轻烧MgO膨胀剂对水泥浆体变形行为的影响

通过1000℃煅烧菱镁矿制备出轻烧MgO膨胀剂,研究了轻烧MgO掺量、养护温度、养护方式对水泥浆体变形行为的影响,并分析了粉煤灰的掺入对含MgO水泥浆变形的影响规律.结果表明,所制备的轻烧MgO膨胀剂具有持续稳定的膨胀性能,掺入后浆体的膨胀变形随温度的升高而加大.40℃养护条件下,掺6%MgO的水泥浆体可表现出自膨胀性.粉煤灰的掺入对MgO的膨胀性能有明显的抑制作用.     

基于水膜理论研究粉煤灰和矿粉对水泥浆体工作性的影响

研究了粉煤灰、矿粉和聚羧酸减水剂对胶凝材料填充密度的影响,通过填充密度计算胶凝材料的水膜厚度,最后分析了水膜厚度与水泥浆体的黏聚性和流动度的关系。结果表明：随着粉煤灰掺量从0增大到40%,胶凝材料的填充密度提升5.31%,而矿粉在相同掺量下仅使填充密度提高了0.92%,聚羧酸减水剂掺入后大幅提高了胶凝材料的填充密度;填充密度增大可使自由水量增多,水膜厚度增大,但比表面积增大会导致水膜厚度下降;粉煤灰的掺入使胶凝材料的水膜厚度增大,水泥浆体黏聚性降低,流动度增大;矿粉掺入后使胶凝材料的水膜厚度降低,水泥浆体流动度下降,但聚羧酸减水剂掺入后水泥浆体的黏聚性显著降低,流动度大幅增加;聚羧酸减水剂通过影响水膜厚度进而影响水泥浆体的黏聚性和流动度。     

外掺MgO水泥浆体孔结构特性研究

通过压汞法研究了不同活性MgO对硬化水泥浆体孔结构的影响,探索了养护制度以及粉煤灰对外掺·MgO硬化水泥浆体孔结构的影响规律.结果表明,40℃水养时,低活性值的MgO显著降低了硬化水泥浆体的孔隙率和毛细孔体积,优化了水泥浆体的孔结构;提高养护湿度或温度,促进了外掺MgO水泥浆体孔结构的优化分布;粉煤灰可进一步优化MgO...     

掺MgO膨胀剂水泥浆体不同养护制度下的变形特性

研究了掺MgO膨胀剂水泥浆体在不同养护制度下的变形特性.结果表明,随着养护湿度的降低,MgO膨胀剂对水泥浆体的收缩补偿效果逐渐下降;提高养护温度,Mgo膨胀剂对水泥浆体的收缩补偿增大,膨胀稳定所需时间缩短.     

粉煤灰、矿粉对掺硫铝酸盐膨胀剂水泥基材料膨胀性能的影响

研究了粉煤灰、矿粉对掺硫铝酸盐膨胀剂(CSA)试件在不同养护条件下的膨胀率、自生体积变形率和干燥收缩的影响。结果表明：粉煤灰对CSA的膨胀性能起正效应,粉煤灰的掺入增大了试件在饱水养护下的早期膨胀率,与3%CSA组试件相比,3%CSA15%FA、3%CSA30%FA和3%CSA45%FA组试件的7 d膨胀率分别增大了11.4%、31.3%和68.0%;粉煤灰的掺入显著提高了试件在绝湿养护下的自膨胀,3%CSA15%FA、3%CSA30%FA和3%CSA45%FA组试件的180 d自膨胀变形率分别为226×10^-6、771×10^-6和2 121×10^-6;粉煤灰的掺入有效改善了试件在干燥养护条件下的干燥收缩,与3%CSA组试件相比,3%CSA15%FA、3%CSA30%FA和3%CSA45%FA组试件的180 d干燥收缩从-2 980×10^-6分别降低为-2 513×10^-6、-2 269×10^-6和-1 709×10^-6;矿粉对CSA...     

外掺MgO水泥浆体自收缩的性能研究

研究了在绝湿条件下养护温度、水胶比和粉煤灰对外掺不同活性Mg O水泥浆体自收缩的影响。研究结果表明:在绝湿条件下,Mg O对水泥浆体收缩补偿的量随着养护温度的升高而增加;降低水灰比,Mg O对水泥浆体自收缩的补偿量减小,自身体积稳定的时间滞后;粉煤灰与Mg O复掺提高了水泥浆体自身体积稳定性,减小了收缩。     

粉煤灰和矿粉对钢渣砂混凝土性能的影响

用经过破碎和磁选处理的钢渣废料作细集料替代天然砂,与水泥浆和碎石配制成混凝土。在流动性一致原则下,研究了粉煤灰和矿粉按不同比例替代水泥后对钢渣砂混凝土的力学性能及水热养护制度下膨胀性能的影响规律。结果表明:随着矿粉和粉煤灰掺量的增加,混凝土7d和28d的强度不断减小;在两种掺合料同掺量下,掺矿粉的钢渣砂混凝土的强度略高于掺加粉煤灰的;但掺加粉煤灰能降低钢渣砂混凝土的膨胀率,改善钢渣砂混凝土的体积稳定性。     

不同养护温度下磨细粉煤灰的反应活性分析

分别使用粉磨前后的粉煤灰制备水泥浆体试样,对不同养护温度下试样的抗压强度和粉煤灰反应程度进行分析,并使用XRD物相分析和热重分析研究其作用机理。结果表明：由于在粉磨过程中部分球形颗粒被破坏,磨细粉煤灰在水泥浆体中消耗更多氢氧化钙而产生强度相,其反应程度随养护温度提高而增加最多;使用磨细粉煤灰制备的水泥浆体各龄期抗压强度均高于其他粉煤灰,温度升高时其强度上升幅度最大,当养护温度为80℃时,掺磨细粉煤灰试样在各龄期强度可达到纯水泥浆体的80%以上。     

不同温度下矿物掺合料对硫铝酸盐水泥水化的影响

研究了20℃、35℃、50℃养护条件下硅灰和矿粉对硫铝酸盐水泥水化的影响,分析了抗压强度、孔溶液p H值和水化产物的变化规律。结果表明:随着养护温度的升高,掺矿粉和硅灰的硫铝酸盐水泥抗压强度提高,但50℃养护条件下纯硫铝酸盐水泥浆体在28 d的抗压强度有明显倒缩现象,是由于高温下水化产物分解所致;掺入硅灰可以有效改善硫铝酸盐水泥后期抗压强度倒缩问题,掺入矿粉由于其细度和活性的限制改善能力有限。     

养护方式对纳米氧化镁水泥浆体强度的影响研究

采用纳米氧化镁(Nano-MgO)替代常规MgO类膨胀剂掺入水泥浆体中,以期望能够提高水泥浆体的抗折、抗压强度。采用不同的养护方式、养护温度和水灰比进行试验,试验中借助了X射线衍射(XRD)等微观测试技术研究其机理。试验结果表明:掺入Nano-MgO可以提高水泥浆体的抗折、抗压强度;适当的提高养护温度有助于浆体强度的增长;同等条件下,饱和氢氧化钙溶液养护和蒸汽养护对强度发展更加有益;相同掺量时,水灰比增大,其强度呈现下降趋势;XRD图谱反映出适当的提高养护温度,Nano-MgO水泥浆体水化更充分,试验对象的强度也随之提升。     

掺加混合材的水泥石自收缩特性研究

研究了不同种类的混合材对水泥石自收缩的影响,并试图通过复合粉煤灰或石灰石粉来降低掺加超细矿渣的水泥石自收缩;应用了交流阻抗谱技术来研究自收缩现象,研制结果表明,水泥石自收缩会随超细矿渣细度的增加而增加;掺加硅灰会增大水泥石的自收缩;石灰石和粉煤灰能够有效地降低自收缩;大量掺加石灰石粉或粉煤灰能够降低复合了超细矿渣的水泥石自收缩;水泥石的交流阻抗值与自收缩率之间有良好的对应关系,自收缩率增加,阻抗值增大。     

轻烧氧化镁膨胀剂对水泥浆体干缩性能的影响

研究了轻烧氧化镁膨胀剂和粉煤灰用于水泥浆体的干缩变形;探讨了轻烧氧化镁膨胀剂和粉煤灰复合作用下对水泥浆体的抗干缩能力.结果表明:轻烧氧化镁和粉煤灰单掺时均能减小浆体的干燥收缩,二者复合双掺后对水泥浆体的干燥收缩减小的幅度更大,表现出更好的抗干缩能力.     

The relationship between autogenous shrinkage and pore structure of cement paste with mineral admixtures

In this paper, the combination of fly ash and silica fume, or fly ash and blast furnace slag were used as the composite mineral admixtures in cement paste. The autogenous shrinkage and the pore structure of the hardened cement paste with mineral admixtures were tested, and the relationship of the autogenous shrinkage and pore structure also was discussed. The results indicate that fly ash can reduce the autogenous shrinkage, and silica fume can increase the autogenous shrinkage, and the effect of blast furnace slag is between the two above; although both silica fume and blast furnace slag can weaken the porosity and the mean diameter of cement paste, and increase the volumetric percentage of pores whose diameter is between 5 and 50 nm and pore specific surface, silica fume is better than blast furnace slag in changing the pore structure. The relationship between the autogenous shrinkage and volumetric percentage of pores whose diameter is between 5 and 50 nm is obviously proportional.     

养护制度对混凝土变形性能影响的试验研究

针对混凝土所处环境特点,研究养护制度对混凝土收缩体积变形的影响,结果表明：各种养护制度下,粉煤灰均有利于减少混凝土的干缩,而矿渣却是增大干缩;延长混凝土的早期水养时间,并不会减少混凝土的干燥收缩值,反而会使干缩速率加快;但早期充分水养可避免混凝土过早产生收缩应力,对提高混凝土早期的体积稳定性具有一定的作用和意义。     

含不同矿物掺合料的高强混凝土的自收缩特性

对比研究纯水泥及含不同矿物掺合料(粉煤灰、石灰石粉、磨细矿渣粉)的高强混凝土早期(7 d以内)自收缩发展规律.结果表明:粉煤灰混凝土与石灰石粉混凝土的自收缩表现出相同的规律,均随粉煤灰或石灰石粉掺量的增加而呈准线性递减,且两者自收缩的大小也几乎相同;矿渣粉混凝土的自收缩在较早龄期随矿渣粉掺量增加而降低的幅度较粉煤灰和石...     

若干掺合料对减水剂塑化效果的影响

研究了经活化处理并磨细的煤矸石及粉煤灰以不同比例等量替代部分水泥后,对掺减水剂水泥浆体流动度的影响规律,并将其与常用的矿物掺合料进行比较.结果表明,对于所选用的3种硅酸盐水泥和2种减水剂,用煤矸石等量替代部分水泥均会对减水剂的塑化效果产生负面影响,而与此相反,粉煤灰、矿渣粉和高钙粉煤灰有助于改善减水剂的塑化效果.分析了煤矸石、粉煤灰、矿渣粉和高钙粉煤灰等矿物掺合料对减水剂塑化效果的影响机理.     

蒸养条件下水泥-粉煤灰复合胶凝材料的水化性能研究

通过测定不同龄期净浆的化学结合水量和抗压强度,并结合SEM,研究在蒸养条件下粉煤灰掺量、细度对水泥-粉煤灰复合胶凝材料水化性能的影响。试验结果表明:蒸养条件提高了水泥粉煤灰复合胶凝材料的水化速度,同时也提高了粉煤灰的活性;蒸养条件下,粉煤灰的细度对水泥粉煤灰复合胶凝材料的早期水化没有显著影响,其后期水化速度随粉煤灰细度的增加而增加;粉煤灰掺量的增加,降低了其早期水化速度,掺入适量的粉煤灰其后期水化程度可以超过纯水泥的水化程度;粉煤灰的掺入有利于水泥的水化,且水泥的水化速度随粉煤灰掺量的增加而增加。     

粉煤灰-矿渣复合超细粉蒸养混凝土力学性能

研究了在蒸汽养护和标准养护条件下掺粉煤灰－矿渣复合超细粉蒸养混凝土的力学性能，试验结果表明：粉煤灰－矿渣复合超细粉的掺入改善了蒸养混凝土的力学性能，并使蒸养混凝土具有较大的后期强度增长度，与空白对比组的混凝土相比，粉煤灰－矿渣复合超细粉混凝土的干缩显著降低。     

贝利特硫铝酸钙水泥的收缩性能

以碳酸钙、黏土和铝矾土为主要原料制备贝利特-硫铝酸钙(BCSAF)水泥,测定了BCSAF熟料的矿物组成、标准稠度用水量和凝结时间,研究了BCSAF水泥以及基准水泥净浆、砂浆的自收缩和干燥收缩,分析了粉煤灰对BCSAF水泥净浆收缩性能的影响.利用低场核磁技术,研究了BCSAF水泥和基准水泥净浆在早龄期的内部孔结构.结果 表明:BCSAF水泥净浆的自收缩大于基准水泥净浆,干燥收缩小于基准水泥净浆;粉煤灰可以有效减少BCSAF水泥净浆的自收缩和干燥收缩;BCSAF水泥砂浆60d龄期的干燥收缩小于基准水泥砂浆.     

矿粉、高钙灰及脱硫石膏对水泥收缩性能的影响

研究了50.0%(质量分数,下同)矿粉和高钙粉煤灰等量替代水泥对水泥净浆早期自收缩性能的影响及水泥砂浆的长期干燥收缩性能和初始开裂敏感性.结果表明,在水泥-矿物材料体系中,自收缩与矿物材料的水化活性成正相关性,用50.0%的矿粉和高钙粉煤灰替代水泥后,水泥浆体的自收缩率随着矿物材料活性的降低而降低;硫酸盐激发材料既具有增加水化程度和提高化学收缩的作用,又具有增加AFt量和产生膨胀的作用,因而对水泥浆体的自收缩影响不大;掺50.0%矿粉及1.0%元明粉可显著提高干燥收缩;脱硫石膏和煅烧脱硫石膏按照一定比例复合能显著降低干燥收缩;初始开裂时间、自收缩与矿物材料水化活性的相关性较大,自收缩越高则其开裂敏感性越大,早强措施增加开裂风险;采用矿物材料尤其是采用低活性矿物材料替代水泥可使水泥水化减缓,自收缩和干燥收缩减少,开裂敏感性降低.