<正>1.未熔合或未焊透未熔合缺陷是指熔敷的焊缝未完全填满接头坡口,或在焊道与焊道之间留有空隙,未熔合一般产生于紧接熔合线处,是一种几乎没有厚度的面状缺陷,如图1所示。     

脱氢反应器内件焊缝断裂分析

采用断口扫描电镜、金相和力学计算，分析了304H脱氢反应器内件锥形封头沿焊缝的断裂原因。研究显示，内部锥形封头的环焊缝上的未焊透和未熔合缺陷是产生断裂事故的根本原因。长期在应力集中作用下缺陷尖端处出现局部的蠕变和蠕变裂纹扩展，形成空洞和沿晶断裂的颗粒状断口。操作中有过载现象，包括压力的超载，也可能因超温导致材料强度下降而使原始缺陷发生裂纹逐渐扩展（其中包括裂纹的蠕变扩展），也促进了裂纹的扩展。     

X80钢输气管道带缺陷环焊缝的力学性能及两类裂纹形成原因

对10处存在缺陷的X80钢输气管道环焊缝进行了力学性能检测和两类裂纹成因分析.结果表明:10处环焊缝抗拉强度不合格率为10％,焊缝中心冲击功不合格率为21.7％,热影响区冲击功全部合格;环焊缝、母材和热影响区的维氏硬度全部合格,但热影响区存在软化.环焊缝中的缺陷以未熔合和裂纹为主,二者占比为75％.裂纹主要为冷裂纹和结...     

球罐焊缝坡口清根过程中的渗透检测及典型缺陷分析

正1.概述大型球罐压力容器的切片球壳板都采用现场焊接成整体的安装工艺。由于球壳板厚度通常都在30mm以上,为避免焊后根部存在裂纹、未熔合、未焊透及夹渣等缺陷而造成质量隐患,所以在焊接过程中必须对焊缝的坡口清根,并进行渗透检测。结果表明,清根坡口渗透检测可以有效检测出根部的表面开口和近表面缺陷。本文主要以某项目现场组     

汽车下摆臂断裂失效分析

采用OM、SEM、 光谱仪等设备对下摆臂焊合件的焊接接头及母材显微组织、 断口显微形貌和材料的化学成分进行了分析,发现焊缝中存在根部裂纹及焊缝边缘存在未熔合缺陷.由于焊接工艺不当,导致下摆臂在焊接接头中形成冷裂纹,在服役应力的作用下,疲劳裂纹扩展,最终导致下摆臂断裂失效.结果表明:通过焊接工艺的改进,增加焊后去应力退火...     

末级过热器U型管与不锈钢吊挂板连接角焊缝的泄漏原因

某电厂末级过热器12Cr1MoVG铁素体钢U型管与1Cr20Ni14Si2奥氏体钢吊挂板连接角焊缝在长时间运行条件下发生泄漏。通过宏观观察、成分分析、显微组织观察和硬度测试等方法对该角焊缝泄漏原因进行了分析。结果表明:U型管与吊挂板连接角焊缝边缘存在未焊全缺陷,焊缝内存在夹渣缺陷,在这些缺陷位置处应力集中现象明显;同时U型管侧熔合线位置存在碳迁移现象,导致硬度增大、塑性下降,在应力集中作用下,熔合线位置萌生裂纹并不断扩展,最终造成角焊缝的开裂失效。     

高强钢厚板激光-GMAW复合双面同步横焊特性研究

针对30 mm厚船用高强钢10Ni5Cr Mo V对接接头横焊应用需求,开展激光-熔化极气体保护电弧(Gas metal arc welding,GMAW)复合双面同步横焊特性研究。研究结果表明,针对横焊位姿因重力、非对称坡口对熔滴、电弧的影响,利用激光对电弧的吸引和收缩作用,通过减小光-丝间距,有效地抑制了电弧侧壁燃弧,熔滴在电磁力和等离子流力的作用下,稳定过渡到熔池中,实现了熔滴过渡稳定性控制,解决了激光-GMAW复合横焊位姿电弧偏离和熔滴下落等过程控制难题与侧壁未熔合问题;厚板激光-GMAW复合双面同步横焊包括打底层和填充层焊接,其中打底层焊接是保证接头焊接质量的关键;采用激光-GMAW复合双面同步横焊新方法,4道焊接完成了30 mm厚船用高强钢10Ni5Cr Mo V横焊位姿的高强、高效连接。焊缝表面成形良好,无裂纹、未焊透和侧壁未熔合等缺陷。接头的抗拉强度高于母材,且其–50℃冲击吸收能量为57.3 J。     

摇动电弧窄间隙立向上MAG焊接技术

针对厚壁大型容器或储罐的立向上窄间隙焊接,提出了一种摇动电弧窄间隙立向上MAG焊接技术,以空心轴步进电动机直接带动折弯导电杆摇动,带动从导电嘴中送出的带有电弧的焊丝在坡口内作圆弧形摇动,并在坡口侧壁作一定时间停留,以达到改善坡口两侧壁熔深的目的,同时保证焊缝在立向上状态下自由成形。焊接试验结果表明:该技术能在立向上焊接时获得良好的焊缝成形,也能形成一定的侧壁熔深;多层焊试验时,焊缝成形良好,达到了减少熔敷金属量,提高焊接效率的目的。     

钢结构焊前准备及焊缝主要缺陷解析

通过直观的现场图片,对钢结构焊前拼装组对中发现的钢柱对接缺陷、梁柱对接缺陷、坡口缺陷及定位点焊缺陷等,以及对焊缝超声波探伤后刨削出来的裂纹、气孔、未焊透及未熔合等主要缺陷进行解析,归纳出针对性的防止措施,以期为钢结构焊接检验提供参考、为提高钢结构制作安装水平提供借鉴。     

手工直流钨极氩弧封底焊

氩弧焊已获得广泛采用,直流钨极氩弧封底焊常为工程机械制造和维修部门采用。手工直流钨极氩弧封底焊最容易出现的缺陷是:焊缝根部的内凹、透瘤、未熔合及未焊透;引弧方法不当导致的焊缝夹钨;送丝方法不当导致的焊缝根部有未熔     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

盘丝极心偏对三爪自定心卡盘找标精度影响的分析

三爪自定心卡盘作为机床的主要附件,已有一百多年的发展历史,尽管目前随着数控技术的不断发展,越来越多地需求高速动力卡盘,但三爪自定心卡盘目前仍有一定的市场。 要保证卡盘可靠地夹紧工件,必须使其有可靠的夹持精度;要保持卡盘的精度,必须要严格控制各零部件公差及误差,如盘丝的极心偏。 　　极心偏是形成圆的渐开线的基圆圆心 (极心 )与盘丝内孔中心不同心所造成的偏差值。它对卡盘精度的影响分两种情况,一是卡爪夹持弧采用配磨,二是卡爪夹持弧采用单磨。本文主要探讨配磨时的影响。 　　卡爪夹持弧采用配磨,即每台卡盘整体…     

圆柱面素线的直线度公差带解析

详细分析了圆柱面素线的直线度公差带在新旧标准中定义和解释的区别，并从对圆柱面素线实际要素检测的角度，提出了推行新标准的实际意义。     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。     

广州地铁APM列车制动机理分析

根据广州市珠江新城旅客自动运输系统(APM)列车的运行特点,介绍APM列车制动系统的制动方式及其特点,分析APM列车动态制动和摩擦制动的工作机理及其区别和联系,阐明APM列车制动系统的电控制过程和气控制过程,从而为APM列车制动系统的维护和管理提供一定的依据.     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

活塞销孔加工工艺的改进

我公司于８０年代末引进Aspera公司年产８０万台冰箱（冷柜）压缩机生产线及软件技术，在压缩机加工中，活塞销孔（如图１所示）的加工是难点之一。用镗床加工，质量一直难以达到要求，废品率很高。后来我们将Aspera公司的加工工艺即精镗后滚光改为精镗后用金刚石铰刀粗、精铰孔，由此解决了这个技术难题。（１）原意大利Aspera公司工艺简述其工艺流程为：钻６．５通孔→扩孔至７＋０．１→粗镗７．４７３＋０．０３６、圆柱度０．０１→精镗至７．９３５＋０．００６、圆柱度０．００２→滚光７．９３８＋０．００６、圆柱度０…     

串联混合动力牵引车蓄电池SOC的监测

文中提出了基于安时法计算混合动力电动牵引车蓄电池已用电量，在求出当前蓄电池荷电状态的基础上，利用根据能量守恒模型计算出的蓄电池SOC进行荷电状态校正，采用80C196KC加上相应的感应器来实现。实验表明，该方法测出的蓄电池荷电状态比较准确，有较高的精度。