Homogeneous complex solution formed through interactions of poly(acrylamide‐co‐acrylic acid)/poly(acrylamide‐co‐dimethyldiallylammonium chloride) complex with M n+ hydration metal ions in aqueous media

A homogeneous complex solution, formed through inter‐polyelectrolyte complexation of poly(acrylamide‐co‐acrylic acid) (P(AM‐AA)) with poly(acrylamide‐co‐dimethyldiallylammonium chloride) (P(AM‐DMDAAC)) and interaction of the P(AM‐AA)/P(AM‐DMDAAC) complex with M ⁿ⁺ hydrated metal ion, was prepared and the structure and properties of the P(AM‐AA)/P(AM‐DMDAAC)/M ⁿ⁺ homogeneous complex solution were studied by UV spectrometry, dynamic light scattering and viscometry. The experimental results show that the homogeneous complex solution can be obtained by controlling the composition of the P(AM‐AA)/P(AM‐DMDAAC) complex and the M ⁿ⁺ metal ion content. Compared to the constituents, ie the P(AM‐AA) solution, the P(AM‐DMDAAC) solution and the P(AM‐AA)/P(AM‐DMDAAC) complex solution, the P(AM‐AA)/P(AM‐DMDAAC)/M ⁿ⁺ complex solution has a new peak at 270 nm in its UV spectrum, a larger hydrodynamic radius, and hence a higher solution viscosity, all of which indicate that there exist specific interactions between polymers and M ⁿ⁺ metal ions. These interactions lead to the formation of a network structure and hence an obvious increase not only in solution viscosity but also in resistance of the polymer solution to simple salts, to temperature changes and to shearing. © 2001 Society of Chemical Industry     

Synthesis and characterization of acrylamide‐based aluminum flocculant for turbidity reduction in wastewater

Polymeric flocculants of aluminum hydroxide‐poly[acrylamide‐co‐(acrylic acid)], AHAMAA, were prepared by solution polymerization using aluminum hydroxide as a coagulant in the presence of acrylamide (AM) and acrylic acid (AA) as a comonomer pair with N,N′‐methylenebisacrylamide as a crosslinking agent. The crosslinking was initiated by ammonium persulfate with N,N,N′,N′‐tetramethylethylenediamine as an initiator. The water absorbency of crosslinked poly[AM‐co‐AA] was always higher than that of AHAMAA and was found to be correlated to the storage modulus of the polymers, which was higher for AHAMAA than that of crosslinked poly[AM‐co‐AA]. The residual aluminum concentration of AHAMAA (0.09–0.2 mg L^?1) indicated the stability of the polymer flocculant which was in good agreement with the observed tan δ and the higher G′′ and G′ values. Both the crosslinked poly[AM‐co‐AA] and AHAMAA satisfactorily reduced the turbidity of kaolin suspensions, but the latter gave a better reduction performance. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Synthesis and characterization of novel poly(acrylamide‐co‐acrylic acid‐co‐2‐hydroxy ethyl actylate) hydrogels: Mathematical approach in investigation of swelling kinetics and diffusion models

In this study, a series of poly(acrylamide‐co‐acrylic acid‐co‐2‐hydroxy ethyl actylate) [AM‐co‐AA‐co‐HEA] hydrogels have been synthesized by varying the acrylic acid (AA)content over eightfold in feed in the range of 33.34–93.76% by keeping other monomer constant. These hydrogels were characterized by FTIR, SEM analysis, elemental analysis, residual acrylic acid analysis, network parameters, and dynamic swelling behavior. The swelling study showed that equilibrium swelling ratio was nonlinearly increased with increasing AA content. Interestingly, the equilibrium swelling ratio decreased from 53.42 to 48.52 for 75–80% AA content hydrogel. The swelling data were found to satisfactorily fit Fick's second law, demonstrating that diffusion rate of water uptake was primarily Fickian. From model fitting, it was observed that early model was applicable for first 30% water absorption, and late model was applicable for latter 70% water absorption for increasing AA content from 33.34–90.90%. For 93.76% AA, early‐time model was extended up to first 50% of water absorption and late model was contracted for latter 50% water absorption, indicating that excessive AA content affects the applicability range of early‐time and late‐time diffusion models for water absorption. Etters model was best applicable to all type of hydrogels and followed over all swelling range. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Multilayer‐coated NPK compound fertilizer hydrogel with controlled nutrient release and water absorbency

A novel trilayered controlled‐release nitrogen, phosphorous, and potassium (NPK) fertilizer hydrogel was prepared by dipping the NPK fertilizer granules sequentially in 7% w v^?1 poly(vinyl alcohol) (PVA) and 2% w v^?1 chitosan (CS) solutions and then cross‐linking the CS layer (cross‐CS) via glutaraldehyde vapor deposition. Different NPK fertilizer hydrogels were then synthesized by inverse suspension polymerization of the dried PVA/cross‐CS bilayer‐coated fertilizer granules in various molar ratios of acrylamide (AM) and acrylic acid (AA) monomers, and polymerization with varying molar ratios of ammonium persulfate, N,N,N′,N′‐tetramethylethylenediamine and N,N′‐methylenebisacrylamide (N‐MBA). The water dissolution time of the obtained PVA/cross‐CS/poly (AA‐co‐AM) trilayer‐coated NPK fertilizer hydrogel granules was prolonged, while the water absorbency increased with increasing AA contents, and decreased with increasing N‐MBA contents in the outer poly(AA‐co‐AM) coating. The optimal trilayer‐coated NPK fertilizer hydrogel obtained released 84 ± 18, 63 ± 12, and 36 ± 15% of the N, P, and K nutrients, respectively, after a 30‐day immersion in water. The release phenomena of the N, P, and K nutrients of the fertilizer hydrogel obeyed both the Korsmeyer‐Peppas and Ritger‐Peppas models with a pseudo‐Fickian diffusion mechanism. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41249.     

Synthesis and properties of carboxymethyl cellulose‐graft‐poly(acrylic acid‐co‐acrylamide) as a novel cellulose‐based superabsorbent

A new cellulose‐based superabsorbent polymer, carboxymethyl cellulose‐graft‐poly(acrylic acid‐co‐acrylamide), was prepared by the free‐radical grafting solution polymerization of acrylic acid (AA) and acrylamide (AM) monomers onto carboxymethyl cellulose (CMC) in the presence of N,N′‐methylenebisacrylamide as a crosslinker with a redox couple of potassium persulfate and sodium metabisulfite as an initiator. The influences of reaction variables such as the initiator content, crosslinker content, bath temperature, molar ratio of AA to AM, and weight ratio of the monomers to CMC on the water absorbency of the carboxymethylcellulose‐graft‐poly(acrylic acid‐co‐acrylamide) copolymer were investigated. The copolymer's structures were characterized with Fourier transform infrared spectroscopy. The optimum reaction conditions were obtained as follows: the bath temperature was 50°C; the molar ratio of AA to AM was 3 : 1; the mass ratio of the monomers to CMC was 4 : 1; and the weight percentages of the crosslinker and initiator with respect to the monomers were 0.75 and 1%, respectively. The maximum water absorbency of the optimized product was 920 g/g for distilled water and 85 g/g for a 0.9 wt % aqueous NaCl solution. In addition, the superabsorbent possessed good water retention and salt resistance. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 1382–1388, 2007     

Improving properties of superabsorbent composite induced by using alkaline protease hydrolyzed‐sericin (APh‐sericin)

A series of superabsorbent polymer composites based on sericin hydrolyzed with alkaline protease (AP) were prepared by grafting with acrylic acid (AA) and acrylamide (AM). The properties of the superabsorbent polymers (SAP) by using hydrolyzed sericin with different amount of alkaline protease (nAPh‐sericin) were compared. It was found that the polymer prepared from 5APh‐sericin (the mass ratio of AP to sericin was 5.0 mg g⁻¹) showed the highest graft percentage and water absorbency, this phenomenon may be attributed to the change of molecular weight of resulting sericin molecules. The molecular structure of the grafted polymers was proved by thermal gravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) measurements. Comparing with PAA‐AM (poly AA‐co‐AM) and 0APh‐sericin/PAA‐AM polymer, 5APh‐sericin/PAA‐AM polymer had the most excellent water retention capacity and enzyme degradability. The morphological features of the polymers with different drying methods were evidenced by SEM images. The water absorbencies of 5APh‐sericin/PAA‐AM polymer prepared with freeze‐drying were 896 g g⁻¹ in deionized water, 424 g g⁻¹ in tap water, and 83 g g⁻¹ in 0.9 wt% aqueous NaCl solution. POLYM. COMPOS., 35:509–515, 2014. © 2013 Society of Plastics Engineers     

Syntheses,characterization, and antibacterial activity of chitosan grafted hydrogels and associated mica‐containing nanocomposite hydrogels

Chitosan (CS) grafted poly[(acrylic acid)‐co‐(2‐hydroxyethyl methacrylate)] (CS‐g‐poly(AA‐co‐HEMA)) at different molar ratios of AA and HEMA, and the associated nanocomposite hydrogels of CS‐g‐poly(AA‐co‐HEMA)/mica were synthesized by radical copolymerization. The grafting positions at the amino or hydroxyl groups in the CS were identified by Fourier transform infrared spectroscopy. CS‐g‐poly(AA‐co‐HEMA) hydrogels were intercalated in the mica and the amount of hydrogel insertion did not affect the spacing of the silicate layers in mica. The higher mica loadings produced a rougher surface of the nanocomposite hydrogel. The water absorbency of the CS‐g‐poly(AA‐co‐HEMA)/mica nanocomposite hydrogels decreased with increasing levels of mica loading to a lower level than those of the CS‐g‐poly(AA‐co‐HEMA) hydrogels. Both CS‐g‐poly(AA) and CS‐g‐poly(AA‐co‐HEMA)/mica nanocomposite hydrogels exhibited a higher antiproliferative activity against Staphylococcus aureus than did the neat CS hydrogel with CS‐g‐poly(AA) revealing a very pronounced minimum inhibition concentration (MIC) of 1.56 mg mL^?1. The extent of mica loading in the CS‐g‐poly(AA‐co‐HEMA) nanocomposite hydrogels did not affect the MIC (12.5 mg mL^?1). © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Synthesis and biological activity of medium molecular weight polymers containing 3,6‐endo‐methylene‐1,2,3,6‐tetrahydrophthalimidobutanoyl‐5‐fluorouracil

A new monomer, 3,6‐endo‐methylene‐1,2,3,6‐tetrahydrophthalimidobutanoyl‐5‐fluorouracil (ETBFU), was synthesized by reaction of 3,6‐endo‐methylene‐1,2,3,6‐tetrahydrophthalimidobutanoyl chloride and 5‐fluorouracil. The homopolymer of ETBFU and its copolymers with acrylic acid (AA) or vinyl acetate (VAc) were prepared by photopolymerization using 2,2‐dimethoxy‐2‐phenylacetophenone as an initiator at 25 °C. The synthesized ETBFU and its polymers were identified by FTIR, ¹H NMR and ¹³C NMR spectroscopies. The ETBFU content in poly(ETBFU‐co‐AA) and poly(ETBFU‐co‐VAc) was 43 and 14 mol%, respectively. The apparent number‐average molecular weight (M_n) of the polymers determined by GPC ranged from 8400 to 11 300. The in vitro cytotoxicity of the samples against mouse mammary carcinoma (FM3A), mouse leukaemia (P388), and human histiocytic lymphoma (U937) cancer cell lines decreased in the order 5‐FU ≥ ETBFU > poly(ETBFU) > poly(ETBFU‐co‐AA) > poly(ETBFU‐co‐VAc). The in vivo antitumour activity of the polymers against Balb/C mice bearing sarcoma 180 tumour cells was greater than that of 5‐fluorouracil at all doses tested. © 2000 Society of Chemical Industry     

Investigation of charge transport properties in conducting copolymers of aniline with 3‐aminobenzenesulfonic acid for their applications as antistatic encapsulation materials blended with low‐density polyethylene

The electrostatic charge dissipative (ESD) properties of conducting self‐doped and PTSA-doped copolymers of aniline (AA), o‐methoxyaniline (methoxy AA) and o‐ethoxyaniline (ethoxy AA) with 3‐aminobenzenesulfonic acid (3‐ABSA) blended with low‐density polyethylene (LDPE) were investigated in the presence of external dopant p‐toluenesulfonic acid (PTSA). Blending of copolymers with LDPE was carried out in a twin‐screw extruder by melt blending by loading 1.0 and 2.0 wt% of conducting copolymer in the LDPE matrix. The conductivity of the blown polymers blended with LDPE was in the range 10^?12–10^?6 S cm^?1, showing their potential use as antistatic materials for the encapsulation of electronic equipment. The DC conductivity of all self‐doped homopolymers and PTSA‐doped copolymers was measured in the range 100–373 K. The room temperature conductivity (S cm^?1) of self‐doped copolymers was: poly(3‐ABSA‐co‐AA), 7.73 × 10^?4; poly(3‐ABSA‐co‐methoxy AA), 3.06 × 10^?6; poly(3‐ABSA‐co‐ethoxy AA), 2.99 × 10^?7; and of PTSA‐doped copolymers was: poly(3‐ABSA‐co‐AA), 4.34 × 10^?2; poly(3‐ABSA‐co‐methoxy AA), 9.90 × 10^?5; poly(3‐ABSA‐co‐ethoxy AA), 1.10 × 10^?5. The observed conduction mechanism for all the samples could be explained in terms of Mott's variable range hopping model; however, ESD properties are dependent upon the electrical conductivity. The antistatic decay time is least for the PTSA‐doped poly(3‐ABSA‐co‐AA), which has maximum conductivity among all the samples. © 2013 Society of Chemical Industry     

Preparation of acrylamide‐based poly‐HIPEs with enhanced mechanical strength using PVDBM‐b‐PEG‐emulsified CO2‐in‐water emulsions

Poly(vinyl acetate‐alt‐dibutyl maleate)‐block‐poly(ethylene glycol) (PVDBM‐b‐PEG) copolymers were synthesized via reversible addition–fragmentation chain transfer radical polymerization and used as emulsifiers to form stable CO₂‐in‐water high internal phase emulsions (C/W HIPEs). Then, highly interconnected cellular polyacrylamide (PAM) and poly(acrylamide‐co‐N‐hydroxymethyl acrylamide) [P(AM‐co‐HMAM)] poly‐HIPEs with enhanced mechanical strength were prepared based on the stable C/W HIPEs. The porous structures of the PAM poly‐HIPEs, as well as morphology and compressive modulus, could be influenced by the surfactant concentration and the length of the CO₂‐philic tails of the surfactants. PAM poly‐HIPEs with the smallest average pore diameter (11.12 ± 0.62 μm) and the highest compressive modulus (22.65 ± 0.10 MPa) could be obtained by using the short CO₂‐philic chains of the PVDBM‐b‐PEG surfactant at a high concentration (1.0 wt %). Moreover, with the copolymerization of N‐hydroxymethyl acrylamide (HMAM) comonomers with acrylamide, the compressive modulus of the obtained P(AM‐co‐HMAM) poly‐HIPEs was three times higher than that of PAM poly‐HIPEs. Both PAM and P(AM‐co‐HMAM) poly‐HIPEs were employed as scaffolds to guide H9c2 cardiac muscle cellular growth. Fluorescence images showed that a smaller average pore size and a narrower pore‐size distribution were helpful for cell growth and proliferation on these materials. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46346.     

Preparation and thermal response behavior of poly(N‐isopropylacrylamide‐co‐a crylic acid) microgels via soap‐free emulsion polymerization based on AIBN initiator

Poly(N‐isopropylacrylamide‐co‐acrylic acid) (poly(NIPAM‐co‐AA)) microgels with different copolymer compositions were prepared through soap‐free emulsion polymerization at 80°C, and 2, 2′‐azobisisobutyronitrile (AIBN) was used as initiator. Scanning electron microscope (SEM) characterization shows that the prepared microgels are regular and smooth and not easy to distort. Result of ¹H‐NMR characterization shows that with increasing of the initial concentration of AA (AA in feed), the AA content in polymer chains increases. The thermal response of microgels latex was investigated by UV‐3010 spectrophometer through detecting the transmittance of the latex at different temperature in the range of 190–900 nm. The thermal response of the poly(NIPAM‐co‐AA) microgels was tested by dynamic light scattering (DLS). The results show that with the increase of AA content in polymer chains, the low critical solution temperature (LCST) of microgels latex first decreases and then increases. Still, with increasing of AA in poly(NIPAM‐co‐AA) microgels, the LCST of microgels first increases and then decreases. The basic reasons causing the changes of LCST of microgels latex and microgels are interpreted clearly in this article from the perspective of hydrogen bonding interaction. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and biological activity of phthalimide‐based polymers containing 5‐fluorouracil

The attachment of anticancer agents to polymers is a promising approach towards reducing the toxic side‐effects and retaining the potent antitumour activity of these agents. A new tetrahydrophthalimido monomer containing 5‐fluorouracil (ETPFU) and its homopolymer and copolymers with acrylic acid (AA) and with vinyl acetate (VAc) have been synthesized and spectroscopically characterized. The ETPFU contents in poly(ETPFU‐co‐AA) and poly(ETPFU‐co‐VAc) obtained by elemental analysis were 21 mol% and 20 mol%, respectively. The average molecular weights of the polymers determined by gel permeation chromatography were as follows: M_n = 8900 g mol^?1, M_w = 13 300 g mol^?1, M_w/M_n = 1.5 for poly(ETPFU); M_n = 13 500 g mol^?1, M_w = 16 600 g mol^?1, M_w/M_n = 1.2 for poly(ETPFU‐co‐AA); M_n = 8300 g mol^?1, M_w = 11 600 g mol^?1, M_w/M_n = 1.4 poly(ETPFU‐co‐VAc). The in vitro cytotoxicity of the compounds against FM3A and U937 cancer cell lines increased in the following order: ETPFU > 5‐FU > poly(ETPFU) > poly(ETPFU‐co‐AA) > poly(ETPFU‐co‐VAc). The in vivo antitumour activities of all the polymers in Balb/C mice bearing the sarcoma 180 tumour cell line were greater than those of 5‐FU and monomer at the highest dose (800 mg kg^?1). © 2002 Society of Chemical Industry     

Fluconazole release through semi‐interpenetrating polymer network hydrogels based on chitosan,acrylic acid,and citraconic acid

Semi‐interpenetrating polymer network hydrogels with different compositions of chitosan (Cs), acrylic acid, and citraconic acid were synthesized via free‐radical polymerization with ethylene glycol dimethacrylate as a crosslinker. The variations of the swelling percentages of the hydrogels with time, temperature, and pH were determined, and Cs–poly(acrylic acid) (PAA) hydrogels were found to be most swollen at pH 7.4 and 37°C. Scanning electron micrographs of Cs–PAA and Cs–P(AA‐co‐CA)‐1 (Cs‐poly(acrylicacid‐co‐citraconir acid)^?1) were taken to observe the morphological differences in the hydrogels. Although the less swollen hydrogel, Cs–P(AA‐co‐CA)‐1, had a sponge‐type structure, the most swollen hydrogel, Cs–PAA, displayed a uniform porous appearance. Fluconazole was entrapped in Cs–P(AA‐co‐CA)‐1 and Cs–PAA hydrogels, and the release was investigated at pH 4.0 and 37°C. The kinetic release parameters of the hydrogels (the gel characteristic constant and the swelling exponent) were calculated, and non‐Fickian diffusion was established for Cs–PAA, which released fluconazole much more slowly than the Cs–P(AA‐co‐CA)‐1 hydrogel. A therapeutic range was reached at close to 1 h for both hydrogels. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

A complex based on imidazole ionic liquid and copolymer of acrylamide and phenoxyacetamide modification for clay stabilizer

A complex system (AM/AA/APO‐EMIN) was obtained by poly (acrylamide‐co‐acrylic acid‐co‐N‐allyl‐2‐phenoxyacetamide) (AM/AA/APO) combining 1‐ethyl‐3‐methyl imidazolium tetrafluoroborate ([EMIM] [BF₄]) for clay stabilizer by using acrylamide (AM), acrylic acid (AA) and N‐allyl‐2‐phenoxyacetamide (APO), N‐methylimidazole, bromoethane, and sodium fluoroborate as raw materials. The complex solution exhibited excellent anti‐swelling rate (up to 94.5% at 10,000 mg/L), satisfying aging resistance (viscosity retention rate 84.2% after 15 days), and marked shear thinning behavior (viscosity retention rate 7.5% under 600 s^?1). From scanning electron microscope (SEM) images, a clear network structure appeared in AM/AA/APO‐EMIM solution. Compared with an existing poly (acrylamide‐co‐diallyl dimethyl ammonium chloride) clay stabilizer (HY‐201S), AM/AA/APO‐EMIN was less content and more effective to reduce the d‐spacing of sodium montmorillonite (Na‐MMT) from 19.1 Å to 15.7 Å. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41536.     

Characterization of polyacrylonitrile,poly(acrylonitrile‐co‐vinyl acetate), and poly(acrylonitrile‐co‐itaconic acid) based activated carbon nanofibers

In this study, three different acrylonitrile (AN)‐based polymers, including polyacrylonitrile (PAN), poly(acrylonitrile‐co‐vinyl acetate) [P(AN‐co‐VAc)], and poly(acrylonitrile‐co‐itaconic acid) [P(AN‐co‐IA)], were used as precursors to synthesize activated carbon nanofibers (ACNFs). An electrospinning method was used to produce nanofibers. Oxidative stabilization, carbonization, and finally, activation through a specific heating regimen were applied to the electrospun fibers to produce ACNFs. Stabilization, carbonization, and activation were carried out at 230, 600, and 750 °C, respectively. Scanning electron microscopy, thermogravimetric analysis (TGA), and porosimetry were used to characterize the fibers in each step. According to the fiber diameter variation measurements, the pore extension procedure overcame the shrinkage of the fibers with copolymer precursors. However, the shrinkage process dominated the scene for the PAN homopolymer, and this led to an increase in the fiber diameter. The 328 m²/g Brunauer–Emmett–Teller surface area for ACNFs with PAN precursor were augmented to 614 and 564 m²/g for P(AN‐co‐VAc) and P(AN‐co‐IA), respectively. The TGA results show that the P(AN‐co‐IA)‐based ACNFs exhibited a higher thermal durability in comparison to the fibers of PAN and P(AN‐co‐VAc). The application of these copolymers instead of AN homopolymer enhanced the thermal stability and increased the surface area of the ACNFs even in low‐temperature carbonization and activation processes. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44381.     

Sequence analysis and fiber properties of a blend of poly(ethylene terephthalate) and poly(ethylene terephthalate‐co‐4,4′‐bibenzoate)

Blends of poly(ethylene terephthalate) (PET) and poly(ethylene terephthalate‐co‐4,4′‐ bibenzoate) (PETBB) are prepared by coextrusion. Analysis by ¹³C‐NMR spectroscopy shows that little transesterification occurs during the blending process. Additional heat treatment of the blend leads to more transesterification and a corresponding increase in the degree of randomness, R. Analysis by differential scanning calorimetry shows that the as‐extruded blend is semicrystalline, unlike PETBB15, a random copolymer with the same composition as the non‐ random blend. Additional heat treatment of the blend leads to a decrease in the melting point, T_m, and an increase in glass transition temperature, T_g. The T_m and T_g of the blend reach minimum and maximum values, respectively, after 15 min at 270°C, at which point the blend has not been fully randomized. The blend has a lower crystallization rate than PET and PETBB55 (a copolymer containing 55 mol % bibenzoate). The PET/PETBB55 (70/30 w/w) blend shows a secondary endothermic peak at 15°C above an isothermal crystallization temperature. The secondary peak was confirmed to be the melting of small and/or imperfect crystals resulting from secondary crystallization. The blend exhibits the crystal structure of PET. Tensile properties of the fibers prepared from the blend are comparable to those of PET fiber, whereas PETBB55 fibers display higher performance. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 1793–1803, 2004     

Synthesis,antitumour and DNA replication activities of polymers containing vinyl‐(5‐fluorouracil)‐ethanoate

A new monomer, vinyl‐(5‐fluorouracil)‐ethanoate (VFUE), was synthesized by reaction of 5‐fluorouracil (5‐FU) and vinyl iodoacetate. The homopolymer of VFUE and its copolymers with acrylic acid (A, A) and maleic anhydride (MAH) were prepared by photopolymerization. The synthesized VFUE and polymers were identified by FTIR, ¹H NMR and ¹³C NMR spectroscopies. The contents of VFUE unit in poly(VFUE‐co‐AA) and poly(VFUE‐co‐MAH) were 21 mol% and 16 mol%, respectively. The number average molecular weights of the polymers determined by gel permeation chromatography were in the range 9600–17900 g mol^?1. The in vitro cytotoxicities of the samples against a normal cell line decreased as follows: 5‐FU > VFUE > poly(VFUE) > poly(VFUE‐co‐AA) > poly(VFUE‐co‐MAH). The in vivo antitumour activities of the polymers against Balb/C mice bearing the sarcoma 180 tumour cells were greater than those of 5‐FU at all concentrations. The inhibition of simian virus 40 DNA replication by the samples was much greater than that of the control. © 2002 Society of Chemical Industry     

Multilayer composite surfaces prepared by an electrostatic self‐assembly technique with quaternary ammonium salt and poly(acrylic acid) on poly(acrylonitrile‐co‐acrylic acid) membranes

An electrostatic self‐assembly technique was applied to prepare ion complex polymer layers on polyacrylonitrile with acrylic acid segments {poly(acrylonitrile‐co‐acrylic acid) [P(AN‐co‐AA)]}. For the ionic complex layers, quaternary ammonium salts, such as cetyl trimethyl ammonium chloride (CTAC) and tetramethyl ammonium chloride (TMAC), were used as cationic species, and also, poly(acrylic acid) (PAA) was used as an anionic species. These cationic and anionic species were self‐assembled alternately on the surface of the P(AN‐co‐AA) membrane. Fourier transform infrared spectroscopy, AFM, and water contact angle measurements of the membrane surface were used to confirm the formation of the multilayer composites on the P(AN‐co‐AA). The permeabilities of water and macromolecules of different molecular weights were evaluated by a membrane filtration technique. The values of permeability strongly depended on the formation layer by layer of these ion composites on the base P(AN‐co‐AA). Through the measurement of the values of the contact angle of water, it was clear that surface nature of the base membrane treated by CTAC or TMAC and PAA dramatically changed. We concluded that such an electrostatic self‐assembly technique is useful for the preparation of multicomposite layers to modify the surface of base P(AN‐co‐AA) membranes. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Self‐assembled poly(styrene‐co‐N‐isopropylacrylamide) film induced by capillary force

The monodisperse poly(styrene‐co‐N‐isopropylacrylamide) (poly(St‐co‐NIPAAm)) particles prepared by emulsifier‐free emulsion polymerization with microwave irradiation were induced by capillary forces to self‐assemble, and formed the two‐dimensional films on the clean glassware wafer substrates. The morphologies of the two‐dimensional films were characterized by scanning electron microscopy (SEM) and atom force microscopy (AFM). The results showed that monodisperse poly(St‐co‐NIPAAm) particles could form ordered two‐dimensional films by capillary forces. With NIPAAm concentration increasing, there gradually appeared surface undulations or surface defective region on the two‐dimensional films. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 99: 3514–3519, 2006     

Synthesis of poly(N,N‐diethylacrylamide‐co‐acrylic acid) hydrogels with fast response rate in NaCl medium

A series of thermo‐ and pH‐sensitive poly (N,N‐diethylacrylamide‐co‐acrylic acid) (P(DEA‐co‐AA)) hydrogels were prepared in NaCl aqueous solutions with different concentrations. Swelling and deswelling studies showed that in comparison with conventional P(DEA‐co‐AA) hydrogels (prepared in distilled water), the P(DEA‐co‐AA) hydrogels thus prepared had almost the same volume phase transition temperature (VPTT), but exhibited much faster response rates as the temperature was raised above their VPTT. Besides, the hydrogels prepared by this method had faster response rates in low pH buffer solutions, and the response rates increased with the increased concentration of the NaCl solutions used during the polymerization. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008