乳液pH值对乳胶粉及其涂料分散涂膜的影响

采用喷雾干燥法制备可再分散苯丙乳胶粉,探讨喷雾乳液pH值对苯丙乳胶粉及其再分散乳液性能的影响,并分析其作用机理;以不同pH值喷雾乳液制备的乳胶粉为成膜物质配制干粉涂料,研究各涂料样品的施工稳定性,并观察漆膜断面微观形貌.结果表明:随着喷雾乳液pH值增大,乳胶粉的再分散性提高、堆积密度增大,再分散乳液粒径变小,施工稳定性...     

可再分散苯丙乳胶粉的制备与表征

采用半连续种子乳液聚合法,以苯乙烯、丙烯酸丁酯、甲基丙烯酸、甲基丙烯酸甲酯等为主要原料合成了苯丙乳液,并用喷雾干燥法制备了可再分散苯丙乳胶粉.探讨了乳胶粒结构形态、硬单体与软单体配比(St/BA)、喷雾干燥温度对制备可再分散苯丙乳胶粉干燥温度、成膜性、颗粒形态的影响及苯丙乳胶粉改性干混砂浆的结构.结果表明,核壳结构苯丙乳液有利于喷雾干燥;当St/BA为15/61时,苯丙乳胶粉在0 ℃下成膜表面光滑,均匀致密;干燥温度升高,可再分散乳胶粉含水率降低,再分散液粒径减小,成膜性提高.但温度过高(>160℃)或过低(≤100℃)均会使乳胶粒子在干燥过程中形成粒径较大的聚合物颗粒,导致粉体滤渣含量增加,对于苯丙乳液来说,适当的喷雾干燥温度为120～140℃.红外光谱分析表明,在100～160℃下的干燥没有明显改变乳胶粒子的分子结构.SEM分析表明,聚合物乳胶粉在干混砂浆基体中形成了连续的互穿网状膜.     

可再分散乳胶粉的制备与性能表征

分别采用间歇法、平衡溶胀法和半连续法等3种种子乳液聚合工艺制备的纯丙乳液，经喷雾干燥可制得性能良好的可再分散乳胶粉。对不同工艺制备的纯丙乳液进行性能测试并作对比，对制得的可再分散乳胶粉性能进行表征。介绍了该可再分散乳胶粉适宜的喷雾干燥条件。     

防水型可再分散乳胶粉的制备及其性能研究

从乳液体系的稳定性出发,通过HLB值寻求合适的乳化剂比例,制备了一种新型防水型可再分散乳胶粉,并研究了其对砂浆接触角、混凝土吸水量和混凝土强度的影响。采用乳化剂HLB为10时,其乳液稳定,可以长期存放。加入防水型可再分散乳胶粉后,砂浆表面接触角明显增加,混凝土吸水量随之降低,证实了防水型可再分散乳胶粉优异的防水性能;在掺量小于0.3%时,防水型可再分散乳胶粉对混凝土强度无负面影响。     

聚合物改性装饰砂浆的试验研究

通过掺加纤维素醚、可再分散性乳胶粉和环氧树脂乳液改善砂浆保水、粘接性能,配制了低吸水性、高粘接性、防水效果良好的高性能装饰砂浆。当纤维素醚掺量为0.03%;可再分散性乳胶粉为0.6%;环氧树脂乳液为6%,该装饰砂浆可以满足《墙体饰面砂浆》要求,应用于装饰工程。     

可再分散乳胶粉

可再分散乳肢粉水乳液为双相体系，它由分散在水中的微小的聚合物颗粒组成，将这种乳胶状液体加到建筑用水硬产品中可以获得某些特殊性能。简单地说，可再分散乳胶粉就是经过喷雾干燥的乳液。但是并不是所有的乳液都能通过喷雾干燥转化为可再分散乳胶粉，必须是经过特制的乳液，才能生产出可再分散乳胶粉。为成功实现此过程，要在乳液中添加一定量的聚乙烯醇上类的保护性胶体，这样乳胶粉在与水接触时才重新分散成乳液，乳胺粉只有具备良好的可再分散性，才能确保达到最佳的功效。在可分散乳胶粉的生产过程中，一个目标就是要确保在分散的乳…     

阳离子型单体DMC对苯丙乳液合成及性能的影响

采用种子乳液聚合法,以苯乙烯(St)、丙烯酸丁酯(BA)、甲基丙烯酸甲酯(MMA)等为主要单体,分别以十六烷基三甲基溴化铵(CTAB)及偶氮二异丁眯盐酸盐(AIBA)为乳化剂和引发剂,并引入功能型阳离子单体甲基丙烯酰氧乙基三甲基氯化铵(DMC)及功能单体丙烯酰胺(AM),合成了刚离子型核壳苯丙乳液.研究表明,合成的阳离子苯丙乳液共聚物的核层玻璃化温度Tg约为-17℃(理论值为-27℃),壳层Tg约为65℃(理论值为77℃);所得聚合物的核壳界面上可能存在具有一定相容性的均聚物聚合物链段扩散,相互贯穿,使聚合物核层与壳层之间Tg的差值比理论值小.TEM照片显示,乳胶粒子呈明显的核壳结构,乳液中加入DMC后对乳胶粒子的核壳结构形态有一定的影响.随着DMC及AM用量的增大,阳离子苯丙乳液的粒径和黏度增大,乳胶粒的ξ电位先增大后减小.当DMC用量为单体总量的2%时,乳液体系的ξ电位最高,为45.1 mV,乳液体系稳定.     

聚合物乳胶粉水分散性影响机理的研究进展

可再分散聚合物乳胶粉是一种绿色环保、便于运输和贮存的新型粉体功能材料.介绍了可再分散聚合物乳胶粉在建筑材料中的强化作用机理,综述了母乳液功能性单体、乳液粒子结构、喷雾液预处理、保护胶体、喷雾干燥温度、雾化器转速和进料速度对聚合物乳胶粉水再分散性的影响机理,并阐述了乳胶粉研究现状及展望.     

可再分散乳胶粉性能影响因素探讨及应用

讨论了可再分散乳胶粉制备过程中乳液合成阶段单体和功能性单体选择、乳胶粒设计和干燥阶段进出口温度、雾化器转速、保护胶体等因素对可再分散乳胶粉性能的影响,并阐述了可再分散乳胶粉的发展和应用.     

可再分散性乳胶粉用醋叔乳液的制备研究

合成了稳定的可用于制备可再分散性乳胶粉的醋叔乳液.讨论了乳化剂、保护胶体、共聚单体、引发剂等对乳液聚合及其性能的影响,并确定了合适的生产工艺.用该工艺生产的醋叔乳液固含量高、黏度低、柔韧性好,初粘性、快干性和耐水性均较常规产品有明显提高.     

Evaluation of low-VOC latex paints

Four commercially available low-volatile organic compound (VOC) latex paints were evaluated as substitutes for conventional latex paints by assessing both their emission characteristics and their performance as coatings. Bulk analysis indicated that the VOC contents of all four paints tested were considerably lower than those of conventional latex paints. Low VOC emissions were confirmed by small chamber emission tests. However, significant emissions of several aldehydes, especially formaldehyde which is a hazardous air pollutant, were detected in emissions from two of the four paints. American Society for Testing and Materials (ASTM) methods were used to evaluate the hiding power, scrub resistance, washability, dry to touch and yellowness index. The results indicated that one of the four low-VOC paints tested showed performance equivalent or superior to that of a conventional latex paint used as control. It was concluded that low-VOC latex paint can be a viable option to replace conventional latex paints for prevention of indoor air pollution. However, paints marketed as "low-VOC" may still have significant emissions of some individual VOCs, and some may not have performance characteristics matching those of conventional latex paints.     

天然乳胶对乳胶海绵气体产生规律的影响

运用顶空-气质联用法测定20NR、80NR的乳胶海绵在不同温度下以及燃烧后残渣在固定温度下挥发性气体成分,并对其产生规律进行分析。加热炉设定温度50、80、120、120 ℃,加热时间为30 min。结果表明：80 ℃时天然乳胶含量为80NR的乳胶海绵产生的挥发性气体种类比20NR的多。120 ℃时,虽然挥发性气体种类数量相同,但80NR的挥发性气体更为复杂。同种天然乳胶含量的乳胶海绵产生的挥发性气体种类会随着温度的增加而增加。除乳胶80NR在50 ℃时未检测到Si大于90的化合物,其他均能检测到二硫化碳、正十一烷、十二碳烷这三类有一定毒性的挥发性气体。     

乳胶漆对比率的测定

对比率是乳胶漆的一项重要性能指标,本文就乳液漆对比率测定过程中应注意的问题做了一些探讨和试验。     

聚合物乳液的成膜

在乳液成膜过程中，毛细管力起辅助作用，本文对这些年来的理论模型进行综述。由于水面的消退形成的力是主要的驱动力，毛细管液体桥力作用较差，环境相对湿度（RH）对这些力无影响。利用光透射技术，研究了温度和湿度对无表面活性剂丁基丙烯酸酯乳液的成膜的影响。在稍低于Tg的温度下可以成功成膜，若假设水是一种溶剂，RH仅轻微促进涂膜的形成。本文对助溶剂在促进涂膜形成中的浓度影响进行了证实。     

彩色有机硅丙烯酸酯乳液的合成

采用聚合方法合成丙烯酸酯乳液,利用有机硅对丙烯酸酯乳液进行改性,并通过用含有—NH2的单体与颜料分子中的—Cl进行反应,通过化学反应直接将颜料分子接入到聚合物链中,从而可得到彩色的硅丙乳液。研究了单体的选择、丙烯酰胺加入方式、丙烯酰胺加入量、颜料加入方式、颜料加入量等对合成彩色乳液的影响,找出了合成彩色硅丙乳液的最佳参数。该乳液具有粘结性强、成膜性好、耐水擦洗、耐光照等性能,具有优异的保色性能,可克服传统工艺颜料分散困难、色泽不自然、易褪色等缺陷。     

新加坡SS 345抗藻型乳胶漆涂料

近年来新加坡的一些大型房地产开发集团陆续进军中国市场,在中国开发的楼盘遵循新加坡的习惯全部采用乳胶漆装饰外墙,这些公司在选择外墙涂料供应商时会提出外墙乳胶漆是否符合新加坡SS345涂料标准。另外,在我国华南地区,由于地理气候条件与新加坡相似,不少业主、设计师通过到新加坡考察也了解到SS345标准即抗藻型乳胶漆涂料标准在新加坡的应用。     

有机硅改性丙烯酸乳液技术研究进展

综述了近几年来有机硅改性丙烯酸乳液研究的新进展,着重介绍了有机硅单体、乳化体系、聚合工艺对乳液聚合及涂膜性能的影响.     

乳液涂料中表面活性剂的研究进展

本文综述了近年来国内外有关聚合物乳液以及乳液涂料中表面活性剂（主要是乳化剂）的研究与发展动向，论述了乳化剂在聚合物乳液和乳液型涂料体系中的作用、表面活性剂在涂料组分中的竞争吸附现象，介绍了新型反应性表面活性剂的开发和应用。     

丙烯酸乳液改性瓷砖粘结剂的研究

瓷砖粘结剂是一种高品质聚合物改性水泥基复合材料,由于采用多种高性能添加剂,能够有效增强瓷砖与基材之间的粘结强度,减少收缩,从根本上克服传统水泥砂浆作粘结材料时存在的瓷砖开裂、脱落等弊端。本文结合目前应用较广泛的“苯板加一层（或两层）玻璃网格布外贴瓷砖”外墙外保温体系,通过压折试验、粘结拉伸试验,对外保温外贴瓷砖在受水平拉应力的条件下的破坏界面进行观察,了解瓷砖饰面的安全性。通过一系列试验,水泥砂浆、水泥砂浆加聚合物进行比较,得出试验结论。     

聚苯乙烯乳液包膜膨胀珍珠岩的研制

将废聚苯乙烯泡沫制成乳液,用包衣机将其包膜在膨胀珍珠岩表面,形成一层柔性的聚合物膜,达到膨胀珍珠岩闭孔的效果,可有效地改善膨胀珍珠岩的吸水性,提高膨胀珍珠岩的强度,解决了闭孔膨胀珍珠岩在运输途中易破碎的问题。