Ni-W-Cu-P沉积机制及在酸性溶液中的腐蚀行为

分别采用浸泡和电化学实验方法对Ni-W-Cu-P镀层在常温和高温20%H2SO4溶液中的耐蚀性进行了研究,用SEM,EDS及XRD对镀层的沉积机制、成分结构进行了分析.结果表明:球形Ni-W-Cu-P核心合并生长形成条状组织;共沉积W和Cu可显著提高Ni-W-Cu-P非晶的热稳定性;400℃热处理非晶的耐蚀性优于镀态非晶和500℃热处理纳米晶的;延长腐蚀时间,非晶和纳米晶镀层的腐蚀速率和腐蚀电流密度增大,阻抗则下降;Ni-W-Cu-P非晶和纳米晶镀层的腐蚀机制分别是选择性腐蚀和点腐蚀.     

Fe-P非晶合金的电沉积行为及热处理对其结构与性能的影响

在以柠檬酸三钠为络合剂的酸性镀液中电沉积Fe-P非晶合金,采用差示扫描量热(DSC)、X射线衍射(XRD)和扫描电镜(SEM)研究该合金镀层的晶化行为和表面微观形貌。结果表明:镀液中加入络合剂,且随着pH值升高和温度降低时,Fe-P非晶合金共沉积的阴极极化增大。镀态Fe-P合金为非晶态结构,于330.5℃时开始晶化;383.6℃时,α-Fe(P)固溶体大量晶化析出;472.5℃时,Fe3P(I-4)相大量脱溶析出。且随着热处理温度升高,合金镀层的耐蚀性能和硬度先增加后下降,450℃热处理所得镀层的耐蚀性能最佳且硬度最大;在400℃以下时,镀膜具有良好的抗热氧化能力,当温度在400℃以上时,抗氧化能力迅速下降。     

非晶态Ni-Mo-P镀层的组织结构与晶化过程

用化学沉积方法在酸性镀液中获得了Ni Mo P非晶镀层 ,运用能谱仪、扫描电镜和X射线衍射仪对该镀层非晶结构的形成、成分与结构及其晶化过程进行了分析 ,并与Ni P镀层进行了对比。结果表明 ,Ni Mo P镀层比Ni P镀层晶化温度高 ,热稳定性好。热处理后Ni Mo P镀层在 5 0 0℃时硬度达到最高值。随着热处理温度的升高 ,镀层的形貌和性能也发生了相应的变化。     

非晶态Ni—Mo—P层的组织结构与晶化过程

用化学沉积方法在酸性镀液中获得了Ni—Mo—P非晶镀层，运用能谱仪、扫描电镜和X射线衍射仪对该镀层非晶结构的形成、成分与结构及其晶化过程进行了分析，并与Ni—P镀层进行了对比。结果表明，Ni—Mo—P镀层比Ni—P镀层晶化温度高，热稳定性好。热处理后Ni—Mo—P镀层在500℃时硬度达到最高值。随着热处理温度的升高，镀层的形貌和性能也发生了相应的变化。     

热处理温度对Ni-Co-P合金镀层组织与性能的影响

研究了不同热处理温度对化学镀Ni-Co-P镀层组织和性能的影响.结果表明:在给定实验条件下,原始镀态Ni-Co-P镀层组织呈非晶结构胞状形态.随加热温度升高至400℃时,经XRD分析可知,镀态的非晶结构Ni-Co-P镀层发生部分晶化,析出亚稳相Ni12P5,500℃热处理后完全晶化,亚稳相转变为稳定的Ni,P相,镀层表面形貌变化不大,但当600℃热处理后镀层表面形貌由胞状变为蠕虫状.镀层硬度随热处理温度的升高先增后降,至400℃时硬度达到最高值,而后随温度的升高而下降,与组织结构的变化相吻合.研究还表明,Ni-Co-P镀层同Ni-P镀层相比,具有更优异的耐硫酸腐蚀性能.     

水溶液中电沉积C0-La薄膜及其性能研究

在氨基乙酸为络合剂的水溶液中采用恒电位法沉积出Co-La薄膜,分别研究了pH、沉积电位对镀层结构的影响.结果表明,在镀液pH=4.5时随沉积电位负移,镀层中La含量先增后减;当沉积电位为-1.050 V(vs. SCE),镀液pH值从4.05至4.90变化时,镀层中La含量增大.循环伏安实验证实:Co-La沉积属诱导共沉积.采用XRD研究了镀层的晶化行为,结果表明:镀态镀层含有Co(hcp)相和非晶相,700℃热处理后晶化为Co-La(fcc)固溶体和Co13La合金相.电化学实验表明,Co-La电极比纯Co电极具有更好的析氢电催化活性.Co-La薄膜具有优异的硬磁性能.     

水溶液中电沉积Co-La薄膜及其性能研究

在氨基乙酸为络合剂的水溶液中采用恒电位法沉积出Co-La薄膜,分别研究了pH、沉积电位对镀层结构的影响。结果表明,在镀液pH=4.5时随沉积电位负移,镀层中La含量先增后减;当沉积电位为–1.050V（vs.SCE）,镀液pH值从4.05至4.90变化时,镀层中La含量增大。循环伏安实验证实：Co-La沉积属诱导共沉积。采用XRD研究了镀层的晶化行为,结果表明：镀态镀层含有Co（hcp）相和非晶相,700℃热处理后晶化为Co-La（fcc）固溶体和Co13La合金相。电化学实验表明,Co-La电极比纯Co电极具有更好的析氢电催化活性。Co-La薄膜具有优异的硬磁性能。     

工艺参数及稳定剂抗坏血酸对电沉积NiFeW合金的影响

为获得性能良好的镍铁钨合金镀层,研究了镀液pH 值、温度、电流密度、稳定剂抗坏血酸浓度对镍铁钨合金镀层成分和镀层沉积速率、显微硬度的影响。结果表明: 镀液pH 值对镀层W含量和镀层沉积速率影响较大;镀液温度对镀层沉积速率、镀层成分和镀层硬度影响均较大;随抗坏血酸浓度增加,镀层沉积速率逐渐降低,镀层表面形貌更加粗糙。在镀液pH = 4,温度60 ℃,电流密度4 A/dm2,抗坏血酸浓度3 g /L 时,镀层沉积速率和镀层的显微硬度较高,表面光亮致密,耐蚀性好。     

工艺参数及稳定剂抗坏血酸对电沉积NiFeW合金镀层的影响（英文）

为获得性能良好的镍铁钨合金镀层,研究了镀液pH值、温度、电流密度、稳定剂抗坏血酸浓度对镍铁钨合金镀层成分和镀层沉积速率、显微硬度的影响。结果表明:镀液pH值对镀层W含量和镀层沉积速率影响较大;镀液温度对镀层沉积速率、镀层成分和镀层硬度影响均较大;随抗坏血酸浓度增加,镀层沉积速率逐渐降低,镀层表面形貌更加粗糙。在镀液pH=4,温度60℃,电流密度4A/dm~2,抗坏血酸浓度3 g/L时,镀层沉积速率和镀层的显微硬度较高,表面光亮致密,耐蚀性好。     

Co-P非晶态合金的电沉积及结构分析

采用硫酸钴—次磷酸钠镀液进行电沉积Co—P非晶态合金,研究了镀液组成、温度、pH值对镀层含P量以及镀层结构的影响。镀层中含P量小于5（wt）％为晶态结构,在5～19（wt）％之间为非晶态结构,高于19（wt）％为金属间化合物。此外,由热处理实验研究了非晶镀层的热稳定性。     

Molybdenum based amorphous and nanocrystalline coatings prepared by high velocity oxy-fuel spraying

The high velocity oxy-fuel(HVOF) based thermal spray process has developed as a potential advantageous approach for fabricating various kinds of functional coatings.In this article,the coatings of Mo-based alloy were synthesized using the HVOF process.The microstructure and the mechanical properties of the HVOF-processed coatings were investigated using SEM,TEM,XRD,and hardness and wear tests.Annealing treatment was applied to the as-sprayed coatings to develop the microstructure and its effect on the microstructure and mechanical properties of the coatings was examined.It is found that the HVOF-processed Mo-based alloy coatings are comprised of an amorphous splat matrix embedded with nano-sized crystalline particles.Annealing at temperatures over 950 ℃ results into crystallization of the amorphous matrix.The mechanical properties of the as-sprayed coatings are enhanced with annealing temperature up to 750 ℃ and from 950 to 1050 ℃,keeps constant between 750 and 950 ℃,and reduce over 1050 ℃.The change of the mechanical property with the microstructure was illustrated in the study.     

Formation and thermal stability of amorphous Ni-Mo-P alloys

The experimental researches on the chemical deposition of Ni-Mo-P amorphous alloys were carried out by adding Na2 MoO4 into acidic solutions. The optimum technology conditions were obtained by orthogonal design experiments. The structures and the relationship between compositions and their thermal stability were studied by energy spectrum (EC), scanning electron micrograph and X-ray diffraction spectrum. Compared with Ni-P amorphous alloys, the Ni-Mo-P amorphous alloys have high crystallization temperature and thermal stability, and the hardness reaches its peak when the annealing temperature is 500 ℃. With the increase of the heat treatment temperature, the surface morphology of the alloys changes.     

Morphology,Structure, Microhardness and Corrosion Resistance of Ni-W Coating Annealed in Hydrogen and Argon Atmosphere

In this paper, an amorphous Ni-W coating was electrodeposited on the low-carbon steel and then annealed in hydrogen and argon atmosphere. Their characterization was carried out using scanning electron microscopy and x-ray diffraction. The corrosion characterization was carried out using the potentiodynamic polarization (Tafel) and electrochemical impedance spectroscopy. The results show that microcracks inevitably exist on the surface of Ni-W coating when annealed at 750 °C or higher temperature. After annealing treatment, amorphous structure transforms to crystalline and some new phases are precipitated, which is significantly affected by the annealing temperature and atmosphere. The microhardness of annealed Ni-W coatings is much higher than that of as-deposited coating, while an adverse corrosion performance is observed for the annealed Ni-W coatings. The coating annealed in hydrogen at 500 °C shows a huge improvement in hardness and a fairly acceptable corrosion resistance compared with the as-deposited Ni-W coating.     

退火对冷轧搪瓷钢氢渗透性及搪瓷鳞爆性的影响

对冷轧钢板进行了模拟连续退火和搪瓷,然后采用电化学方法测量其氢渗透参数,研究退火温度对冷轧搪瓷钢板夹杂物形态和分布、氢渗透性和搪瓷鳞爆性的影响。结果表明,钢于650℃退火后以变形组织为主,夹杂物呈条带状;750℃退火后为等轴晶并有少量第二相在晶界析出;在750℃以下,随着退火温度的升高,试验用铜的氢扩散系数增大,但在750℃退火的钢氢扩散系数下降,随后随着退火温度的升高而再次上升;750℃退火的铜的抗鳞爆性最佳。     

V元素对TiAlN涂层高温氧化行为的影响

为了考察V元素对Ti—Al-N涂层高温氧化行为的影响,用多弧离子镀法在W18Cr4V1Co5高速钢试样表面涂镀了Ti—Al-N和Ti—Al-V—N涂层。对两种涂层试样在不同温度和不同时间下进行氧化处理。用SEM观测两种涂层的组织结构,用XRD分析其相组成,用CTA分析其升温氧化和恒温氧化动力学行为。实验结果表明,V的加入使涂层晶粒细化,组织更加致密;两种涂层均在750℃以后才测量到氧化增重;Ti-Al-N涂层的氧化转折点为920℃,超过920℃,涂层迅速氧化,逐渐失效;Ti—Al-V—N涂层在超过1000℃增重仍非常缓慢,并具有抗氧化保护的作用。V元素的加入大大降低了氧化速率,从而有效地提高了涂层的抗氧化性能。     

超音速等离子喷涂FeCrBSi涂层组织和残余应力分析

采用超音速等离子喷涂技术制备了FeCrBSi涂层,利用扫描电子显微镜(SEM)、X射线衍射仪(XRD)和纳米压痕仪等研究了涂层的微观组织和力学性能。采用X射线应力仪对不同厚度及不同温度退火后涂层的表面残余应力进行测试。结果表明涂层表面的残余应力为拉应力,且随着涂层厚度的增加而增加;对试样进行退火处理可以有效地缓和涂层表面的残余应力,随着温度的升高涂层表面的残余应力不断降低,到260℃左右变为压应力;压应力值随着退火温度的升高而变大,但当温度升高到大约400℃以上时,保持在80 MPa左右。     

Mg合金的腐蚀与防护

介绍了Mg合金的腐蚀原理、腐蚀类型以及合金元素在镁合金中的作用。综述了Mg合金的化学转化膜、阳极氧化、微弧氧化、化学镀等经典的表面处理方法 ,以及快速凝固工艺和表面改性技术对Mg合金表面耐蚀性能的影响。Mg合金易发生全面腐蚀、电偶腐蚀、点蚀、应力腐蚀和高温氧化。解决Mg合金腐蚀的方法有 :一是研究新合金 ,提高Mg合金自身的热力学稳定性 ,稀土Mg合金是最有前途的耐蚀合金 ;二是通过表面处理使Mg合金表面富SiO2 和Al2 O3 、含SiC和F-等物质或获得的非晶态的涂层结构能有效地提高Mg合金的耐蚀耐磨性能 ;三是改进加工工艺 ,快速凝固和激光退火不仅能获得力学性能优秀的Mg合金产品 ,还能获得纳米结构的表面涂层防护膜 ,提高Mg合金的耐蚀耐磨性能。使镁合金表面涂层结构纳米化、玻璃化是表面处理工艺的发展趋势。     

退火温度对IrO_2+ZrO_2涂层结构和电容性能的影响

采用热分解法在Ti基上被覆了IrO_2+ZrO_2氧化物涂层。通过XRD、SEM、EDX、XPS和循环伏安法等分析了退火温度对IrO_2-ZrO_2二元氧化物涂层的物相、表面形貌和电容性能的影响,引用非线性方程q~*(v)=A_1exp~(-v/t_1)+A_2exp~(-v/t_2)+y_0计算了涂层的内外活性点。结果表明:IrO_2-ZrO_2涂层的临界晶化温度为340~360℃,340℃退火的涂层物相为非晶结构,360℃退火,含有晶态和非晶态2种结构组织,其离子价态为Ir~(3+)、Ir~(4+)以及过饱和IrO_(2+x)(x0)。电容性能随着温度的升高呈先增大后减小变化,360℃退火的电极有最大的电容值,与其"非晶态/晶态"两相共存组织结构有关。涂层中质子迁移能力比电子导电能力对电容的影响要大,扫描速度对质子迁移的影响大于对电子导电的影响。     

PROPERTIES OF ELECTRODEPOSITED AMORPHOUS Ni-W-P-SiC COMPOSITE COATINGS

ＰＲＯＰＥＲＴＩＥＳＯＦＥＬＥＣＴＲＯＤＥＰＯＳＩＴＥＤＡＭＯＲＰＨＯＵＳＮｉ－Ｗ－Ｐ－ＳｉＣＣＯＭＰＯＳＩＴＥＣＯＡＴＩＮＧＳＧＵＯＺｈｏｎｇｃｈｅｎｇ;ＬＩＵＨｏｎｇｋａｎｇ;ＷＡＮＧＺｈｉｙｉｎ;ＷＡＮＧＭｉｎ（ＤｅｐａｒｔｍｅｎｔｏｆＭｅｔａ...     

退火温度对MAO-TC4钛合金表面组织及腐蚀性能的影响

通过微弧氧化技术(Micro-arc oxidation, MAO)对TC4合金进行表面处理,随后采用X射线衍射仪、场发射扫描电镜、激光共聚焦显微镜、硬度测试以及电化学腐蚀等方法研究不同退火温度下MAO-TC4合金的表面氧化膜层形貌、厚度、硬度、相结构以及电化学腐蚀行为。结果表明:随着退火温度的升高,MAO-TC4合金表面氧化膜层的显微硬度亦随之增大,当退火温度为850 ℃时,其最高显微硬度为592 HV0.2。450~850 ℃退火温度范围内,随退火温度升高,MAO-TC4合金的膜层耐腐蚀性先增加后降低;当退火温度为650 ℃时,膜层的自腐蚀电流密度为0.125 μA/cm²,耐腐蚀性能最佳。