The formation of β‐polypropylene crystals in a compatibilized blend of isotactic polypropylene and polyamide‐6

Compatibilized polypropylene (PP)/polyamide (PA6) blends with and without β nucleating agent (β‐NA) are prepared, and are designated as Blend‐0.3 and Blend‐0, respectively. The melting and crystallization characteristic of the blends crystallized under different cooling rates and different crystallization temperatures are studied. It is observed that high β‐PP content can be developed in Blend‐0.3 only at slow cooling rates (<5°C/min), whereas high α‐PP content is formed at fast cooling rates. Isothermal crystallization analysis of Blend‐0 indicates that PA6 is an effective NA for α‐PP in the lower temperature range, whereas the α‐nucleating effect disappears in the higher temperature range. Blend‐0.3 can, therefore, be viewed as a system containing both α‐ and β‐NAs, simultaneously. PA6 is competing with β‐NA in inducing PP crystallization. Under the normal injection of Blend‐0.3, the melt will be cooled through the higher temperature that favors the effectiveness of β‐NA rapidly because of the faster cooling rate. However, the α‐nucleation effect from PA6 predominate at the lower temperature. This explains the difficulty in obtaining high β‐PP content in Blend‐0.3 from injection molding. POLYM. ENG. SCI., 2011. © 2010 Society of Plastics Engineers     

Nonisothermal crystallization and melting behavior of β‐nucleated isotactic polypropylene and polyamide 66 blends

A highly novel nano‐CaCO₃ supported β‐nucleating agent was employed to prepare β‐nucleated isotactic polypropylene (iPP) blend with polyamide (PA) 66, β‐nucleated iPP/PA66 blend, as well as its compatibilized version with maleic anhydride grafted PP (PP‐g‐MA), maleic anhydride grafted polyethylene‐octene (POE‐g‐MA), and polyethylene‐vinyl acetate (EVA‐g‐MA), respectively. Nonisothermal crystallization behavior and melting characteristics of β‐nucleated iPP and its blends were investigated by differential scanning calorimeter and wide angle X‐ray diffraction. Experimental results indicated that the crystallization temperature (T) of PP shifts to high temperature in the non‐nucleated PP/PA66 blends because of the α‐nucleating effect of PA66. T of PP and the β‐crystal content (K_β) in β‐nucleated iPP/PA66 blends not only depended on the PA66 content, but also on the compatibilizer type. Addition of PP‐g‐MA and POE‐g‐MA into β‐nucleated iPP/PA66 blends increased the β‐crystal content; however, EVA‐g‐MA is not benefit for the formation of β‐crystal in the compatibilized β‐nucleated iPP/PA66 blend. It can be relative to the different interfacial interactions between PP and compatibilizers. The nonisothermal crystallization kinetics of PP in the blends was evaluated by Mo's method. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Effect of carbon nanotube‐supported β nucleating agent on the thermal properties,morphology, and mechanical properties of polyamide 6/isotactic polypropylene blends

A new kind of β nucleating agent, multi‐wall carbon nanotube (MWCNT)‐supported calcium pimelate was introduced into polyamide 6 (PA 6)/isotactic polypropylene (iPP; 10/90 by weight) blend and the thermal properties, morphology, and mechanical properties were investigated. The results showed that β‐iPP appeared at low content of MWCNT‐supported calcium pimelate which surmounted the α‐nucleating effect of PA 6 for iPP, and the content of β‐iPP increased with increasing content of MWCNT‐supported calcium pimelate. The impact strength, elongation at break, and flexural modulus were improved with increasing content of MWCNT‐supported calcium pimelate without significantly deteriorating the tensile strength. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

A highly active and selective β‐nucleating agent for isotactic polypropylene and crystallization behavior of β‐nucleated isotactic polypropylene under rapid cooling

Zinc adipate (Adi‐Zn) was observed to be a highly active and selective β‐nucleating agent for isotactic polypropylene (iPP). The effects of Adi‐Zn on the mechanical properties and the β‐crystals content of nucleated iPP were investigated. The impact strength of iPP nucleated with 0.2 wt % Adi‐Zn was 1.8 times higher than that of neat iPP. In addition, wide‐angle X‐ray diffraction analysis indicated that the content of β‐crystals in nucleated iPP (k_β value) reached 0.973 with 0.1 wt % Adi‐Zn, indicating that Adi‐Zn is a highly active and selective β‐nucleating agent for iPP. Furthermore, fast scanning chip calorimetry (FSC) studies using cooling rates from 60 to 13,800 °C min^?1 revealed that the formation of β‐crystals significantly depended on the cooling rates. At cooling rates below 3000 °C min^?1, only β‐crystals existed. However, at cooling rates above 6000 °C min^?1, β‐crystals failed to form. Moreover, a lower critical crystallization temperature that corresponded to the generation of β‐crystals was investigated using cooling‐induced crystallization, and the results are in good agreement with those of a previous study. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43767.     

A novel β‐nucleating agent for isotactic polypropylene

The nucleating ability of p‐cyclohexylamide carboxybenzene (β‐NA) towards isotactic polypropylene (iPP) was investigated by differential scanning calorimetry, X‐ray diffraction, polarized optical microscopy and scanning electron microscopy. β‐NA is identified to have dual nucleating ability for α‐iPP and β‐iPP under appropriate kinetic conditions. The formation of β‐iPP is dependent on the content of β‐NA. The content of β‐phase can reach as high as 96.96% with the addition of only 0.05 wt% β‐NA. Under non‐isothermal crystallization the content of β‐iPP increases with increasing cooling rate. The maximum β‐crystal content is obtained at a cooling rate of 40 °C min^–1. The supermolecular structure of the β‐iPP is identified as a leaf‐like transcrystalline structure with an ordered lamellae arrangement perpendicular to the special surface of β‐NA. Under isothermal crystallization β‐crystals can be formed in the temperature range 80–140 °C. The content of β‐crystals reaches its maximum value at a crystallization temperature of 130 °C. © 2012 Society of Chemical Industry     

A novel highly efficient β‐nucleating agent for isotactic polypropylene

A novel highly efficient β‐nucleating agent for isotactic polypropylene (iPP), hexahydrophthalic barium (HHPA‐Ba), was found and its effects on the mechanical properties, the β‐phase content, and crystallization behavior of iPP were investigated, respectively. The results show that the β‐phase content of nucleated iPP (k_β value) can reach 80.2% with 0.4 wt % HHPA‐Ba. The impact strength and crystallization peak temperature of nucleated iPP are greatly increased. Compared with pure iPP, the impact strength of nucleated iPP can increase 2.4 times. Meanwhile, the spherulite size of nucleated iPP is dramatically decreased than that of pure iPP. The Caze method was used to investigate the nonisothermal crystallization kinetics of nucleated iPP and the crystallization active energy was achieved by Kissinger method. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Influence of different β‐nucleating agent on crystallization behavior,morphology, and melting characteristic of multiwalled carbon nanotube‐filled isotactic polypropylene nanocomposites

To obtain isotactic polypropylene (iPP) nanocomposites with high β‐crystal content, TMB5, calcium pimelate and calcium pimelate supported on the surface of nano‐CaCO₃ were used as β‐nucleating agent and MWCNT filled β‐nucleated iPP nanocomposites were prepared. The effect of different β‐nucleating agent and MWCNT on the crystallization behavior and morphology, melting characteristic and β‐crystal content of β‐nucleated iPP nanocomposites were investigated by DSC, XRD and POM. The results indicated that addition of MWCNT increased the crystallization temperature of iPP and MWCNT filled iPP nanocomposites mainly formed α‐crystal. The β‐nucleating agent can induce the formation of β‐crystal in MWCNT filled iPP nanocomposites. The β‐nucleating ability and β‐crystal content in MWCNT filled β‐nucleated iPP nanocomposites decreased with increasing MWCNT content and increased with increasing β‐nucleating agent content due to the nucleation competition between MWCNT and β‐nucleating agents. It is found that the calcium pimelate supported on the surface of inorganic particles as β‐nucleating agent has stronger heterogeneous β‐nucleation than calcium pimelate and TMB5. The MWCNT filled iPP nanocomposites with high β‐crystal content can be obtained by supported β‐nucleating agent. POLYM. COMPOS., 36:635–643, 2015. © 2014 Society of Plastics Engineers     

Effects of melt structure on crystallization behavior of isotactic polypropylene nucleated with α/β compounded nucleating agents

In this study, the melt structure of isotactic polypropylene (iPP) nucleated with α/β compounded nucleating agents (α/β‐CNA, composed of the α‐NA of 0.15 wt % Millad 3988 and the β‐NA of 0.05 wt % WBG‐II) was tuned by changing the fusion temperature T_f. In this way, the role of melt structure on the crystallization behavior and polymorphic composition of iPP were investigated by differential scanning calorimetry (DSC), wide‐angle X‐ray scattering (WAXD) and scanning electron microscopy (SEM). The results showed that when T_f = 200°C (iPP was fully molten), the α/β‐CNA cannot encourage β‐phase crystallization since the nucleation efficiency (NE) of the α‐NA 3988 was obviously higher than that of the β‐NA WBG‐II. Surprisingly, when T_f was in 179–167°C, an amount of ordered structures survived in the melt, resulting in significant increase of the proportion of β‐phase (achieving 74.9% at maximum), indicating that the ordered structures of iPP played determining role in β‐phase crystallization of iPP nucleated with the α/β‐CNA. Further investigation on iPP respectively nucleated with individual 3988 and WBG‐II showed that as T_f decreased from 200°C to 167°C, the crystallization peak temperature T_c of iPP/3988 stayed almost constant, while T_c of iPP/WBG‐II increased gradually when T_f < 189°C and became higher than that of iPP/3988 when T_f decreased to 179°C and lower, which can be used to explain the influence of ordered structure and α/β‐CNA on iPP crystallization. Using this method, the selection of α‐NA for α/β‐CNA can be greatly expanded even if the inherent NE of β‐NA is lower than that of the α‐NA. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41355.     

Highly active thermally stable β‐nucleating agents for isotactic polypropylene

Calcium salts of suberic (Ca‐Sub) and pimelic (Ca‐Pim) acids were synthesized and implemented as in different grades of isotactic polypropylene (iPP). Propylene homopolymer, as well as random and block copolymers containing these additives, crystallized iPP into pure or nearly pure β modification in the isothermal and nonisothermal crystallization experiments. Recently, Ca‐Sub proved to be the most effective β‐nucleating agent of iPP. The Ca‐Sub nucleating agent widens the upper crystallization temperature range of pure β‐iPP formation up to 140°C. In this study the effect of the these additives on the crystallization, melting characteristics, and structure of the PP were studied. The degree of crystallinity of β‐iPP was markedly higher than that of α‐iPP. A widening in the melting peak of the samples crystallized in a high temperature range was first observed and discussed in regard to literature results of the same phenomenon for α‐iPP. The morphology of the β‐iPP samples was revealed by scanning electron microscopy. Independent of the type of polymer or nucleating agent, hedritic structures were found in the early stages of growth of the β‐spherulites. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 2357–2368, 1999     

Variation of non‐isothermal crystallization behavior of isotactic polypropylene with varying β‐nucleating agent content

The non‐isothermal crystallization behavior, the crystallization kinetics, the crystallization activation energy and the morphology of isotactic polypropylene (iPP) with varying content of β‐nucleating agent were investigated using differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). The DSC results showed that the Avrami equation modified by Jeziorny and a method developed by Mo and co‐workers could be successfully used to describe the non‐isothermal crystallization process of the nucleated iPPs. The values of n showed that the non‐isothermal crystallization of α‐ and β‐nucleated iPPs corresponded to a tridimensional growth with homogeneous and heterogeneous nucleation, respectively. The values of crystallization rate constant showed that the rate of crystallization decreased for iPPs with the addition of β‐nucleating agent. The crystallization activation energy increased with a small amount (less than 0.1 wt%) of β‐nucleating agent and decreased with higher concentration (more than 0.1 wt%). The changes of crystallization rate, crystallization time and crystallization activation energy of iPPs with varying contents of β‐nucleating agent were mainly determined by the ratio of the content of α‐ and β‐phase in iPP (α‐PP and β‐PP) from the DSC investigation, and the large size and many intercrossing lamellae between boundaries of β‐spherulites for iPPs with small amounts of β‐nucleating agent and the small size and few intercrossing bands among the boundaries of β‐spherulites for iPPs with large amounts of β‐nucleating agent from the SEM examination. Copyright © 2010 Society of Chemical Industry     

A highly efficient β‐nucleating agent for impact‐resistant polypropylene copolymer

In this work, we reported calcium tetrahydrophthalate as a high efficient β‐nucleating agent (β‐NA) for impact‐resistant polypropylene copolymer (IPC). The relative fraction of the β‐crystal can reach as high as 93.5% when only 0.03% β‐NA is added. The non‐isothermal and isothermal crystallization behaviors, morphology, lamellar structure and mechanical properties of IPCs with various β‐NA contents were studied. During non‐isothermal crystallization, the cooling rate has an important influence on the relative fraction of the β‐crystal, which decreases remarkably as the cooling rate increases. The β‐NA also greatly accelerates crystallization rate of IPC, resulting from both more crystal nuclei and larger Avrami exponent. The small angle X‐ray scattering characterization shows that more amorphous components are included into the inter‐lamellae after addition of β‐NA. Dynamical mechanical analysis (DMA) reveals that the storage modulus at low temperature and the loss factor above 0 °C from the PP component can be enhanced upon addition of β‐NA and reach a maximum at the β‐NA content of 0.05 wt %. Impact test shows that the impact strength of the IPC at 0°C can be improved as much as 40% when the content of calcium tetrahydrophthalate is 0.10 wt %. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40753.     

Comparative study on the crystallization behavior of β‐isotactic polypropylene nucleated with different β‐nucleation agents —effects of thermal conditions

In this study, the crystallization behavior of the β‐isotactic polypropylene (β‐iPP) samples nucleated by a rare earth based β‐nucleating agent (β‐NA) WBG‐II and a metal salts compound β‐NA NAB83 (denoted as WPP and NPP, respectively) under different cooling conditions were comparatively investigated. The thermal conditions such as the cooling rate, isothermal crystallization temperature, isothermal crystallization time, and the subsequent cooling to room temperature. The results of WAXD, SEM, and nonisothermal crystallization reveal that under the same processing conditions, the crystallite size of NPP is smaller, which arrange more compactly as compared with WPP. Meanwhile, NPP has shorter crystallization rate and higher β‐nucleation selectivity, but WPP can crystallization at wider temperature range. The results of isothermal crystallization showed that NPP has higher selectivity and higher β‐nucleation efficiency, which favors the formation of high proportion of β‐phase at the isothermal crystallization temperature of 110–130°C with and without subsequent cooling; WPP has lower selectivity, which can only induce high content of β‐phase under isothermal crystallization without subsequent cooling to 25°C. In tuning the crystallization behavior and the properties of β‐PP, the joint influence of the efficiency and selectivity of the β‐NA, and the thermal conditions should be taken into consideration. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40115.     

Effect of N,N′‐diphenyl adipamide on the formation of the β‐crystalline form in isotactic polypropylene

The polymorphic compositions and mechanical properties of isotactic polypropylene (iPP) samples nucleated by a selective β‐nucleating agent [N,N′‐diphenyl adipamide (DPA)] were investigated with wide‐angle X‐ray diffraction, polarized light microscopy, scanning electron microscopy, and mechanical tests. It was found that β‐phase crystals emerged with the addition of DPA, and the relative proportion of the β‐crystalline form reached the maximum value of 0.97 with the addition of 0.1 wt % DPA. The curved lamellae in the β spherulites were like flowers. The β spherulites were etched more easily than α spherulites because amorphous regions were distributed inside the β spherulites. The Izod notched impact strength increased sharply with the addition of DPA and attained the maximum value of 7.30 kJ/m² (the value of blank iPP was 3.13 kJ/m²) with the addition of 0.1 wt % DPA. An analysis of the misfit factors between DPA and β‐iPP showed that β‐iPP could epitaxially crystallize on the DPA crystal well. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

A comparative study of polypropylene nucleated by individual and compounding nucleating agents. I. Melting and isothermal crystallization

In this study, melting and isothermal crystallization behaviors of polypropylene (PP) nucleated with different nucleating agents (NAs) have been comparatively studied. α‐phase NA 1,3 : 2,4‐bis (3,4‐dimethylbenzylidene) sorbitol (DMDBS, Millad 3988), β‐phase NA aryl amides compound (TMB‐5), and their compounds were introduced into PP matrix, respectively. The crystallization and melting characteristics as well as the crystallization structures and morphologies of nucleated PP were studied by differential scanning calorimetry (DSC), wide angle X‐ray diffraction (WAXD), and polarized light microscopy (PLM). As indicated by previous work that a few amounts of α‐phase NA (DMDBS) or β‐phase NA (TMB‐5) has apparent nucleation effect for PP crystallization. However, the crystallization of PP nucleated with compounding NAs is dependent on the content of each NA. In the sample of PP with 0.1 wt % DMDBS and 0.1 wt % TMB‐5, the nucleation efficiency of TMB‐5 is much higher than that of DMDBS and PP crystallization is mainly nucleated by TMB‐5, and in this condition, β‐phase PP is the main crystallization structure. For the sample of PP with 0.2 wt % DMDBS and 0.2 wt % TMB‐5, 0.2 wt % DMDBS has higher nucleation efficiency than 0.2 wt % TMB5, and α‐phase is the main crystalline structure in this sample. The isothermal crystallization kinetics and crystallization structure have been analyzed in detail in this work. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Combined effect of organic phosphate sodium and nanoclay on the mechanical properties and crystallization behavior of isotactic polypropylene

Combined effect of α‐nucleating agent (NA) sodium 2,2′‐methylene‐bis(4,6‐di‐tert‐butylphenyl) phosphate (NA11) and nanoclay (NC) on the mechanical properties and crystallization behavior of isotactic polypropylene (iPP) was investigated by mechanical testing, wide‐angle X‐ray scattering (WAXD), differential scanning calorimetry (DSC), polarized optical microscopy (POM), and scanning electron microscopy (SEM). The mechanical testing results indicated that the separate addition of NA11 and NC only increased the stiffness of iPP while the combined addition of NA11, NC, and maleic anhydride grafted polypropylene (PP‐g‐MA) simultaneously improved stiffness and toughness of iPP. Compared to pure iPP, the tensile strength, the flexural modulus, and impact strength of iPP composites increased 9.7, 38.6, and 42.9%, respectively. The result indicated good synergistic effects of NC, NA11, and PP‐g‐MA in improving iPP mechanical properties. WAXD patterns revealed NA11, and NC only induced the α‐crystals of iPP. SEM micrograph showed that the PP‐g‐MA could effectively improve the dispersing of NC in iPP. Finally, the nonisothermal crystallization kinetics of neat iPP and PP nanocomposites was described by Caze method. The result indicated that the addition of NA overcame the shortcoming of low crystallization rate of NC nanocomposites and maintained the excellent mechanical properties, which is another highlight of the combined addition of NAs and nanoclay. Meanwhile, the result showed that nuclei formation and spherulite growth of iPP were affected by the presence of NA and nanoclay. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Effect of α‐ and β‐nucleating agents on the fracture behavior of polypropylene‐co‐ethylene

The effect of α‐ and β‐nucleating agents (NA) of various amounts on the fracture behavior of polypropylene‐co‐ethylene (CPP) was evaluated using the essential work of fracture (EWF) method. The specific EWF values of CPPs incorporated with α‐NA of different amount were all lower than that of pure CPP, while the specific nonessential work of fracture was the highest at relative low α‐NA loading (0.1 wt %), and then decreased with further increasing amount of α‐NA. Similar trend of variation was observed with increasing amount of β‐NA in CPP, and it was found that the variation of K_β for β‐NA nucleated CPP versus NA content accorded well with the EWF versus NA content, which indicated that the addition of β‐NA could lead to effectively increased β‐crystal content and consequently improved fracture resistance of CPP. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Isothermal crystallization and melting behavior of polypropylene with lanthanum complex of cyclodextrin derivative as a β‐nucleating agent

A novel highly active β‐nucleating agent, β‐cyclodextrin complex with lanthanum (β‐CD‐MAH‐La), was introduced to isotactic polypropylene (iPP). Its influence on isothermal crystallization and melting behavior of iPP was investigated by differential scanning calorimeter (DSC), wide‐angle X‐ray diffraction (WAXD), and polarized light microscopy (PLM). WAXD results demonstrated that β‐CD‐MAH‐La was an effective β‐nucleating agent, with β‐crystal content of iPP being strongly influenced by the content of β‐CD‐MAH‐La and the isothermal crystallization temperature. The isothermal crystallization kinetics of pure iPP and iPP/β‐CD‐MAH‐La was described appropriately by Avrami equation, and results revealed that β‐CD‐MAH‐La promoted heterogeneous nucleation and accelerated the crystallization of iPP. In addition, the equilibrium melting temperature (T) of samples was determined using linear and nonlinear Hoffman‐Weeks procedure. Finally, the Lauritzen‐Hoffman secondary nucleation theory was applied to calculate the nucleation parameter (K_g) and the fold surface energy (σ_e), the value of which verify that the addition of β‐CD‐MAH‐La reduced the creation of new surface for β‐crystal and then led to faster crystallization rate. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

β‐Nucleation of pimelic acid supported on metal oxides in isotactic polypropylene

To investigate the nucleation of metal pimelate for isotactic polypropylene (iPP) crystallization, iPP filled with a series of metal oxides with and without metal pimelate on their surface was prepared. There was a chemical reaction between pimelic acid (PA) and metal oxides MgO, CaO, BaO or ZnO, but not TiO₂. The corresponding metal pimelate formed by the chemical reaction between PA and MgO, CaO, BaO or ZnO had a different influence on the crystallization behavior and melting characteristics of iPP. Addition of metal oxides increased the crystallization temperature of iPP and mainly formed α‐phase due to the heterogeneous α‐nucleation of metal oxides. The α‐nucleation of CaO could be easily changed into β‐nucleation using CaO‐supported PA, and 90.1% β‐phase was obtained. The β‐nucleation of BaO could be markedly enhanced by barium pimelate formed using supported PA. However, no β‐phase was observed for iPP filled with MgO‐ or ZnO‐supported PA. The various metal oxides with supported PA had a different influence on the crystallization behavior and melting characteristics of iPP due to the different structure of metal pimelate formed by chemical reaction between PA and the metal oxides. Copyright © 2012 Society of Chemical Industry     

Crystalline morphology and dynamical crystallization of antibacterial β‐polypropylene composite

The crystalline morphology and dynamical crystallization of antibacterial polypropylene composite and pure polypropylene were investigated via differential scanning calorimeter (DSC), wide angle X‐ray diffraction (WAXD), and real‐time hot‐stage optical microscopy (OM). The results reveal that the crystalline morphology of antibacterial PP composites changes with variations of the crystallization conditions and compositions. The crystalline phase consists of both α‐PP and β‐PP crystals. The content of β‐PP decreases with the increase in antibacterial agent content and cooling rate. With the addition of β‐nucleating agent, the morphologies of all dynamically crystallized antibacterial PP composites show no obvious spherulitic morphology, and the decrease of crystal perfection and the increase of nucleation density of antibacterial PP composite system could be observed. With the increase of antibacterial agent content, the overall crystallization rates of the antibacterial PP composite increase dramatically, while the content of β‐PP in all antibacterial PP composite decrease distinctly under given cooling conditions. These results can be explained by the interruptive effect of antibacterial agent on interactions of β‐nucleating agent components and the obstructing effect of antibacterial agent on the mobility of PP chains in melts. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Melting characteristic and β‐crystal content of β‐nucleated polypropylene/polyamide 6 alloys prepared using different compounding methods

BACKGROUND: The distribution of nucleating agents in different phases is still an open question in general, and how to control conditions to prepare alloys rich in β‐crystals of polypropylene (PP) is hardly reported. The main goal of this study was to find out the factors influencing the β‐crystal content in β‐nucleated PP/polyamide 6 (PA6) alloys and determine the best preparation conditions to obtain β‐nucleated PP/PA6 alloys rich in β‐crystals. RESULTS: The compounding methods had little influence on the crystallization temperature of both PP and PA6. However, the melting characteristic and β‐crystal content in β‐nucleated PP/PA6 alloys not only depended upon the compounding methods, but also on the temperature at which the nucleating agent was added. A higher β‐crystal content can be obtained by adding the nucleating agent at a temperature below 190 °C, which is also dependent on the mixing time. CONCLUSION: It is proved by etching the alloys with sulfuric acid that the nucleating agent mainly disperses in the PA6 phase and/or the interface between PP and PA6 when blended at high temperature. Copyright © 2009 Society of Chemical Industry