非晶态合金Fe_(71)Ni_(10)B_(13)Si_4C_2磁各向异性的Mssbauer谱研究

本文研究了Fe_(71)Ni_(10)B_(13)Si_4C_2非晶态合金在磁场退火时的反常磁各向异性变化。结果表明,在430℃磁场热处理时优先发生了表面晶化现象,导致垂直磁各向异性的反常增大。磁矩取向的择优性取决于压应力引起的和磁场热处理感生的两种磁各向异性。     

MSSBAUER STUDY ON MAGNETIC ANISOTROPY OF AMORPHOUS ALLOY Fe_(71)Ni_(10)B_(13)Si_4C_2

本文研究了Fe_(71)Ni_(10)B_(13)Si_4C_2非晶态合金在磁场退火时的反常磁各向异性变化。结果表明,在430℃磁场热处理时优先发生了表面晶化现象,导致垂直磁各向异性的反常增大。磁矩取向的择优性取决于压应力引起的和磁场热处理感生的两种磁各向异性。     

低频脉冲电流退火对CoFeSiB非晶薄带巨磁阻抗效应的影响

研究了经不同低频脉冲电流密度退火的Co66.3Fe3．7Si12B18非晶薄带的巨磁阻抗（GMI）效应。结果表明，在低频脉冲电流下，巨磁阻抗效应的大小与退火电流密度密切相关。非晶带的GMI变化率△Z／Z先随退火电流密度的增加而增强，当电流密度为104A／mm^2时，△Z／Z达到最大值53．8％，此后随电流密度增大，GMI变化率开始减小。对脉冲电流退火影响巨磁阻抗效应的机制作了定性分析。并分析了由脉冲电流退火在材料内感生的横向各向异性场凤对GMI效应的影响，发现HK有利于提高GMI效应的峰值，但同时存在一个临界值，当超过这个值时，GMI效应的峰值减弱。     

非晶合金Fe_(80-x)Cu_xSi_5B_(15)和(Fe_(1-y)Co_y)_(82)Cu_(0.4)Si_(4.4)B_(13.2)的晶化行为

用X射线衍射、吸收和内转换电子发射Mossbauer谱技术,研究了Fe_(80-x)Cu_xSi_5B_(15)和(Fe_(1-y)Co_y)_(82)Cu_(0.4)Si_(4.4)B_(13.2)两系列非晶合金的晶化行为.单辊急冷法制备的非晶带,晶化首先从贴辊面开始,晶化产物为α-Fe相.在Fe_(80)Si_5B_(15)非晶合金中以少量Cu替代Fe可以提高晶化温度.我们的结果表明,过渡金属的含量超过80at.-%,如增加到82at.-%,晶化温度就明显降低.所研究两系列含Si的铁基非晶合金在400—450℃范围内退火2h,都出现α-Fe,Fe_3B和Fe_2B三种晶态相共存状态.退火温度再升高,亚稳相Fe_3B逐渐转变为Fe_2B和α-Fe.     

非晶态Fe_(46)Ni_(32)V_2Si_(14)B_6合金的分形断裂

测定了结构弛豫阶段退火温度ＴＲ对非晶态Ｆｅ４６Ｎｉ３２Ｖ２Ｓｉ１４　Ｂ６合金条带室温断裂韧性（Ｋｃ）的影响．ＴＲ小于２００℃时,ＫＣ大致不变,平均值约８ＭＰａｍ１／２;随着ＴＲ由２００℃增加至３５０℃,ＫＣ值逐渐下降至２ＭＰａｍ１／２;相应地断裂剖面形貌由不规则特征（分形的）逐渐变为平直的或光滑的特征．用垂直截面法测定断裂剖面裂纹轮廓线的分形维数Ｄｆ．实验结果表明,在准二维脆性断裂条件下,Ｋｃ值与分形维数增量的平方根成正比,并讨论不同结构弛豫阶段断裂特征长度ａｃ与断裂机制     

非晶态Fe_(1-x)(Si,B)_x合金的内禀磁性和磁各向异性

非晶态Fe_(1-x)(Si,B)_x合金的磁矩和磁致伸缩随着Si和B含量的增多而缓慢降低,而Curie温度约在25%(Si+B)含量时呈现出最大值;Si与B的含量对磁各向异性并无明显影响,但表面条纹退磁效应对磁各向异性却有较大的影响。这些实验现象可以借助电子转移和非晶态合金的结构模型得到定性的解释。     

Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9非晶合金的晶化动力学

用差热分析(DTA)结合X射线衍射(XRD),研究了Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9非晶合金的晶化动力学。结果表明:温度在0～700℃范围内,该合金的晶化相为α-Fe和Fe_2B;α-Fe相晶化表观激活能为452.39kJ/mol,Fe_2B相的晶化表观激活能395.23kJ/mol;两相在晶化初期激活能最小,随晶化量X_c的增加而迅速增大,在α-Fe的体积分数为30％～80％,Fe_2B的体积分数为40％～80％时,呈现极大值。     

铜模吸铸法制备的Fe_(74)Al_4Sn_2P_(10)Si_4B_4C_2块体非晶合金圆棒及圆管

利用铜模吸铸法制备了直径1.0mm,1.5mm和2.0mm的Fe74Al4Sn2P10Si4B4C2块体非晶合金圆棒,利用振动样品磁强计测试了圆棒的磁性能,其饱和磁感应强度较高,矫顽力较低。利用铜模吸铸法制备了Φ5mm×Φ7mm×15mm的Fe74Al4Sn2P10Si4B4C2块体非晶合金圆管,并测试了其DSC曲线,块体非晶合金圆管与块体非晶合金圆棒的热性质一致。Fe74Al4Sn2P10Si4B4C2块体非晶合金显示出优良的铸造性能。     

高导磁Fe_(73.5)Cu_1Nb_2V_1Si_(13.5)B_9合金的中、高频损耗行为

在 f=0 .3～ 10 3kHz和Bm =0 .0 5～ 1.0T的范围内 ,考查了具有高起始磁导率的纳米晶合金的每周损耗频率关系。结果表明 ,在 f =0 .3～ 30kHz和Bm ≤ 0 .8T的范围内 ,惯用的损耗分离原则是适用的 ,可用Bertotti的统计理论描述P/f—f行为 ;对于Bm =1T ,这种描述在直到150kHz的范围内都适用。大约在 30kHz的高频区和 Bm ≤ 0 .8T的范围内 ,不能采用惯用的损耗分离法 ,P/f—f行为可用线性方程P/f =Peh Keclf来描述。这种描述对于Bm =1T的行为也很好地适用     

MOSSBAUER STUDY ON MAGNETIC ANISOTROPY OF AMORPHOUS ALLOY Fe_(71)Ni_(10)B_(13)Si_4C_2

Magnetic anisotropies of the amorphous alloy Fe_(71)Ni_(10)B_(13)Si_(14)C_2 annealed in magnetic fieldhave been studied using Mossbauer spectroscopy and X-ray diffraction.It is shown that thedistribution of moments in the annealed sample are determined by both stress-produced andthermomagnetic treatment-induced magnetic anisotropies.     

CRYSTALLIZATION AND MAGNETIC PROPERTIES OF AMORPHOUS Nd_6Fe_(81)B_(13)ALLOY

The magnetic properties and the crystallization and its influence on the magnetic and struc-tural properties for rapidly quenched amorphous Nd_6Fe_(81)B-(13) alloy have been studied.The lowtemperature magnetic properties,the Curie temperature and the crystallization behavior arediscussed.A small addition(6at.-%)of Nd in amorphous Fe-B alloys increases largely thecrystallization temperature T_x but causes a decrease of the Curie temperature Tc·A newphase was observed in the sample annealed at 873 K.     

EFFECT OF PREPARATION CONDITION ON THERMAL EXPANSION ANISOTROPY FOR AMORPHOUS Fe_(78)B_(13)Si_9 ALLOY

The thermal expansion along the longitudinal and transverse directions for amorphousFe_(78)B_(13)Si_9 alloy prepared under various preparing conditions were investigated.The thermalexpansion anisotropy appears in all specimens.The expansion along the longitudinal directionis less than that along the transverse direction.The cooling rate,the melt temperature beforejet casting and the cycling temperature affect the thermal expansion coefficients andanisotropy.The amisotropy of thermal expansion originates from the orientation of atomicinteraction force,the atomic oscillatory frequency and short range order structure or thedirectional arrangement of defects in the alloy.     

制备条件对非晶态Fe78B13Si9合金的热膨胀各向异性的影响

本文研究了不同条件下形成的非易态Fe_(78)B_(13)Si_9合金在长轴和短轴方向上的热膨胀。结果表明,在所有条件下均存在热膨胀的各向异性。热膨胀系数随着冷却速度的增加而增加,但其各向异性减小;随着熔体喷铸温度的提高两者均减小。在热循环的作用下,短轴方向的热膨胀系数及其各向异性均减小;而在长轴方向的热膨胀系数却增大。我们认为热膨胀各向异性来源于原子交互作用力的方向性、原子振动频率和短程有序结构或缺陷的方向性。     

非晶Nd6Fe81B13合金的晶化和磁性

本文研究了非晶Nd_6Fe_(81)B_(13)合金的磁性和晶化及其对样品结构和磁性的影响。讨论了非晶样品的低温磁性和Nd对昌化温度和Curie温度的影响。在873K退火的样品中得到一个新相。     

快淬非晶合金制备态磁各向异性研究SCIEI

本文详细研究了铁基、铁镍基和钴基非晶合金条带制备态的平面磁各问异性。测定了退火前后试样中各向异性的变化及各向异性常数K_(us)随温度的变化,得出K_(us)(T)∝M_s^2(T)关系,由此得出平面磁各向异性由应力各向异性和表面形状各向异性两部分组成。     

Al原子在非晶合金Fe78Si9B13中的扩散

利用二次离子质谱(SIMS)并结合离子剥落研究了Al原子在非晶Fe_(78)Si_9B_(13)合金中的扩散。实验结果表明:在320-380℃温区内,扩散系数D位于2.43×10~(-22)-2.01×10~(-21)m~2s~(-1)之间,且它随温度的变化符合Arrhenius关系,D=D_0 exp(-Q/kT),其中指数前因子D_0=2.02×10~(-12)m~2s~(-1)。扩散激活能Q=1.17eV。     

Fe_（73．5）Cu_（1．0）Mo_（3．0）Si_（13．5）B_（9．0

用Ｘ射线衍射及磁测量等方法研究了不同退火温度下Ｆｅ_（７３．５）Ｃｕ_（１．０）Ｍｏ_（３．０）Ｓｉ_（１３．５）Ｂ_（９．０）纳米软磁合金的结构与磁性．发现合金的显微组织结构与退火温度有关，退火温度为５００─５２０℃时，合金具有最佳软磁性能，合金中如出现Ｆｅ－Ｂ化合物，软磁性能恶化．     

Fe73.5Cu1.0Mo3.0Si13.5B9.0纳米软磁合金的结构与磁性

用X射线衍射及滋测量等方法研究了不同退火温度下Fe73.5Cu1.0Mo3.0Si13.5B9.0纳米软磁合金的结构与磁性,发现合金的显微组织结构与退火温度有关，退火温度为500-520℃时，合金具有最佳软磁性能，合金中如出现Fe-B化合物，软磁性能恶化.