马钢10#高炉高Al2O3炉渣冶炼实践

针对10#高炉炉渣中Al2O3高的特性,通过对炉渣性能的分析,调整操作制度,改善炉渣性能,加强炉前管理等,使10#高炉生产水平明显提高.     

Al2O3含量对Cu-ZnO-Al2O3-SiO2催化剂性能的影响

研究了Al2O3含量对Cu-ZnO-Al2O3-SiO2催化剂在CO2加氢合成二甲醚中催化性能的影响,并用XRD,H2-TPR,XPS,NH3-TPD和CO2-TPD等手段进行了表征.研究结果表明,Al2O3延缓了CuO和ZnO晶粒的长大,同时使催化剂变得难以还原.加入的Al2O3富集于催化剂表面,改变了催化剂表面Cu2+和Zn2+的摩尔分数.Al2O3还与SiO2产生无定形SiO2-Al2O3混合相,提供二甲醚合成所必需的酸碱中心.反应结果表明,Al2O3在催化剂中的质量分数低于1.4%时,对转化率的提高有促进作用;当Al2O3在催化剂中的质量分数为4.0%时,甲醇合成以及甲醇脱水的活性中心呈现出较好的"协同催化效应",目标产物二甲醚的收率最高.研究认为,Al2O3通过影响CuO与Al2O3之间的相互作用以及催化剂的表面酸性,从而使催化剂对CO2加氢合成二甲醚表现出不同的催化性能.     

高钛型高炉渣中TiO_2的还原规律

探讨攀钢高炉现场渣在实验室条件下,模拟高炉情况时渣中TiO_2的还原规律,对于生产中以渣中Ti(C.N)百分含量来反映还原程度给予了解释。     

Al2O3含量对高炉炉渣流动性影响的实验研究

以宝钢高炉渣中的四大组元(CaO,SiO2,Al2O3,MgO)为基础,实验研究MgO,Al2O3含量及碱度对炉渣的熔化性温度和流动性的影响.实验结果表明炉渣Al2O3含量控制在16%,配制适宜的MgO(9%～10%)含量,在1 500℃以上的高温区域,仍能保持正常的流动性,适合炉缸温度保持充沛的高炉使用;MgO含量由6%增加到10%粘度的递减值0.07～0.15 Pa·s,明显降低炉渣高温流动性.     

马钢4000m^3高炉高Al2O3炉渣渣系优化实验研究

以马钢现场高炉渣样为基准,研究w（Al2O3）=15％～20％的高炉炉渣性能。结果表明,在目前的冶炼条件下,马钢第三炼铁厂炉渣中的w（Al2O3）不宜超过18％,w（MgO）不宜超过12％。在高温区,MgO对炉渣性能的影响大于Al2O3,低温区相反,并提出了合理的渣系组成。     

烧结温度对高钛高炉渣制备微晶泡沫玻璃的影响

采用高钛高炉渣和废玻璃为主要原料,CaCO3作为发泡剂,硼砂Na2B4O7·10H2O作为助熔剂,磷酸钠Na3PO4·12H2O作为稳泡剂,通过“一步法”烧结制备了微晶泡沫玻璃。研究了烧结温度对微晶泡沫玻璃的影响,通过SEM及XRD对高钛高炉渣制备微晶泡沫玻璃的显微组织结构和物相进行分析。研究表明：在850℃~950℃之间,高钛高炉渣内的钙钛矿随烧结温度的增加逐渐分解,与其他物质反应生成透辉石Ca(Mg,Al)(Si,Al)2O6、普通辉石Ca(Mg,Fe,Al)(Si,Al)2O6、Ca(Mg,Fe)(Si,Al)2O6和硅辉石CaSiO3等晶体。微晶泡沫玻璃的孔径随烧结温度的增加逐渐增大,最后形成大孔和连通孔,同时,孔壁上析出的晶体数量增加,且晶体的形状从颗粒状变成层片状。在烧结温度为900 ℃时,微晶泡沫玻璃综合性能达到最佳：密度为0.6312 g/cm3,气孔率为74.5 %,吸水率为8.3 %,抗压强度为9.09 MPa。     

焙烧温度对S2O8^2-／Al2O3-Fe2O3固体酸催化性能的影响

制备S2O8^2-／Al2O3-Fe2O3型固体酸催化剂,用于催化乙酸和正丁醇合成乙酸正丁酯,采用TG／DSC、IR、SEM、XRD等对其结构和性能进行了表征,并研究了焙烧温度对其催化性能的影响。结果表明,不同焙烧温度对S2O8^2-／Al2O3-Fe2O3系列催化剂的结构和性能均产生一定的影响;随着焙烧温度的升高,酯化率呈先增加后降低的趋势,其中500℃焙烧的催化剂具有最佳的催化活性,其酯化率达到90．78％。     

Al2O3-C耐火材料的性能研究

为提高Ａｌ２Ｏ３－Ｃ耐火材料的性能，研究了烧成温度和石墨含量对Ａｌ２Ｏ３－Ｃ耐火材料气孔率、体积密度、常温耐压强度的影响，得出了适宜的烧成温度范围和最佳的石墨加入量，并对此进行了理论分析，同时，还研究了烧成温度对材料抗氧化性能的影响。     

Effect of applied electric field on slag erosion resistance of Al2O3 -C refractory

By using different particle size of fused white corundum （ 〈 74 μm, 74 - 147 μm, 〉 147 μm）, flake graphite, solid resin, commercial alcohol, zirconia （calcium oxide as stabilizer） as the raw materials, Al2O3-C samples with the length of 850 mm, inner （alumina-graphite） diameter of 50 mm and outer （zirconium） diameter of 85 mm were prepared by cold isostatic compaction pressed at 160 MPa after prilling in granulator. An electric field was applied to Al2O3-C refractory and the effect of current intensity （0. 5 A, 1 A and 5 A） on slag erosion resistance was investigated in this paper. The results show that with the increasing of current intensity, the thickness of build-up in cathode increases significantly. CaO · 6AL2 O3, a high melting point compound generated on the surface of slag line, decreases the slag erosion rate of Al2O3 -C refractory dramatically.     

Effect Of components on desulfurization of an Al2O3-CaO base pre-molten slag containing SrO

The desulfurization experiment of an Al2O3-CaO base pre-molten refining slag containing SrO was carried out. Experimental samples were made from industrial materials. In order to predict the slag‘s desulfurization ability, sulphur capacity was calculated by means of optical basicity, and there is consistency between calculated results and experimental data. A mathematical model between components and sulphur partition ratio was established with the experimental data. Based on the regression equation, the effects of single and interactive components on sulphur partition ratio were discussed. The results show that the sulphur capacity and distribution ratio decrease with the increment of Al2O3/CaO. SrO and MgO can increase the sulphur partition ratio. The best content of SrO in the slag should not be more than 10%, and the MgO content should be about 8%. The effect of CaF2 on sulphur partition ratio is not obvious, therefore the addition should be limited for environmental protection.     

注射成型Al2O3陶瓷喂料的制备工艺

研究了Al2O3陶瓷注射成型喂料的制备工艺,探讨了加料顺序、混炼温度、混炼时间等参数对喂料性能的影响．结果表明：先对PP、PE混炼,再逐渐加入预先搅拌好的PL与Al2O3、DBP、SA的混合物,最后混炼0．5h,即得较均匀的注射喂料．     

F,MgO对包钢高炉渣性能影响的实验研究

根据目前包钢高炉渣的成分采用二次回归方法配制合成渣,通过对合成渣的粘度、熔化性温度及熔化区间的测定,研究F和MgO对包钢高炉渣性能的影响程度,寻求适宜的高炉渣成分.实验结果表明,当炉渣中w(F)≤1%时,CaF2具有降低炉渣开始熔化温度,增加炉渣熔化区间,降低炉渣热焓,降低炉渣粘度和炉渣熔化性温度的作用.随着炉渣中MgO的质量分数的增加,炉渣的热稳定性提高,炉渣粘度降低,当w(MgO)=11.652%时,熔化性温度达到最高值.     

Al2O3与LaF3薄膜在紫外波段的特性研究

用电子束蒸发方法制造了Al2O3、LaF3单层膜,对比研究了沉积速率和基板温度对薄膜紫外（193 nm）光学特性、微结构的影响.实验结果表明,LaF3在紫外波段的光学损耗明显小于Al2O3.AFM测试发现,在相同的工艺条件下,Al2O3表面粗糙度大于LaF3,且3薄膜表面粗糙度随基板温度增加而增加.Al2O3薄膜在紫外波段的光学特性严重依赖于沉积速率等制备条件,而沉积速率对3薄膜特性的影响不明显,即使是在5 nm/s的速率条件下,LaF3仍具有良好的光学特性.X射线衍射（XRD）测试发现,电子束蒸发制备的Al2O3薄膜为非晶态,LaF3薄膜有结晶现象.     

掺杂对Al_2O_3/TiAl复合材料性能的影响

本研究采用Ti-Al-TiO2-La2O3体系,通过热压烧结工艺原位合成了Al2O3/TiAl复合材料.借助X射线衍射(XRD)、扫描电镜(SEM)等分析研究了材料的物相组成和微观组织结构,同时分别将掺杂La2O3和掺杂Fe2O3对合成Al2O3/TiAl复合材料微观结构和力学性能的影响进行了对比.结果表明:掺杂La2O3合成的Al2O3/TiAl复合材料基体尺寸相对掺杂Fe2O3合成产物较小,分散更加均匀,致密度更高.当La2O3掺杂量为3.93wt%时,Al2O3/TiAl复合材料的抗弯强度和断裂韧性达到最大值,分别为701.95MPa和7.79MPa·m1/2.由于稀土氧化物具有对基体和增强颗粒的净化,细化晶粒等作用,因此提高了TiAl基体与Al2O3增强颗粒结合强度,所以掺杂La2O3合成材料的力学性能相比掺杂Fe2O3合成的产物较高.     

Al2O3对3Ti/Si/2C体系自蔓延高温合成Ti3SiC2的影响

以3Ti/Si/2C粉体为原料,通过自蔓延高温合成技术合成了Ti3SiC2材料。研究了Al2O3助剂对自蔓延高温合成Ti3SiC2的影响。研究结果表明,3Ti/Si/2C粉体会发生自蔓延反应,产物的组成相为TiC、Ti3SiC2和Ti5Si3,产物中Ti3SiC2含量约为23%。添加适量的细粒度Al2O3可显著促进反应合成Ti3SiC2,3Ti/Si/2C/0.1Al2O3原料反应后得到的产物中Ti3SiC2含量达64%。