NOx Storage and Reduction Catalysts for Automotive Lean-Burn Engines: Effect of Parameters and Storage Materials on NOx Conversion

The effect of various parameters on the NO _x conversion over NO _x storage and reduction catalysts supported on alumina was investigated. The Pt/BaO/Al₂O₃ catalyst exhibited a higher NO _x reduction activity than the Pt/Al₂O₃ catalyst under the static and cycling conditions. The activity of Pt/BaO/Al₂O₃ catalyst was improved in the cycled feedstream. The Pt/SrO/Al₂O₃ was found to have as high activity as Pt/BaO/Al₂O₃ for NO _x reduction. In order to achieve effective reduction of NO _x , NO _x storage in the form of Me(NO₃)₂ (Me = Ba or Sr) is more favorable than other nitrates and the rich condition should be chosen in such a way that the sorption capacity can be fully regenerated at a fast rate and the inhibition effect by strongly adsorbed molecules derived from C₃H₆ and CO can be minimized.     

Platinum Oxidation and Sulphur Deactivation in NOx Storage Catalysts

Flow reactor experiments and X-ray photoelectron spectroscopy (XPS) measurements were used to investigate the importance of platinum oxide formation on Pt/BaO/Al₂O₃ NO _x storage catalysts during reactions conditions. The reaction studied was NO(g) + 1/2 O₂(g) NO₂(g). During NO₂ exposure of the catalyst the NO₂ dissociation rate decreased during the reaction. This activity decrease with time was also studied with XPS and it was found to be due to platinum oxide formation. The influence of sulphur exposure conditions on the performance of the NO _x storage catalysts was studied by exposing the samples to lean and/or rich gas mixtures, simulating the conditions in a mixed lean application, containing SO₂. The main results show that all samples are sensitive to sulphur and that the deactivation proceeds faster when SO₂ is present in the feed under rich conditions than under lean or continuous SO₂ exposure. Additionally, the influence of the noble metals present in the catalysts was investigated regarding sulphur sensitivity and it was found that a combination of platinum and rhodium seems to be preferable to retain high performance of the catalyst under SO₂ exposure and subsequent regeneration. Finally, the behaviour of micro-fabricated model NO _x storage catalysts was studied as a function of temperature and gas composition with area-resolved XPS. These model catalysts consisted of a thin film of Pt deposited on one-half of a BaCO₃ pellet. It was found that the combination of SO₂ and O₂ resulted in migration of Pt on the BaCO₃ support up to one mm away from the Pt/BaCO₃ interface.     

Characterisation by TPR, XRD and NOx Storage Capacity Measurements of the Ageing by Thermal Treatment and SO2 Poisoning of a Pt/Ba/Al NOx-Trap Model Catalyst

The deactivation of a Pt/Ba/Al₂O₃ NO _x -trap model catalyst submitted to SO₂ treatment and/or thermal ageing at 800 °C was studied by H₂ temperature programmed reduction (TPR), X-ray diffraction (XRD) and NO _x storage capacity measurements.The X-ray diffractogram of the fresh sample exhibits peaks characteristic for barium carbonate. Thermal ageing leads to the decomposition of barium carbonate and to the formation of BaAl₂O₄. The TPR profile of the sulphated sample shows the presence of (i) surface aluminium sulphates, (ii) surface barium sulphates, (iii) bulk barium sulphates. The exposure to SO₂ after ageing leads to a small decrease of the surface barium-based sulphates, expected mainly as aluminate barium sulphates. This evolution can be attributed to a sintering of the storage material. TPR experiments also show that thermal treatment at 800 °C after the exposure to SO₂ involves the decomposition of aluminium surface sulphates to give mainly bulk barium sulphates, also pointed out by XRD. Thus, the thermal treatment at 800 °C leads to a stabilization of the sulphates.These results are in accordance with the NO _x storage capacity measurements. On non-sulphated catalysts, the treatment at 800 °C induces to a decrease of the NO _x storage capacity, showing that barium aluminate presents a lower NO _x storage capacity than barium carbonate. Sulphation strongly decreases the NO _x storage capacity of catalysts, whatever the initial thermal treatment, showing that barium sulphates inhibit the NO₂ adsorption. Moreover, the platinum activity for the NO to NO₂ oxidation is lowered by thermal treatments.     

Sulfur deactivation and regeneration of Pt/BaO/Al2O3 and Pt/SrO/Al2O3 NO x storage catalysts

Transient experiments were performed to study sulfur deactivation and regeneration of Pt/BaO/Al₂O₃ and Pt/SrO/Al₂O₃ NO _x storage catalysts. It was found that the strontium-based catalysts are more easily regenerated than the barium-based catalysts and that a higher fraction of the NO _x storage sites are regenerated when H₂ is used in combination with CO₂ compared to H₂ only.     

Fundamental Investigations of Thermal Aging Phenomena of Model NOx Storage Systems

Investigations of the aging behavior induced by high temperatures coupled with oxidizing atmosphere of model NO _x storage systems Ba/Al₂O₃ and Ba/CeO₂ are reported in this paper. The samples were prepared, calcined and exposed to temperatures between 500 and 1000 °C in air for 12 h for thermal aging. Samples were characterized with XRD, HRSEM, DSC-TGA-MS and BET analyses. In XRD investigations of all model systems calcined at 500 °C for 2 h, the NO _x storage component was present in form of BaCO₃. The release of CO₂ as a result of the decarbonization of the NO _x storage component at increased temperatures was verified by thermogravimetric investigations. In the case of Ba/Al₂O₃, already during calcination a partial reaction of the NO _x storage component with Al₂O₃ resulting in the formation of barium aluminate was observed. In the model system Ba/CeO₂ the decomposition of the barium carbonate started above 780 °C and the formation of a barium cerium mixed oxide was observed. The presence of the barium containing NO _x storage component has a strong influence on the specific surface area of the model NO _x storage systems. The morphology and crystallite size of CeO₂ modified with the barium containing NO _x storage component exhibited distinct changes compared to the unmodified oxide. The NO _x storage efficiency determined by model gas tests of freshly prepared and engine aged model NO _x storage catalysts correlates well with the above described observations.     

Influence of the storage material on the storage of NO x at low temperatures

The NO _x storage performance at low temperature (100–200 °C) has been studied for model NO _x storage catalysts. The catalysts were prepared by sequentially depositing support, metal oxide and platinum on ceramic monoliths. The support material consisted of acidic aluminium silicate, alumina or basic aluminium magnesium oxide, and the added metal oxide was either ceria or barium oxide. The NO _x conversion was evaluated under net-oxidising conditions with transients between lean and rich gas composition and the NO _x storage performance was studied by isothermal adsorption of NO₂ followed by temperature programmed desorption of adsorbed species. The maximum in NO _x storage capacity was observed at 100 °C for all samples studied. The Pt/BaO/Al₂O₃ catalyst stored about twice the amount of NO _x compared with the Pt/Al₂O₃ and Pt/CeO₂/Al₂O₃ samples. The storage capacity increased with increasing basicity of the support material, i.e. Pt/Al₂O₃ · SiO₂ < Pt/Al₂O₃ < Pt/Al₂O₃ · MgO. Water did not significantly affect the NO _x storage performance for Pt/Al₂O₃ or Pt/BaO/Al₂O₃.

     

NO x uptake mechanism on Pt/BaO/Al2O3 catalysts

The NO _x adsorption mechanism on Pt/BaO/Al₂O₃ catalysts was investigated by performing NO _x storage/reduction cycles, NO₂ adsorption and NO + O₂ adsorption on 2%Pt/(x)BaO/Al₂O₃ (x = 2, 8, and 20 wt%) catalysts. NO _x uptake profiles on 2%\Pt/20%BaO/Al₂O₃ at 523 K show complete uptake behavior for almost 5 min, and then the NO _x level starts gradually increasing with time and it reaches 75% of the inlet NO _x concentration after 30 min time-on-stream. Although this catalyst shows fairly high NO _x conversion at 523 K, only ~2.4 wt% out of 20 wt% BaO is converted to Ba(NO₃)₂. Adsorption studies by using NO₂ and NO + O₂ suggest two different NO _x adsorption mechanisms. The NO₂ uptake profile on 2%Pt/20%BaO/Al₂O₃ shows the absence of a complete NO _x uptake period at the beginning of adsorption and the overall NO _x uptake is controlled by the gas–solid equilibrium between NO₂ and BaO/Ba(NO₃)₂ phase. When we use NO + O₂, complete initial NO _x uptake occurs and the time it takes to convert ~4% of BaO to Ba(NO₃)₂ is independent of the NO concentration. These NO _x uptake characteristics suggest that the NO + O₂ reaction on the surface of Pt particles produces NO₂ that is subsequently transferred to the neighboring BaO phase by spill over. At the beginning of the NO _x uptake, this spill-over process is very fast and so it is able to provide complete NO _x storage. However, the NO _x uptake by this mechanism slows down as BaO in the vicinity of Pt particles are converted to Ba(NO₃)₂. The formation of Ba(NO₃)₂ around the Pt particles results in the development of a diffusion barrier for NO₂, and increases the probability of NO₂ desorption and consequently, the beginning of NO _x slip. As NO _x uptake by NO₂ spill-over mechanism slows down due to the diffusion barrier formation, the rate and extent of NO₂ uptake are determined by the diffusion rate of nitrate ions into the BaO bulk, which, in turn, is determined by the gas phase NO₂ concentration.     

Excellent sulfur resistance of Pt/BaO/CeO2 lean NOx trap catalysts

In this work, we investigated the NO_x storage behavior of Pt/BaO/CeO₂ catalysts, especially in the presence of SO₂. High surface area CeO₂ (110 m²/g) with a rod like morphology was synthesized and used as a support. The Pt/BaO/CeO₂ sample demonstrated slightly higher NO_x uptake in the entire temperature range studied compared with Pt/BaO/γ-Al₂O₃. More importantly, this ceria-based catalyst showed higher sulfur tolerance than the alumina-based one. The time of complete NO_x uptake was maintained even after exposing the sample to 3 g/L of SO₂. The same sulfur exposure, on the other hand, eliminated the complete NO_x uptake time on the alumina-based NO_x storage catalysts. TEM images show no evidence of either Pt sintering or BaS phase formation during reductive de-sulfation up to 600 °C on the ceria-based catalyst, while the same process over the alumina-based catalyst resulted in both a significant increase in the average Pt cluster size and the agglomeration of a newly formed BaS phase into large crystallites. XPS results revealed the presence of about five times more residual sulfur after reductive de-sulfation at 600 °C on the alumina-based catalysts in comparison with the ceria-based ones. All of these results strongly support that, besides their superior intrinsic NO_x uptake properties, ceria-based catalysts have (a) much higher sulfur tolerance and (b) excellent resistance against Pt sintering when they are compared to the widely used alumina-based catalysts.     

Deterioration Mode of Barium-Containing NOx Storage Catalyst

Barium-containing NO _x storage catalyst showed serious deactivation under thermal exposure at high temperatures. To elucidate the thermal deterioration of the NO _x storage catalyst, four types of model catalyst, Pt/Al₂O₃, Ba/Al₂O₃, Pt–Ba/Al₂O₃, and a physical mixture of Pt/Al₂O₃ + Ba/Al₂O₃ were prepared and their physicochemical properties such as BET, NO TPD, TGA/DSC, XRD, and XPS were evaluated while the thermal aging temperature was increased from 550 to 1050°C. The fresh Pt–Ba/Al₂O₃ showed a sorption capacity of 3.35 wt%/g-cat. but the aged one revealed a reduced capacity of 2.28 wt%/g-cat. corresponding to 68% of the fresh one. It was found that this reduced sorption capacity was directly related to the deterioration of the NO _x storage catalyst by thermal aging. The Ba on Ba/Al₂O₃ and Pt–Ba/Al₂O₃ catalysts began to interact with alumina to form Ba–Al solid alloy above 600°C and then transformed into stable BaAl₂O₄ having a spinel structure. However, no phase transition was observed in the Pt/Al₂O₃ catalyst having no barium component, even after aging at 1050°C.     

Changes in Ba Phases in BaO/Al2O3 upon Thermal Aging and H2O Treatment

The effects of thermal aging and H₂O treatment on the physicochemical properties of BaO/Al₂O₃ (the NO_x storage component in the lean NO_x trap systems) were investigated by means of X-ray diffraction (XRD), BET, TEM/EDX and NO₂ TPD. Thermal aging at 1000 °C for 10 h converted dispersed BaO/BaCO₃ on Al₂O₃ into low surface area crystalline BaAl₂O₄. TEM/EDX and XRD analysis showed that H₂O treatment at room temperature facilitated a dissolution/reprecipitation process, resulting in the formation of a highly crystalline BaCO₃ phase segregated from the Al₂O₃ support. Crystalline BaCO₃ was formed from conversion of both BaAl₂O₄ and a dispersed BaO/BaCO₃ phase, initially present on the Al₂O₃ support material after calcinations at 1000 and 500 °C, respectively. Such a phase change proceeded rapidly for dispersed BaO/BaCO₃/Al₂O₃ samples calcined at relatively low temperatures with large BaCO₃ crystallites observed in XRD within 10 min after contacting the sample with water. Significantly, we also find that the change in barium phase occurs even at room temperature in an ambient atmosphere by contact of the sample with moisture in the air, although the rate is relatively slow. These phenomena imply that special care to prevent the water contact must be taken during catalyst synthesis/storage, and during realistic operation of Pt/BaO/Al₂O₃ NO_x trap catalysts since both processes involve potential exposure of the material to CO₂ and liquid and/or vapor H₂O. Based on the results, a model that describes the behavior of Ba-containing species upon thermal aging and H₂O treatment is proposed.     

Transient Surface Processes of Storage and Conversion of NOx Species on Pt–Me/Al2O3 Catalysts (Me = Ba,Ce, Cu)

The transient reactivity and surface phenomena of storage and conversion of NO _x species on Pt(1%)–Me/Al₂O₃ catalysts, where Me = Ba, Ce and Cu, were studied by the RWF (rectangular wavefront) method. The Me component has a relevant influence on the processes of surface storage and transformation. The reduction of NO _x by propene in the presence of oxygen is promoted by adding Cu to a Pt/Al₂O₃ catalyst, while cerium promotes transient conversion of NO in the absence of propene, but inhibits the reduction of NO _x in the presence of propene. Copper is suggested to be a promising element to add together with Ba for new NO _x storage-reduction catalysts due to its capacity to act both as a storage element and as promoter for NO _x reduction.     

Influence of the Type of Reducing Agent (H2, CO, C3H6 and C3H8) on the Reduction of Stored NOX in a Pt/BaO/Al2O3 Model Catalyst

In this investigation, a comparative study for a NO _X storage catalytic system was performed focusing on the parameters that affect the reduction by using different reductants (H₂, CO, C₃H₆ and C₃H₈) and different temperatures (350, 250 and 150 °C), for a Pt/BaO/Al₂O₃ catalyst. Transient experiments show that H₂ and CO are highly efficient reductants compared to C₃H₆ which is somewhat less efficient. H₂ shows a significant reduction effect at relatively low temperature (150 °C) but with a low storage capacity. We find that C₃H₈does not show any NO _X reduction ability for NO _X stored in Pt/BaO/Al₂O₃ at any of the temperatures. The formation of ammonia and nitrous oxide is also discussed.     

Steam effect on NO x reduction over lean NO x trap Pt–BaO/Al2O3 model catalyst

The effect of steam on NO _x reduction over lean NO _x trap (LNT) Pt–Ba/Al₂O₃ and Pt/Al₂O₃ model catalysts was investigated with reaction protocols of rich steady-state followed by lean–rich cyclic operations using CO and C₃H₈ as reductants, respectively. Compared to dry atmosphere, steam promoted NO _x reduction; however, under rich conditions the primary reduction product was NH₃. The results of NO _x reduction and NH₃ selectivity versus temperature, combined with temperature programmed reduction of stored NO _x over Pt–BaO/Al₂O₃ suggest that steam causes NH₃ formation over Pt sites via reduction of NO _x by hydrogen that is generated via water gas shift for CO/steam, or via steam reforming for C₃H₈/steam. During the rich mode of lean–rich cyclic operation with lean–rich duration ratio of 60 /20 s, not only the feed NO, but also the stored NO _x contributed to NH₃ formation. The NH₃ formed under these conditions could be effectively trapped by a downstream bed of Co²⁺ exchanged Beta zeolite. When the cyclic operation was switched into lean mode at T < 450 °C, the trapped ammonia in turn participated in additional NO _x reduction, leading to improved NO _x storage efficiency.     

The Effect of a Changing Lean Gas Composition on the Ability of NO2 Formation and NOx Reduction over Supported Pt Catalysts

Three model catalysts (Pt/Al₂O₃, Pt/TiO₂, Pt/V₂O₅/TiO₂) were examined in regard to their NO₂ formation ability under a changing lean gas composition. The results show that the NO to NO₂ oxidation function as well as the NO _x reduction under lean gas conditions is affected by a change in the lean gas atmosphere. The NO oxidation activity also decreased with time, for Pt/Al₂O₃ and Pt/TiO₂, and a possible explanation may be platinum oxide formation. This deactivation was not observed for Pt/V₂O₅/TiO₂.     

Role of Support in Lean DeNOx Catalysis

FTIR and pulse thermal analysis were applied to investigate catalysts containing Pt (1 wt%)/Ba (17 wt%) supported on -Al₂O₃, SiO₂ and ZrO₂. The aim was to learn how the support material affects the thermal stability of barium carbonate and its activity in the reaction to bulk Ba(NO₃)₂. The lower thermal stability of BaCO₃ in alumina supported samples was found to influence the formation of barium nitrate during the NO _x storage process. Quantification of Ba(NO₃)₂ formed during NO _x storage indicated that for alumina supported catalysts only ca. 30% of barium present in the sample is involved in the storage process. The low thermal stability found for alumina supported barium nitrite excludes its role in the formation of barium nitrate during interaction of NO _x with the catalyst at 300 °C. The studies indicate that -Al₂O₃ plays a major role in influencing the thermal stability of BaCO₃ and Ba(NO₃)₂. This finding seems to be relevant for the higher activity of -Al₂O₃-supported catalysts in NO _x storage reduction reactions.     

Performance of potassium-promoted catalysts for NO x and soot removal from simulated diesel exhaust

In order to elucidate the effect of support in the catalytic performance, two selected potassium-promoted catalysts (K1Cu/beta and KCu2/Al₂O₃) were tested for the simultaneous NO _x /soot removal from a simulated diesel exhaust. For comparative purpose, the behaviour of a platinum catalyst (Pt/beta) was also studied. Isothermal experiments revealed that the potassium-promoted catalysts show a high activity for NO _x /soot removal in the 350–450 °C temperature range. In addition, the catalysts present the advantage that the main reaction products are N₂ and CO₂. Among the catalysts tested, KCu2/Al₂O₃ presents the best global performance at 450 °C: the highest soot consumption rate, even higher than the platinum catalysts, and a high NO _x reduction.     

Role of cobalt on γ-Al2O3 based NO x storage catalyst

Co/Pt/Ba/γ-Al₂O₃, Co/Ba/γ-Al₂O₃, Pt/Ba/γ-Al₂O₃, Co/Pt/γ-Al₂O₃, Ba/γ-Al₂O₃, Pt/γ-Al₂O₃, and Co/γ-Al₂O₃ type catalysts were prepared by a conventional impregnation method, and their NO _x storage capacities were evaluated by colorimetric assay. Co-containing catalysts had a higher NO _x storage capacity than that of Co-free counterparts. The role of each component, especially Co, for the catalysts prepared was investigated by using in-situ FTIR. The high NO _x storage for Co-containing catalysts including Co/Ba/γ-Al₂O₃ and Co/Pt/Ba/γ-Al₂O₃ is mainly due to the formation of Co₃O₄ on the catalyst surface identified by XAFS.     

NOx storage capacity,SO2 resistance and regeneration of Pt/(Ba)/CeZr model catalysts for NOx-trap system

NOx storage capacity, sulphur resistance and regeneration of 1wt%Pt/Ce_0.7Zr_0.3O₂ (Pt/CeZr) and 1wt%Pt/10wt%BaO/Ce_0.7Zr_0.3O₂ (Pt/Ba/CeZr) catalysts were studied and compared to a 1wt%Pt/10wt%BaO/Al₂O₃ (Pt/Ba/Al) model catalyst submitted to the same treatments. Pt/Ba/CeZr presents the best NOx storage capacity at 400 °C in accordance with basicity measurements by CO₂ TPD and Pt/CeZr shows the better performance at 200 °C mainly due to a low sensitivity to CO₂ at this temperature. For all samples, sulphating induces a detrimental effect on NOx storage capacity but regeneration at 550 °C under rich conditions generally leads to the total recovery of catalytic performance. However, the nearly complete sulphur elimination is only observed on Pt/CeZr. Moreover, an oxidizing treatment at 800 °C leads to partial sulphates elimination on the Pt/CeZr catalyst whereas a stabilization of sulphates on Ba containing species is observed.     

The Effect of Carbon Monoxide and Hydrocarbons on NOx Storage at Low Temperature

One possible way to reduce NO _x in lean exhausts is by using NO _x trap catalysts. This paper addresses storage of NO _x on such catalysts at temperatures below the catalyst light-off. Experiments carried out on commercial samples in synthetic exhausts revealed a large capacity for storage of NO _x when NO₂ was added at temperatures below 150°C. In contrast, when NO was added instead, no storage took place. CO was found to decrease the storage by reacting with NO₂ and forming NO and CO₂. Propene inhibited the reaction between NO₂ and CO and therefore gave rise to larger NO _x storage when CO was present. The paper concludes with a discussion of a possible mechanism for the storage of NO _x at low temperatures.