A SiO₂─Al₂O₃─CaO─CaF₂ ionomer glass was investigated using thermal analysis, X-ray diffraction, and scanning electron microscopy. The purpose of this investigation was to control the susceptibility of the glass to acid attack. The differential thermal analysis trace exhibited a sharp glass transition at about 645°C and two exotherms. The first exotherm corresponded to liquid–liquid phase separation followed by crystallization of fluorite. The second, much larger, exotherm was the result of crystallization of the remaining glass phase to form anorthite. Prolonged heat treatment below the glass-transition temperature demonstrated that crystallization of fluorite can occur without prior liquid–liquid phase separation.     

Subsolidus Relations in the La2O3─CuO─CaO Phase Diagram and the La2O3─CuO Binary Join

The phase diagram for the CuO-rich part of the La₂O₃─CuO join was redetermined. La₂Cu₂O₅ was found to have a lower limit of stability at 1002°± 5°C and an incongruent melting temperature of ∼1035°C. LagCu₇O₁₉ had both a lower (1012°± 5°C) and an upper (1027°± 5°C) limit of stability. Subsolidus phase relations were studied in the La₂O₃─CuO─CaO system at 1000°, 1020°, and 1050°C in air. Two ternary phases, La_1.9Ca_1.1Cu₂O_5.9 and LaCa₂Cu₃O_8.6, were stable at these temperatures, with three binary phases, Ca₂CuO₃, CaCu₂O₃, and La₂CuO₄. La₂Cu₂O₅ and La₈Cu₇O₁₉ were stable only at 1020°C, and did not support solid-solution formation.     

Thermodynamics of Nitrogen in B2O3, B2O3─SiO2, and B2O3─CaO Systems

The BN solubilities for B₂O₃, B₂O₃─SiO₂, and B₂O₃─CaO systems have been measured mainly at 1823 K using a graphite crucible. The capability of the systems for nitrogen dissolution is compared with that of silicate systems in terms of nitride capacity. The dependence of nitrogen solubility in molten CaO containing 15 mol% of B₂O₃ on oxygen and nitrogen partial pressures is also investigated. It has been found that there are two mechanisms for nitrogen dissolution, namely as chemically bonded nitrogen and as physically dissolved nitrogen gas.     

Effect of Carbon Reduction on the Properties of 13 mol% Tio2─3 mol% Y2O3─84 mol% ZrO2

Fully tetragonal and sintered 13 mol% TiO₂─3 mol% Y₂O₃─84 mol% ZrO₂ was thermally treated at 1300°C for 1 h in argon in the presence of carbon. No phase changes occurred on the as-received surface and in the bulk of the material, but t → m transformation occurred on polished surfaces under reducing conditions, and it resulted in increased fracture toughness, Young's modulus, and modulus of rigidity. Deoxidation of the system occurred and 0.174 wt% of carbon was found in the sample. This seemed to stabilize the tetragonal phase.     

Subsolidus Phase Relationships in Part of the System Si,Al,Y/N,O: The System Si3N4─AIN─YN─Al2O3─Y2O3

The subsolidus phase relationships in the system Si,Al,Y/N,O were determined. Thirty-nine compatibility tetrahedra were established in the region Si₃N₄─AIN─Al₂O₃─Y₂O₃. The subsolidus phase relationships in the region Si₃N₄─AIN─YN─Y₂O₃ have also been studied. Only one compound, 2YN:Si₃N₄, was confirmed in the binary system Si₃N₄─YN. The solubility limits of the α'─SiAION on the Si₃N₄─YN:3AIN join were determined to range from m = 1.3 to m = 2.4 in the formula Y _{m /3}Si_{12- m} Al _m N₁₆. No quinary compound was found. Seven compatibility tetrahedra were established in the region Si₃N₄─AIN─YN─Y₂O₃.     

Viscosity of Molten Na2O─B2O3 Slags

The viscosity of sodium borate slags at high Na₂O concentrations (37.3 to 49.4 mol%) and high temperatures (1000° to 1300°C) follows an Arrhenius-type relationship. This relationship was also observed for sodium borate slags (mass% Na₂O/mass% B₂O₃= 0.86) containing CaO and CaF₂ for the same temperature range. There has been a reduction in viscosity of the sodium borate slags (mass% Na₂O₃mass% B₂O = 0.53 to 0.86) with increase in Na₂O concentration. On adding CaO (10 to 50 mass%) to the sodium borate slag (mass% Na₂O/mass% B₂O₃= 0.86), the viscosity increased considerably, while an addition of CaF₂ (S to 15 mass%) to the slag (30.9 mass% Na₂O₃ 35.8 mass% B₂O₃, 33.3 mass% CaO) decreased the viscosity. The average activation energies of Na₂O─B₂O₃, Na₂O─B₂O₃─CaO₃ and Na₂O─B₂O₃─CaO─CaF₂ slag systems have been estimated as 14.6, 124.7, and 41.4 kJ/mol, respectively, for the given composition ranges and 1000° to 1300°C temperature range.     

Ionic Conductivity of the Fluorite-Type Hafnia–R2O3 Solid Solutions

The ionic conductivity of the hafnia-scandia, hafnia-yttria, and hafnia-rare earth solid solutions with high dopant concentrations of 8, 10, and 14 mol% was measured in air at 600° to 1050°C. Impedance spectroscopy was used to obtain lattice conductivity. A majority of the investigated samples exhibited linear Arrhenius plots of the lattice conductivity as a function of temperature. For all investigated dopant concentrations the ionic conductivity was shown to decrease as the dopant radius increased. The activation enthalpy for conduction was found to increase with dopant ionic radius. The fact that the highest ionic conductivity among 14-mol%-doped systems was obtained with HfO₂─Sc₂O₃ suggested that the radius ratio approach should be used to predict the electrical conductivity behavior of HfO₂─R₂O₃ systems. A qualitative model based on the Kilner's lattice parameter map does not seem to apply to these systems. For the three systems HfO₂─Yb₂O₃, HfO₂─Y₂O₃, and Hf₂O₃─Sm₂O₃ a conductivity maximum was observed near the dopant concentration of 10 mol%. Deep vacancy trapping is responsible for the decrease in the ionic conductivity at high dopant concentrations. Formation of microdomains of an ordered compound cannot explain the obtained results. A comparison between the ionic conductivities of doped HfO₂ and ZrO₂ systems indicated that the ionic conductivities of HfO₂ systems are 1.5 to 2.2 times lower than the ionic conductivities of ZrO₂ systems.     

Li2O─SiO2─Al2O3─MeIIO Glass-Ceramic Systems for Tile Glaze Applications

In order to verify the possibility of using glass-ceramic materials as tile coatings, the devitrification processes of three industrial formulations belonging to the Li₂O─Al₂O₃─SiO₂ glass-ceramic system were investigated by differential thermal analysis, X-ray diffractometry, scanning electron microscopy, and IR spectroscopy. Compositional variations were made by addition of large amounts of MgO or CaO or PbO (ZnO) oxides as well as through smaller additions of other oxides. In these systems the surface crystallization contributes appreciably to the bulk crystallization mechanism. All the systems investigated show a high tendency toward crystallization even at very high heating rates, developing a very close network of interlocked crystals of synthetic β-spodumene-silica solid solutions (LiAlSi₄O₁₀). The results of this research are expected to establish the conditions under which these glass-ceramic systems can be practically used as tile glazes.     

Effect of Aqueous Processing Conditions on the Microstructure and Transformation Behavior in Al2O3─ZrO2(CeO2) Composites

Aqueous processing of Al₂O₃─ZrO₂ (123 mol% CeO₂) composites, combined with sintering conditions, was used to control the microstructure and its influence on the martensitic transformation temperature of t -ZrO₂ and the transformation-toughening contribution at room temperature. The resultant ZrO₂ grain sizes in the dense composites were related to the transformation-toughening behavior of t -ZrO₂. The data show that (1) the best processing conditions exist when the electrophoretic mobilities of the two solids are positive, adequately high to ensure colloidal stability, efficient packing,and uniform ZrO₂ distribution but differ greatly in magnitude, (2) the colloidal stability of ZrO₂ controls the overall stability and the rheological and processing behavior of this mixture, (3) the grain size distribution in dense pieces sintered for 1 h at 1500°C is comparable to the particle size distribution of the powders, (4) the martensite start temperature for the tetragonal to-monoclinic transformation in Al₂O₃ containing 20 and 40 vol% ZrO₂ increases and can approach 0°C with increasing average ZrO₂ grain size, and as a result, (5) the fracture toughness values at room temperature are raised from 4–5 MPa.m^1/2 to 9–12 MPa.m^1/2 for these two compositions.     

The System MgO─P2O5─H2O at 25°C

The phase diagram for the ternary system MgO─P₂O₅─H₂O at 25°C has been constructed. The magnesium phosphates represented are Mg(H₂PO₄)₂· n H₂O ( n = 4, 2, 0), MgHPO₄·3H₂O, and Mg₃(PO₄)₂· m H₂O ( m = 8, 22). Because of the large differences in the solubilities of these compounds, the technique which involves plotting the mole fractions of MgO and P₂O₅ as their 10th roots has been employed. With the exception of MgHPO₄·3H₂O, the magnesium phosphates are incongruently soluble. Because incongruency is associated with a peritectic-like reaction, the phase Mg₂(PO₄)₃· 8H₂O persists metastably for an extended period.     

Grain-Size Distribution in Al2O3─ZrO2 Generated by High-Temperature Annealing

Grain-size distribution in various Al₂O₃─ZrO₂ (2.5 mol% Y₂O₃) ceramics during high-temperature annealing was examined. In alumina-rich alloys, the grain size of major and minor phases was very different, while grain size was almost uniform in zirconia-rich alloys. This difference in grainsize distribution was related to the difference in grain growth rate of the major phase and to the effectiveness of grain-boundary pinning by minor-phase grains.     

Sintering and Crystallization of CaO–Al2O3–ZrO2–SiO2 Glasses Containing Different Amount of Al2O3

In this work several complementary techniques have been employed to carefully characterize the sintering and crystallization behavior of CaO–Al₂O₃–ZrO₂–SiO₂ glass powder compacts after different heat treatments. The research started from a new base glass 33.69 CaO–1.00 Al₂O₃–7.68 ZrO₂–55.43SiO₂ (mol%) to which 5 and 10 mol% Al₂O₃ were added. The glasses with higher amounts of alumina sintered at higher temperatures (953°C [lower amount] vs. 987°C [higher amount]). A combination of the linear shrinkage and viscosity data allowed to easily find the viscosity values corresponding to the beginning and the end of the sintering process. Anorthite and wollastonite crystals formed in the sintered samples, especially at lower temperatures. At higher temperatures, a new crystalline phase containing ZrO₂ (2CaO·4SiO₂·ZrO₂) appeared in all studied specimens.     

Revised Phase Diagram for the System Al2O3—SiO2

On the basis of 190 runs made up to 1860°C in sealed noble-metal containers the following revisions have been made in the equilibrium diagram for the system A1₂O₃–SiO₂. Mullite melts congruently at 1850°C. The extent of equilibrium solid solution in mullite at solidus temperature is from approximately 60 mole % Al₂O₃ (3/2 ratio) to 63 mole % A1₂O₃. Metastable solid solutions can be prepared up to about 67 mole % Al₂O₃. There is no evidence for stable solubility of excess SiO₂ beyond the 3/2 composition at pressures below 3 kbars. Refractive indices are presented for glasses containing up to 60 mole % Al₂O₃ and from them the composition of the eutectic is confirmed at 5 mole % SiO₂. The variation in lattice constants of the mullite solid solution is not an unequivocal guide to composition since mullites at one composition produced at different temperatures show differences in spacing, no doubt reflecting Al-Si ordering phenomena. The possibility of quartz and corundum being the stable assemblage at some low temperatures and pressures cannot be ruled out. A new anhydrous phase in the system is described, which was previously thought to be synthetic andalusite; it is probably a new polymorph of the Al₂SiO₅ composition with ortho-rhombic unit-cell dimensions a =7.55 A, b =8.27 A, and c = 5.66 A.     

The Al2O3-Nd2O3 Phase Diagram

A tentative phase diagram for the system Al₂0₃-Nd₂O₃ is presented. Three compounds were obtained: a β -A1₂O₃-type compound, the perovskite NdAlO₃, and Nd₄Al₂O₉. The perovskite melts congruently (mp 2090°C), and the two other compounds exhibit incongruent melting behavior: β -Nd/Al₂O₃, mp 1900°C; Nd₄Al₂O₉, mp 1905°C. Two eutectics exist with the following compositions and melting points: 80 mol% Al₂O₃, 1750°C; 23 mol% Al₂O₃,1800°C. Nd₄Al₂O9 decomposes in the solid state at 1780°C.     

Change in Chemical Composition of Mullite Formed from 2SiO2°3Al2O3 Xerogel During the Formation Process

The chemical composition of mullite which was termed from 2SiO₂3Al₂O₃ xerogel by firing was examined by analytical TEM. Mullite formed at 950°C firing showed around 66 mol% Al₂O₃, which was fairly Al₂O₃ rich compared with the bulk composition. The chemical composition of mullite gradually approached the bulk composition as the firing temperature increased to 1400°C and slightly departed again above that firing temperature.     

Cassiterite Solubility in High-Silica K2O-Al2O3-SiO2 Liquids

The saturation surface of cassiterite, SnO₂, was determined for liquids in the system K₂O–Al₂O₃–SiO₂ as a function of bulk composition and temperature. At fixed K₂O/Al₂O₃ cassiterite solubility varies weakly with SiO₂ concentration (76 to 84 mol%), temperature (1350° to 1550°C), and log ( f _O2) (−0.7 to −5.3). Cassiterite solubility is also approximately independent of composition in liquids with molar ratios of K₂O/Al₂O₃ lessthan equal to 1 (peraluminous liquids). As K₂O/Al₂O₃ increases from 1 (peralkaline liquids), however, cassiterite solubility increases steeply and approximately linearly with K₂O in excess of Al₂O₃. It is proposed that potassium in excess of aluminum combines with Sn⁴⁺ to form quasi-molecular complexes with an effective stoichiometry of K₄SnO₄.     

Subsolidus Phase Equilibria of the MgO─V2O5─SiO2 System

The subsolidus phase equilibria of the MgO─V₂O₅─SiO₂ system was studied by solid-state reaction and powder X-ray diffractometry. The resulting ternary is discussed with respect to corrosion of magnesia- and silica-containing refractories by vanadium-containing fuels.     

The System Al2O3-Cr2O3-Sio2

Liquidus phase equilibrium data are presented for the system Al₂O₃-Cr₂O₃-SiO₂. The liquidus diagram is dominated by a large, high-temperature, two-liquid region overlying the primary phase field of corundum solid solution. Other important features are a narrow field for mullite solid solution, a very small cristobalite field, and a ternary eutectic at 1580°C. The eutectic liquid (6Al₂O₃-ICr₂O₃-93SiO₂) coexists with a mullite solid solution (61Al₂O₃-10Cr₂O₃-29SiO₂), a corundum solid solution (19Al₂O₃-81Cr₂O₃), and cristobalite (SO₂). Diagrams are presented to show courses of fractional crystallization, courses of equilibrium crystallization, and phase relations on isothermal planes at 1800°, 1700°, and 1575°C. Tie lines were sketched to indicate the composition of coexisting mullite and corundum solid solution phases.     

Densities of SiO2-Al2O3 Melts

The densities of binary aluminosilicate melts were measured X-radiographically as a function of Al₂O₃, concentration between 1800° and 2000°C. Within this temperature range, the density curves vary linearly and are parallel from fused SiO₂ to ≊30 to 45 mol% Al₂O₃, depending on the temperature. At higher Al₂O₃ contents, negative deviation from linearity increases with increasing temperature. Recent supplementary research efforts on various aspects of the system SiO₂-Al₂O₃ indicate that the changing coordination and structural role of the aluminum ion may be a primary factor in determining the shapes of the density curves.     

Mullite Crystallization from SiO2-Al2O3 Melts

SiO₂-Al₂O₃ melts containing 42 and 60 wt% A1₂O₃ were homogenized at 2090°C (∼10°) and crystallized by various heat treatment schedules in sealed molybdenum crucibles. Mullite containing ∼78 wt% A1₂O₃ precipitated from the 60 wt% A1₂O₃ melts at ∼1325°± 20°C, which is the boundary of a previously calculated liquid miscibility gap. When the homogenized melts were heat-treated within this gap, the A1₂O₃ in the mullite decreased with a corresponding increase in the Al₂O₃ content of the glass. A similar decrease of Al₂O₃ in mullite was observed when crystallized melts were reheated at 1725°± 10°C; the lowest A1₂O₃ content (∼73.5 wt%) was in melts that were reheated for 110 h. All melts indicated that the composition of the precipitating mullite was sensitive to the heat treatment of the melts.