有机硅改性聚丙烯酸酯静电植绒黏合剂

采用种子乳液聚合法,以无羟甲基活性单体为交联剂,有机硅乳液为种子乳液,合成核壳型有机硅改性丙烯酸酯静电植绒黏合剂,并通过红外光谱和差示扫描量热法表征了自制聚合物的结构。试验研究了上胶量、有机硅用量及焙烘温度对植绒效果的影响,结果表明,当控制上胶量为250 g/m2,有机硅用量为15%,60℃预烘5 min,80℃焙烘4 min时,所得植绒织物可达到较高的植绒牢度(≥6 100次),各项指标均达到FZ/T 64011—2001《静电植绒织物》优等品的标准。     

苯乙烯改性静电植绒黏合剂SA

采用预乳化种子乳液聚合法制备苯乙烯改性丙烯酸酯类静电植绒黏合剂SA.通过系统研究苯乙烯单体含量、乳化剂质量分数与配比对单体转化率、聚合稳定性、胶膜吸水性和胶接抗剥离性能的影响,确定了合成工艺:苯乙烯质量分数为单体总量的8％,乳化剂[m(平平加O)∶m(SDS)=2∶1]为单体总量的3％,制得的SA外观呈乳白泛蓝光乳液.用其制备的静电植绒织物耐磨性试验大于6 000次,静电压小于2000V,各项指标均达到FZ/T 64011-2001《静电植绒织物》优等品标准.     

无皂黏合剂乳液的合成及其在静电植绒中的应用

为克服传统乳液聚合中游离乳化剂的存在影响黏合剂粘着力等缺点,采用可聚合乳化剂——马来酸酐脂肪醇聚氧乙烯醚单酯化物合成了无皂丙烯酸酯黏合剂乳液,优化了无皂黏合剂乳液的聚合工艺,采用FT-IR、激光粒度仪、TEM和DSC对乳液进行了表征。结果表明：乳液粒子粒径分布均匀,乳液耐电解质性能较好,乳液膜耐水性有所改善。将该乳液用于静电植绒,分析植绒工艺因素与植绒牢度等关系,结果表明,无皂黏合剂的粘着性能良好,植绒织物的植绒牢度达到2000次以上,符合植绒服装面料的牢度要求。     

静电植绒粘合剂DS的合成及应用

通过半连续种子乳液聚合法,采用双丙酮丙烯酰胺(DAAM)作为交联单体,研制出静电植绒粘合剂DS.用红外分析表征了DS的结构,研究了乳液聚合过程中乳化剂用量与配比、引发剂用量及交联单体用量对单体转化率和凝聚率等性能的影响,确定了较佳的合成工艺:乳化剂2.5%,引发剂0.4%,DAAM 3%;产品应用于静电植绒,效果较佳,所得植绒织物植绒牢度4 000次,手感柔软,半衰期1 s,抗静电性能优良,各项指标均达到了静电植绒织物FZ/T 64011-2001一等品的标准.     

静电植绒技术及其应用

静电植绒是静电技术应用的一个方面。近几年我国静电植绒在家纺行业中的应用,本文着重介绍静电植绒原理、工艺、设备以及原材料等有关静电植绒技术的应用,并探讨静电植绒的家纺新产品开发。     

静电植绒的现状与发展趋势

文章介绍了国内外静电植绒业的发展现状,静电植绒的原理、工艺及材料的选择及静电植绒业的发展趋势。     

静电植绒技术及其在我国的发展

介绍了静电植绒技术的原理和工艺流程，讨论了静电植绒的关键技术，概述了我国静电植绒技术的发展状况，并展望了静电植绒的开发趋势和前景。     

静电植绒纸的加工方法

本文介绍了静电植绒原理和其加工方法.     

YC—1静电植绒交联剂的配制与应用

简要介绍了交联剂的应用原理和现状,以及静电植绒用交联剂应有的技术质量要求,并在此基础上,重点阐述了ＹＣ－１交联剂的配制和应用实践及其效益分析。     

静电植绒粘合剂FS-496的合成及应用

采用反应性乳化剂和特殊交联单体，以种子乳液聚合法合成了静电植绒粘合剂FS-496；并应用于100％涤纶经编起毛布的静电植绒工艺，介绍了应用该粘合剂时的涂胶、静电植绒、烘干固化和柔软整理等工艺条件。结果表明，使用该粘合剂得到的植绒产品手感柔软，弹性好，悬垂性佳，并具有很好的摩擦牢度，各项技术指标均达到设计要求。     

Preparation and application of low-temperature-curable,alkylphenol ethoxylate-free,and flame-retardant flocking adhesive

In this study, a low temperature-curable and alkylphenol ethoxylate-free acrylic emulsion was synthesized with diacetone acrylamide (DAAM) and adipic dihydrazide (ADH) as a crosslinking system; butyl acrylate (BA), ethyl acrylate (EA), methyl methacrylate (MMA), and acrylic acid (AA) as monomers; vinyl siloxane as a modifier; sodium-dodecyl sulphate (SDS) and AEO-9 as a compound emulsifier by means of semicontinuous emulsion polymerization. The optimal polymerization conditions by weight proportion determined by the orthogonal experiments were emulsifier amount, 4%, initiator amount, 0.5%, DAAM amount, 2.5%, and core–shell ratio, 3/2. Three flame-retardant additives, namely, ammonium polyphosphate (APP), FR-5, and organic montmorillonite, were mixed with the acrylic emulsion to synthesize the flocking adhesive SA. The char length, afterglow time, and afterflame time of the flocking fabrics were characterized to evaluate the fire-retardant properties of the adhesives. The results clearly evidence an outstanding improvement in fire-retardant properties using adhesive SA based on good flocking fastness and fabric handle.     

植绒织物植绒密度的分析研究

讨论了外加电压值U、极板距离d、植绒时间t、纤维种类、纤维长度L、纤维细度D、纤维喂入量M07个变量下植绒绒面密度的变化,实验发现纤维长度、纤维细度和电压值对植绒密度有较显著的影响,其中纤维长度的影响最大。     

静电植绒简介

介绍了静电植绒的原理及植绒绒毛加工使用情况，阐述静电植绒产品的应用与开发，指出静电植绒产品可广泛应用于家纺、服装、汽车内饰、绝缘材料、防污防蚀材料、防伪材料等方面。     

苯乙烯/丙烯酸酯共聚物的共混型阻燃黏合剂

采用预乳化种子乳液聚合工艺合成苯乙烯/丙烯酸酯共聚物黏合剂,并在黏合剂中添加无机阻燃剂聚磷酸铵(APP),以制备共混型阻燃黏合剂(BSA).系统研究了APP用量、添加APP时引发剂用量、反应温度对乳液稳定性、胶膜抗剥离性和涂层阻燃性的影响;并利用热重分析仪(rG)测试了BSA的热性能.结果表明,当APP用量为黏合剂总量的8％,引发剂用量为单体总量的0.4％,乳液聚合温度为80℃时,制备的BSA稳定,且在保证抗剥离性能的同时具有良好的阻燃性能.     

超细协同阻燃剂的制备及应用

对几种无机阳燃剂的超细化和复配用传统轧烘-焙方法对棉织物进行整理，确定聚磷酸铵与氢氧化镁起协同阳燃时可取得较为理想的效果，并确定协同配比[质量比m（聚磷酸铵）：m（氢氧化镁）]为5：1，阻燃剂用量在（22～24）g／100g整理腹，粘合剂用量为12g时，阳燃效果最佳，且织物的白度、断裂强力及撕破强力下降较小，符合阻燃整理的要求．     

氨基硅油改性丙烯酸酯黏合剂的合成及在芳纶印花中的应用

针对涂料印花用丙烯酸酯黏合剂出现的手感发硬及耐摩擦色牢度差等问题,合成了氨基硅油改性丙烯酸酯黏合剂,并对黏合剂乳液及胶膜进行了性能测试.结果表明,氨基硅油改性丙烯酸酯黏合剂乳液平均粒径为91.79 nm,转化率为92.33％,凝胶率为2.52％,表面张力为29.47 mN/m,胶膜玻璃化温度10.5℃,质量损失50％时...