Surface hardness improvement of plasma-sprayed AISI 316L stainless steel coating by low-temperature plasma carburizing

Low-temperature carburizing below 773 K of austenite stainless steel can produce expanded austenite, known as S-phase, where surface hardness is improved while corrosion resistance is retained. Plasma-sprayed austenitic AISI 316L stainless steel coatings were carburized at low temperatures to enhance wear resistance. Because the sprayed AISI 316L coatings include oxide layers synthesized in the air during the plasma spraying process, the oxide layers may restrict carbon diffusion. We found that the carbon content of the sprayed AISI 316L coatings by low-temperature carburizing was less than that of the AISI 316L steel plates; however, there was little difference in the thickness of the carburized layers. The Vickers hardness of the carburized AISI 316L spray coating was above 1000 HV and the amount of specific wear by dry sliding wear was improved by two orders of magnitude. We conclude that low-temperature plasma carburizing enabling the sprayed coatings to enhance the wear resistance to the level of carburized AISI 316L stainless steel plates. As for corrosion resistance in a 3.5 mass% NaCl solution, the carburized AISI 316L spray coating was slightly inferior to the as-sprayed AISI 316L coating.     

Synthesis of nanostructured zirconia electrodeposited films on AISI 316L stainless steel and its behaviour in corrosion resistance assessment

This work deals with the study of AISI 316L stainless steel samples coated with nanostructured zirconia thin films, using electrodeposition methods. The chemical composition and compounds formed were determined by X-ray photoelectron spectroscopy (XPS). The morphology of zirconia films was analysed by scanning electron microscopy (SEM) and atomic force microscopy (AFM).Corrosion resistance of the coated steel was tested in a chloride environment. XPS analysis results show zirconium element on the metal surface, bound to oxygen-forming zirconia. The anodic polarization curves obtained in Hank's solution show that zirconia coating can be used as protective coating against pitting corrosion of AISI 316L stainless steels.     

Preparation and characterization of sol-gel derived yttria doped zirconia coatings on AISI 316L

A stable 4 mol% yttria-stabilized zirconia (YSZ) sol has been synthesized for coating stainless steel AISI 316L for biomedical applications. The sol was prepared by controlled hydrolysis of zirconium n-butoxide using acetylacetone and nitric acid as chelating agent and catalyst, respectively. X-ray diffractograms of calcined YSZ xerogel indicated a tetragonal structure at temperature as low as 400 °C. Stainless steel was dip-coated in transparent yellow YSZ sol followed by heat treatment between 400 and 600 °C for 2 h in air. A homogeneous and crack-free YSZ film was, thus, obtained on the stainless steel surface. Adhesion strength, measured by scratch test in progressive loading sequence on coated AISI 316L, showed 27 ± 3 N critical load. Corrosion performance of the surface coating was evaluated through open-circuit potential (OCP) measurement, impedance, polarization and chronoamperometry in Ringer's solution at 37 °C. The coating enhanced the pitting potential of the substrate. The metal ions released from AISI 316L was effectively controlled by the coating.     

奥氏体不锈钢离子渗碳后的腐蚀行为

为了提高奥氏体不锈钢零件的使用寿命,利用低温离子渗碳技术对AISI 316L奥氏体不锈钢进行了表面渗碳处理.用X射线衍射仪和光学显微镜分析了渗碳层的微观组织结构,用显微硬度计测试了渗碳层的硬度分布,通过电化学极化曲线测试技术和化学腐蚀试验研究了离子渗碳AISI 316L不锈钢的腐蚀行为.渗碳层为单相碳过饱和奥氏体固溶体,由此明显提高了AISI 316L不锈钢的抗腐蚀性能,渗碳层硬度梯度平缓,表面显微硬度高达900 HV.结果表明,奥氏体不锈钢低温离子渗碳处理不仅提高了其表面硬度,而且提高了不锈钢表面的耐腐蚀性能,从而提高了其使用寿命.     

Rate dependent cyclic behavior simulation of cold worked AISI 316L stainless steel pipe member

This research aims to simulate rate-dependent cyclic behavior of cold worked AISI 316L stainless steel pipe member using a developed FE analysis program. A rate-dependent cyclic plasticity model for cold worked AISI 316L stainless steel is derived based on the monotonic and cyclic loading experiments within quasi-static and dynamic strain rate ranges. Validity of the FE simulation program is presented by comparing analytical results to experimental data. Cyclic behavior of cold worked AISI 316L stainless steel pipe member is clearly simulated as a function of loading rate.     

Interface microstructures in diffusion bonding of titanium alloys to stainless and low alloy steels

Abstract

Commercial purity Ti and a Ti 6242 alloy have been diffusion bonded to an AISI 316L stainless steel and an AISI 4130 low alloy steel. The microstructures of the as processed products have been analysed using optical metallography, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM) techniques. The interdiffusion of the different elements through the interface has been determined using energy dispersive spectroscopy microanalysis in both a SEM and a STEM. For the combinations AISI 316L–commercially pure Ti and AISI 316L–Ti 6242 several regions surrounding the original interface have been observed. Starting from the 316L side, first a α phase is observed, followed by an Fe₂ Ti intermetallic, an FeTi intermetallic, and finally an Fe₂Ti₄O oxide just before the Ti and Ti 6242. Because the diffusion ofTi in Fe is faster than the diffusion of Fe in Ti, a Kirkendall effect is produced. In the AISI 4130–Ti 6242 combination a thin layer of TiC is observed at the interface, limiting the interdiffusion of elements.

MST/1746     

Friction and wear behaviors of a gradient nano-grained AISI 316L stainless steel under dry and oil-lubricated conditions

A gradient nano-grained (GNG) surface layer was fabricated on an AISI 316L stainless steel (SS) by using the surface mechanical rolling treatment (SMRT). Reciprocating dry and oil-lubricated sliding tests of the GNG 316L SS in air at room temperature were conducted in comparison with the coarse-grained (CG) counterpart. Worn surface morphologies and subsurface microstructures were investigated for both 316L SS samples. 316L SS with a GNG surface layer shows a significantly improved wear resistance, especially under oil-lubricated condition. The notably wear resistance enhancement of the GNG 316L SS is attributed to the GNG surface layer with high strain accommodation ability and high hardness, which can reduce the wear volume in the running-in stage effectively.     

A discussion on evaluation criteria for crevice corrosion of various stainless steels

In this study,crevice corrosion performances of a newly developed LDSS 2002 and three commercial stainless steels(AISI 304,AISI 316L and DSS 2205)were investigated and discussed.Crevice repassivation potential(ER,CREV),which was measured by the potentiodynamic-galvanostatic-potentiodynamic(PDGS-PD)test,was applicable to crevice corrosion evaluation of 304 and 316 L stainless steels.However,much lower(ER,CREV values were obtained for DSS 2205 and LDSS 2002.These abnormal(ER,CREV values for duplex stainless steels may be related to the selective attack of the less corrosion-resistant phase,the lower corrosion potential in the crevice-like solution,and more crevice corrosion sites in the PD-GS-PD test.A critical chloride concentration of crevice corrosion(CCCCREV)measurement was introduced for crevice corrosion evaluation of various stainless steels.The derived CCCCREVwas proved to be a valid criterion for crevice corrosion evaluation of both the austenitic and duplex stainless steels.An order of crevice corrosion resistance of AISI 304≈LDSS 2002相似文献   

Characterization of the oxides formed at 1000 °C on the AISI 316L stainless steel—Role of molybdenum

In the present work, in situ X-ray diffraction (XRD) was used to identify the oxides formed on the AISI 316L stainless steel (SS) during isothermal oxidation at 1000 °C, in air. The results were compared with those obtained on the AISI 304 SS in order to better explain the role of molybdenum on the oxidation process of the AISI 316L (containing 2% Mo). A good oxidation behavior is observed on the AISI 316L considering kinetics, structural characteristics and scale adherence. It is shown that molybdenum plays a similar protective role as the one observed with silicon. Moreover, it is possible to add a higher content of molybdenum in the stainless steel compared with silicon (usually 0.5 wt%). This higher protective element content hinders the external iron diffusion and leads to the lower growth rate and the better scale adherence. The oxide scale is then composed of Cr₂O₃ with a small amount of Mn_1.5Cr_1.5O₄ at the external interface. The better scale adherence appears to be also related to a pegging effect at the internal interface.     

Novel fluorapatite/niobium composite coating for metallic human body implants

This study's aim was to design and prepare a novel composite coating in order to improve the biocompatibility of the metallic implants. AISI 316L stainless steel (SS) was used as a substrate and a filler-matrix fluorapatite/niobium (FA/Nb) composite coating was performed on the substrate by using plasma-spray technique. XRD and SEM analyses were utilized to characterize the coatings. Electrochemical polarization tests were carried out in two types of physiological solutions in order to evaluate the corrosion behavior of the coated specimens as an indication of biocompatibility. The results indicated that the corrosion current density of the FA/Nb coated samples was much lower than the obtained values for the FA coated SS substrates. Obviously, the novel FA/Nb composite coating could improve the corrosion resistance and the biocompatibility of the SS implants.     

Experimental investigation on corrosion and hardness of ion implanted AISI 316L stainless steel

The AISI 316L stainless steel has been widely used both in artificial knee and hip joints in bio-medical applications. In the present study AISI 316L SS was implanted with two different ions: nitrogen and helium at 100 keV with a dose of 1 × 10¹⁷ ions/cm² at room temperature. The crystallographic orientation and surface morphology were studied using X-ray diffraction (XRD) and scanning electron microscope (SEM). The effects of ion implantation on the corrosion performance of AISI 316L stainless steel was evaluated in 0.9% NaCl solution using electro chemical test both on the virgin and implanted samples. The subsequent Tafel analysis shows that the ion implanted specimens were more corrosion resistant when compared to the bare specimens. Microhardness was also measured by Vickers method by varying the loads. The results of the studies indicated that there was a significant improvement in both corrosion resistance and hardness of implanted samples.     

Keyhole gas tungsten arc welding of AISI 316L stainless steel

Keyhole gas tungsten arc welding (K-TIG) was used to weld AISI 316L stainless steel of mid-thickness (thickness ranging 6–13 mm). 316L plates of 10-mm thickness were jointed using an I-groove in a single pass without filler metal. The effects of welding parameters on the fusion zone profile were investigated. The weld properties, including mechanical properties, microstructure, and corrosion resistance, were analyzed. The primary weld microstructures were austenite and δ-ferrite. The tensile strength and impact property of the weld were almost the same as those of the base metal, while the corrosion resistance of the weld was even better than that of the base metal. High-quality 316L stainless steel joints can be realized through K-TIG welding with high productivity and low processing cost. The practical application of K-TIG welding to join mid-thickness workpieces in industry is well demonstrated and an ideal process for welding AISI 316L of mid-thickness with high efficiency and low cost is presented.     

Microstructure and Corrosion Resistance of Dissimilar Weld-Joints between Duplex Stainless Steel 2205 and Austenitic Stainless Steel 316L

The microstructure and corrosion resistance of dissimilar weld-joints between stainless steel SAF 2205 and stainless steel AISI 316 L were investigated. Welding was accomplished by different types of welding wires AWS ER 347, AWS ER 316 L and AWS ER 309 L. To verify soundness of welded samples, nondestructive tests were performed. Metallographic samples were prepared from cross-section areas of weldjoints to investigate microstructure of different regions of weld-joints by optical microscopy and scanning electron microscopy. Corrosion resistance of weld-joints was evaluated in NaCl solution by potentiodynamic polarization and electrochemical impedance techniques. In the weld metal AWS ER 347, the brittle sigma phase was created, resulting in the decrease of weld-joint corrosion resistance. According to the results of metallurgical investigations and corrosion tests, welding wire AWS ER 309 L was suitable for welding duplex stainless steel(SAF 2205) to austenitic stainless steel(AISI 316L) by gas tungsten arc welding(GTAW)process.     

Effect of a nanoparticle-filled lubricant in turning of AISI 316L stainless steel (SS)

Release of heat and generation of friction associated with machining operation ever posture a problem which not only reduce the tool life but also impair the quality of the product. Nano cutting fluids play a significant role in machining operations and impact tool life and quality of work. In the present work, tool flank wear is analyzed during turning AISI 316L Stainless steel (SS) under a nano cutting environment. Experiments are conducted by turning of AISI 316L SS under wet machining with and without multiwalled carbon nanotube (MWCNT) inclusions in the conventional lubricant. The second order quadratic models were developed to predict tool wear using response surface methodology (RSM) based D-optimal design. Machining parameters such as speed, feed rate, and depth of cut are chosen as numerical factors and the type of lubricant is considered as the categorical factor. The results show that the influence of the feed rate is more significant while machining the AISI 316L SS with a whisker reinforced ceramic insert. The addition of MWCNTs in SAE20W40 enhances the tool performance with their enhanced penetration. After turning experiment, a scanning electron microscope (SEM) with energy dispersive X-ray (EDS) was used to investigate the tool wear.     

Advances in DLC coatings by hybrid PSII and PECVD as a barrier to corrosion in simulated body fluid*

In this study, diamond-like carbon (DLC) films were deposited on biomedical AISI316L stainless steel by hybrid plasma source ion implantation (PSII) and plasma-enhanced chemical vapour deposition (PECVD). Potentiodynamic polarization tests and Electrochemical Impedance Spectroscopy (EIS) have been employed to investigate the corrosion performance of different DLC films in Tyrode's simulated body fluid (pH = 7.4). The corrosion resistance of the DLC films by PECVD deteriorated rapidly after 24 h of immersion, but those made by hybrid PSII and PECVD offered more effective barrier for AISI316L stainless steel during 72 h of immersion. The test results demonstrated that the DLC film by hybrid PSII and PECVD possessed less corrosion current density, greater corrosion resistance, and more positive breakdown potential in simulated body fluid.     

Structural,mechanical, and tribological properties of AISI 304 and AISI 316L steels submitted to nitrogen–carbon glow discharge

Glow discharge (GD) nitrocarburizing, at low-carbon content and different working temperatures, was performed on AISI 316L and AISI 304 stainless steels. Structural compositions were studied by X-ray diffraction. Instrumented indentation and conventional Vickers method allowed hardness profiles to be determined. Tribological behavior was studied by means of reciprocating sliding and nanoscratch tests. After nitrocarburizing, both steels showed similar embedded nitride and carbide formations. The layer formed by GD in nitrogen–carbon atmosphere is thicker than those consisting solely of nitrogen particularly for AISI 316L. At working temperatures higher than 400 °C, roughness increased and wear was limited to asperity compaction. Wear mechanisms were similar in both steels. However, wear was reduced by up to a factor of 5 in treated steels. No difference in elastic surface recovery was observed after nitrocarburizing in either steel.     

Effect of porosity and density on the mechanical and microstructural properties of sintered 316L stainless steel implant materials

In this study, the microstructure and mechanical properties of sintered AISI 316L stainless steel implant materials produced by powder metallurgy (P/M) method were investigated as a function of porosity amount. AISI 316L stainless steel powders were cold-pressed with 800 MPa pressure and sintered at 1200 °C, 1250 °C and 1300 °C for 30 min in a nitrogen atmosphere. The mechanical properties of the 316L implant samples were determined by tensile, fatigue and microhardness tests. Metallographic studies such as pore formation, and fractured surface analyses were performed by Scanning Electron Microscopy (SEM) and Light Optical Microscopy (LOM). The results of this study indicate that, irregular pore formation tendencies increase with an increase in porosity (%). Furthermore, an increase in porosity was shown to decrease the mechanical properties of sintered AISI 316L stainless steel. Sintering temperature is important parameter in decreasing the porosity of P/M materials.     

Effect of Surface Treatment and Metallic Coating on Corrosion Behavior and Biocompatibility of Surgical 316L Stainless Steel Implant

Surface engineering technology is a suitable method for coatings on the metal surfaces or performing surface modification treatment,which can improve corrosion resistance and biocompatibility of metals.In this research,corrosion behavior of Nb coating on H 2 SO 4 and HNO 3 treated AISI stainless steel 316L (SS) was evaluated.Nb coating was carried out using physical vapor deposition process on the SS.Characterization techniques including scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) technique were used to investigate the microstructure and morphology of the coated and treated SS.Electrochemical potentiodynamic tests were performed in two types of physiological solutions and compared with the pristine SS specimens.Cyclic polarization tests were performed to evaluate resistivity against pitting.Experimental results indicate that Nb coating and surface treatment of the SS had a positive effect on improvement of corrosion behavior.The decrease in corrosion current densities was significant for coated and treated specimens.The corrosion current density was much lower than the values obtained for pristine specimens.     

Influence of temperature and hydrodynamic conditions on the corrosion behavior of AISI 316L stainless steel in pure and polluted H3PO4: Application of the response surface methodology

Phosphoric acid is mainly produced by the wet acid process, where corrosion problems could be intensified due to the presence of impurities in the phosphate ores. Operating temperatures and flowing conditions aggravate the aforementioned problems. This work studies the influence of temperature (25–60 °C) and hydrodynamic conditions (Reynolds numbers from 1456 to 5066) on the corrosion of AISI 316L stainless steel in pure and polluted phosphoric acid solutions, by means of cyclic potentiodynamic polarization curves in a hydrodynamic circuit. The effect of temperature is the same as that caused by impurities, that is, higher corrosion rates and hindered passivation and repassivation resistance of the alloy. Statistical analysis by means of surface response methodology proved that the effect of temperature on the corrosion parameters of AISI 316L is more influential than the Reynolds number effect. The Reynolds number seems to have no significant influence on the corrosion behavior of stainless steel. Furthermore, the influence of temperature on the corrosion rate is much higher than on the rest of the corrosion parameters analyzed, especially in polluted phosphoric acid solutions. AISI 316L stainless steel has a clear interest for the phosphoric acid industry as a component material of some equipment due to its good corrosion properties at the different temperatures and Reynolds numbers studied even in polluted media.     

A study on low magnetic permeability gas tungsten arc weldment of AISI 316LN stainless steel for application in electron accelerator

Low magnetic permeability is an important criterion in selection of the material of construction of beam pipes and vacuum chambers of electron accelerators for safeguarding against distortion of the magnetic field. In the modified design of new 20 MeV/30 mA Injector Microtron for the existing synchrotron radiation sources Indus-1 and Indus-2, AISI 316 LN stainless steel has been identified as the material of construction of its vacuum chamber. Welding of AISI 316LN stainless steel with conventional filler alloys like ER316L and ER317L of AWS A5.9 produces duplex weld metal with 3–8% ferro-magnetic delta ferrite to avoid solidification cracking. The results of the study has demonstrated that GTAW of AISI 316LN SS with high Mn adaptation of W 18 16 5 N L filler produced a crack free non-magnetic weld with acceptable mechanical properties. Moreover, AISI 316LN stainless steel is not required to be solution annealed after the final forming operation for obtaining a low magnetic permeability, thereby avoiding solution annealing of large vacuum chamber in vacuum/controlled atmosphere furnace and associated problems of distortion. Besides Injector Microtron, the study also provides useful input for design of future indigenous accelerators with vacuum chambers of austenitic stainless steel.