激光淬火齿轮与渗碳淬火齿轮的接触疲劳强度对比实验研究

在40CrNiMoA钢激光相变硬化基础工艺研究的基础上,通过采用齿轮激光热处理关键技术,获得了沿齿廓均匀分布的理想硬化层.40CrNiMoA钢激光淬火齿轮和20Cr2Ni4A钢渗碳淬火齿轮接触疲劳强度试验表明:激光淬火齿轮的接触疲劳极限应力均高于渗碳淬火齿轮,且接触疲劳寿命离散度小,所以激光淬火齿轮可以代替渗碳淬火齿轮.     

圆锯片齿部激光热处理工艺研究

用CO2激光器对切割钢管用的圆锯片齿部进行激光相变硬化处理,选择最佳工艺参数,达到圆锯片齿部最佳的金相组织,硬度及淬火深度等技术条件.     

齿轮宽带激光淬火组织和应力分析

利用扫描电镜、透射电镜和X射线应力分析系统,对齿轮宽带激光淬火后淬硬层显微组织和应力特性进行了细致分析.结果表明其组织分为:淬硬层、过渡层、高温回火区三层.淬硬层主要是由马氏体和残余奥氏体组成;过渡层为马氏体和回火索氏体混合组织;高温回火区由回火索氏体组织组成.激光淬火硬化层应力状态为压应力.     

激光淬火齿轮组织和应力分析

采用扫描电镜、透射电镜和X射线应力分析系统，对齿轮宽带激光淬火后淬硬层显微组织和应力特性进行了研究，结果表明：激光淬火硬化区依其组织特征，大致分为3层：第1层为表面完全淬硬层，其主要是由马氏体和残余奥氏体组成；第2层为过渡层，由马氏体和基体上分布着回火析出的碳化物混合组成；第3层为高温回火区，由回火索氏体组织组成．激光淬火硬化层应力状态为压应力．     

激光相变硬化对42CrMo钢的组织与性能的影响

本文对低温回火态的42CrMo钢的激光相变硬化进行了实验研究,试验了激光相变硬化处理的工艺参数对硬化层显微组织、硬化深度、显微硬度变化以及对耐磨性能的影响。结果表明:经激光相变硬化处理后,42CrMo钢的表面层硬度可达Hv1150,硬化层的显微组织主要是高缺陷密度的隐针马氏体。与常规淬火处理相比,显微硬度提高一倍多,耐磨性提高四倍左右。最后探讨了激光相变硬化的机理。     

亚共析钢激光相变硬化显微组织的研究

研究了正火态基体和调质态基体的45钢激光淬火后的组织及其形成过程,指出由于激光相变硬化过程的高速性和极端的不平衡性,导至碳的局部区域扩散是造成正火态基体45钢激光淬火后,出现屈氏体多样化分层组织的根本原因。通过研究表明,45钢采用调质态基体进行激光淬火时,可使整个激光相变硬化层获得全马氏体组织。     

65Mn冷切锯片齿部电接触淬火的研究

试验研究了６５Ｍｎ钢制冷切锯片齿部重新电接触加热淬火工艺参数，齿部显微组织，硬化层深度，硬度及耐磨性，并进行了电接触淬火锯片实际寿命考核以及经济效益分析。     

汽轮机叶片局部激光表面淬火工艺试验研究

对汽轮机叶片进气边局部进行激光淬火工艺试验，研究工艺参数，搭接对硬化层深度，硬度及硬度分布的影响，分析了淬火后的组织特征，结果显示：激光淬火可得到深度为0．25－0.45mm的硬化层，平均硬度为HV588，20％的搭接量可满足实际使用要求。从而，得到符合实际需要的优化工艺，以替代传统工艺。     

CO_2 激光切割金属材料的工艺参数与性能关系的研究

本文研究了用 CO_2激光切割金属材料时,切割工艺参数对热影响区显微组织及力学状况的影响和相互关系.结果得出,激光切割淬火回火态金属材料时,热影响区由表及里出现三层不同的显微组织,即白亮的熔化层,相变硬化层(它由白色的淬火层和灰色的回火层组成),以及黑色的回火层.对各层形成的原因及其显微硬度,残余应力场的分布进行了分析试验结果说明,对一些特殊性能下使用的金属材料,既须考虑切割参数对切割表面质量的影响,还须考虑它们对热影响区显微组织和力学状态的影响.不同材料应根据情况选用优选工艺参数.     

火力发电厂锅炉用碎渣机凸轮材料磨损性能研究

采用激光和等离子弧淬火表面硬化技术,对火力发电厂锅炉用碎渣机凸轮常用材料合金钢40Cr进行激光表面硬化处理,并将其在销盘式摩擦试验机上进行了摩擦磨损试验.结果表明,激光硬化处理的表面能够有效地改善材料表面硬度和耐磨性.     

激光淬火齿轮组织分析

利用扫描电镜、透射电镜对40CrNiMoA钢激光淬火齿轮淬火区组织进行了细致的分析。结果表明：其组织分为淬硬层、过渡区和基体三层。淬硬层为马氏体组织，过渡区为马氏体与回火索氏体的混合组织，基体为四火索氏体。     

齿轮宽带激光强化技术研究

本文针对齿轮表面宽带激光强化工艺的特点, 提出了采用该工艺所需的关键技术。实验结果表明, 在采用所提出的关键技术条件下, 对齿轮进行宽带激光强化处理, 获得了沿齿廓均匀分布的硬化层     

Wear performance of laser surface hardened GCr15 steel

In order to assess the new tribological properties of laser surface hardened GCr15 steel, the wear resistance between specimens treated with laser and those of conventionally hardened under dry sliding conditions was compared. The change of wear mechanisms in laser hardened GCr15 resulted in a distinct difference in wear rates. The results showed that quenched zones not only had sufficient depth of hardening and higher hardness, but had more retained austenite and finer carbides because of a higher degree of carbide dissolution. Laser surface hardened GCr15 steel specimens exhibited superior wear resistance to their conventionally hardened specimens due to the effects of the microstructure hardening, high hardness and toughness. The wear mechanism for both the laser quenched layer and conventionally hardened layer was highly similar, generally involving adhesive, material transfer, wear-induced oxidation and plowing. When conventionally hardened block specimens rubbed against the laser hardened specimens, the surface of conventionally hardened block specimens was polished. The microstructural thermal stability was increased after laser surface treatment.     

Wear Performance of Laser Surface Hardened GCr15 Steel

In order to assess the new tribological properties of laser surface hardened GCr15 steel, the wear resistance between specimens treated with laser and those of conventionally hardened under dry sliding conditions was compared. The change of wear mechanisms in laser hardened GCr15 resulted in a distinct difference in wear rates. The results showed that quenched zones not only had sufficient depth of hardening and higher hardness, but had more retained austenite and finer carbides because of a higher degree o...     

工艺参数对45钢激光表面强化组织与性能的影响

通过改变激光功率和扫描速度等参数,研究其对45钢激光表面强化组织与性能的影响。实验结果表明,单道扫描时,当保持扫描速度v为15mm/s时,增加激光功率P,可增加硬化层的深度,最大深度可达1.5mm以上。另外,P/v比值越大,硬化层深度越大;而当P/v比值保持不变时,硬化层深度随着激光功率的增加而增加,其中激光功率从1.2kW到1.8kW时,硬化层深度值增加较快;当激光功率大于1.8kW后,深度值的增长随功率增加变缓;而且硬化层的硬度都达到700HV以上,远高于基体的硬度。在激光多道搭接扫描时,激光能量的再次输入会导致靠近搭接区的前一道硬化层产生回火软化,其硬度接近基体的硬度。     

凸轮材料的表面强化及其摩擦学特性

研究了汽车用铁基烧结凸轮材料在3种表面处理状态下(烧结态、激光表面淬火和高频感应淬火)的显微组织、显微硬度及其摩擦学特性。研究结果表明:经2种表面淬火后,材料的表面得到一均匀的硬化层,其组织为细针状的马氏体组织,材料表面的耐磨性和摩擦系数得到了显著的改善。激光淬火凸轮材料的表面摩擦学特性略优于高频淬火凸轮材料。在本试验参数范围内,随着试验载荷的提高,激光淬火铁基烧结凸轮材料的磨损机制发生转变,由轻微氧化磨损和磨粒磨损机制转化为严重氧化磨损、磨粒磨损和剥层磨损机制。     

激光功率参数对GCr15钢组织和抗磨性能的影响

为研究不同激光功率参数对激光硬化后的最终显微组织、硬度和耐磨性的影响,应用宽带扫描技术进行了GCr15轴承钢激光强化处理试验,用光学显微镜和扫描电镜、x射线衍射仪等现代测试手段对GCr15轴承钢试样的显微组织和形貌尺寸特征进行了分析,磨损试验在MM200磨损试验机上进行.结果表明,激光参数变化所产生的显微组织变化造成了表面硬度值和磨损率的较大差异.激光功率大时,激光硬化层表面未溶碳化物量减少,使得表面马氏体中碳的质量分数增加,表面硬度增高.在干摩擦磨损过程中,激光改性层表面发生摩擦诱发马氏体相变.在干摩擦和油润滑两种条件下,激光功率越大,激光硬化层的抗磨损性越好.     

基于微磁检测技术的钢杆淬硬层深度定量预测

为将微磁检测原理应用于钢杆淬硬层深度的定量检测,设计了可同步检测切向磁场强度时变信号、磁滞回线和巴克豪森噪声信号的多功能传感器,从3类微磁信号中提取出共8项特征参数用于淬硬层深度表征.基于逐步回归方法,筛选出显著水平小于0.07的4项微磁特征参数(即矫顽力Hc、切向磁场强度时变信号的3次谐波幅值A3和谐波畸变因子K、巴克豪森噪声信号蝶形曲线的参数H_(cm)),建立了四元线性回归预测模型.该模型对淬硬层深度的预测平均误差仅为3.87%.上述基于多功能传感器的微磁检测方法,可以推广应用于铁磁性杆类构件表面硬化层深度的定量检测.