扩散退火对热浸镀铝层组织与抗高温氧化性的影响

借助X射线衍射仪(XRD)和环境扫描电镜(SEM/EDAX)对45钢热浸镀铝镀层及其扩散退火处理后的微观组织进行了研究.结果表明,热浸镀铝镀层由铝层和扩散层组成,外层铝层中主要成分为Al和FeAl3,内层扩散层中则主要为Fe2Al5和FeAl3等.扩散退火处理后镀层亦由内外两层组成,外层成分主要为Fe2Al5,内层则主要为FeAl.通过静态氧化增重法研究了45钢热浸镀铝扩散退火后的抗高温氧化性能,结果表明其抗高温氧化性好于未经扩散处理试样,显著优于45钢基体.     

氩弧重熔对球墨铸铁热浸镀铝层组织和性能的影响

将球墨铸铁在780℃热浸镀铝后进行氩弧重熔处理,利用扫描电镜和X射线衍射仪对热浸镀铝层和氩弧重熔层组织进行观察,测定了氩弧重熔前后试件截面的显微硬度。结果表明:球墨铸铁热浸镀铝后,镀层由富铝层及扩散层构成,富铝层包含降温形成的针状FeAl3相,扩散层由FeAl3、Fe2Al5相组成,扩散层形状呈柱状延伸到基体中。热浸镀铝层经氩弧重熔处理后,试件由重熔层和过渡层及基体构成。重熔层由Al、Fe、C和FeAl3相组成,过渡层组织为马氏体+残留奥氏体+少量球状石墨。氩弧重熔处理能明显提高热浸镀铝层的显微硬度。重熔层硬度值可达900 HV,在过渡层硬度下降缓慢,直至基体。     

球铁浸镀微弧氧化陶瓷层的制备与组织分析

通过热浸镀铝及微弧氧化的方法在球墨铸铁表面上获得了陶瓷层,并对该涂层进行了XRD、SEM分析.研究结果表明:浸镀温度越高,镀层越厚,直到达到一峰值;浸镀时间越长,镀层越厚.球墨铸铁浸镀微弧氧化获得的涂层由涂层表面至基体依次为陶瓷层、纯铝层、扩散层、基体.陶瓷层主要为Al2O3相,扩散层由FeAl3、Fe2Al5相组成.     

304不锈钢热浸镀Al-3%Si-0.5%RE工艺及镀层组织研究

采用Al-3%Si-0.5%RE浸镀液,通过改变热浸镀温度与时间、扩渗温度与时间,对304不锈钢进行热浸镀铝工艺研究。借助扫描电镜对镀层组织进行观察,采用EDS及XRD对镀层不同区域进行成分及相分析。结果表明:当浸镀温度740℃,浸镀15 min时,获得铝镀层平均厚度约为100μm;再经820℃扩渗4 h,获得较好的扩渗层,其平均厚度约为115μm。镀层经扩散退火后由表面铝层和扩渗层组成,表面铝层组织主要为Al和少量Al_2O_3相,扩散层组织主要为FeAl、FeAl_3和Fe_2Al_5相。     

园林钢护栏的表面镀层与耐蚀性能研究

对园林钢护栏进行表面热浸镀铝处理,观察热浸镀层的表面和截面形貌,研究扩散退火对镀层形貌、物相、成分和耐腐蚀性能的影响。结果表明,扩散退火前钢护栏表面镀层较为致密、均匀,镀层与基体界面结合良好,未发现有显微裂纹或者孔洞缺陷,外表层为富Al层,次表层为Fe-Al合金层。扩散退火后,表面镀层发生了Fe、Al元素的扩散,镀层表层的氧化物为Al_2O_3,而镀层内层主要为FeAl。经过扩散退火处理后,镀层的耐腐蚀性能明显提高。     

冷轧钢板热浸镀铝层剥落的研究

借助附带能谱分析(EDS)的扫描电镜(SEM)研究了冷轧钢板热浸镀铝过程中的镀层剥落问题,发现镀铝钢板过渡层由靠近基体的Fe2Al5相和靠近纯铝层的FeAl3相组成。对镀层剥落后的表面进行X-射线检测,得出镀层剥落发生在FeAl3与纯铝层接触区域,剥落是由脆性相FeAl3引起的。     

扩散处理热浸镀铝钢高温抗氧化行为的研究

对经不同扩散工艺处理的热浸镀铝层高温抗氧化性进行了研究,通过SEM、TEM、XRD分析了经扩散处理后,热浸镀铝层高温氧化过程中组织结构的变化情况,分析了热浸镀铝层高温抗氧化性能和微观结构的关系,确定了提高热浸镀铝层高温抗氧化性的适宜扩散温度.结果表明,经750℃扩散处理,热浸镀铝层结构由较厚的外表层(Fe2Al5+FeAl2)及内层(FeAl+条状FeAl2)组成,条状FeAl2的形成为氧提供了扩散通道,其抗氧化性较差;经950℃扩散处理,镀层外表层变薄,外表层转为单一FeAl2、内层为FeAl,并出现早期内氧化裂纹,其抗氧化性较差:当扩散处理温度为850℃时,镀层外表层变薄,结构转为FeAl2+少量Fe2Al5,而内层增厚,其结构为FeAl+球状FeAl2,而内层FeAl2球化,增强了氧由内层向基体扩散的阻碍作用,使氧只能逐层形成Al2O3+Fe2O3的氧化膜,提高了镀层的高温抗氧化性.     

扩散处理热浸镀铝钢高温抗氧化行为的研究

对经不同扩散工艺处理的热浸镀铝层高温抗氧化性进行了研究,通过SEM、TEM、XRD分析了经扩散处理后,热浸镀铝层高温氧化过程中组织结构的变化情况,分析了热浸镀铝层高温抗氧化性能和微观结构的关系,确定了提高热浸镀铝层高温抗氧化性的适宜扩散温度.结果表明,经750℃扩散处理,热浸镀铝层结构由较厚的外表层(Fe2Al5+FeAl2)及内层(FeAl+条状FeAl2)组成,条状FeAl2的形成为氧提供了扩散通道,其抗氧化性较差;经950℃扩散处理,镀层外表层变薄,外表层转为单一FeAl2、内层为FeAl,并出现早期内氧化裂纹,其抗氧化性较差当扩散处理温度为850℃时,镀层外表层变薄,结构转为FeAl2+少量Fe2Al5,而内层增厚,其结构为FeAl+球状FeAl2,而内层FeAl2球化,增强了氧由内层向基体扩散的阻碍作用,使氧只能逐层形成Al2O3+Fe2O3的氧化膜,提高了镀层的高温抗氧化性.     

温度对热浸铝及后续扩散中镀层的影响

采用热浸镀铝法在不锈钢表面制备铁铝镀层并分析了镀层的组织结构及其影响因素。结果表明：热浸镀纯铝后,镀层由表面铝层和合金层组成,层间结合紧密,镀层较厚。随浸铝温度的升高,外层铝层减薄,而内层合金层明显增厚,镀层总厚度并没有太大差异,在800℃时镀层质量最为优异。在热扩散实验时,900℃时形成的扩散层质量最佳,为韧性相FeAl固溶体和a-Fe（Al）固溶体,镀层中没有孔洞及裂纹生成,为理想的过渡层材料。     

硅对45钢热浸镀铝层真空扩散处理显微组织的影响

利用扫描电镜和能谱分析手段研究了铝池中的硅对热浸镀铝层在真空高温扩散处理过程中的显微组织演变的影响。确定了扩散层的组成相,研究了镀层的生长动力学,讨论了扩散层空洞带的形成机理。研究表明,铝池中的硅能减少热浸镀铝层的厚度。在同样的扩散条件下硅的添加抑制了Fe2Al5的生长,促进了FeAl和富铝α-Fe层的生长。扩散处理时从含硅的Fe2Al5中容易析出τ1-（Al,Si）5Fe3相或FeAl相。硅的加入使得FeAl层和富铝α-Fe层间的空洞或晶间裂纹易于早期出现,但随着扩散时间的延长,又逐渐减小或消失。空洞的形成与消失与硅在FeAl层中的富聚有关。由于Fe2Al5相与其中析出的τ1-（Al,Si）5Fe3相发生包共晶反应,即：τ1＋Fe2Al5L＋FeAl,形成了不连续的外侧FeAl层。     

Investigation on the influence of the dielectrics on the material removal characteristics of EDM

A systematical and comprehensive investigation of the material removal characteristics of the electrical discharge machining (EDM) process using various dielectrics as the working fluids was conducted in this work. Five dielectrics, including gaseous dielectrics, air and oxygen, and liquid dielectrics, de-ionized water, kerosene and water-in-oil (W/O) emulsion were used as the working fluids. The whole geometry parameters of the craters, including the recast material in the craters, were precisely determined by metallographic method. The volume of melted and removed material and removal efficiency in different dielectrics were comparatively investigated. By relating the material removal characteristics to the evolution of the discharge generated bubbles in different dielectrics which was done by computer simulation, it seems that the pressure above the discharge point is an important factor that can affect material removal characteristics. The results of this work were supposed to be helpful for further clarifying the complicated material removal mechanism of EDM.     

铝防盗盖表面流纹成因的研究

研究了铝防盗盖成型过程中铝板的应力,应变状态和金属流动特征,从理论上和铝板的组织状态方面分析了流纹的成因;同时从铝板表面粗糙度和表面缺陷方面分析了流纹的成因,提出了铝防盗表面流纹的控制方法。     

基于渐进成形的修复体加工实验

板料数控渐进成形工艺是一种柔性成形工艺,这种工艺非常适合加工小批量、多品种和形状复杂的板料产品。以医疗修复体为实验对象,分别采用正成形、负成形工艺在渐进成形专用机床上完成渐进成形加工。针对工具头与支撑体间隙不合理导致零件表面产生挤压痕迹的问题,提出一种基于零件模型的整体偏置方法生成支撑体模型,很好的解决了加工件表面的质量问题。对成形零件变形区厚度及回弹变形进行测量,并对所得数据进行分析。试验结果表明,数控渐进成形中材料厚度变化遵循正弦定律;负成形加工件的厚度误差、回弹量均比有支撑的正成形大,并对影响零件厚度、回弹的主要因素进行了初步分析。     

铸件表面合金化层性能研究

针对采用水玻璃、树脂等作为粘结剂进行铸件表面合金化时，合金层中容易产生气孔、夹渣缺陷的问题，研究了一种铸件表面合金化新工艺，即加入一种YB成型剂将合金粉末压制成块的方法进行表面合金化，在铸钢ZG65Mn本体表面得到高含Cr、W等元素的合金化层。结果表明，通过消失模铸造工艺，使用YB成型剂较好地消除了水玻璃等粘结剂造成的气孔、夹渣，合金化层和本体之间实现了冶金结合；合金化层具有较好的耐磨性和耐热性能，加入WC后耐磨性可达本体材料的4．82倍，抗氧化性能提高50％左右，且合金化粉末压块放置操作简便、可靠。     

氢化锆表面多元复合膜层制备和研究

采用尿素高温分解产生的氧化性气氛在氢化锆表面制备多元复合膜层。利用XRD、SEM、EDS、XPS、AES等分析测试手段对氢化锆表面膜层的相结构、截面形貌、元素成分及价态进行性能表征。物相分析结果表明膜层主要有氧化锆相和Zr N相,且氧化锆相由单斜相(m-ZrO_2)和四方相(t-ZrO_2)组成。扫描电镜形貌分析表明原位生长氧化物膜层致密,膜层与氢化锆基体结合紧密。俄歇电子能谱结果表明膜层由C、N、O、Zr元素组成,并具有明显的分层现象,膜层由外向内分为富(C/N)层及富O层,随膜层表面溅射时间增加,O、Zr元素相对含量明显增加,C、N元素相对含量明显降低。X射线光电子能谱分析表明多元复合膜层存在Zr-O、Zr-C、Zr-N-O、Zr-N、O-H等键。     

配流盘定位设计对强度的影响研究

以轴向柱塞马达配流盘为研究对象,针对不同定位方式对配流盘工作强度进行有限元分析,得到应力分布和变形情况,为高压轴向柱塞马达(泵)配流盘的定位设计提供了参考。     

横向应变对声双折射系数的影响分析

以时基延迟效应为基础的声弹法应力测量,对微小应变都非常敏感。整个加载过程中,横向微小应变引起的时间差会累积到声时检测设备中,给应力定量测量带来很大的误差。采用回振法对45号钢在拉伸和压缩状态下的声双折射现象进行了试验研究。在研究超声波垂直于应力传播过程中,建立了声时差与应力的关系模型,试验证明了该模型的正确性。利用声速与动弹模量及动泊松比之间的关系,引入了横向应变对声双折射系数的修正项。     

磁场对电火花放电通道的影响研究

放电过程中的横向静磁场可使带电粒子受到洛伦兹力而改变运动轨迹,造成工件上放电点的位置变化,进而引起电蚀坑形貌的变化。利用理论方法推算出磁场作用下的电子运动轨迹,得到工件上放电点的理论偏移值,并通过实验证明洛伦兹力改变了放电点的位置。结果表明:部分电蚀坑出现明显的拉长型畸变,放电点沿洛伦兹力方向移动,放电通道在洛伦兹力与工作液阻力的作用下逐渐发生偏移。电蚀坑被拉长后其深度会变浅,大而浅的电蚀坑将有助于提高电火花加工的表面质量。