聚丙烯酸酯的乳液聚合及其吸油性能研究

以丙烯酸十二酯、丙烯酸丁酯等为原料,采用乳液聚合法合成了聚丙烯酸酯树脂。讨论了乳化剂、搅拌速度、反应温度对聚丙烯酸酯乳液性能的影响,考察了单体配比、引发剂用量、交联剂种类及用量、致孔剂用量等对聚丙烯酸酯树脂吸油性能的影响。发现当反应单体丙烯酸丁酯与丙烯酸十二酯的摩尔比为3∶1,交联剂二乙烯基苯用量为单体质量的2%,引发剂过硫酸铵用量为单体质量的2%,致孔剂乙酸乙酯用量为单体质量的50%时,合成的聚丙烯酸酯树脂对煤油、甲苯和CCl4的吸收率分别为7.12、18.10和33.39g·g-1,表现出良好的吸油性能。     

新型高吸油树脂的制备

以丙烯酸正丁酯(BA)和甲基丙烯酸甲酯(MMA)为单体,采用改进的悬浮聚合法合成高吸油树脂。考察了单体配比、引发剂和交联剂用量、AIBN加入量及加入时间对树脂吸油性能的影响。结果表明,最佳合成条件为:单体配比BA∶MMA质量比为4∶1,引发剂BPO用量为单体质量的0.4%,交联剂N,N’-亚甲基双丙烯酰胺为单体质量的0.15%,发泡剂偶氮二异丁腈(AIBN)为单体质量的18%,在此条件下合成的树脂对甲苯的吸油率最高可达40.17 g/g,速率也明显提高。     

高吸油性树脂的合成

以丙烯酸烷基酯为单体,过氧化苯甲酰（BPO）为引发剂,二丙烯酸乙二醇酯为交联剂,采用悬浮聚合法合成聚丙烯酸酯类吸油树脂。本文讨论了单体结构、引发剂用量、交联剂用量对吸油树脂性能的影响。     

苯乙烯用量对丙烯酸系吸油树脂性能的影响

以质量比为2:1的丙烯酸丁酯、甲基丙烯酸甲酯为单体,1.0%的过氧化苯甲酰(BPO)为引发剂,0.5%的二乙烯苯(DVB)为交联剂,采用悬浮聚合法合成了丙烯酸系吸油树脂(合成过程中加入一定量的苯乙烯)。研究了苯乙烯单体对吸油树脂微观结构的影响,分析了树脂的吸油性和缓释行为。结果表明:添加苯乙烯后,树脂颗粒表面有孔洞出现,硬度增加;苯乙烯用量为15%时,树脂对小分子CCl4的吸油性最优,同时树脂的热分解温度提高到373.3℃。     

高吸油树脂的制备及性能研究

采用丙烯酸和十二(烷)醇直接酯化法制备丙烯酸十二酯,然后以丙烯酸十二酯和丙烯酸丁酯为单体,N,N′-亚甲基双丙烯酰胺为交联剂,过氧化苯甲酰为引发剂,明胶为分散剂,水为分散介质,采用悬浮聚合法制备了自溶胀型的高吸油性树脂。通过正交试验,得到制备该树脂的最优方案,同时对其吸附动力学进行了研究。结果表明,n_(丙烯酸十二酯):n_(丙烯酸丁酯)=1:2,引发剂用量3.0%,交联剂用量2.2%,分散剂用量2.8%,水油体积比8:1,温度80℃,反应时间5 h时,生成的树脂吸油性能最好,对甲苯的吸油率达16.5 g/g,对甲苯和四氯化碳的吸附量也在10 g/g以上。在3 h内,树脂基本达到饱和吸油状态,同时保油率达到90%以上。     

高吸油树脂性能与再生的研究

采用悬浮聚合的方法合成一种交联适中的聚丙烯酸系高吸油性树脂。研究了单体组成及配比,引发剂用量和交联剂用量对树脂吸油性能的影响,并且对树脂的再生进行了研究。实验结果表明:当m(甲基丙烯酸十二酯):m(苯乙烯)为2:3,引发剂用量为单体质量的1%,交联剂用量为单体质量的1%时,吸油效果最为理想;通过乙醇溶剂萃取法进行再生脱油率可达92.3%。     

乳液聚合制备丙烯酸酯类吸油树脂及其性能研究

采用乳液聚合,以甲基丙烯酸月桂酯,甲基丙烯酸丁酯和甲基丙烯酸甲酯为单体,二乙烯基苯为交联剂,过硫酸铵为引发剂,合成了丙烯酸酯类高吸油树脂。研究了乳化剂、引发剂、交联剂用量,单体配比对吸油树脂性能的影响。     

丙烯酸酯类高吸油树脂的合成及其吸油性能研究

以甲基丙烯酸丁酯（BMA）和丙烯酸丁酯（BA）为单体,二乙烯苯（DVB）为交联剂,过氧化苯甲酰（BPO）为引发剂,采用悬浮聚合法制备了丙烯酸短链烷基酯类高吸油树脂。通过研究单体配比、引发剂用量、交联剂用量和分散剂种类及用量等对树脂吸油率的影响,得到了制备的高吸油树脂最佳工艺配方。实验结果表明：当n（BMA）∶n（BA）=0.67,BPO质量分数为0.5%,DVB质量分数为0.5%,采用聚乙烯醇（PVA）为分散剂且其质量分数为3%时,树脂的形态结构最好,且吸油率最大。研究表明,树脂可吸收四氯化碳11.2 g/g,甲苯6.0 g/g,汽油3.9 g/g,柴油2.2 g/g,且树脂的保油率在90%以上。     

偶联剂KH570对吸油树脂性能的影响

采用悬浮聚合,以甲基丙烯酸甲酯、丙烯酸丁酯和苯乙烯为单体,过氧化苯甲酰(BPO)为引发剂,二乙烯苯(DVB)为交联剂,合成了吸油树脂。研究了单体配比,引发剂、交联剂用量对树脂吸油率的影响,在聚合过程中引入偶联剂KH570共聚合,分析了树脂的吸油性能和缓释行为。结果表明:当丙烯酸丁酯和甲基丙烯酸甲酯的质量比为2∶1,BPO和DVB用量分别为单体总质量的1.0%,0.5%时,树脂的综合吸油率最好;使用KH570的树脂开始分解温度和最大分解速率温度分别升高到383.9,406.9℃,树脂对机油的保油性得到明显的改善。     

多元共聚高吸油树脂的合成研究

以甲基丙烯酸十八酯(SMA)、丙烯酸丁酯(BA)和苯乙烯(St)为单体,二乙烯苯(DVB)为交联剂,过氧化苯甲酰(BPO)作引发剂,采用悬浮聚合法合成了高吸油性树脂,研究了体系中单体组成及配比、交联剂、分散剂及致孔剂用量等因素对吸油树脂性能的影响。结果表明:m(SMA):m(BA):m(St)=33:67:12,w(DVB)=1%,w(PVA)=1.2%,w(CHCl3)=35%时,所合成的树脂吸油性能最佳,其对柴油、甲苯、四氯化碳的饱和吸油倍率分别可达11.2g/g、18.9g/g、27.4g/g。     

石蜡填充型丙烯酸酯吸油性树脂的合成及性能

以过氧化苯甲酰(BPO)为引发剂,N,N'-亚甲基双丙烯酰胺为交联剂,甲基丙烯酸丁酯为单体,聚乙烯醇为分散剂,石蜡为填充剂,采用悬浮聚合法合成了填充型吸油树脂。通过对产物的吸油率、保油率和脱油性能的测试研究了各反应物用量对树脂性能的影响,用正交实验法确定了最佳工艺。结果表明:石蜡、引发剂、交联剂和分散剂的质量分数分别为1.0%、0.4%、1.6%和1.0%(基于单体质量),反应温度80℃,反应时间5 h,水与单体质量比8∶1时,合成的树脂在48 h饱和吸油率为23.80 g/g。与未添加填充剂的吸油树脂比较,石蜡填充型丙烯酸酯吸油性树脂的吸油率、保油率提高,脱油性能更好,但凝胶分率变化不大。     

有机膨润土改性高吸油树脂的制备与性能研究

对膨润土进行了预处理,然后使用十六烷基三甲基溴化铵(HDTMAoBr)对其进行有机化改性,最后将有机膨润土加入到丙烯酸酯有机单体、交联剂、引发剂的混合液中聚合制得复合高吸油树脂。结果表明,加入单体总质量1.5 %的膨润土所得的树脂最大吸油可达14.1 g/g。通过正交实验讨论了最佳工艺条件。有机膨润土与丙烯酸酯吸油树脂具有良好的相容性,与未添加膨润土的树脂相比,复合树脂吸油性能、热分解温度均有提高。     

多元共聚高吸油树脂合成及性能研究

以(甲基)丙烯酸酯类、苯乙烯为主要共聚单体,双甲基丙烯酸乙二醇酯(EGDMA)、二乙烯基苯(DVB)等为交联剂,采用悬浮共聚工艺合成了一系列高吸油树脂.研究了树脂共聚单体组成、丙烯酸单体链长、交联剂种类、交联度、引发剂量以及聚合工艺等因素对吸油树脂吸油量等性能的影响.结果表明:采用EGDMA交联时以丙烯酸十四酯的效果最佳,采用DVB交联时以丙烯酸十二酯效果最佳;交联剂种类及交联度大小对树脂吸油性能及树脂形态有明显影响;树脂交联度的大小明显影响树脂共聚物的转化率与可溶性分率,也明显影响树脂产品的收率.在最佳合成条件下制备的高吸油树脂具有较佳的吸油性能,对甲苯的吸附量可达17.32 g/g树脂.     

Synthesis and characterization of a novel high‐oil‐absorbing resin

A high‐oil‐absorbing resin, which was a low crosslinking resin, was synthesized by conventional suspension copolymerization in this study. The effects of the monomer ratio, crosslinker, initiator, ratio of water to oil, and defined optimum reaction conditions were studied. The highest oil absorptivity of the resin was about 11.5 g/g in diesel and the oil‐absorption saturation time was 3 days when the best process conditions were as follows: ratio of styrene to ethylene–propylene–diene terpolymer = 40/60 w/w, amount of crosslinker divinylbenzene = 1.0 wt %, amount of benzoyl peroxide = 1.0 wt %; proportion of gelatin to calcium phosphate = 0.2 g/0.1 g, stirring speed = 500 r/min, and proportion of water to oil = 15 : 1. By using such methods as infrared spectroscopy, thermogravimetric analysis, and other methods, we studied the oil‐absorbing resin structure, oil‐absorption rate, oil‐absorption saturation time, and oil‐absorption rate twice. The oil‐absorbing resins were used repeatedly through the extraction of ethanol. The experiment results show little effect on the oil‐absorption properties. The oil‐absorption rate constant was evaluated for diesel, and the oil‐absorbing process obeyed the first‐order kinetics equation. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

接枝改性法制备天然橡胶吸油材料的工艺研究

以丙烯酸丁酯为单体,N,N′-亚甲基双丙烯酰胺为交联剂,过氧化苯甲酰为引发剂,采用乳液聚合法合成吸油性橡胶。研究了引发剂和交联剂种类和用量、反应时间和温度、天然胶乳和单体配比对吸油性能的影响,并对吸油橡胶的吸油倍率及对水面浮油的回收性能等进行了考察。通过对煤油等几类油品的吸收对比,确定最佳的工艺条件。制得的吸油橡胶吸煤油最高可以达11.92g/g;吸四氯化碳为15.21g/g。     

Synthesis and properties of oil absorption resins filled with polybutadiene

Polybutadiene (PB) is used to fill an oil absorption resin as a physical crosslinker to construct a kind of 3‐dimensional network with a high degree crosslinking and low crosslink density. A series of acrylic resin particles with various compositions are prepared by suspension polymerization, using benzoyl peroxide (BPO) as an initiator and ethylene glycol dimethacrylate (EGDMA) as a chemical crosslinker. The effects of the polymerization temperature, initiator concentration, monomer feed ratio, and chemical and physical crosslinker concentrations on the oil absorbency and gel fraction (degree of crosslinking) are studied. The recipe and operation conditions are optimized as follows: a mass ratio of 3:1 for styrene (St)/dodecyl methacrylate or St/butyl acrylate, 0.5 wt % BPO, and 80°C for 7–8 h. The effect of the physical crosslinker (PB) concentration is complex. The oil absorbency increases with increasing PB at lower EGDMA concentrations. However, under this same condition, particles cannot be formed if the PB concentration is higher than a certain value. By contrast, there is an optimum PB concentration when the EGDMA concentration is higher. The oil absorption speed is also investigated. The presence of PB can speed up absorption. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3309–3314, 2003     

魔芋粉-丙烯酸-丙烯酰胺接枝共聚合成高吸水树脂

以魔芋粉,丙烯酸和丙烯酰胺等为原料,经接枝聚合合成了魔芋粉－丙烯酸－丙烯酰胺类超强吸水性树脂。讨论了引发剂,交联剂,丙烯酸,丙烯酰胺等用量以及反应时间和反应温度等因素对树脂吸水性能的影响。结果表明: 在魔芋粉与单体质量比为1:4,引发剂用量为0.35%（占单体的质量）,丙烯酸/丙烯酰胺（质量）为1:1,丙烯酸中和度为80% ,反应温度为55～65℃,交联剂用量为0.75%（占单体的质量）的条件下,制得的SAP吸去离子水可达720g/g,吸0.9%的NaCl溶液为110g/g。     

环保型水性印刷光油的研究

以甲基丙烯酸甲酯（MMA）、丙烯酸丁酯（BA）、丙烯酸甲酯（MA）、苯乙烯（St）等为单体,以过硫酸钾为引发剂,以十二烷基硫酸钠（SDS）、聚乙二醇辛基苯基醚（OP-10）为乳化剂,通过预乳化种子聚合法获得水性乳液型上光油。探讨了乳化剂用量和配比、引发剂用量、反应温度和时间、后续单体滴加时间、保温反应时间、搅拌速度及中和剂对乳液综合性能的影响。通过固化成膜试验对水性上光油的光泽度、耐磨性、耐水性等性能测定。结果表明：乳化剂用量为乳液的2．0％～3．0％（质量分数）,阴/非离子乳化剂配比为1：2,引发剂质量分数为单体的0．55％,反应温度78—84℃,反应时间4h,后续滴加单体时间为90min,保温时间2．0h,搅拌速率为120r／min,使用NaHCO3作为中和剂时乳液性能最佳。主要技术指标：光泽度为92;固含量为46％。