys (<2200 MPa). Besides superior mechanical strength, the novelty of these alloys lies in the unique microstructure comprising uniform distribution of either nanometric (~10 nm) oxide (Y₂Ti₂O₇/Y₂TiO₅ or un-reacted Y₂O₃) or intermetallic (Fe₁₁TiY and Al_9.22Cr_2.78Y) particles' ferritic matrix useful for grain boundary pinning and creep resistance.     

High Strength and Retained Ductility Achieved in a Nitrided Strip Cast Nb-Microalloyed Steel

The current study investigates the strengthening of an Nb-microallyed CASTRIP^® steel at 798 K (525 °C) by nitriding in a KNO₃ salt bath. Nitriding up to 1 hour dramatically increased the yield strength of the steel by ~35 pct (from 475 to 645 MPa) with no sacrifice of ductility (~16 pct). Further nitriding led to brittle fracture. Hardness profiles of the nitrided steels through the thickness reveal hard surfaces and a relatively softer core. The hardening of the shell in the nitrided steels is thought to be the combined effect of solid solution strengthening from nitrogen and dispersion strengthening from clusters and precipitates. The retained ductility is attributed to the hard-shell–soft-core structure through nitriding.     

Kinetics of Z-Phase Precipitation in 9 to 12 pct Cr Steels

The Z-phase nitride is seen as a detrimental phase in 9 to 12 pct Cr steels as it is in competition with the beneficial MX particles. Two model steels, with 9 pct Cr and 12 pct Cr content, respectively, were designed to study the effect of Cr on Z-phase precipitation kinetics. The steels were isothermally aged at 873 K, 923 K, and 973 K (600 °C, 650 °C, and 700 °C) for up to 30,000 hours in order for Z-phase to replace MX. X-ray diffraction (XRD) analysis of extracted precipitates was used to quantitatively follow the evolution of the nitrides population. It was found that the 12 pct Cr steel precipitated Z-phase 20 to 50 times faster than the 9 pct Cr steel. Transmission electron microscopy (TEM) was applied to follow the Z-phase precipitation, using energy-dispersive X-ray spectroscopy (EDS) line scans and atomic resolution imaging.     

Influence of Warm Tempforming on Microstructure and Mechanical Properties in an Ultrahigh-Strength Medium-Carbon Low-Alloy Steel

A 0.4 pct C-2 pct Si-1 pct Cr-1 pct Mo steel was quenched and tempered at 773 K (500 °C) and deformed by multi-pass caliber rolling (i.e., warm tempforming). The microstructures and the mechanical properties of the warm tempformed steels were investigated as a function of the rolling reduction. At rolling reductions of more than 28 pct, not only extension of the martensite blocks and/or the packets in the rolling direction (RD) but also a grain subdivision became more significant, and an ultrafine elongated grain (UFEG) structure with a strong ??110??//RD fiber deformation texture was formed after 78 pct rolling. The tensile deformation behavior became significantly anisotropic in response to the evolution of UFEG structure. The longitudinal yield strength (??_y) of the quenched and tempered sample increased from 1480 to 1860 MPa through the 78 pct rolling, while the transverse ??_y leveled off at around 1600 MPa up to 28 pct rolling. The transverse true fracture stress was also markedly degraded in contrast to the longitudinal one. Charpy impact properties were enhanced at a rolling reduction of 52 pct or more. The 52 pct-rolled sample underwent a ductile-to-brittle transition in the temperature range from 333 K to 213 K (60 °C to ?60 °C), while the 78 pct-rolled sample showed an inverse temperature dependence of the impact toughness because of brittle delamination. The tensile and Charpy impact properties are discussed in association with the microstructural evolution.     

Third Generation 0.3C-4.0Mn Advanced High Strength Steels Through a Dual Stabilization Heat Treatment: Austenite Stabilization Through Paraequilibrium Carbon Partitioning

In excess of 30 vol. pct austenite can be retained in 0.3C-4.0Mn steels subjected to a dual stabilization heat treatment (DSHT) schedule—a five stage precisely controlled cooling schedule that is a variant of the quench and partition process. The temperature of the second quench (stage III) in the DSHT process plays an essential role in the retained austenite contents produced at carbon-partitioning temperatures of 723 K or 748 K (450° C or 475 °C) (stage IV). A thermodynamic model successfully predicted the retained austenite contents in heat-treated steels, particularly for a completely austenitized material. The microstructure and mechanical behavior of two heat-treated steels with similar levels of retained austenite (~30 vol. pct) were studied. Optimum properties—tensile strengths up to 1650 MPa and ~20 pct total elongation—were observed in a steel containing 0.3C-4.0Mn-2.1Si, 1.5 Al, and 0.5 Cr.     

Strength and toughness of Fe-10ni alloys containing C,Cr, Mo,and Co

The effects of C (0.10 to 0.20 pct), Cr (0 to 3 pct), Mo (0 to 2 pct), and Co (0 to 8 pct) on the yield strength, toughness (Charpy shelf energy), and tempering behavior of martensitic lONiCr-Mo-Co steels have been investigated. Variations in the carbon content between 0.10 and 0.20 pct result in yield strengths between 160 and 210 ksi (1.1 and 1.45 GN/m²) when these steels are tempered at 900° to 1000°F (480° to 540°C) for times of 1 to 100 h. These steels exhibit a secondary-hardening peak at 900° to 1000° F (480° to 540°C) where coarse Fe₃C carbides are gradually replaced by a fine, dislocation-nucleated dispersion of (Mo, Cr)₂C carbides. Maximum toughness at a given yield strength in these steels is only obtained when they are tempered for sufficiently long times so that the coarse Fe₃C carbides are completely dissolved. Molybdenum is primarily responsible for the secondary-hardening peak observed in these steels. However, chromium additions do result in lower secondaryhardening temperatures and promote coarsening of the secondary-hardening carbide. Best combinations of strength and toughness are obtained with steels containing 2 pct Cr and 1 pct Mo. Cobalt increases the yield strength of these steels over the entire tempering range and results in a higher secondary-hardening peak. This effect of cobalt is attributed to 1) a retardation in the rate of recovery of the dislocation substructure of the martensite, 2) the formation of a finer dispersion of secondary-hardening carbides, and 3) solid-solution strengthening. The finer dispersion of secondary-hardening carbides in steels containing cobalt is favored by the finer dislocation substructure in these steels since the (Mo, Cr)₂C carbide is dislocation-nucleated. This fine dispersion of (Mo, Cr)₂C carbide combined with the high nickel content accounts for the excellent combination of strength and toughness exhibited by these steels.     

M5C2 Carbides in a High-Chromium Ferritic/Martensitic Steel

The precipitate phases in an 11 pct Cr ferritic/martensitic steel normalized at 1323 K (1050 °C) for 0.5 hour and tempered at 1053 K (780 °C) for 1.5 hours have been investigated. Except for dominant phases, Cr-rich M₂₃C₆ carbide and Nb-rich, Ta-Nb-rich, and V-rich MC carbides, needle-like precipitates with a typical size of 70 to 310 and 10 to 30 nm for the length of the long and short axis of the needles, respectively, were also observed on the extraction carbon replica of the steel. The typical metallic element composition of the needle-like precipitates is about 53-82Fe, 14-26Cr, 0.5-18Ta, 1-6W, and 2-5Co in atomic pct. Through energy dispersive X-ray analysis and electron diffraction along with calculations regarding lattice parameter and interplanar spacing, the needle-like precipitates were identified as a Fe-rich M₅C₂ carbide, which is not known to have been reported previously in high-chromium steels. The M₅C₂ carbide has a base-centered monoclinic crystal structure with the approximate lattice parameters a/b/c = 1.142/0.5186/0.5383 nm and β = 104.68 deg. The formation of the Fe-rich M₅C₂ carbides in the steel has been discussed. The effect of chromium content in matrix and boron addition on the precipitate phases in ferritic/martensitic steels has also been discussed.