FHX-2高速卷烟胶粘剂的制备

通过醋酸乙烯与丙烯酸酯类的共聚制备卷烟接嘴用FHX -2高速卷烟胶粘剂 ,该胶具有初粘力大、干燥速度快、粘接强度高、胶质细腻流动性好 ,废品率低 ,不含有害添加剂 ,可以满足接嘴车速 70 0 0～ 80 0 0支 分钟的要求     

利用洋茉莉醛部分设备转产VA—102卷烟接嘴胶

本文介绍了VA-102高速卷烟接嘴胶性能、质量标准、工艺流程、生产方法。以及利用被迫停产部分洋茉莉醛设备改产VA-102胶的措施和经济效益。     

薄荷型卷烟接嘴胶的制备及其应用

以T5053烟用接嘴胶为主要原料,通过合理添加薄荷香精和SSOS(辛烯基琥珀酸淀粉酯钠),优选出制备薄荷型接嘴胶的最佳配方;然后将该接嘴胶用于卷烟高速接装过程中。研究结果表明:薄荷型接嘴胶的黏度、固含量、pH、粒度、外观特征、储存稳定性等参数均满足卷烟胶的标准要求,其可在卷烟车速为6 000~8 000支/min范围内正常使用,并且粘接效果良好(废品率较低)。薄荷型接嘴胶能赋予卷烟诸多优良特性(如薄荷清凉、嗅香突出、口感舒适纯净、加香效果稳定以及储存稳定性良好等),并且卷烟在抽吸过程中香味释放均匀。     

高速卷烟胶的研制

采用醋酸乙烯酯与丙烯酸酯为原料进行乳液共聚 ,研制出性能优良的高速卷烟胶。对影响产品性能的各种因素进行了探讨     

VAc/AA改性的VAE乳液高速接嘴卷烟胶的研制

介绍了VAc/AA改性的VAE乳液高速接嘴卷烟胶的制备方法。研究了各种因素对胶粘剂性能的影响。结果表明 :VAc/AA用量增加 ,VAE乳液的粘接性能增强。选择与VAE乳液相适应的乳化剂和控制适宜的pH值 ,可以增加VAE乳液的稳定性。采用滴加引发剂和混合单体的方法 ,可以避免过速反应产生及大粒径胶粒生成     

快干卷烟胶用VAc/AA/MMA三元共聚乳液的制备

以醋酸乙烯酯(VAc)、丙烯酸(AA)和甲基丙烯酸甲酯(MMA)等为原料合成了一种快干卷烟胶用三元共聚乳液。以单体配比、聚合温度和保温时间等为主要因素,乳液固含量为考核指标,采用L9(34)正交实验法优选合成三元共聚乳液的最佳工艺条件。实验结果表明,当n(VAc)∶n(MMA)∶n(AA)=4.5∶1.4∶0.1、聚合温度为70℃以及无回流后在92℃左右的保温时间为30min时,所制取的三元共聚乳液的综合性能较好,其固含量为38.42%,黏度为1120mPa·s,并且完全满足快干卷烟胶的使用要求。     

FC—Ⅰ型高速卷烟接嘴胶的研制

介绍了以醋酸乙烯酯和丙烯酸酯为主要原料，研制出具有初粘性好、干燥速度快、粘接强度高、胶质细腻的高速卷烟接嘴胶，并探讨了各种因素对产品性能的影响。     

FC—I型高速卷烟接嘴胶的研制

介绍了以醋酸乙烯酯和丙烯酸酯为主要原料，研制出具有初粘性好，干燥速度快，粘接强主高，胶质细腻的高卷烟接嘴胶，并探讨了各种因素对产品性能的影响。     

卷烟胶生产中黏度的控制

卷烟胶主要品种是卷烟搭口胶、卷烟接嘴胶,均由PVAC乳液、VAE乳液及其改性体构成。卷烟搭口胶的保护胶体含量较低、乳液粒子的成型是影响旋转黏度测定值的主要因素,卷烟接嘴胶的保护胶体含量较高,保护胶体的含量是影响涂-4杯黏度值的主要因素。旋转黏度与涂-4杯黏度对比测定控制生产的卷烟胶,旋转黏度值与涂-4杯黏度值波动范围小,卷烟胶用于卷烟机时,使用连续性和胶体流动性好,卷烟机的平均车速高于用单一旋转黏度控制生产的卷烟胶。     

WHT-1型高速卷烟通用胶粘剂的制备

<正> 卷烟胶包括高速卷烟接嘴胶、高速中缝搭口胶、高速包装胶、滤棒胶、贴税花胶等,其种类繁多,名称较复杂,其中尤以高速接嘴卷烟胶、高速     

溶液共混法制备聚氨酯／碳纳米管复合材料及其性能

 通过强酸处理方法对碳纳米管进行改性处理并对其结构和分散稳定性进行分析。采用溶液共混法制备了聚氨 酯/碳纳米管复合材料,利用FTIR对其结构进行了分析,探讨了碳纳米管对复合材料力学性能、热稳定性能以及弹 性回复率的影响。结果表明,碳纳米管经酸处理后添加了羧酸活性基团,提高了其在溶剂中的分散性|在复合材料 中,碳纳米管以较强氢键与大分子连接,复合材料的力学性能和热稳定性能都有所提高,而弹性回复率没有受到很 大影响。     

PVC抗冲改性机理和新型PVC冲击改性剂的设计

对PVC冲击改性剂——MBS、CPE和ACR的分子组成和分子结构进行了分析,研究了其抗冲改性机理及对PVC制品低温冲击强度、耐候性、维卡软化点、韧性的影响。从高分子热力学的角度分析了CPE和ACR在PVC中分散所形成的制品结构。指明了传统ACR和CPE在PVC改性中所存在的优缺点。在此基础上分析了理想冲击改性剂ACR应具有的结构特点,并设计和开发了新型冲击改性剂ACRHL-56和HL-58,通过试验对其性能与传统冲击改性剂ACR和CPE进行了比较,发现其性能远优于后者。     

非平衡等离子体水处理技术研究进展

回顾了高压脉冲电源的发展概况,对现行研究中使用的非平衡等离子体水处理反应器进行了分类,系统总结了液相、气相和气液两相放电反应器的研究现状,指出了待改进之处和发展趋势。归纳了脉冲放电过程中催化剂的使用状况,分析了催化剂在脉冲放电过程中的作用,指出了不同催化剂在使用过程中存在的问题及进一步研究的方向。     

聚氨酯/碳纳米管复合材料的制备及其性能研究

通过强碱球磨方法对多壁碳纳米管(MWCNTs)进行了改性处理,并对其化学结构和微观形态进行了分析.采用溶液共混法制备了聚氨酯(PUR)/MWCNTs复合材料.利用扫描电子显微镜、傅立叶变换红外光谱仪对其进行了表征.探讨了MWCNTs对PUR/MWCNTs复合材料力学性能、热稳定性以及电导率的影响.结果表明,MWCNTs...     

Repair bond strength of resin composite with experimental primers – effect of formulation variables

The aim of this study was to prepare experimental resin-based primers with varied components (silane – S, polyacrylic acid – PA, or methacrylic acid – MA) and evaluate their repair bonding ability to resin composite. Primers were prepared containing methacrylate monomers, acidic monomer, ethanol, photoinitiators and 0, 10, or 20 wt% of S, PA, or MA. Degree of C=C conversion and pH were measured. Composite blocks (Opallis, FGM) were aged by 5000 thermal cycles and composite cylinders (repairs) were built up on their surfaces. The cylinders were tested under shear stress after 24 h. Failure modes were classified under magnification. Data were statistically analyzed at α = 0.05. Primers containing MA were the most acidic compositions, whereas S-containing primers were less acidic. Incorporation of 20 wt% of the varied components decreased C=C conversion. PA-based primers had higher C=C conversion than MA-based materials. Repair bond strength results were dependent on the component added and its concentration. MA-based primers presented higher bond strength than primers containing PA. Cohesive failures within composite were predominant for S-based primers, whereas mixed failures were more prevalent for PA-based primers. In conclusion, the overall best repair abilities were observed for primers containing 10 wt% of the components tested.     

偶氮苯甲酸类衍生物的合成、表征及光学性能研究

设计合成了三种偶氮苯甲酸类化合物,产率均达84%以上.通过元素分析、1H NMR、MS及红外光谱对产物进行了表征,结果与预期产物吻合.通过紫外光谱和荧光光谱研究化合物的光学性能,发掘偶氮苯甲酸类化合物的光学特性与应用.     

预应力FRP抗弯加固混凝土梁性能研究

采用嵌入式CFPR筋和外贴碳/玄武岩纤维混杂布加固混凝土梁,设计比较了对加固材料施加预应力后的增强效果,共进行了6根梁的4点弯曲试验,并就计算结果和试验结果进行了验证,提出了设计方法.结果表明：相比于无预应力加固,施加预应力后能够进一步提升梁的开裂荷载和屈服荷载,并提高梁的服役性能.计算结果和试验结果比较吻合.     

我国微生物法水处理技术的研究进展

介绍了微生物絮凝剂的基本研究方法,综述了4种絮凝机理,对其絮凝效果的因素进行了探讨,阐述了微生物絮凝剂在众多领域的应用情况,指出了微生物絮凝剂在生产过程中的现存问题和解决措施,微生物絮凝剂具有高效、无毒,无二次污染、成本低等优点,为水处理技术的研究和发展提供了一个新的方向.     

水稻抽穗前后施用农药情况对稻米中农药残留量的影响研究

水稻抽穗前、后施药的时期,农药种类,施药剂量与次数和稻米的安全性密切相关。供试的有机磷农药除敌敌畏未检出外,其余农药都在稻米中残留,残留量三唑磷〉乙酰甲胺磷〉甲胺磷〉毒死蜱〉吡虫啉〉敌敌畏。水稻抽穗前用药2次,甲胺磷、三唑磷均超标;用药3次,毒死蜱残留量与国家标准相当,乙酰甲胺磷未达标。上述农药剂量提高1倍,残留量提高30％～50％,用药2次除毒死蜱外,残留量均超过国家标准。水稻抽穗后用药,农药残留量明显提高,甲胺磷、乙酰甲胺磷、三唑磷、毒死蜱常规剂量用药2次,除乙酰甲胺磷未超标外,其余残留量都高于国家标准。吡虫啉抽穗前后使用,其残留量均低于食品中最高允许标准。农药残留量与糙米贮存期有关,一般贮存90d后,农药残量即低于允许残留标准。降低农药施用次数,适当降低用药量,尽量选择抽穗前用药,选用高效、安全、低残留农药,是无公害水稻生产中的重要措施。     

Performance of Dowel-Welded L-joints for Wood Furniture

Rotationally welded wood dowels were used to hold together step butt and mortise and tenon L-joints and these joints were tested against European Norms for these types of joints. A factorial experiment was carried out in which (1) these two types of joints were tested, (2) 4 or 6 dowels per joint were used, (3) dowels were inserted at either 45° or 90° to the surface of the wood, (4) two types of wood were used, beech and European ash, and (5) two types of tests were carried out, namely compression and tension tests. The strength results were used to find out which of these were the most important individual parameters and their interactions, namely type of joint, number of dowels, and type of test. The strength results were well in excess of the relevant L-joints standard specifications for wooden windows.