TA15钛合金的高周疲劳性能和断裂特征

研究了双态组织的TA15钛合金的高周疲劳性能和疲劳断裂特征,结果表明,β转变组织中次生α相的数量和形态对疲劳性能有显著影响,次生相α相的球化显著降低了合金抗裂纹扩展的能力,而大量的片状次生α相则通过造成疲劳裂纹的分枝有效地降低了疲劳裂纹的扩展速度,提高了疲劳极限.     

Ti—15—3钛合金的疲劳断裂行为研究

研究了Ｔｉ－１５－３合金板材光滑和缺口疲劳及疲劳裂纹萌和方式，发现光滑疲劳试样裂纹多起源于板材原始表面，形成面源；面具有中心孔和边缺口试样的疲劳裂纹多起源于缺口处的机加工端面，形成角源的线源。而且５２０℃时效后所获得的板材的拉伸强度是比５４０℃时效的高７３ＭＰａ，但疲劳极限差别不大。     

TNM-Ti Al合金室温高周疲劳性能研究

采用升降法与成组法对TNM-TiAl合金试样进行了应力比R=-1的室温拉压疲劳和R=0.1的室温拉伸疲劳试验,得到TNM-TiAl合金的P-S-N曲线,并对断口进行了分析。结果表明:TNM-TiAl合金对应力十分敏感,R=-1和R=0.1时的曲线整体呈较为平直的斜线,R=-1时的疲劳极限为414.7 MPa,R=0.1时的疲劳极限为285.6 MPa。R=0.1的S-N曲线远低于R=-1的S-N曲线;R=-1时,应力幅与疲劳寿命的关系满足Basquin方程。疲劳试件宏观断口较为粗糙,静态拉伸宏观断口平整,两者差异较大。拉伸断口整体分为裂纹萌生区与扩展区,其中起裂源均位于试样表面或板状试件的边角棱线处,起裂源区域包括γ相的解理断裂面、片层团的沿层解理面以及β₀相平整的穿晶断裂平面等特征。疲劳断口整体分为裂纹萌生区、扩展区与瞬断区,其中裂纹萌生区分为表面沿层起裂和γ相起裂。TNM-TiAl合金的疲劳断裂为脆性断裂,主要体现在扩展区上大量的片层团穿层断裂、扭折撕裂、γ相解理断裂和β₀相穿晶断裂。同寿命量级下,R=-1的断口与R=0.1的断口断裂类型...     

锻造火次对TB6钛合金断裂韧性和高周疲劳性能的影响

研究了在相同开坯锻造工艺,相同改锻温度下,不同锻造火次对TB6合金Ф220 mm规格锻棒的断裂韧性和高周疲劳性能的影响。通过SEM电镜观察了不同锻造火次锻棒高周疲劳试样的宏观、微观断口,分析了不同火次疲劳试样断口的不同区域的形貌。结果表明,在相同锻造温度下,20火次锻棒的组织均匀,断裂韧性、高周疲劳性能有较佳的匹配。     

一种近α型钛合金Ti—8Al—1Mo—1V的研究

本文研究了Ti-8Al-1Mo-1V近α型钛合金的熔炼工艺,锻造工艺和热处理工艺。等轴组织具有良好的室、高温拉伸强度、塑性和适当的高温蠕变抗力,并具有优良的冲击韧性。双态组织和网蓝组织的综合性能则次之。但塑性和冲击韧性最差。     

Ti3Al＋11Nb合金的氧化有Nb的作用

用光学金相、扫描电镜、Ｘ射线衍射仪、电子探针等方法对Ｔｉ３Ａｌ＋１１Ｎｂ合 高温氧化后的表面状况、断口形貌、显微组织、氧化层结构、元素支中的分布等氧化特征进行分析，并讨论了Ｎｂ对该合金抗氧化性能的影响。     

一种单晶高温合金的高周疲劳行为

本文对一种单晶高温合金在℃经高周疲劳实验的断裂特征和微观变形机制进行了详细研究，发现该单晶合金存在两种断形貌，一种是定向解理断裂，一种是蜂窝状撕裂，这两种断裂方式分别与按确定取向的滑移变形机制和位错胞变形机制相联系。还观察到了小角晶界的变形机制，合金中存在的极微量ＭＣ碳化物仍然是重要的疲劳源，该单晶高温合金的高周疲劳强度极限较之相应的铸造ＩＮ７３８合金和低偏析定向凝固ＤＥ３８Ｇ合金大幅度提高。     

Ti—33Al—3Cr—0.5Mo合金非平衡组织转变

采用光学金相显微镜和透射电子显微镜，研究了经过１０４０℃，３１０＾４Ｓ＾－１，８２６％等温锻造的６ｉ－３３Ａｌ－３Ｃｒ－０．５Ｍｏ合金在α＋β两相区加热时，发生的显微组织转变。发现，当热变形是在α２／γ层片状晶团内的γ相板条上形成与层片方面平行的变形享晶时，即发生γ相板条窄化现象，这种晶财则表现出高的显微组织结构的热稳定性。     

渗氢对Ti-25Al-10Nb-3V-1Mo锻态合金显微组织的影响

对锻态Ti-25Al-10Nb-3V-1Mo合金进行了渗氢处理,研究了渗氢引起的合金显微组织的变化.实验结果表明,渗氢前的合金由α2相,O相和B2相组成,渗氢有效地促进α2相和B2相向O相的转变,且使O相组织中有γ氢化物析出.渗氢引起合金组织发生变化的本质原因是氢导致α2相和B2相的晶格畸变,以及α2相和B2相之间的元素再分配.     

Ti-15Mo-2.7Nb-3Al-0.2Si高强钛合金的相变

利用透射、扫描电镜及Ｘ－射线衍射分析较系统地研究了Ｔｉ－１５Ｍｏ－２．７Ｎｂ－３Ａｌ－０．２Ｓｉ钛合金中亚稳β相在时效过程中的分解特性,并建立了相应的时效动力学转变图。研究结果表明,在５００℃以上时效,β相直接析出次生α相,该温度以下,先析出ω过渡相,再逐步过渡到平衡α相。最后,对该合金的时效硬化效应及硅化物沉淀特性也进行了讨论。     

Hydrogen Effects on the Mechanical Properties of Ti-24Al-11Nb-3V-1Mo Alloy

The effects of hydrogen on the mechanical properties at room temperature of a Ti3Al based alloy Ti-24Al-11Nb-3V-1Mo have been investigated. The results show a parabolic rate relationship between the average hydrogen concentration of the alloy at constant temperature and charging time. The mechanical properties (ultimate bending strength and deflection) decrease with increasing hydrogen content in the alloy. The fractographic feature indicates that the decrease of the mechanical properties is due to the crack nucleation and propagation at the hydride Ti3AIH     

Superplasticity of a Ti-24Al-14Nb-3V-0.5Mo Intermetallic Alloy

Superplastic properties and microstructural evolution of a Ti-24Al-14Nb-3V-0.5Mo (at. pct) intermetallic alloy were studied. Optimum superplastic properties were obtained for temperatures in the interval 960℃≤5 T≤5980℃. The apparent activation energy in the superplastic regime was determined and the deformation mechanism was also discussed. Based on the studies, a curve panel with three sheets sandwich structure was fabricated successfully. The microstructures corresponding to different strain in the part were also studied.     

Ti-6Al-3Nb-2Zr-0.8Mo合金的焊接性评价

针对Ti 6Al 3Nb 2Zr 0.8Mo合金及其配套焊接材料,通过大量的试验研究,对其焊接工艺性能、焊接接头的抗裂性能、常规力学、断裂力学、应力腐蚀性能等进行了评价。结果表明:Ti 6Al 3Nb 2Zr 0.8Mo合金焊接性能优良,是一种优良的船用结构钛合金。     

基于TiH2原料的粉末冶金Ti-6Al-3Nb-2Zr-1Mo合金的组织与性能研究

目的 研究烧结工艺对Ti-6Al-3Nb-2Zr-1Mo合金组织演变及力学性能的影响.方法 以TiH2粉末为原料,采用粉末冶金工艺制备低成本高性能的Ti-6Al-3Nb-2Zr-1Mo合金,分析合金在不同烧结条件下组织与性能的变化规律.结果 TiH2的脱氢温度区间集中在450～700℃;Ti-6Al-3Nb-2Zr-1...     

Texture Evaluation of α_2 Phase in Ti-25Al-10Nb-3V-1Mo Alloy Sheet

The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {0001}(1210) textures a {1210}(1010) texture and a {0001}(uvtw)fibre texture are formed after cold rolling. The {0001} (1210) texture is also strengthened simultaneously. The activation process of slip systems is discussed concerning formation of the rolling texture. Because of the disappearance of {0001} (nvtw) fibre texture the primary recrystallization process should occur and the {1210}(1010) texture forms during annealing     

载荷频率对金属及其合金高周疲劳特性的影响

采用超声高频加载方法进行高周疲劳试验时,应考察载荷频率对材料疲劳特性的影响。本文从微观组织结构和外部环境两方面论述了疲劳特性的频率效应,从裂纹扩展率、断口分析等方面回顾和介绍了频率对合金钢、钛合金、铝合金三类常用金属疲劳特性的影响,比较了三者异同。最后展望了高周和超高周疲劳研究的方向和方法及其在工程中的应用。     

MB8镁合金高周疲劳实验研究

采用升降法对MB8镁合金室温高周疲劳行为进行实验研究。结果表明:利用升降法计算出MB8镁合金在应力比R=0.1,循环基数为107条件下的疲劳强度为90.2MPa,相当于其抗拉强度的34%左右;合金的疲劳裂纹萌生于试样表面,裂纹扩展区由小的平面状断面组成,没有明显的疲劳辉纹存在,合金疲劳断口呈现韧性断裂特征。